轧机牌坊激光熔覆修复研究

为找寻一种合适的轧机牌坊表面修复方法,根据实际工况,对几种激光熔覆涂层在150℃水蒸气环境中的抗氧化性能及抗磨损性能进行了测试分析,测试结果表明,制备的钴基涂层具有优异的抗水蒸气氧化性能和抗摩擦磨损性能。选用该钴基材料在牌坊模拟件上模拟现场施工状况进行了激光熔覆,同时监测了熔覆过程中的动态应力演变。监测结果表明,应力演变最大值并未超过基体铸钢的屈服强度,这种大面积激光熔覆不会引起结构的宏观变形,表明激光熔覆方法是一种适用于轧机牌坊大面积表面修复的方法。     

激光熔覆技术在轧机牌坊修复中的应用

针对秦皇岛首秦金属材料有限公司粗轧机牌坊上的机架辊定位槽两侧面磨损、腐蚀较严重的问题,采用激光熔覆在线修复技术对机架辊定位槽进行了修复,修复后涂层表面基本无腐蚀磨损现象,年磨损量约0.1 mm,完全满足使用要求。     

激光熔覆修复齿轮轴工艺研究

采用激光熔覆工艺对某船用减速齿轮箱齿轮轴的磨损齿面进行尺寸修复.为制定合理的修复方案,建立了齿轮轴齿面激光熔覆温度场模型,通过计算分析,结合样块试验,确定了修复过程中的激光熔覆主要工艺参数;选用单向送粉双向扫描的熔覆方法,解决了熔覆层开裂的问题;针对计算结果中出现的齿面进出端和齿顶热集中效应和热冲击效应引起的过烧现象,提出了搭接熔覆和包覆熔覆的熔覆工艺,较好地消除了过烧现象.最终在磨损轮齿上得到了厚度达0.7mm质量稳定的优质熔覆层,完成了磨损轮齿的尺寸修复.该激光熔覆工艺可为类似的修复问题提供借鉴和指导.     

磨损零件的激光熔覆修复实验研究

研究采用激光熔覆方法修复磨损的零件,将2Cr12基体材料与激光熔覆后的F321合金进行磨损对比实验的结果表明,激光熔覆后的F321合金的耐磨性是基体材料2Cr12的5倍,被修复的2Cr12零件其耐磨性大大提高.在较软的合金粉末中添加硬质相如WC等陶瓷颗粒时,可大大提高软性合金粉末的耐磨性.激光熔覆由软合金和硬质颗粒组成的复合粉末,能使硬质颗粒分散均匀.激光熔覆316L不锈钢熔覆层的实验表明,熔覆层内的硬度分布较均匀.     

激光熔覆修复单螺杆挤压机螺杆的试验研究

单螺杆挤压机螺杆磨损后，选用Ｎｉ６０Ｂ合金粉末，并经氧乙炔焰喷涂和激光重熔后，熔覆合金层硬度可达到超过原基体材料的硬度，涂层与基体之间形成冶金结合，可满足零件性能要求。     

激光熔覆修复技术研究进展

介绍了激光熔覆修复技术的应用概况,并对激光熔覆修复工艺、激光熔覆专用铁基粉末进行了分析和综述,指出了激光熔覆修复的发展方向。     

轴类部件表面镍基合金激光熔覆 修复层力学性能研究

核电设备用轴类部件经常由于磨损或腐蚀导致性能退化,从而影响到设备和电站的安全运行。利用激光熔敷技术修复受损部件,使其达到或超过原来的服役性能要求,可为电厂节省大量维修和采购成本。针对材质为410马氏体不锈钢的电机转轴,选用镍基合金C276粉末对轴表面缺陷进行激光熔覆修复,并取样进行硬度和抗拉强度测试,以评估熔覆修复层的力学性能。结果表明,C276熔覆修复层在室温下硬度较410不锈钢提高约20%,抗拉强度提高约7%,但塑韧性有所下降。     

激光熔覆修复单螺杆挤压机螺杆的试验研究

单螺杆挤压机螺杆磨损后，选用Ni60B合金粉末，并经氧乙炔焰喷涂和激光重熔后，熔覆合金层硬度可达到或超过原基体材料的硬度，涂层与基体之间形成冶金结合，可满足零件性能要求。     

激光熔覆修复技术的基础试验研究

激光熔覆修复是近年来迅速发展的一项有许多突出优点的零件修复技术,文章对该技术进行了基础性的试验研究,模拟实际零件的修复情况,通过在基体材料上加工一个"U"形缺口并用激光熔覆技术进行修复.把激光熔覆修复件制作成力学性能试件,获得了相关的试验数据,并对试验结果进行了分析,为激光熔覆修复技术的实际工程应用提供了理论依据.     

