Mechanical Properties and Fracture Toughness of α-Al2O3-Platelet-Reinforced Y-PSZ Composites at Room and High Temperatures

YPSZ/Al₂O₃-platelet composites were fabricated by conventional and tape-casting techniques followed by sintering and HIPing. The room-temperature fracture toughness increased, from 4.9 MPa·m^1/2 for YPSZ, to 7.9 MPa·m^1/2 (by the ISB method) for 25 mol% Al₂O₃ platelets with aspect ratio = 12. The room-temperature fiexural strength decreased 21% and 30% (from 935 MPa for YPSZ) for platelet contents of 25 vol% and 40 vol%, respectively. Al₂O₃ platelets improved the high-temperature strength (by 110% over YPSZ with 25 vol% platelets at 800°C and by 40% with 40 vol% platelets at 1300°C) and fracture toughness (by 90% at 800°C and 61% at 1300°C with 40 vol% platelets). An amorphous phase at the Al₂O₃-platelet/YPSZ interface limited mechanical property improvement at 1300°C. The influence of platelet alignment was examined by tape casting and laminating the composites. Platelet alignment improved the sintered density by >1% d _th , high-temperature strength by 11% at 800°C and 16% at 1300°C, and fracture toughness by 33% at 1300°C, over random platelet orientation.     

Transformation, Microstructure Development, and Densification in α-Fe2O3-Seeded Boehmite-Derived Alumina

Addition of α-Fe₂O₃ seed particles to alkoxide-derived boehmite sols resulted in a 10-fold increase in isothermal rate constants for the transformation of γ- to α-Al₂O₃. Changes in porosity and surface area with sintering temperature showed no effect of seeding on coarsening of the transition alumina gels, but the 200-fold decrease in surface area associated with transformation to α-Al₂O₃ occurred ∼ 100°C lower in seeded gels compared with unseeded materials. As a result of high nucleation frequency and reduced microstructure coarsening, fully transformed seeded alumina retained specific surface areas >22 m²/g and exhibited narrow pore size distributions, permitting development of fully dense, submicrometer α-Al₂O₃ at ∼ 1200°C.     

Transformation Strengthening of β"Al2O3 with Tetragonal ZrO2

The solid sodium electrolyte β"-Al₂O₃ (Li-stabilized) was strengthened with additions of tetragonal ZrO₂ (15 vol%). The conductivity of this composite material, measured in an Na/Na cell, was 7.7 Ω· at 300°C. Average values of strength and the critical stress intensity factor were 350 MPa and 4.5 MPa·m_1/2, respectively, for the sintered composite material.     

Growth of Tabular α-Al2O3 Grains on Porous Alumina Substrate

Gradient, porous alumina ceramics were prepared with the characteristics of microsized tabular α-Al₂O₃ grains grown on a surface with a fine interlocking feature. The samples were formed by spin-coating diphasic aluminosilicate sol on porous alumina substrates. The sol consisted of nano-sized pseudo-boehmite (AlOOH) and hydrolyzed tetraethyl orthosilicate [Si(OC₂H₅)₄]. After drying and sintering at 1150°–1450°C, the crystallographic and chemical properties of the porous structures were investigated by analytical electron microscopy. The results show that the formation of tabular α-Al₂O₃ grains is controlled by the dissolution of fine Al₂O₃ in the diphasic material at the interface. The nucleation and growth of tabular α-Al₂O₃ grains proceeds heterogeneously at the Al₂O₃/glass interface by ripening nano-sized Al₂O₃ particles.     

Spark-Plasma Sintering of Silicon Carbide Whiskers (SiCw) Reinforced Nanocrystalline Alumina

The combined effect of rapid sintering by spark-plasma-sintering (SPS) technique and mechanical milling of γ-Al₂O₃ nanopowder via high-energy ball milling (HEBM) on the microstructural development and mechanical properties of nanocrystalline alumina matrix composites toughened by 20 vol% silicon carbide whiskers was investigated. SiC_w/γ-Al₂O₃ nanopowders processed by HEBM can be successfully consolidated to full density by SPS at a temperature as low as 1125°C and still retain a near-nanocrystalline matrix grain size (∼118 nm). However, to densify the same nanopowder mixture to full density without the benefit of HEBM procedure, the required temperature for sintering was higher than 1200°C, where one encountered excessive grain growth. X-ray diffraction (XRD) and scanning electron microscopy (SEM) results indicated that HEBM did not lead to the transformation of γ-Al₂O₃ to α-Al₂O₃ of the starting powder but rather induced possible residual stress that enhances the densification at lower temperatures. The SiC_w/HEBMγ-Al₂O₃ nanocomposite with grain size of 118 nm has attractive mechanical properties, i.e., Vickers hardness of 26.1 GPa and fracture toughness of 6.2 MPa·m^1/2.     

