Influence of pyrolysis and melt infiltration temperatures on the mechanical properties of SiCf/SiC composites

In order to improve the degree of matrix densification of SiC_f/SiC composites based on liquid silicon infiltration (LSI) process, the microstructure and mechanical properties of composites according to various pyrolysis temperatures and melt infiltration temperatures were investigated.Comparing the microstructures of SiC_f/C carbon preform by a one-step pyrolysis process at 600 °C and two-step pyrolysis process at 600 and 1600 °C, the width of the crack and microcrack formation between the fibers and matrix in the fiber bundle increased during the two-step pyrolysis process. For each pyrolysis process, the density, porosity, and flexural strength of the SiC_f/SiC composites manufactured by the LSI process at 1450–1550 °C were measured to evaluate the degree of matrix densification and mechanical properties. As a result, the SiC_f/SiC composite that was fabricated by the two-step pyrolysis process and LSI process showed an 18% increase in density, 16%p decrease in porosity, and 150% increase in flexural strength on average compared to the composite fabricated by the one-step pyrolysis process.In addition, among the SiC_f/SiC specimens fabricated by the LSI process after the same two-step pyrolysis process, the specimen that underwent the LSI process at 1500 °C showed 30% higher flexural strength on average than those at 1450 or 1550 °C. Furthermore, under the same pyrolysis temperature, the mechanical strength of SiC_f/SiC specimens in which the LSI process was performed at 1500 °C was higher than that of the 1550 °C although both porosity and density were almost similar. This is because the mechanical properties of the Tyranno-S grade SiC fibers degraded rapidly with increasing LSI process temperature.     

Microstructure and damage evolution of SiCf/PyC/SiC and SiCf/BN/SiC mini-composites: A synchrotron X-ray computed microtomography study

SiC_f/PyC/SiC and SiC_f/BN/SiC mini-composites comprising single tow SiC fibre-reinforced SiC with chemical vapor deposited PyC or BN interface layers are fabricated. The microstructure evolutions of the mini-composite samples as the oxidation temperature increases (oxidation at 1000, 1200, 1400, and 1600?°C in air for 2?h) are observed by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction characterization methods. The damage evolution for each component of the as-fabricated SiC_f/SiC composites (SiC fibre, PyC/BN interface, SiC matrix, and mesophase) is mapped as a three-dimensional (3D) image and quantified with X-ray computed tomography. The mechanical performance of the composites is investigated via tensile tests.The results reveal that tensile failure occurs after the delamination and fibre pull-out in the SiC_f/PyC/SiC composites due to the volatilization of the PyC interface at high temperatures in the air environment. Meanwhile, the gaps between the fibres and matrix lead to rapid oxidation and crack propagation from the SiC matrix to SiC fibre, resulting in the failure of the SiC_f/PyC/SiC composites as the oxidation temperature increases to 1600?°C. On the other hand, the oxidation products of B₂O₃ molten compounds (reacted from the BN interface) fill up the fracture, cracks, and voids in the SiC matrix, providing excellent strength retention at elevated oxidation temperatures. Moreover, under the protection of B₂O₃, the SiC_f/BN/SiC mini-composites show a nearly intact microstructure of the SiC fibre, a low void growth rate from the matrix to fibre, and inhibition of new void formation and the SiO₂ grain growth from room to high temperatures. This work provides guidance for predicting the service life of SiC_f/PyC/SiC and SiC_f/BN/SiC composite materials, and is fundamental for establishing multiscale damage models on a local scale.     

Mechanical,thermal, and dielectric properties of SiCf/SiC composites reinforced with electrospun SiC fibers by PIP

Electrospun unidirectional SiC fibers reinforced SiC_f/SiC composites (e-SiC_f/SiC) were prepared with ∼10% volume fraction by polymer infiltration and pyrolysis (PIP) process. Pyrolysis temperature was varied to investigate the changes in microstructures, mechanical, thermal, and dielectric properties of e-SiC_f/SiC composites. The composites prepared at 1100 °C exhibit the highest flexural strength of 286.0 ± 33.9 MPa, then reduced at 1300 °C, mainly due to the degradation of electrospun SiC fibers, increased porosity, and reaction-controlled interfacial bonding. The thermal conductivity of e-SiC_f/SiC prepared at 1300 °C reached 2.663 W/(m∙K). The dielectric properties of e-SiC_f/SiC composites were also investigated and the complex permittivities increase with raising pyrolysis temperature. The e-SiC_f/SiC composites prepared at 1300 °C exhibited EMI shielding effectiveness exceeding 24 dB over the whole X band. The electrospun SiC fibers reinforced SiC_f/SiC composites can serve as a potential material for structural components and EMI shielding applications in the future.     