激光熔覆修复Z形导杆的研究

进口的Cr12MoV高碳高合金钢Z形导杆磨损后,选用Ni60A合金粉末,经氧乙炔焰喷涂和激光重熔处理后,熔覆合金层硬度可达到或超过原基体材料的硬度,而且合金层结构致密、晶粒细小,涂层与基体之间形成冶金结合,可满足零件性能要求。     

激光熔覆硬韧材料齿面的电解磨削

某重载履带车辆侧减速器主动齿轮磨损后,应用激光熔覆技术制备Fe-Mn-C呈亚稳奥氏体组织的熔覆修复层.齿面熔覆层在加工过程中,因表层发生应变诱发马氏体相变而使材料呈硬韧特性,难以完成加工.为此,通过改进专用的加工设备、开发实用的电解磨削溶液,优化了电解磨削工艺参数,解决了硬韧材料齿面的加工难题,其磨削效率高(9个齿18个齿面在120 min左右即可完成),齿面粗糙度Ra达0.4μm～0.2 μm.     

激光熔覆技术

概括地介绍了激光熔覆技术的机理、材料体系、工艺参数及国内外发展现状。     

激光熔覆技术

概括地介绍了激光熔覆技术的机理、材料体系、工艺参数及国内外发展现状。     

激光熔覆工艺参数对单道熔覆层宏观尺寸的影响

研究了扫描速度、送粉速率对单道熔覆层的宽度、高度及单道熔覆层接触角的影响。结果表明,熔覆层的宽度、高度随扫描速率的增大而减小;熔覆层的宽度随送粉速率的改变变化不大;熔覆层的高度随送粉速率的增加而增加;接触角随熔覆层高宽比的改变而变化。     

激光熔覆层力学性能评价方法的研究

提出了采用改进的拉伸试验来评价激光熔覆层力学性能的新方法。它可以比较快速而准确地综合反映激光熔覆层的力学性能。     

In Situ Production of Hard Metal Matrix Composite Coating on Engineered Surfaces Using Laser Cladding Technique

The growing need for high wear-resistant surface with enhanced physical properties has led to extensive researches in the field of surface engineering. Laser cladding emerged to be a promising method to achieve these objectives in a cost-effective way. The present paper studies the viability of cladding of tungsten disulfide (WS₂) powder by using 400 W continuous-wave fiber laser. WS₂ was used as a coating material, which was decomposed at higher temperature and underwent several chemical reactions. By this process, in situ formation of metal matrix composites and hard face coating on the substrate surface were attained. The characterization of laser cladded surface was done to study its morphological, microstructural, mechanical and tribological properties. It was observed that cladding of WS₂ powder on 304 SS resulted in the formation of Cr-W-C-Fe metal matrix composite having improved mechanical and tribological properties. The value of microhardness of the coated surface was found to increase three to four times in comparison with the parent material surface. Wear test results indicated a decrease in wear by 1/9th (maximum) as compared to the parent 304 SS surface. The volume fractions of tungsten particles on the cladded surface were also investigated through EDS analysis.     

High-Power Laser Beam Cladding

This paper reports major advances in the understanding, refinement and application of high-power laser beam cladding. The most important relationships between essential laser process variables and clad characteristics are defined. The unmatched control of energy inherent in laser beam processing has satisfied challenging, requirements in material cladding applications. Significant refinements in control of optics, substrate and consumables are reported. Unprecedented applications, such as cladding of copper on steel and cladding within confined space envelopes, highlight the technical advantages of the laser process and underscore rewards of investments in laser metalworking development.     

国外激光熔覆设备

国外激光熔覆使用的激光器类型有CO2激光器、灯泵浦Nd:YAG激光器、二级管泵浦Nd；YAG激光器和二极管激光器，开发了多种合金材料供给设备，诸如同轴送粉系统，三料斗送粉系统，送丝系统等，使用众多种类的反射式、透射式和光纤传输的匀光光束处理系统，研制了熔覆过程激光束各参量、送粉率、粉末束流的浓度和温度分布以及熔池行为等的在线监控系统，从而保证了熔覆质量的稳定性和复重性。     

激光熔覆技术的研究进展

综述了激光熔覆技术的原理、工艺特点和熔覆材料的选择,分析了激光熔覆技术的应用范围,对其未来的发展方向作了展望.