Frictional behavior and wear resistance performance of gradient cermet composite tool materials sliding against hard materials

Gradient cermet composites possessing high surface hardness, flexural strength and interface bonding strength were fabricated using vacuum hot-pressing sintering. Ball-on-disk tests were performed to investigate the tribological properties of the gradient cermet composites against 440 C stainless steel, Al₂O₃ and Si₃N₄ balls at different sliding speed and load in comparison with traditional Ti(C,N) cermets. The tribological behavior was characterized in terms of friction coefficient and wear rate. The results showed that friction coefficient was significantly dependent on the sliding speed and load when sliding against Al₂O₃ and Si₃N₄. However, there was no obvious relation between them during sliding against 440 C stainless steel due to the formation of metal adhesive layer. Gradient cermet composites exhibited a higher friction coefficient but lower wear rate than traditional Ti(C,N) cermets. The main wear mechanism of gradient cermet composites was adhesion wear during sliding against 440 C stainless steel, while abrasion wear was the predominant mechanism during sliding against Al₂O₃ and Si₃N₄. It was expected that gradient cermet composites would be excellent candidates for cutting tool materials.     

The influence of different SiC amounts on the microstructure,densification, and mechanical properties of hot-pressed Al2O3-SiC composites

The hot pressing process of monolithic Al₂O₃ and Al₂O₃-SiC composites with 0-25 wt% of submicrometer silicon carbide was done in this paper. The presence of SiC particles prohibited the grain growth of the Al₂O₃ matrix during sintering at the temperatures of 1450°C and 1550°C for 1 h and under the pressure of 30 MPa in vacuum. The effect of SiC reinforcement on the mechanical properties of composite specimens like fracture toughness, flexural strength, and hardness was discussed. The results showed that the maximum values of fracture toughness (5.9 ± 0.5 MPa.m^1/2) and hardness (20.8 ± 0.4 GPa) were obtained for the Al₂O₃-5 wt% SiC composite specimens. The significant improvement in fracture toughness of composite specimens in comparison with the monolithic alumina (3.1 ± 0.4 MPa.m^1/2) could be attributed to crack deflection as one of the toughening mechanisms with regard to the presence of SiC particles. In addition, the flexural strength was improved by increasing SiC value up to 25 wt% and reached 395 ± 1.4 MPa. The scanning electron microscopy (SEM) observations verified that the increasing of flexural strength was related to the fine-grained microstructure.     

Fabrication and mechanical properties of Al2O3-SiCw-TiCnp ceramic tool material

Whiskers and nanoparticles are usually used as reinforcing additives of ceramic composite materials due to the synergistically toughening and strengthening mechanisms. In this paper, the effects of TiC nanoparticle content, particle size and preparation process on the mechanical properties of hot pressed Al₂O₃-SiC_w ceramic tool materials were investigated. The results showed that the Vickers hardness and fracture toughness of the materials increased with the increasing of TiC content. The optimized flexural strength was obtained with TiC content of 4 vol% and particle size of 40 nm. The particle size has been found to have a great influence on flexural strength and small influence on hardness and fracture toughness. It was concluded that the flexural strength increased remarkably with the decreasing of the TiC particle size, which was resulted from the improved density and refined grain size of the composite material due to the dispersion of the smaller TiC particle size. SEM micrographs of fracture surface showed the whiskers to be mainly distributed along the direction perpendicular to the hot-pressing direction. The fracture toughness was improved by whisker crack bridging, crack deflection and whisker pullout; the TiC nanoparticles in Al₂O₃ grains caused transgranular fracture and crack deflection, which improved the flexural strength and fracture toughness with whiskers synergistically. Uniaxial hot-pressing of SiC whisker reinforced Al₂O₃ ceramic composites resulted in the anisotropy of whiskers’ distribution, which led to crack propagation differences between lateral crack and radical crack.     

Microstructure,mechanical properties and toughening mechanisms of graphene reinforced Al2O3-WC-TiC composite ceramic tool material

The low fracture toughness of Al₂O₃-based ceramics limited their practical application in cutting tools. In this work, graphene was chosen to reinforce Al₂O₃-WC-TiC composite ceramic tool materials by hot pressing. Microstructure, mechanical properties and toughening mechanisms of the composite ceramic tool materials were investigated. The results indicated that the more refined and denser composite microstructures were obtained with the introduction of graphene. The optimal flexural strength, Vickers hardness, indentation fracture toughness were 646.31?±?20.78?MPa, 24.64?±?0.42?GPa, 9.42?±?0.40?MPa?m^1/2, respectively, at 0.5?vol% of graphene content, which were significantly improved compared to ceramic tool material without graphene. The main toughening mechanisms originated from weak interfaces induced by graphene, and rugged fractured surface, grain refinement, graphene pull-out, crack deflection, crack bridging, micro-crack and surface peeling were responsible for the increase of fracture toughness values.     