Influence of Cr and Fe on Formation of α-Al2O3 from γ-Al2O3

The effect of Cr and Fe in solid solution in γ-Al₂O₃ on its rate of conversion to α-Al₂O₃ at 1100°C was studied by X-ray diffraction. The δ form of Al₂O₃ was the principal intermediate phase produced from both pure γ-Al₂O₃ and that containing Fe³⁺ in solid solution, although addition of Fe greatly reduced crystallinity. Reflectance spectra and magnetic susceptibilities showed that Cr exists as Cr⁶⁺ in γ-Al₂O₃ and as Cr³⁺ in α-Al₂O₃, with θ-Al₂O₃ as the intermediate phase. The intermediates formed rapidly, and the rates of their conversion to α-Al₂O₃ were increased by 2 and 5 wt% additions of Fe and decreased by 2 and 4 wt% additions of Cr. An approximately linear relation observed between α-Al₂O₃ formation and decrease in specific surface area was only slightly affected by the added ions. This relation can be explained by a mechanism in which the sintering of δ- or θ-Al₂O₃, within the aggregates of their crystallites, is closely coupled with conversion of cubic to hexagonal close packing of O^2- ions by synchro-shear.     

Pulse Electric Current Sintering of Al2O3/3 vol% ZrO2 with Constrained Grains and High Strength

The pulse electric current sintering technique (PECS) was demonstrated to be effective in rapid densification of fine-grained Al₂O₃/3Y-ZrO₂ using available commercial powders. The composites attained full densification (>99% of TD) at 1450°C in less than 5 min. The composites sintered at a high heating rate had a fine microstructure. The incorporation of 3 vol% 3Y-ZrO₂ substantially increased the average fracture strength and the toughness of alumina to as high as 827 MPa and 6.1 MPa·m^1/2, respectively. A variation in the heating rate during the PECS process influenced grain size, microstructure, and strength, though there was little or no variation in the fracture toughness.     

Critical Surface Energies of Al2O3 and Graphite

Based on the wetting properties of a -Al₂O₃, and pyrolytic graphite by liquid metals, the critical surface energy for spreading was determined and compared with the surface energy of the ceramics. The surface energy γ-₈ (ergs/cm²) of the (0001) surface of a -Al₂O₃ is estimated to be 892–0.12 T (°C), that of the c plane of pyrolytic graphite 1139–0.13 T (°C), and that of the a plane of pyrolytic graphite 1300–0.17 T (°C). Also, the liquid-solid interfacial energies were calculated and found compatible with the values reported in the literature. The surface energy of liquid Ag or liquid Cu is not significantly affected by carbon.     

Seeding with γ-Alumina for Transformation and Microstructure Control in Boehmite-Derived α-Alumina

The dehydration, transformation, and densification of boehmite (γ-AlOOH) are enhanced by addition of γ-Al₂O₃ seed particles. α-Al₂O₃ microstructures with uniform 1- to 2-μm grain size and sintered densities 98% of theoretical are achieved at 1300°C Thermal analysis shows that γ-Al₂O₃ seed particles transform to α-Al₂O₃ before the matrix, thus controllably nucleating the transformation of θ-AI₂O₃ to α-Al₂O₃.     

Synthesis of Nanocrystalline Aluminum Nitride by Nitridation of δ-Al2O3 Nanoparticles in Flowing Ammonia

Nanocrystalline aluminum nitride (AlN) with surface area more than 30 m²/g was synthesized by nitridation of nanosized δ-Al₂O₃ particles using NH₃ as a reacting gas. The resulting powders were characterized by CHN elemental analysis, X-ray diffraction (XRD), Fourier transform infrared spectra, X-ray photoelectron spectra, field-emission scanning electron microscopy, transmission electron microscopy, and Brunauer–Emmett–Teller surface area techniques. It was found that nanocrystalline δ-Al₂O₃ was converted into AlN completely (by XRD) at 1350°–1400°C within 5.0 h in a single-step synthesis process. The complete nitridation of nanosized alumina at relatively lower temperatures was attributed to the lack of coarsening of the initial δ-Al₂O₃ powder. The effect of precursor powder types on the conversion was also investigated, and it was found that α-Al₂O₃ was hard to convert to AlN under the same conditions.     

