利用商业软件Flow-3D,模拟了A356合金半固态触变压铸和普通压铸的充型流动过程。模拟结果表明:相同模具结构中的半固态压铸和普通压铸充型过程,半固态流动平稳,普通压铸由于湍流流动,因而容易出现气孔、卷气夹杂等缺陷。半固态触变压铸和普通压铸具有相同的流动通道。 相似文献
3.
4.
5.
对近期国内外铝合金半固态触变成形过程的数值模拟进行了系统的论述,介绍了数值模拟过程中用到的基本假设和模型建立方法以及数值模拟模型的建立过程,并对铝合金半固态触变成形过程的数值模拟的发展进行了展望. 相似文献
6.
7.
8.
9.
半固态合金触变铸造数值模拟方法的研究 总被引:13,自引:2,他引:13
总结了铸造成形过程常用的数值模拟方法,分析了半固态合金触变铸造的主要特点,认为局部网格细化的拉格朗日法比尤拉法更适合于半固态合金触变铸造过程的数值模拟。对其算法进行了探讨,并给出了一个算例。 相似文献
10.
针对高固相率条件下半固态触变锻造成形,开发了一个热力耦合触变锻造模拟模型.对触变锻造成形过程中温度场分布、最高/最低温度分布规律以及成形过程中模具运动速度对成形力的影响规律等,进行了计算和分析.研究发现,在半固态触变锻造成形过程中常伴有低于半固态温度的热加工现象出现,高成形速度会降低成形力,同时也会导致成形坯料的液固相分离.试验验证中最大成形力与模拟得到的最大成形力相吻合的事实表明,所开发的计算模型能较准确地预测触变锻造成形最大成形力, 但成形过程中两者所得到的成形力仍存在一定差异,这表明计算模型还需要一步优化. 相似文献
11.
1 INTRODUCTIONSincethethixotropic propertiesofvigorouslystirredtin leadslurrieswerediscoveredbySpenceretal[1] atMIT ,investigationandapplicationofthese mi solidtechnologyhavebeendevelopedquickly .Thestudyontheapparentviscosityisnotonlyoftheoreti calbutalsoofutilizationsignificance .Manyinvesti gatorshavecarriedoutagreatdealofexperimentalresearchandputforwardmanymathematicalmodelsofthesemi solidapparentviscosity .Someofthesemodels ,whicharerelatedto popularexponentialfunctionandaclassica… 相似文献
12.
铝合金半固态感应加热的计算机模拟 总被引:11,自引:0,他引:11
根据实际条件确定了感应加热线圈的计算结构和材料的有关参数, 应用改进的商业ANSYS软件, 采用一维轴对称模型对铝合金中频感应加热温度及其分布进行了模拟. 结果表明, 在大功率和小功率的加热条件下, 模拟结果与实测结果均相当吻合. 相似文献
13.
采用包套挤压成形方法,成功地实现了不锈钢与半固态铝合金的连接与成形。采用数值模拟与试验相结合的方法,研究了不锈钢包套的变形行为以及铝合金固相率、挤压比对材料复合后界面强度和组织性能的影响,采用光学显微镜对界面组织结构进行了观察分析。结果表明,在大挤压比的情况下不锈钢包套破裂发生在凹模出口处,界面剪切强度随挤压比的增大而提高,固相率为30%时达到最大值;铝合金固相组织与低熔点液相组织以一定比例交替与不锈钢表面接触,由于液相扩散能力大于固相成分,从而形成非均匀扩散的新型界面组织。 相似文献
14.
半固态加工技术及应用 总被引:111,自引:24,他引:87
金属半固态成形作为21世纪一种近净成形新技术,愈来愈引起人们的广泛关注,为了推动该技术在我国工业中应用,从理论研究,坯料制备、二次(重熔)加热、成形工艺、国外应用的最新进展及发展趋势等方面进行了分析和讨论,指出半固态加工技术在我国汽车、电子和军工等领域潜在的应用前景,并阐明应采取的对策。 相似文献
15.
Mensuration and simulation of mold filling process in semi-solid die-cast of aluminum alloy 总被引:1,自引:0,他引:1
To understand the flow trace of semi-solid slurry in mold cavity, some thermocouples were inserted in mold cavity, and the reaction timing of thermocouples showed the arrival of fluid. The filling time and rate were estimated by comparison between the experiment and calculation. The introduction of computer simulation technique based on ADSTEFAN was to predict injectionforming process and to prevent defects during trial manufacture of various parts. By comparing the formed appearance of parts in experiment and in simulation, and observing the relationship between internal defects inspected by X-ray or microscope and the flow field obtained in simulation, it was indicated that both have quite good agreement in simulation and experiment. Right predictions for cast defects resulted from mold filling can be carried out and proper direction was also proposed. The realization of numerical visualization for filling process during semi-solid die-cast process will play an important role in optimizing technology plan. 相似文献
16.
液相线半连续铸造7075铝合金触变成型力的工程法求解 总被引:1,自引:0,他引:1
采用工程法和近似塑性条件dσr=dσz, 并将接触面假设为混合摩擦条件, 对液相线半连续铸造法获得的7075铝合金半固态浆料的触变成型力进行了计算. 计算结果表明 在变形的开始阶段, 成型力为32kN; 在变形的终了阶段, 成型力为667.09kN, 与实测结果721kN基本符合. 相似文献
17.
半固态复合熔铸过程中SiC与2A11合金的润湿性 总被引:5,自引:1,他引:4
研究了SiC增强铝基复合材料的半固态法制备, 分析了SiC颗粒与基体金属之间的润湿性, 提出了解决SiC颗粒与基体金属之间润湿的措施. 结果表明 将SiC颗粒进行高温处理, 在其表面涂覆K2ZrF6, 在2A11合金熔体中添Mg元素, 可改变SiC与铝基体的浸润性. 相似文献
18.
19.
半固态铝合金触变成形流场的模拟仿真 总被引:11,自引:1,他引:10
从流变学基本方程出发 ,使用MAGMASOFT Version3.1软件 ,模拟半固态铝合金触变成形过程的流场分布、温度场。对比模拟值与试验中的不同阶段的充型试样。将计算机模型控制点的模拟温度和压力与试验中的测量值进行对比。 相似文献
20.
The new filling system is smooth filling without gas gap.It works well in avoiding the generation of defects such as porosity and inclusion.The pouring basin,sprue,runner and the gate of the bolster casting were designed according to the principle of the new filling system.The filling and solidification process of the bolster casting were also simulated.It was found that the filling process was smooth,and air entrapment and shrinkage were avoided.Finally,a further validation of the new filling system of bolster casting was carried out in a foundry. 相似文献