Microstructure and mechanical properties of quasi-isotropic chopped fiber-reinforced PyC–SiC matrix composite prepared by novel nondamaging method

In this work, quasi-isotropic chopped carbon fiber-reinforced pyrolytic carbon and silicon carbide matrix (C_f/C–SiC) composites and chopped silicon carbide fiber-reinforced silicon carbide matrix (SiC_f/SiC) composites were prepared via novel nondamaging method, namely airlaid process combined with chemical vapor infiltration. Both composites exhibit random fiber distribution and homogeneous pore size. Young's modulus of highly textured pyrolytic carbon (PyC) matrix is 23.01 ± 1.43 GPa, and that of SiC matrix composed of columnar crystals is 305.8 ± 9.49 GPa in C_f/C–SiC composites. Tensile strength and interlaminar shear strength of C_f/C–SiC composites are 52.56 ± 4.81 and 98.16 ± 24.62 MPa, respectively, which are both higher than those of SiC_f/SiC composites because of appropriate interfacial shear strength and introduction of low-modulus and highly textured PyC matrix. Excellent mechanical properties of C_f/C–SiC composites, particularly regarding interlaminar shear strength, are due to their quasi-isotropic structure, interfacial debonding, interfacial sliding, and crack deflection. In addition to the occurrence of crack deflection at the fiber/matrix interface, crack deflection in C_f/C–SiC composites takes also place at the interface between PyC–SiC composite matrix and the interlamination of multilayered PyC matrix. Outstanding mechanical properties of as-prepared C_f/C–SiC composites render them potential candidates for application as thermal structure materials under complex stress conditions.     

Thermal stability of CVI and MI SiC/SiC composites with Hi-Nicalon™-S fibers

The influence of high-temperature argon heat-treatment on the microstructure and room- temperature in-plane tensile properties of 2D woven CVI and 2D unidirectional MI SiC/SiC composites with Hi-Nicalon?-S SiC fibers was investigated. The 2D woven CVI SiC/SiC composites were heat-treated between 1200 and 1600 °C for 1- and 100-hr, and the 2D unidirectional MI SiC/SiC composites between 1315 and 1400 °C for up to 2000 hr. In addition, the influence of temperature on fast fracture tensile strengths of these composites was also measured in air. Both composites exhibited different degradation behaviors. In 2D woven CVI SiC/SiC composites, the CVI BN interface coating reacted with Hi-Nicalon?-S SiC fibers causing a loss in fast fracture ultimate tensile strengths between 1200 and 1600 °C as well as after 100-hr isothermal heat treatment at temperatures > 1100 °C. In contrast, 2D unidirectional MI SiC/SiC composites showed no significant loss in in-plane tensile properties after the fast fracture tensile tests at 1315 °C. However, after isothermal exposure conditions from 1315° to 1400°C, the in-plane proportional limit stress decreased, and the ultimate tensile fracture strain increased with an increase in exposure time. The mechanisms of strength degradation in both composites are discussed.     

Oxidation and microstructure of SiCf/SiC composites in moist air up to 1600°C by X-ray tomographic characterization

SiC_f/SiC composites that possess PyC or BN interface layers were fabricated and then oxidized in moist air at 1000, 1200, 1400, and 1600°C. High-resolution CT was used for capturing 3D images and quantifying the SiC phase, mesophase, and voids. The oxidation behavior and microstructural evolution of SiC_f/SiC with PyC or BN interface are discussed in this study. The microstructure of the SiC_f/SiC with a PyC layer was seriously damaged in moist air at high temperature, whereas the BN interface layer enhanced the oxidation resistance of the SiC_f/SiC. These results are also confirmed by using XRD, oxidation mass gain, tensile testing, and SEM measurements. The results of the oxidation behavior and microstructural evolution for SiC_f/SiC oxidized in dry air are also compared with the results of this study. Comparing the SiC_f/SiC with a PyC interface layer, the composite with a BN interface layer oxidized in moist air exhibits a high void growth rate and a low SiO₂ grain growth rate from 1000 to 1600°C. This work will provide guidance for predicting the service life of SiC_f/SiC for multiscale damage rate models of materials at a local scale and will also provide guidance on the life service design of SiC_f/SiC materials.     