Synthesis of AlN Nanopowder from γ-Al2O3 by Reduction–Nitridation in a Mixture of NH3–C3H8

Aluminum nitride (AlN) powders were synthesized by gas reduction–nitridation of γ-Al₂O₃ using NH₃ and C₃H₈ as the reactant gases. AlN was identified in the products synthesized at 1100°–1400°C for 120 min in the NH₃–C₃H₈ gas flow confirming that AlN can be formed by the gas reduction–nitridation of γ-Al₂O₃. The products synthesized at 1100°C for 120 min contained unreacted γ-Al₂O₃. The ²⁷A1 MAS NMR spectra show that Al–N bonding in the product increases with increasing reaction temperature, the tetrahedral AlO₄ resonance decreasing prior to the disappearance of the octahedral AlO₆ resonance. This suggests that the tetrahedral AlO₄ sites of the γ-Al₂O₃ are preferentially nitrided than the AlO₆ sites. AlN nanoparticles were directly formed from γ-Al₂O₃ at low temperature because of this preferred nitridation of AlO₄ sites in the reactant. AlN nanoparticles are formed by gas reduction–nitridation of γ-Al₂O₃ not only because the reaction temperature is sufficiently low to restrict grain growth, but also because γ-Al₂O₃ contains both AlO₄ and AlO₆ sites, by contrast with α-Al₂O₃ which contains only AlO₆.     

Nanocrystalline α-Al2O3 Using Sucrose

Nanocrystalline α-Al₂O₃ ceramic powders have been prepared from an aqueous solution of aluminum nitrate and sucrose. Soluble Al ion-sucrose solution forms the precursor material once it is completely dehydrated. Heat treatment of the dehydrated precursors at low temperature (600°C) results in the formation of porous single-phase α-Al₂O₃. The precursor and heat-treated powders have been characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and BET surface area analysis. The phase-pure nanocrystalline α-Al₂O₃ particles had an average specific surface area of >190 m²/g, with an average pore size between 18 and 25 nm.     

Fabrication, Mechanical Properties, and Electrical Conductivity of Co3O4 Ceramics

Well-densified Co₃O₄ ceramics (98.3% of theoretical) have been fabricated by the combined use of hot pressing (800°C/I h/30 MPa) and hot isostatic pressing (880°C/2 h/196 MPa). Their Vickers hardness and fracture toughness are 10.3 GPa and 4.2 MPa·m^1/2, respectively. They exhibit a high electrical conductivity of 3.35 × 10' S·cm⁻¹ at 800°C.     

Toughening and Strengthening of NiAl with Al2O3 by the Addition of ZrO2(3Y)

NiAl/10-mol%-ZrO₂(3Y) composites of almost full density have been fabricated via spark plasma sintering (SPS) for 10 min at 1300°C and 30 MPa. The former intermetallic compound, which contains a trace amount of Al₂O₃, has been prepared via self-propagating high-temperature synthesis. The composite microstructures are such that tetragonal ZrO₂ (∼0.2 μm) and Al₂O₃ (∼0.5 μm) particles are located at the grain boundaries of the NiAl (∼46 μm) matrix. Improved mechanical properties are obtained: the fracture toughness and bending strength are 8.8 MPa·m^1/2 and 1045 MPa, respectively, and high strength (>800 MPa) can be retained up to 800°C.     

Sol–Gel Processed Y-PSZ Ceramics with 5 wt% Al2O3

Y-PSZ ceramics with 5 wt% Al₂O₃ were synthesized by a sol–gel route. Experimental results show that powders of metastable tetragonal zirconia with 2.7 mol% Y₂O₃ and 5 wt% Al₂O₃ can be fabricated by decomposing the dry gel powder at 500°C. Materials sintered in an air atmosphere at 1500°C for 3 have high density (5.685 g/cm³), high content of metastable tetragonal zirconia (>96%), and high fracture toughness (8.67 MPa.m^1/2). Compared with the Y-PSZ ceramics, significant toughening was achieved by adding 5 wt% Al₂O₃.     

