稳定剂对环保型无铅无镉釉上彩熔剂性能影响的研究

在碱-硼-硅系统基础熔剂中引入稳定剂，运用正交实验方法对无铅无镉釉上彩熔剂性能进行研究。通过化学稳定性、堆烧、粘度测试、印花彩烤等一系列对比试验，研究了稳定剂ZrO2、ZnO、SnO2和TiO2的最佳引入量。实验结果表明：在基础熔剂配方的基础上。稳定剂ZrO2的最佳引入量为6％；SnO2引入量不应超过5％；ZnO引入量10％为最好；TiO2引入1％的最低水平即可，8#为本研究中的最佳配方。     

低铋环保型无铅釉上彩熔剂的研究

在碱-硼-硅系统基础熔剂中引入外加剂,通过多种碱金属、碱土金属及外加剂等复合效应来代替铅在熔剂中的作用进而研制低铋环保型无铅熔剂。并通过对试样进行化学稳定性、热膨胀性、光泽度、堆烧、粘度测试、印花彩烤等一系列对比实验考察所用外加剂对熔剂性能的影响。实验结果表明:在基础熔剂配方的基础上外加剂氧化铋、氧化镧、氧化钼、氧化钨的外加量分别控制在5%,1%,1.25%,1%时即可满足熔剂各种性能要求。     

氧化硼对环保型无铅无镉釉上彩熔剂性能影响的研究

运用正交实验方法对无铅无镉釉上彩熔剂性能进行研究。通过化学稳定性、堆烧、粘度测试、印花彩烤等一系列对比试验考察了B2O3的加入量、SiO2/Al2O3及SiO2/B2O3的影响。试验结果表明最优条件为:B2O3加入量为22.32%;SiO2/Al2O3为11.05;SiO2/B2O3为1.81。     

低铋环保型无铅釉上彩熔剂的制备研究

在碱-硼-硅系统基础熔剂中引入外加剂,通过多种碱金属、碱土金属及外加剂等复合效应来代替铅在熔剂中的作用进而研制低铋环保型无铅熔剂.并通过对试样进行化学稳定性、热膨胀性、光泽度、堆烧、粘度测试、印花彩烤等一系列对比实验考察所用外加剂对熔剂性能的影响.实验结果表明:在基础熔剂配方的基础上外加剂氧化铋、氧化镧、氧化钼、氧化钨的外加量分别控制在5%、1%、1.25%、1%时即可满足熔剂各种性能要求.     

助熔助色剂对无铅无镉釉上彩熔剂性能的影响

用正交实验法研究了在碱.硼.硅系统基础熔剂中, 外加助熔助色成分MgO、CaO、SrO、BaO四种碱土金属氧化物的添加量及R2O:RO、SrO:CaO、RO:SiO2对无铅无镉釉上彩熔剂性能的影响规律.综合考虑熔剂的熔融性能、化学稳定性、彩烤效果等,对上述影响因素的最佳值进行了讨论.     

釉上彩红色颜料熔剂的研制

以碱-硼-硅系为基础,加入锶-氟复合助溶助色剂,研制了适应红色色剂的无铅无镉熔剂。其彩烤温度范围为680-820℃,对红色色剂呈色鲜艳明快稳定,光泽度好,耐酸性强,铅镉溶出符合ISO6486-2：1999（E）标准,完全能达到铅熔剂的效果。     

CeO2对无铅低温熔剂结构和性能的影响

采用传统熔融-水淬法制备了碱硼硅酸盐(ABS)低温熔剂.探讨了加入CeO2对ABS无铅低温熔剂性能的影响规律;对样品进行了XRD、FTIR、热膨胀分析,从结构上阐释了其性能变化的原因.结果表明:当加入CeO2的量在1.48 mol％-3.12 mol％之间时,熔剂中逐渐析出Ce(BO2)3,当加入量达到3.9 mol％...     

碱金属氧化物对cBN陶瓷结合剂性能的影响

综述了碱金属氧化物对cBN陶瓷结合剂性能的影响。从目前国内外cBN陶瓷结合剂的研究现状来看,高性能结合剂需满足以下条件：有较高的本征强度;结合剂耐火度控制在700℃-800℃;结合剂热膨胀系数略高于cBN磨粒的热膨胀系数,且需抑制降温过程中的相变;高温下结合剂要有较好的流动性和对cBN磨粒有较好的润湿性。     

MgO/(CaO+MgO)对碱硼硅酸盐系统低温熔剂耐磨性的影响

通过调整MgO/(CaO+MgO)摩尔比(简写为:RMg),探讨了混合碱土金属效应对ABS无铅低温熔剂的耐磨性及相关的光泽度、光泽损失、维氏硬度、热膨胀系数等性能的影响规律;对样品进行了 XRD、FTIR、SEM及热膨胀分析,从结构上阐释了其性能变化的原因.结果表明:在ABS熔剂结构中存在[SiO4]、[BO4]、[B...     