Evolution on phase composition and properties of alumina-based ceramics fabricated from high-titania special-grade natural bauxite micropowder

In this study, Al₂O₃-based ceramics were fabricated with natural bauxite powder as the raw material. The phase compositions evolution behavior during the heat treatment and its influence on the properties of fabricated ceramics were investigated. With increasing heat treatment temperature, the sintering degree of high-titania special-grade bauxite became better. The samples showed decreased porosity, increased bulk density, Vickers hardness, fracture toughness and flexural strength. However, when the heat temperature increased to 1650 °C, decomposition of tieillite occurs in sample, leading to increased Al₂O₃ and TiO₂ content in the liquid phase. Corundum and mullite grains with anisotropic growth appeared in the samples, leading to a decrease in the density, the Vickers hardness and flexural strength of samples decreased consequently. However, those anisotropic grains could prolong the crack propagation path and improve the fracture toughness of the material.     

High temperature mechanical properties of Al2O3/TiC micro–nano-composite ceramic tool materials

A type of Al₂O₃-based composite ceramic tool material simultaneously reinforced with micro-scale and nano-scale TiC particles was fabricated by the hot-pressing technology with different contents of cobalt additive. The effects of cobalt on the ambient temperature mechanical properties and high temperature flexural strength were investigated. The flexural strength and fracture toughness of the composite with 3 vol% cobalt as a function of temperature were investigated. Cobalt greatly enhanced the ambient temperature flexural strength and fracture toughness, while further increasing the content of cobalt led to a dramatic strength degradation, especially at high temperature. The flexural strength of the composite containing 3 vol% cobalt decreased as the temperature increased from 20 to 1200 °C, and the fracture toughness decreased as a function of the temperature up to 1000 °C but increased at 1200 °C. The degradation of high temperature flexural strength was ascribed to the change of the fracture mode, the grain and grain boundary oxidation, the decrease of elastic modulus and the grain boundary sliding.     

Fabrication of in-situ Ti(C,N) phase toughened Al2O3 based ceramics from natural bauxite

Al₂O₃–Ti(C,N) ceramics were fabricated via carbothermal reduction nitridation method with high-titania special-grade bauxite as the raw material. The formation mechanism of in-situ Ti(C,N) phase and its effect on the properties of materials are discussed. After nitrided at 1700 °C, Ti(C,N) phase could be formed in-situ with appropriate C/TiO₂ molar ratio. Due to the residual stress field formed by Ti(C,N) particles, the path of crack propagation is changed, leading to the crack deflection and pinning. Therefore, the mechanical properties of the materials are improved by forming in-situ Ti(C,N) phase. With a C/TiO₂ molar ratio of 2.2 and nitridation temperature of 1700 °C, Al₂O₃–Ti(C,N) ceramic with a hardness of 13.9 GPa, a fracture toughness of 8.28 MPa m^1/2 and a flexural strength of 387 MPa could be fabricated.     

Fine Ti‐dispersed Al2O3 composites and their mechanical and electrical properties

Al₂O₃/Ti composites containing 0‐30 vol% dispersed fine Ti particles were fabricated using a hot‐press sintering method at 1500°C from mixtures of Al₂O₃ and TiH₂ powders. During sintering, TiH₂ decomposed to form metallic Ti. The effects of the Ti content on the mechanical and electrical properties of the composites were then investigated. No Ti‐Al intermetallic compounds were detected by X‐ray diffraction, and energy‐dispersive X‐ray spectroscopy indicated the presence of Al‐Ti‐O solid solution and Ti‐O phases. The composites showed enhanced densification; the measured densities were higher than the calculated theoretical values. Microstructural observation revealed homogeneously distributed fine Ti particles dispersed in the Al₂O₃ matrix. The Ti particle size ranged from submicrometer to a few micrometers depending on the Ti content. The fracture mode of the composites was primarily transgranular, in contrast to the intergranular fracture mode of monolithic Al₂O₃. Although the flexural strength was decreased with increase in Ti content, the composite containing 20 vol% Ti displayed the maximum fracture toughness of 4.3 MPa·cm^1/2, which was 37% greater than that of monolithic Al₂O₃. The composites containing more than 15 vol% Ti exhibited drastic decreases in resistivity (~10^?1 Ωcm), which were attributed to the formation of interconnected Ti networks at these Ti contents. The percolation threshold volume for electrical conduction in the present system was calculated to be 13.8 vol%. The results indicate that dispersing fine Ti particles into Al₂O₃ increased the fracture toughness and improved the conductivity of Al₂O₃.     

