Transient liquid phase diffusion process for porous mullite ceramics with excellent mechanical properties

Porous mullite ceramics were fabricated by the transient liquid phase diffusion process, using quartz and fly-ash floating bead (FABA) particles and corundum fines as starting materials. The effects of sintering temperatures on the evolution of phase composition and microstructure, linear shrinkage, porosity and compressive strength of ceramics were investigated. It is found that a large amount of quartz and FABA particles can be transformed into SiO₂-rich liquid phase during the sintering process, and the liquid phase is transient in the Al₂O₃-SiO₂ system, which can accelerate the mullitization rate and promote the growth of mullite grains. A large number of closed pores in the mullite ceramics are formed due to the transient liquid phase diffusion at elevated temperatures. The porous mullite ceramics with high closed porosity (about 30%) and excellent compressive strength (maximum 105?MPa) have been obtained after fried at 1700?°C.     

A novel and green preparation of porous forsterite ceramics with excellent thermal isolation properties

This work provides a novel and green approach to preparing porous forsterite ceramics by a transient liquid phase diffusion process based on fused magnesia and quartz powders without detrimental additives. The size of quartz particles markedly affected the sintering behaviors, phase composition, microstructure and properties of the porous forsterite ceramics. Fine quartz particles (D₅₀, 3.87?µm) accelerated the rate of the forsterite formation at elevated temperatures and promoted solid-state sintering behavior of the porous ceramics. Conversely, coarse quartz particles (D₅₀, 25.38?µm) reduced the rate of the solid state reaction and a large amount of unreacted SiO₂ and enstatite (MgSiO₃) phases transformed into a transient liquid-phase during the firing process. This effect resulted in a high porosity (approximately 58.89%) and formation of many large pores (mean pore size of 42.36?µm). These features contributed to the excellent thermal isolation properties of the prepared porous forsterite ceramics. The strength of the obtained porous ceramics (about 23.6?MPa) is relatively high compared with those of conventional ceramics.     

Effects of porosity on electrical and thermal conductivities of porous SiC ceramics

The effects of porosity on the electrical and thermal conductivities of porous SiC ceramics, containing Y₂O₃–AlN additives, were investigated. The porosity of the porous SiC ceramic could be controlled in the range of 28–64 % by adjusting the sacrificial template (polymer microbead) content (0–30 wt%) and sintering temperature (1800–2000 °C). Both electrical and thermal conductivities of the porous SiC ceramics decreased, from 7.7 to 1.7 Ω⁻¹ cm⁻¹ and from 37.9 to 5.8 W/(m·K), respectively, with the increase in porosity from 30 to 63 %. The porous SiC ceramic with a coarser microstructure exhibited higher electrical and thermal conductivities than those of the ceramic with a finer microstructure at the equivalent porosity because of the smaller number of grain boundaries per unit volume. The decoupling of the electrical conductivity from the thermal conductivity was possible to some extent by adjusting the sintering temperature, i.e., microstructure, of the porous SiC ceramic.     

High-strength thermal insulating porous mullite fiber-based ceramics

How to improve the strength of fibrous porous ceramics dramatically under the premise of no sacrificing its low density and thermal conductivity has remained a challenge in the high-temperature thermal insulation field. In this paper, a new kind of high-strength mullite fiber-based ceramics composed of interlocked porous mullite fibers was prepared by nanoemulsion electrospinning and dry pressing method. Results show that as to the porous ceramics with the same density (～ 0.8 g/cm³), the three-dimensional skeleton structure composed of porous mullite fibers was much denser than that composed of solid mullite fibers. Therefore, porous mullite fiber-based ceramics exhibited a higher compressive strength (5.53 MPa) than that of solid mullite fiber-based ceramics (3.21 MPa). In addition, porous mullite fiber-based ceramics exhibited a superior high-temperature heat insulation property because the porous structure in fibers could reduce the radiant heat conduction. This work provides new insight into the development of high-temperature thermal insulators.     

Improved mechanical strength and thermal resistance of porous SiC ceramics with gradient pore sizes

Thermal insulation applications of porous SiC ceramics require low thermal conductivity and high mechanical strength. However, low thermal conductivity and high mechanical strength possess a trade-off relationship, because improving the mechanical strength requires decreasing the porosity, which increases the thermal conductivity. In this study, we established a new strategy for improving both the mechanical strengths and thermal resistances of porous SiC ceramics with micron-sized pores by applying a double-layer coating with successively decreasing pore sizes (submicron- and nano-sized pores). This resulted in a unique gradient pore structure. The double-layer coating increased the flexural strengths and decreased the thermal conductivities of the porous SiC ceramics by 24–70 % and 29–49 % depending on the porosity (48–62 %), improving both their mechanical strengths and thermal resistances. This strategy may be applicable to other porous ceramics for thermal insulation applications.     