SiO2/Al2O3摩尔比对无毒低温釉上彩熔剂性能的影响

本文探讨了不同SiO2/Al2O3摩尔比对碱-硼-硅(ABS)系统无毒低温熔剂耐蚀性、光泽度、热膨胀系数等性能的影响规律;并采用SEM、FT-IR分析技术,对熔剂进行表征,从结构方面阐释了其性能变化的原因.结果表明:当n(SiO2)/n(Al2O3)取值范围为8～8.5时,熔剂的耐蚀性强、光泽度好、热膨胀系数低,原因是在此取值范围内熔剂结构中[BO3]伸缩振动峰和弯曲振动峰比较窄,即此时熔剂中的[BO3]数量较少,试样的显微结构更致密所致.     

金属氧化物对金属光泽釉呈色的影响

本文采用佛山地区通用原料，通过正交实验，得出了金属光泽釉的最佳组成。实验发现MnO2是发色主要氧化物；使色差减小的氧化物可同时增加光泽度。与以前金属釉配方相比，所需铅的含量大为降低。     

过渡金属氧化物掺杂钛酸钡取代位置及价态的研究

从BaTiO3的晶体结构出发,分析了固溶能和晶格畸变对不同价态的过渡金属离子掺杂BaTiO3时取代位置的影响。分析结果表明:Ti4+离子在BaTiO3晶体结构中具有一定的几何松散度,Cr3+、Fe3+、Co3+和Ni2+离子半径与Ti4+的接近,取代Ti位的固溶能均较小;大量实验结果表明,掺杂前后晶格常数的变化与取代Ti位的理论结果相吻合;过渡金属(Cr、Fe、Co和Ni)氧化物掺杂BaTiO3时分别以Cr3+、Fe3+、Co3+和Ni2+取代Ti位掺杂。确定某种贱金属氧化物在BaTiO3中的具体取代位置对制备抗还原的贱金属内电极的BaTiO3基MLCC有重要意义。     

THE EFFECT OF THICKENER ON THE RHEOLOGY OF COATING COLORS

The effect of type and amount of thickener on the shear and extensional rheological properties of paper coating colors was studied. A coarse delaminated kaolin clay was used as pigment and either a carboxy methylcellulose (CMC) or an associative gum was used as thickener. The shear properties were evaluated with a stress controlled rheometer and the extensional properties were obtained at high strain rates using an orifice flow meter. The apparent extensional viscosity was compared to the shear viscosity in terms of the Trouton ratio, which was shown to exceed considerably the theoretical value of 3 expected for Newtonian fluids. Suspensions formulated with the associative gum exhibited more pronounced strain hardening at high strain rates than those prepared with CMC.     

THE EFFECT OF THICKENER ON THE RHEOLOGY OF COATING COLORS

The effect of type and amount of thickener on the shear and extensional rheological properties of paper coating colors was studied. A coarse delaminated kaolin clay was used as pigment and either a carboxy methylcellulose (CMC) or an associative gum was used as thickener. The shear properties were evaluated with a stress controlled rheometer and the extensional properties were obtained at high strain rates using an orifice flow meter. The apparent extensional viscosity was compared to the shear viscosity in terms of the Trouton ratio, which was shown to exceed considerably the theoretical value of 3 expected for Newtonian fluids. Suspensions formulated with the associative gum exhibited more pronounced strain hardening at high strain rates than those prepared with CMC.     

掺铈新型氧化物系统无公害釉上颜料用熔剂的研制

研制了掺铈新型氧化物系统无公害釉上颜料用熔剂。用Y-4型X-射线衍射仪、ZA-P型高温显微镜、SP-1000电脑测色分光光度计、WGG-60型微机光泽度仪和RPZ-1型晶体管式自动热膨胀仪研究了其相组成、始熔温度、彩烤效果、光泽度、热膨胀性和化学稳定性等方面的性质,分析了不同氧化铈添加量对熔剂性能产生的影响。结果表明,氧化铈的外加量在0.25%～0.5wt%范围内,能较好地改善熔剂的热膨胀性、花面呈色和光泽度,对耐酸性没有影响。     

论色彩在陶瓷艺术肌理中的作用与运用

陶瓷艺术肌理按其所处部位及作用可分为胎肌理、釉肌理和彩肌理三大类型,有着各自不同的审美特征及演变历程。色彩在其中发挥着举足轻重的作用,是其不可或缺的最重要组成因素之一。在陶瓷艺术肌理的色彩运用中,陶瓷艺术家需要有良好的工艺、审美和文化基础,并依据一些原则及采取切实有效的实施策略。     

用X射线衍射仪剖析金属熔剂产品方法探讨

用Ｘ射线衍射仪系统地剖析了金属熔剂产品,试验从粒度分布、水溶性、物相组成与含量等方面进行了综合分析,不仅避免了常规化学分析只能检测元素组成与含量的缺点,而且避免了只注重元素组成不重视样品粒度组成与分布的问题,从而保证了金属熔剂产品质量稳定、使用性能优良可靠     

湿式催化氧化处理炼油碱渣废水试验研究

采用200L／d湿式催化氧化(CWO)小型工业试验装置对碱渣废水进行处理试验研究,结果表明CWO技术装置对处理碱渣废水(COD39600～139200mg／L、挥发酚3900～34500mg／L)具有良好的技术可行性。在270℃、9MPa的条件下,该废水经处理后(催化反应时间60～90min),废水中COD、挥发酚的去除率可达到98％以上,处理水中的COD浓度可低于1000mg／L、挥发酚浓度可低于排放标准值(0．5mg／L),而且脱色除臭效果良好。