An advanced self-lubricating ceramic composite with the addition of core-shell structured CaF2@Al2O3 powders

Aiming to improve the performance of self-lubricating ceramic tools, an advanced self-lubricating ceramic composite was developed. Core-shell structure CaF₂@Al₂O₃ powders were synthesized by liquid-phase non-uniform nucleation method. Al₂O₃/Ti(C,N)/CaF₂@Al₂O₃ composite made by adding CaF₂@Al₂O₃ powders exhibited notable improvements in microstructure and mechanical properties as compared with Al₂O₃/Ti(C,N)/CaF₂ composite made by adding uncoated CaF₂ powders. The core-shell coated self-lubricating ceramic tool with different content of CaF₂@Al₂O₃ was designed and prepared by hot pressing sintering process. The results show that when the content of CaF₂@Al₂O₃ is 10 vol%, The composite has the best mechanical properties, the flexural strength, and the fracture toughness and the hardness is 680 MPa, 6.50 MPa·m^1/2, and 17.29 GPa. Compared with the tool material with only CaF₂ solid lubricant added, the above performances were increased by 8.91%, 29.48%, and 14.50% respectively. The influence of different CaF₂@Al₂O₃ content on the physical and mechanical properties and microstructure of the tool material was analyzed.     

Sintering behaviour of alumina–niobium carbide composites

Ceramic cutting tools have been developed as a technological alternative to cemented carbides in order to improve cutting speeds and productivity. Al₂O₃ reinforced with refractory carbides improve fracture toughness and hardness to values appropriate for cutting applications. Al₂O₃–NbC composites were either pressureless sintered or hot-pressed without sintering additives. NbC contents ranged from 5 to 30 wt%. Particle dispersion limited the grain growth of Al₂O₃ as a result of the pinning effect. Pressureless sintering resulted in hardness values of approximately 13 GPa and fracture toughness around 3.6 MPa m^1/2. Hot-pressing improved both hardness and fracture toughness of the material to 19.7 GPa and 4.5 MPa m^1/2, respectively.     

Microstructure and mechanical properties of Al2O3–Ti(C,N)–cBN composites prepared by a novel hot-forging process

Al₂O₃–cBN has received considerable attention in the field of ceramic cutting tools due to its high hardness, high wear resistance, and low cost, but poor interfacial bonding affects the performance of the composite. In this study, a novel hot-forging process was used to prepare high-performance Al₂O₃–cBN composites using Ti(C,N) as a binder. The evolution of the morphology, phase, and microstructure of the hot-forged Al₂O₃–Ti(C,N)–cBN composites was determined, and the mechanical properties were measured. The relative density of the composites increases significantly after hot forging, and the deformation of the composites increases with the hot-forging temperature. The highest performing Al₂O₃–Ti(C,N)–cBN composite was prepared by hot forging at 1600°C and has a hardness of 20 GPa, a bending strength of 647 MPa and a fracture toughness of 5.37 MPa m^1/2, which are superior to those of a directly hot-pressed sintered composite. However, at hot-forging temperatures higher than 1700°C, Al₅O₆N and TiB₂ are formed in the composite. In the composite hot forged at 1800°C, serrated grain boundaries promote the strength and toughness of the composite to 877 MPa and 6.76 MPa m^1/2, respectively. Therefore, the novel hot-forging process is expected to enhance material properties.     

Reliability prediction of a microwave sintered Si3N4-based composite ceramic tool

The wear life reliability prediction model of microwave sintered Si₃N₄/(W,Ti)C/Y₂O₃/MgO/Al₂O₃ composite ceramic tools based on the random distribution characteristics of hardness and fracture toughness of ceramic tool material was established. It showed that the Vickers hardness of ceramic tool materials followed a normal distribution and the fracture toughness followed a lognormal distribution. Distribution law of wear life can be determined by the joint distribution of hardness and fracture toughness. Experimental research on tool reliability of continuous dry cutting quenched high quality carbon steel T10A was carried out and the applicability of the tool reliability prediction model was verified. The results showed that the error between the theoretical reliable life and the actual life of the ceramic tool was less than 5% under the same reliability when the reliability was above 0.5.     

