采用熔盐法在钼基体上制备硅化钼涂层的结构

采用熔盐法在钼基体上制备了硅化钼涂层,利用SEM、EDS和XRD等分析了涂层的显微结构、元素分布及物相组成,并研究了硅化钼的生成机制。结果表明:硅化钼是通过反应扩散形成的,涂层由外至内分别为MoSi2、Mo5Si3和基体;当熔盐中Na2SiF6和NaF两种活化剂共存时,涂层的厚度较大,1 000℃保温10h制备的硅化钼涂层的高温抗氧化性能相对较好;涂层厚度随温度的升高和保温时间的延长而增加,但温度的影响比保温时间的更显著。     

熔盐法制备镁橄榄石轻质保温隔热材料的物相及性能

以Na2CO3和不同粒径的镁橄榄石粉(分别为44,74,250μm)为主要原料,采用熔盐法分别在900,1 000,1 050,1 100℃下烧结制备了镁橄榄石轻质保温隔热材料,研究了镁橄榄石粉粒径和烧结温度对所制备材料物相组成、密度和抗压性能的影响。结果表明:所有试样的主要物相均为Mg2SiO4、Na2MgSiO4和MgO,但各物相的含量不同;烧结温度越高,镁橄榄石粉粒径越小,烧结试样的显气孔率越低,体积密度越大,抗压强度越高;粒径为74μm的镁橄榄石粉为原料经1 000℃烧结后得到的试样有比较好的气孔分布和较高的强度,其体积密度为1.76g·cm-3,抗压强度为12.31MPa。     

V2O5掺杂对ZnNb2O6介质陶瓷性能的影响

采用传统的固相反应法制备了V2O5掺杂ZnNb2O6介质陶瓷,借助XRD、SEM和LCR测试仪等研究了陶瓷的烧结特性及介电性能.结果表明V2O5掺杂能有效地降低ZnNb2O6陶瓷的烧结温度,提高介电常数,改善频率温度系数,但介电损耗有所增加.经1050℃烧结,1.0%V2O5掺杂的ZnNb2O6陶瓷具有较好的介电性能,εr=28,tanδ=0.000 6,τf=-42.50×10-6℃-1.     

Y2O3对45钢表面激光熔覆镍基合金的影响

研究了Y2O3对镍基合金激光熔覆层显微组织、相结构以及性能的影响。结果表明加入Y2O3的镍基激光熔覆层显微组织细小均匀，且不出现微裂纹。熔覆层形成的物相有Fe-C，Fe-B和NiCrFe等。与纯镍基熔覆层相比，加入Y2O3的镍基熔覆层显微硬度有较大提高，其耐磨性能比淬火和软氮化后明显提高；加稀土的激光合金化比不加稀土的激光合金化的耐磨性要有所提高。     

Y2O3对镍基碳化钛金属陶瓷熔覆层组织的影响

利用 HTWY180-MK 激光焊接机在45*钢基体表面熔覆了含Y2O3,的镍基 TiC 金属陶瓷复合涂层,研究了稀土Y2O3,对激光熔覆镍基金属陶瓷复合涂层组织及性能的影响.结果表明:在镍基金属陶瓷复合层中加入一定量的稀土氧化物Y2O3,可有效改善熔覆层的组织及性能,减少复合涂层中的裂纹、孔洞、杂质,加速熔覆层中 TiC 颗粒的溶解,并改善了 TiC 颗粒的形状,同时使得激光熔覆层的组织及硬度更加均匀.在本文所述试验条件下,熔覆层中添加稀土氧化物Y2O3,最佳质量分数为0.5%.     

磁控溅射法制备ZrW2O8薄膜及其性能

利用射频磁控溅射法在单晶硅片和石英基片上沉积了非晶态ZrW2O8薄膜,对不同温度下热处理的薄膜进行了XRD分析;用扫描电镜观察了薄膜的表面形貌,用阻抗分析仪和分光光度计分别研究了薄膜的介电性能和透光性能.结果表明:非晶态薄膜在740℃热处理3 min可以制得具有较好负热膨胀特性的ZrW2O8薄膜,其热膨胀系数为-2.54×10-5 /℃;介电常数和介电损耗均随着频率的增加而减小;在可见光范围内薄膜的透光率达75%.     

La2O3对ZL108镍基激光熔覆层摩擦学性能的影响

利用激光在ZL108的表面上熔覆镍基自熔合金粉末,并对添加和不添加La2O3的熔覆层进行检测和比较。结果表明,添加La2O3可以提高熔覆层的硬度、耐磨性,降低摩擦因数。La2O3对改善熔覆层的摩擦学性能起到了较大的帮助。     

La2O3对AZ91D镁合金表面激光熔覆Al-Cu涂层的影响

试验采用Nd:YAG 激光器在AZ91D镁合金表面激光熔覆不同La2O3含量的Al-Cu涂层,借助扫描电子显微镜、能谱仪、X射线衍射仪、显微硬度计和滑动磨损试验机,分析稀土对熔覆层表面形貌、显微组织、物相结构、显微硬度和耐磨性能的影响。研究结果表明：稀土氧化物La2O3在Al-Cu涂层中能够细化晶粒,改善熔覆层的质量,并生成稀土化合物Mg17La2和LaAl3;当添加质量分数为1.2%的La2O3时,熔覆层组织均匀,晶粒细小,显微硬度最高;添加La2O3的熔覆层的平均摩擦因数比镁基体和未添加La2O3的熔覆层的平均摩擦因数小,说明稀土氧化物能够减小熔覆层的摩擦因数,提高涂层的耐磨性。     