Effect of SiC interphase on the mechanical,high-temperature dielectric and high-temperature microwave absorption properties of the SiCf/SiC/Mu composites

In this study, SiC interphase was prepared via a precursor infiltration-pyrolysis process, and effects of dipping concentrations on the mechanical, high-temperature dielectric and microwave absorption properties of the SiC_f/SiC/Mu composites had been investigated. Results indicated that different dipping concentrations influenced ultimate interfacial morphology. The SiC interphase prepared with 5 wt% PCS/xylene solution was smooth and homogeneous, and no bridging between the fiber monofilament could be observed. At the same time, SiC interphase prepared with 5 wt% PCS/xylene solution had significantly improved mechanical properties of the composite. In particular, the flexural strength of the composite prepared with 5 wt% PCS/xylene solution reached 281 MPa. Both ε′ and ε′′ of the SiC_f/SiC/Mu composites were enhanced after preparing SiC interphase at room temperature. The SiC_f/SiC/Mu composite prepared with 5 wt% PCS/xylene solution showed the maximum dielectric loss value of 0.38 at 10 GHz. Under the dual action of polarization mechanism and conductance loss, both ε′ and ε′′ of the SiC_f/SiC/Mu composites enhanced as the temperature increased. At 700 °C, the corresponding bandwidth (RL ≤ ?5 dB) of SiC_f/SiC/Mu composites prepared with 5 wt% PCS/xylene solution can reach 3.3 GHz at 2.6 mm. The SiC_f/SiC/Mu composite with SiC interphase prepared with 5 wt% PCS/xylene solution is expected to be an excellent structural-functional material.     

Excellent ablation resistance and reusability of silicon carbide fiber reinforced silicon carbide composite in dissociated air plasmas

This work explores the potentials of SiC fiber reinforced SiC matrix composites (SiC_f/SiC) with SiC coating to resist aerodynamic ablations for thermal protection purpose. A plasma wind tunnel is employed to evaluate their anti-ablation property in dissociated air plasmas. The results suggest a critical ablation temperature of SiC coated SiC_f/SiC, ≈ 1910 °C, which is the highest ever reported in literatures. Benefited by ‘all-SiC’ microstructures and relative flat ablated surfaces, the SiC_f/SiC is still ablation-resistant up to ≈ 1820 °C after the occurrence of ablation. This implies an excellent ablation resistance and reusability property of SiC_f/SiC, which surpasses that of traditional carbon fiber reinforced composites. Finally, an ablation mechanism dominated by surface characteristic is proposed. For the SiC coated SiC_f/SiC, ablation is prone to take place at surface cracks formed by thermal mismatch; while for the ablated SiC_f/SiC, ablation is triggered at the exposed fiber bundles which is over-heated in the plasmas.     

Effects of grain boundary volume fraction on the threshold dose of irradiation-induced SiC amorphization at 30 °C

SiC fiber-reinforced matrix composites (SiC_f/SiC) have limited applications because of the irradiation-induced shrinkage of SiC fibers; the fiber shrinkage mechanism is still not fully understood. In this study, we tried to clarify the effect of annealing temperature on the proportion of fiber shrinkage and swelling. SiC_f/SiC was irradiated at 30 °C to 100 dpa, and the deterioration of mechanical properties was evaluated after irradiation. The compressive displacement of > 60% of the fibers before failure increased to more than 1.5 times that of the as-received specimen. Significant swelling was observed, indicating that the proportion of swelling was higher than that of shrinkage after irradiation. This can be attributed to the amorphization of SiC, and its amorphization threshold dose increased with decreasing grain boundary volume fraction. The findings of this study provide insights into the mechanism of irradiation-induced fiber amorphization and can be useful in developing improved SiC_f/SiC.     