Microstructure and mechanical properties of hot pressed Al2O3/SiC nanocomposites

Al₂O₃/SiC micro/nano composites containing different volume fractions (5, 10, 15, and 20 vol.%) of SiC were prepared by mixing a sub-micron alumina powder with respective amounts of either micro- or nano-sized silicon carbide powders. The powder mixtures were hot pressed 1 h at 1740 °C and 30 MPa in the atmosphere of Ar. The effect of SiC addition on the microstructure and mechanical properties, i.e. hardness, fracture toughness, and room temperature flexural strength were investigated. The flexural strength increased with increasing volume fraction of silicon carbide particles. The maximum flexural strength (655 ± 90 MPa) was achieved for the composite containing 20 vol.% of coarse-grained SiC, which is more than twice as high as in the Al₂O₃ reference. Hardness and fracture toughness were also moderately improved. The observed improvement of mechanical properties is mainly attributed to alumina matrix grain refinement and grain boundary reinforcement.     

Preparation and cutting performance of Ti(C7, N3)/TiB2/WC cermet tool material

In this paper, a Ti(C₇, N₃)/TiB₂/WC cermet tool material was prepared by plasma sintering. The components of the tool material and sintering process parameters were optimized through testing mechanical property. The cutting performance of the prepared tool was studied in the cutting experiment of 06Cr19Ni10 austenitic stainless steel. A comparison was made between the prepared tool and the commercial cermet tool SNMN120708. It is shown that when the volume fractions of TiB₂ and WC were 20% and 15%, respectively, at the sintering temperature of 1550 °C and with the holding time of 30 min, the prepared tool would possess the flexural strength of 1096.45 Mpa, the hardness of 18.9 Gpa, the fracture toughness of 9.85 Mpa·m^1/2 and the optimal cutting speed of 150 m/min. At the cutting speeds of 100 m/min and 150 m/min, the cutting distance of the developed tool was larger than that of SNMN120708. When the cutting speeds were 200 m/min and 250 m/min, the cutting distance of SNMN120708 tool was relatively large. The main wear mechanism of Ti(C₇, N₃)/TiB₂/WC and SNMN120708 tool was adhesive wear, with no trace of abrasive wear.     

Microstructure and mechanical properties of TiC0.7N0.3-HfC cermet tool materials

TiC_0.7N_0.3-HfC cermet tool materials were fabricated by hot-press sintering. Effects of different metal additives (Ni, Co, Ni-Co and Ni-Mo), sintering temperature and holding time on the microstructures and mechanical properties of TiC_0.7N_0.3-HfC cermets were investigated. Results showed that Ni-Mo or Ni-Co as metal additives was better for the mechanical properties of TiC_0.7N_0.3-HfC cermets than only Ni or only Co as the metal additives and Ni-Mo better than Ni-Co. HfC particle dispersion existed in these four cermets and only in the TiC_0.7N_0.3-HfC-Ni-Mo cermet the core-rim structure obviously existed. TiC_0.7N_0.3-HfC-Ni-Mo cermet had significantly smaller grains than the other three cermets because Ni-Mo can significantly refine the grain. With the sintering temperature increasing from 1450?°C to 1650?°C, grains grew gradually; Vickers hardness and flexural strength decreased gradually and the fracture toughness increased firstly and then decreased. With the holding time increasing from 15?min to 60?min, grains grew gradually; Vickers hardness, flexural strength and the fracture toughness increased firstly and then decreased. TiC_0.7N_0.3-HfC-Ni-Mo cermets sintered at 1450?°C with 30?min holding time had the better comprehensive mechanical properties with flexural strength of 1346.41?±?31?MPa, fracture toughness of 8.46?±?0.23?MPa?m^1/2 and Vickers hardness of 22.91?±?0.22?GPa.     