Bi_2O_3基电解质抗还原性测量与研究

本文对Bi_2O_3基固体电解质的抗还原性进行了测量和进一步的研究,实验发现,在Bi_2O_3-Y_2O_3系统中掺入B_2O_3,可抑制Bi_2O_3的还原,原因是B~(3+)改变了晶体中的应力状态和点缺陷的分布。本研究可促进Bi_2O_3基固体电解质的实用化。     

316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为

采用浸没法腐蚀试验研究了在真空及空气两种环境中316L不锈钢在700℃熔融LiCl-3%Li2O混合熔盐中的热腐蚀行为.结果表明:316L不锈钢在两种条件下的腐蚀产物均为LiCrO2,腐蚀质量损失均随时间的延长而增大;在真空条件下腐蚀质量损失明显小于空气条件下,氧分压对腐蚀行为的影响显著.     

Multiferroic behavior of the functionalized surface of a flexible substrate by deposition of Bi2O3 and Fe2O3

Thin films of bismuth and iron oxides were obtained by atomic layer deposition (ALD) on the surface of a flexible substrate poly(4,4′-oxydiphenylene-pyromellitimide) (Kapton) at a temperature of 250°C. The layer thickness was 50 nm. The samples were examined by secondary-ion mass spectrometry, and uniform distribution of elements in the film layer was observed. Surface morphology, electrical polarization, and mechanical properties were investigated by atomic force microscope, piezoelectric force microscopy, and force modulation microscopy. The values of current in the near-surface layer varied in the range of ±80 pA when a potential of 5 V was applied. Chemical analysis was performed by X-ray photoelectron spectroscopy, where the formation of Bi₂O₃ and Fe₂O₃ phases, as well as intermediate phases in the Bi–Fe–O system, was observed. Magnetic measurements were carried out by a vibrating sample magnetometer that showed a ferromagnetic response. The low-temperature method of functionalization of the Kapton surface with bismuth and iron oxides will make it possible to adapt the Bi–Fe–O system to flexible electronics.     

无机盐先驱体溶胶-凝胶法制备Al2O3薄膜的研究

用无机盐先驱体，溶胶-凝胶工艺在氧化铝基工程陶瓷上成功制备了Al2O3薄膜。用差热分析（DTA）、扫描电子显微镜（SEM）、X射线衍射（XRD）、二次离子质谱（SIMS）等手段对Al2O3薄膜的物相组成、表面和断面形貌及界面结构进行了分析。结果表明：制备的薄膜完整，内部无明显的宏观缺陷：Al2O3晶粒均匀，主要物相为a-Al2O3；基体中的元素在薄膜中有明显的扩散，有助于提高界面结合强度。     

复合电铸Ni-La2O3纳米复合材料的组织结构和性能

采用复合电铸工艺制备了不同La2O3纳米颗粒含量的Ni—La2O3纳米复合材料，用扫描电子显微镜和X射线衍射仪观察分析了纳米复合材料的表面形貌及组织结构，与电沉积纯镍作对比研究了纳米复合材料的显微硬度和耐磨损性能。结果表明，由于La2O3纳米颗粒的存在，导致Ni-La2O3纳米复合材料的组织结构发生了改变，它比纯镍沉积层具有更高的显微硬度及耐磨性，且La2O3纳米颗粒质量分数越大，纳米复合材料的显微硬度越高，耐磨性越好。     

SHS/PHIP法制备的Ti3AlC2陶瓷的可加工性

研究了用SHS/PHIP技术制备的Ti3AlC2层状陶瓷的可加工性及其机理。结果表明,Ti3AlC2陶瓷具有自润滑结构、室温显微塑性以及高电导率,用普通高速钢刀具即可进行切削加工,也可采用电火花等特种加工方式进行机械加工。     

B位替代对Bi_2(Zn_(1/3)Nb_(2/3))O_7陶瓷介电性能的影响

采用传统的二次球磨固相反应法制备了Bi2(Zn1/3 Nb2/3-x)O7(M为Sn,Zr,Ti)陶瓷,并使用X射线衍射仪、扫描电镜、介电性能测试仪等研究了Sn4+,Zr4+,Ti4+的B位替代对陶瓷烧结温度、物相、显微形貌以及介电性能的影响.结果表明:当替代量x≤0.25时,所得陶瓷均保持单一的单斜焦绿石相结构;Zr4+,Ti4+什替代的陶瓷达到最致密的烧结温度与未经替代的一致,而Sn4+替代的陶瓷在1 020℃烧结才可以达到最致密;用Ti4+,Zr4+替代的陶瓷晶粒尺寸与基体的相当,而Sn4+替代的陶瓷晶粒尺寸大小不一;Sn4+,Zr4+替代的陶瓷介电常数温度系数随着替代量的增加逐渐减小,Sn4+替代的陶瓷在x=0.25时为负值,Ti4+替代的陶瓷介电常数温度系数随着替代量的增加先增大后减小,但始终为正值.     

烧结助剂La2O3含量对热压烧结制备Si3N4-AlN复相陶瓷性能的影响

以Si3N4和AlN为原料,La2O3为烧结助剂,在氮气气氛和1 800℃、30 MPa压力下热压烧结保温1 h制备出了Si3N4-AlN复相陶瓷,研究了La2O3含量对复相陶瓷烧结性能、抗弯强度、热导率及介电损耗的影响.结果表明:随La2O3含量的增加,复相陶瓷的孔隙率先减小然后趋于稳定,Si3N4由α相向β相逐渐转...