Preparation of SiCf/Si–O–C composites by impregnation pyrolysis of polysiloxane and its electromagnetic wave absorption properties

High-temperature structural electromagnetic wave (EMW) absorption materials are increasing in demand because they can simultaneously possess the functions of mechanical load-bearing, heatproof, and EMW absorption. Herein, SiC_f/Si–O–C composites were prepared by precursor impregnation pyrolysis using continuous SiC fibers needled felt as reinforcement and polysiloxane as a precursor, respectively. The phase composition, microstructure, complex permittivity, and EMW absorption properties of SiC_f/Si–O–C composites after annealing at various temperatures were investigated. The annealing at 1400–1500°C affects positively the EMW absorption performance of the composites, because the β-SiC microcrystals and SiC nanowires were generated by the activation of carbothermal reduction reaction in the composites, and the aspect ratio of SiC nanowires increased with the rise of temperature. The composites exhibit optimal EMW absorption performance, with the effective absorption bandwidth covering the entire X-band and the minimum reflection loss (RL_min) of −32.8 dB at 4.0 mm when the annealing temperature is raised to 1500°C. This is because that the impedance matching is improved as the rising of ε′ and decreasing of ε″ due to the conversion of free carbon in the composite into SiC nanowires.     

Phase-field simulation of microscale crack propagation/deflection in SiCf/SiC composites with weak interphase

To understand the microscale toughening mechanism, the crack propagation, and stress–strain response of unidirectional SiC_f/SiC composites with h-BN interphase under transverse and longitudinal tension are investigated by a promising micromechanical phase field (PF) method along with representative volume element. Of much interest, the calculation results are well consistent with the available experimental results. With a strong dependence on the interphase strength, the toughening mechanisms during crack propagation are well presented, for example, fiber pull-out, crack deflection, and interphase debonding. Furthermore, the longitudinal tensile strength of SiC_f/SiC composites increases with decreasing the interphase strength, where only a weak enough interphase can result in a significant crack deflection by its cracking. In particular, the ratio of the interphase strength along fibers to the matrix strength should be less than 1.254 to ensure crack deflection in the interphase and fiber pull-out. Moreover, the transverse tensile strength of SiC_f/SiC composites reaches a maximum with increasing the interphase thickness into the range of 0.25–0.5 µm.     

Pressure-less joining of SiCf/SiC composites by Y2O3–Al2O3–SiO2 glass: Microstructure and properties

In this study, Y₂O₃–Al₂O₃–SiO₂ (YAS) glass was prepared from Y₂O₃, Al₂O₃, and SiO₂ micron powders. Thermal expansion coefficient of as-obtained YAS glass was about 3.9 × 10⁻⁶, matching-well with that of SiC_f/SiC composites. SiC_f/SiC composites were then brazed under pressure-less state by YAS glass and effects of brazing temperature on microstructures and properties of resulting joints were investigated. The results showed that glass powder in brazed seam sintered and precipitated yttrium disilicate, cristobalite, and mullite crystals after heat treatment. With the increase in temperature, joint layer gradually densified and got tightly bonded to SiC_f/SiC composite. The optimal brazing parameter was recorded as 1400 °C/30 min and shear strength of the joint was 51.7 MPa. Formation mechanism of glass-ceramic joints was proposed based on combined analysis of microstructure and fracture morphology of joints brazed at different temperatures. Thermal shock resistance testing of joints was also carried out, which depicted decline in shear strength with the increase of thermal shock times. The strength of the joint after three successive thermal shock cycles at 1200 °C was 35.6 MPa, equivalent to 69% of that without thermal shock.     

Microstructure and mechanical properties of hot-pressed SiC nanofiber reinforced SiC composites

This study reports on the preparation and mechanical properties of a novel SiC_nf/SiC composite. The single crystal SiC nanofiber(SiC_nf) reinforced SiC ceramic matrix composites (CMC) were successfully fabricated by hot pressing the mixture of β-SiC powders, SiC_nf and Al–B–C powder. The effects of SiC_nf mass fraction as well as the hot-pressing temperature on the microstructure and mechanical properties of SiC_nf/SiC CMC were systematically investigated. The results demonstrated that the 15 wt% SiC_nf/SiC CMC obtained by hot pressing (HP) at 1850 °C with 30 MPa for 60 min possessed the maximum flexural strength and fracture toughness of 678.2 MPa and 8.33 MPa m^1/2, respectively. The nanofibers pull out, nanofibers bridging and cracks deflection were found by scanning electron microscopy, which are believed can strengthen and toughen the SiC_nf/SiC CMC via consuming plenty of the fracture energy. Besides, although the relative density of the prepared SiC_nf/SiC CMC further increased with the sintering temperature rose to 1900 °C, the further coarsend composites grains results in the deterioration of the mechanical properties for the obtained composites compared to 1850 °C.     