Preparation,microstructure and mechanical properties of MoAlB-0.15% Si ceramics with superior strength and toughness

MoAlB has been regarded as a promising high-temperature structural ceramic, but the strength and toughness are still insufficient in the practical application. In this work, MoAlB ceramic bulk with superior hardness, strength and toughness has been fabricated by adding 0.15 mol. % Si. The MoAlB-0.15Si bulk is composed of Si-doped MoAlB, Mo(Al, Si)₂ and ultrafine Al₂O₃. The Vickers hardness ranges from 14.2 to 12.5 GPa with the tested load increasing from 10 to 200 N. The Vickers indentation remains the intact tetragonum in spite of the appearance of corner cracks, indicating the excellent damage tolerance. The flexural strength, fracture toughness and compressive strength of MoAlB-0.15Si are 518.46 MPa, 7.01 MPa m^1/2 and 2.62 GPa, respectively, obviously superior to the present MoAlB polycrystalline bulk. Si doping, grain refinement, strengthening effect of ultrafine Al₂O₃ and phase transformation from Al₈Mo₃ to Mo(Al, Si)₂ jointly account for the improvement of comprehensive properties of MoAlB bulk.     

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

B₄C-based composites were synthesized by spark plasma sintering using B₄C、Ti₃SiC₂、Si as starting materials. The effects of sintering temperature and second phase content on mechanical performance and microstructure of composites were studied. Full dense B₄C-based composites were obtained at a low sintering temperature of 1800 °C. The B₄C-based composite with 10 wt% (TiB₂+SiC) shows excellent mechanical properties: the Vickers hardness, fracture toughness, and flexural strength are 33 GPa, 8 MPa m^1/2, 569 MPa, respectively. High hardness and flexural strength were attributed to the high relative density and grain refinement, the high fracture toughness was owing to the crack deflection and uniform distribution of the second phase.     

Low temperature pressureless sintering of α-SiC with Al2O3 and CeO2 as additives

The combination of Al₂O₃ and CeO₂ was testified as suitable sintering additive for liquid phase sintering of SiC ceramics, which has lower sintering temperature than that sintered with Al₂O₃ and Y₂O₃ as sintering aids. However, the mechanical properties including flexural strength, Vickers’ hardness and fracture toughness of this system were similar to those of the samples sintered with Al₂O₃ and Y₂O₃ as sintering aids. The good wettability of the eutectic liquid phase on SiC plate, the high solubility of SiC particles into the liquid phase and the penetration of the liquid phase along the SiC–SiC grain boundaries all confirmed the suitability of the combination of Al₂O₃ and CeO₂ as liquid phase sintering additive for SiC.     

Fast preparation of ZTA-TiC-FeCrNi cermets by high-gravity combustion synthesis

ZTA-TiC-FeCrNi cermets are prepared by a fast and furnace-free way called high-gravity combustion synthesis. The synthesized cermet samples show the maximum relative density of 97.6% and a hierarchical microstructure with grain sizes from submicron to >50 µm. The content of TiC has a strong influence on the microstructure and mechanical properties of the cermet samples. A higher TiC content results in refined microstructure, improved hardness, and reduced coefficient of friction. With increasing TiC content, the strength and toughness of the samples first increase and then drops, and reach the maximum of 469±26 MPa and 11.3±0.2 MPa m^1/2 at 20% TiC. Compared with commercial polycrystalline Al₂O₃ ceramics, the ZTA-TiC-FeCrNi cermets exhibit better wear resistance, and the volume loss is lower by one magnitude than Al₂O₃ under the same condition.     

Fine TiC dispersed Al2O3 composites fabricated via in situ reaction synthesis and conventional process

To further improve the mechanical performance and reduce the percolation threshold by controlling microstructures, Al₂O₃-TiC composites containing 0-20 vol% TiC were fabricated via in situ reaction synthesis. Graphite (ATC) and carbon nanotubes (ATCT) were used as carbon sources. The composites were also fabricated via a conventional process using a TiC starting powder (AT). X-ray diffraction analysis and scanning electron microscopy observation results indicated successful fabrication of the composites with various microstructures. TiC particles in ATCT were completely dispersed at grain boundaries, whereas in ATC and AT, these particles were either intragranular or intergranular dispersed. The composites could be listed as follows, ATCT > ATC > AT, that is, in descending order of the reinforcing flexural strength and fracture toughness. The nanoindentation measurement indicated the optimum hardening effect of ATCT. The ATCT composite also exhibited the highest fracture toughness, which was 49% higher than that of the monolithic Al₂O₃. Crack deflection was considered as the main toughening mechanism while crack bridging behavior also occurred in ATCT. For a given TiC content, ATCT exhibited the lowest electrical resistivity, owing mainly to the complete grain-boundary dispersion of the relatively large TiC particles. The similarity of the Al₂O₃ grain size and TiC particle size of ATCT contributed to the lowest percolation threshold achieved (11.2%), which (to date) is the lowest value that has been reported for the Al₂O₃-TiC system.