Growth of Single-Crystal and Polycrystalline Thin Films of MgAl2O4 and MgFe2O4

Single-crystal and polycrystalline films of Mg-Al₂O₄ and MgFe₂O₄ were formed by two methods on cleavage surfaces of MgO single crystals. In one procedure, aluminum was deposited on MgO by vacuum evaporation. Subsequent heating in air at about 510°C formed a polycrystalline γ-Al₂O₈ film. Above 540°C, the γ-Al₂O, and MgO reacted to form a single-crystal MgAl₂O₄ film with {001} MgAl₂O₄‖{001} MgO. Above 590°C, an additional layer of MgAl₂O₄, which is polycrystalline, formed between the γ-Al₂O₃ and the single-crystal spinel. Polycrystalline Mg-Al₂O₄ formed only when diffusion of Mg²⁺ ions proceeded into the polycrystalline γ-Al₂O₃ region. Corresponding results were obtained for Mg-Fe₂O₄. MgAl₂O₄ films were also formed on cleaved MgO single-crystal substrates by direct evaporation, using an Al₂O₃ crucible as a source. Very slow deposition rates were used with source temperatures of ∼1350°C and substrate temperatures of ∼800°C. Departures from single-crystal character in the films may arise through temperature gradients in the substrate.     

Mechanical Properties of CoAl Materials with the Combined Additions of ZrO2(3Y) and Al2O3

Intermetallic CoAl powder has been prepared via self-propagating high-temperature synthesis (SHS). Dense CoAl materials (99.6% of theoretical) with the combined additions of ZrO₂(3Y) and Al₂O₃ have been fabricated via spark plasma sintering (SPS) for 10 min at 1300°C and 30 MPa. The microstructures are such that tetragonal ZrO₂ (0.3 μm) and Al₂O₃ (0.5 μm) particles are located at the grain boundaries of the CoAl (8.5 μm) matrix. Improved mechanical properties are obtained; especially the fracture toughness and the bending strength of the materials with ZrO₂(3Y)/Al₂O₃= 16/4 mol% are 3.87 MPa·m^1/2 and 1080 MPa, respectively, and high strength (>600 MPa) can be retained up to 1000°C.     

Fabrication of Hard and Strong α/β-Si3N4 Composites With MgSiN2 as Addivitives

α/β-Si₃N₄ composites with various α/β phase ratios were prepared by hot pressing at 1600°–1650°C with MgSiN₂ as sintering additives. An excellent combination of mechanical properties (Vickers indentation hardness of 23.1 GPa, fracture strength of about 1000MPa, and toughness of 6.3 MPa·m^1/2) could be obtained. Compared with conventional Si₃N₄-based ceramics, this new material has obvious advantages. It is as hard as typical in-situ-reinforced α-Sialon, but much stronger than the latter (700 MPa). It has comparable fracture strength and toughness, but is much harder than β-Si₃N₄ ceramics (16 GPa). The microstructures and mechanical properties can be tailored by choosing the additive and controlling the heating schedule.     

Effect of Monovalent Cation Additives on the γ-Al2O3-to-α-Al2O3 Phase Transition

The effect of monovalent cation addition on the γ-Al₂O₃-to-α-Al₂O₃ phase transition was investigated by differential thermal analysis, powder X-ray diffractometry, and specific-surface-area measurements. The cations Li⁺, Na⁺, Ag⁺, K⁺, Rb⁺, and Cs⁺ were added by an impregnation method, using the appropriate nitrate solution. β-Al₂O₃ was the crystalline aluminate phase that formed by reaction between these additives and Al₂O₃ in the vicinity of the γ-to-α-Al₂O₃ transition temperature, with the exception of Li⁺. The transition temperature increased as the ionic radii of the additive increased. The change in specific surface area of these samples after heat treatment showed a trend similar to that of the phase-transition temperature. Thus, Cs⁺ was concluded to be the most effective of the present monovalent additives for enhancing the thermal stability of γ-Al₂O₃. Because the order of the phase-transition temperature coincided with that of the formation temperature of β-Al₂O₃ in these samples, suppression of ionic diffusion in γ-Al₂O₃ by the amorphous phase containing the added cations must have played an important role in retarding the transition to α-Al₂O₃. Larger cations suppressed the diffusion reaction more effectively.     

Analytical Electron Microscope Analysis of the Formation of BaO · 6Al2O3

The formation process of barium hexaaluminate (BaO 6Al₂O₃) from BaCO₃/γ-Al₂O₃ powders or hydrolyzed alkoxides was studied by analytical electron microscopy. Barium hexaaluminate is produced by a two-step solid-state reaction from BaCO₃ and Al₂O₃ via formation of BaO·Al₂O₃. Marked grain growth and inclusion of nonequilibrium phase were inevitable in this powder mixture process. However, in an alkoxide-derived precursor, homogeneous mixing of components is attained and hence the formation of BaO·6Al₂O₃ proceeds readily. Powders obtained by this latter route consisted of fine planar particles with a uniform size and retained a large surface area (20.2 m²/g) even after heating at 1300°C. Electron diffraction results implied that suppression of crystal growth along the c axis is the reason for the large surface area of BaO·6Al₂O₃.