Mechanical properties and strengthening mechanism of SiCf/SiC mini-composites modified by SiC nanowires

The effects of the SiC nanowires (SiCNWs) and PyC interface layers on the mechanical and anti-oxidation properties of SiC fiber (SiC_f)/SiC composites were investigated. To achieve this, the PyC layer was coated on the SiC_f using a chemical vapour infiltration (CVI) method. Then, SiCNWs were successfully coated on the surface of SiC_f/PyC using the electrophoretic deposition method. Finally, a thin PyC layer was coated on the surface of SiC_f/PyC/SiCNWs. Three mini-composites, SiC_f/PyC/SiC, SiC_f/PyC/SiCNWs/SiC, and SiC_f/PyC/SiCNWs/PyC/SiC, were fabricated using the typical precursor infiltration and pyrolysis method. The morphologies of the samples were examined using scanning electron microscopy and energy dispersive X-ray spectrometry. Tensile and single-fibre push-out tests were carried out to investigate the mechanical performance and interfacial shear strength of the composites before and after oxidization at 1200 °C. The results revealed that the SiC_f/PyC/SiCNWs/SiC composites showed the best mechanical and anti-oxidation performance among all the composites investigated. The strengthening and toughening is mainly achieved by SiCNWs optimization of the interfacial bonding strength of the composite and its own nano-toughening. On the basis of the results, the effects of SiCNWs on the oxidation process and retardation mechanism of the SiC_f/SiC mini-composites were investigated.     

Ring compression properties of SiCf/SiC composites prepared by chemical vapor infiltration

SiC fiber reinforced SiC matrix (SiC_f/SiC) composites prepared by chemical vapor infiltration are one of promising materials for nuclear fuel cladding tube due to pronounced low radioactivity and excellent corrosion resistance. As a structure component, mechanical properties of the composites tubes are extremely important. In this study, three kinds of SiC_f preform with 2D fiber wound structure, 2D plain weave structure and 2.5D shallow bend-joint structure were deposited with PyC interlayer of about 150–200?nm, and then densified with SiC matrix by chemical vapor infiltration at 1050?°C or 1100?°C. The influence of preform structure and deposition temperature of SiC matrix on microstructure and ring compression properties of SiC_f/SiC composites tubes were evaluated, and the results showed that these factors have a significant influence on ring compression strength. The compressive strength of SiC_f/SiC composites with 2D plain weave structure and 2.5D shallow bend-joint structure are 377.75?MPa and 482.96?MPa respectively, which are significantly higher than that of the composites with 2D fiber wound structure (92.84?MPa). SiC_f/SiC composites deposited at 1100?°C looks like a more porous structure with SiC whiskers appeared when compared with the composites deposited at 1050?°C. Correspondingly, the ring compression strength of the composites deposited at 1100?°C (566.44?MPa) is higher than that of the composites deposited at 1050?°C (482.96?MPa), with a better fracture behavior. Finally, the fracture mechanism of SiC_f/SiC composites with O-ring shape was discussed in detail.     

Mechanical properties and microstructure evolution of 3D Cf/SiBCN composites at elevated temperatures

3D C_f/SiBCN composites were fabricated by an efficient polymer impregnation and pyrolysis (PIP) method using liquid poly(methylvinyl)borosilazanes as precursor. Mechanical properties and microstructure evolution of the prepared 3D C_f/SiBCN composites at elevated temperatures in the range of 1500‐1700°C were investigated. As temperature increased from room temperature (371 ± 31 MPa, 31 ± 2 GPa) to 1500°C (316 ± 29 MPa, 27 ± 3 GPa), strength and elastic modulus of the composite decreased slightly, which degraded seriously as temperature further increased to 1600°C (92 ± 15 MPa, 12 ± 2 GPa) and 1700°C (84 ± 12 MPa, 11 ± 2GPa). To clarify the conversion of failure mechanisms, interfacial shear strength (IFSS) and microstructure evolution of the 3D C_f/SiBCN composites at different temperatures were investigated in detail. It reveals that the declines of the strength and changes of the IFSS of the composites are strongly related to the defects and SiC nano‐crystals formed in the composites at elevated temperatures.     

Improving thermal stability of SiC whiskers via nanoscale Ti3SiC2 coatings

Effects of SiC whiskers (SiC_w) on the mechanical properties of composites largely depend on their thermal stability at high temperature. In this study, pure SiC_w and Ti₃SiC₂ coated SiC_w were thermal treated at 1600–1800°C for 1 h. Their phase assemblage, morphology, and structural evolution were investigated. Oxygen partial pressures in the graphite furnace resulted in the breakdown of SiC_w into particles at 1600°C, and the degradation became more pronounced with temperature increasing. The thermal stability of SiC whiskers at 1600–1700°C was significantly improved by a thin Ti₃SiC₂ coating on them, as both thermodynamic calculations and experimental observations suggest Ti₃SiC₂ coating could be preferentially oxidized/decomposed, prior to the active oxidation of SiC. At 1800°C, the protective role of the coating on the whiskers became weakened. SiC was converted into gaseous SiO and CO, with the remaining of interconnected TiC micro-rods and amorphous carbon.     

Preparation and tensile behavior of SiCf/SiC mini composites containing different types and thicknesses of interphase

SiC fiber-reinforced SiC matrix (SiC_f/SiC) composites are promising materials for high-temperature structural applications. In this study, KD-II SiC fiber bundles with a C/Si ratio of approximately 1.25 and an oxygen amount of 2.53%, were used as reinforcement. PyC interphase, PyC-SiC co-deposition interphase I and II, with different thicknesses, and SiC matrix were deposited into the SiC fiber bundles by using chemical vapor infiltration (CVI) to form SiC_f/SiC mini composites. When the thickness of the interphase is approximately 1000 nm, the ultimate tensile stress and strain of SiC_f/SiC mini composites with PyC-SiC co-deposition interphase I can reach 1120.0 MPa and 0.72%, respectively, which are significantly higher than those of SiC_f/SiC mini composites with a PyC interphase (740.0 MPa, 0.87%) and PyC-SiC co-deposition interphase II (645.0 MPa, 0.54%). The effect of thicknesses and types of interphase on tensile fracture behavior of mini composites and then the fracture mechanism are discussed in detail.     

Long-term oxidation and ablation behavior of Cf/ZrB2–SiC composites at 1500, 2000, and 2200°C

Although C_f/ZrB₂–SiC composites prepared via direct ink writing combined with low-temperature hot-pressing were shown to exhibit high relative density, high preparation efficiency, and excellent flexural strength and fracture toughness in our previous work, their oxidation and ablation resistance at high and ultrahigh temperatures had not been investigated. In this work, the oxidation and ablation resistance of C_f/ZrB₂–SiC composites were evaluated via static oxidation at high temperature (1500°C) and oxyacetylene ablation at ultrahigh temperatures (2080 and 2270°C), respectively. The thickness of the oxide layer of the C_f/ZrB₂–SiC composites is <40 μm after oxidizing at 1500°C for 1 h. The C_f/ZrB₂–SiC composites exhibit non-ablative properties after oxyacetylene ablation at 2080 and 2270°C for >600 s, with mass ablation rates of 3.77 × 10⁻³ and 5.53 × 10⁻³ mg/(cm² s), and linear ablation rates of −4.5 × 10⁻⁴ and −5.8 × 10⁻⁴ mm/s, respectively. Upon an increase in the ablation temperature from 2080 to 2270°C, the thickness of the total oxide layer increases from 360 to 570 μm, and the carbon fibers remain intact in the unaffected region. Moreover, the oxidation and ablation process of C_f/ZrB₂–SiC at various temperatures was analyzed and discussed.     

Effect of interphase on mechanical properties and microstructures of 3D Cf/SiBCN composites at elevated temperatures

Interphase between the fibers and matrix plays a key role on the properties of fiber reinforced composites. In this work, the effect of interphase on mechanical properties and microstructures of 3D C_f/SiBCN composites at elevated temperatures was investigated. When PyC interphase is used, flexural strength and elastic modulus of the C_f/SiBCN composites decrease seriously at 1600°C (92 ± 15 MPa, 12 ± 2 GPa), compared with the properties at room temperature (371 ± 31 MPa, 31 ± 2 GPa). While, the flexural strength and elastic modulus of C_f/SiBCN composites with PyC/SiC multilayered interphase at 1600°C are as high as 330 ± 7 MPa and 30 ± 2 GPa, respectively, which are 97% and 73% of the values at room temperature (341 ± 20 MPa, 41 ± 2 GPa). To clarify the effect mechanism of the interphase on mechanical properties of the C_f/SiBCN composites at elevated temperature, interfacial bonding strength (IFBS) and microstructures of the composites were investigated in detail. It reveals that the PyC/SiC multilayered interphase can retard the SiBCN matrix degradation at elevated temperature, leading to the high strength retention of the composites at 1600°C.