Fabrication and properties of SiC porous ceramics using a polyurethane preparation process

SiC porous ceramics can be prepared by introducing the polyurethane preparation method into the production process of ceramic biscuits, followed by sintering at 1300?°C for 2?h under N₂ flux after the cross-linking of polycarbosilane at 220?°C for 4?h in air. The microstructures, mechanical properties and infiltrations of the SiC porous ceramics are investigated in detail. The best dispersal effect comes from the SiC slurry with xylene as the solvent and a mixture of Silok®7096 (1?wt%) and Anjeka®6041 (4?wt%) as the dispersant. The compressive strength of SiC porous ceramics with high porosity (69.53%) reaches 16.9?MPa. The heat treatment can increase infiltration, the rate of which (4.296?×?10^?7 mm²) after the heat treatment at 750?°C in air is approximately two times faster than that before the heat treatment. The SiC porous ceramics fabricated in this study will have potential application in active thermal protection systems.     

Fabrication of porous silica ceramics by gelation-freezing of diatomite slurry

Diatomite-derived porous silica ceramics with high porosities of up to 90% were fabricated using a gelation-freezing method, which resulted in unidirectional cellular or random microstructure with micrometer-sized cells. The ice crystals that were formed during freezing of a diatomite powder dispersed gel were removed by sublimation during vacuum drying, and the green bodies were sintered at 1150–1350 °C for 2 h in air. The thermal conductivity of the porous ceramics prepared with initial solid loadings of 5 and 10 vol% ranged from 0.09 to 0.16 W/(mK) at room temperature. The proposed method is therefore promising for the preparation of ceramic thermal insulators with very low thermal conductivity.     

High-strength thermal insulating mullite nanofibrous porous ceramics

Mullite fibrous porous ceramics is one of the most commonly used high temperature insulation materials. However, how to improve the strength of the mullite fibrous porous ceramics dramatically under the premise of no sacrificing the low sample density has always been a difficult scientific problem. In this study, the strategy of using mullite nanofibers to replace the mullite micron-fibers was proposed to fabricate the mullite nanofibrous porous ceramics by the gel-casting method. Results show that mullite nanofibrous porous ceramics present a much higher compressive strength (0.837 MPa) than that of mullite micron-fibrous porous ceramics (0.515 MPa) even when the density of the mullite nanofibrous porous ceramics (0.202 g/cm³) is only around three quarters of that of the mullite micron-fibrous porous ceramics (0.266 g/cm³). The obtained materials that present the best combination of mechanical and thermal properties can be regarded as potential high-temperature thermal insulators in various thermal protection systems.     

Processing and properties of silica-bonded porous nano-SiC ceramics with extremely low thermal conductivity

Silica-bonded porous nano-SiC ceramics with extremely low thermal conductivity were prepared by sintering nano-SiC powder-carbon black template compacts at 600–1200 °C for 2 h in air. The microstructure of the silica-bonded porous nano-SiC ceramics consisted of SiC core/silica shell particles, a silica bonding phase, and hierarchical (meso/macro) pores. The porosity and thermal conductivity of the silica-bonded porous nano-SiC ceramics can be controlled in the ranges of 8.5–70.2 % and 0.057–2.575 Wm⁻¹ K⁻¹, respectively, by adjusting both, the sintering temperature and template content. Silica-bonded porous nano-SiC ceramics with extremely low thermal conductivity (0.057 Wm⁻¹ K⁻¹) were developed at a very low processing temperature (600 °C). The typical porosity, average pore size, compressive strength, and specific compressive strength of the porous nano-SiC ceramics were ∼70 %, 50 nm, 2.5 MPa, and 2.7 MPa·cm³/g, respectively. The silica-bonded porous nano-SiC ceramics were thermally stable up to 1000 °C in both air and argon atmospheres.     

叔丁醇基凝胶注模成型制备氧化铝多孔陶瓷

以微米级Al2O3粉料为原料,叔丁醇为溶剂,采用凝胶注模成型工艺制备了氧化铝多孔陶瓷,并研究了Al2O3浆料的固相体积分数(分别为8%、10%、13%和15%)对1 500℃保温2 h烧后氧化铝多孔陶瓷的气孔率、气孔孔径分布、耐压强度、热导率和显微结构的影响.结果表明:当Al2O3浆料的固相体积分数从8%增加到15%时,氧化铝多孔陶瓷烧结体的总气孔率从71.2%逐渐降低至61.2%,气孔平均孔径从1.0 μm逐渐减小至0.78 μm,耐压强度从16.0 MPa逐渐增大至45.6 MPa,而热导率从1.03 W·(m·K)-1逐渐增大至1.83W·(m·K)-1.     

New multifunctional porous Yb2SiO5 ceramics prepared by freeze casting

New porous Yb₂SiO₅ ceramics were prepared by a water-based freeze casting technique using synthesized Yb₂SiO₅ powders. The prepared porous Yb₂SiO₅ ceramics exhibit multiple pore structures, including lamellar channel pores and small pores, in its skeleton. The effects of the solid content and sintering temperature on the pore structure, porosity, dielectric and mechanical properties of the porous Yb₂SiO₅ ceramics were investigated. The sample with 20 vol% solids content prepared at 1550 °C exhibited an ultra-low linear shrinkage (i.e. 4.5%), a high porosity (i.e. 79.1%), a high compressive strength (i.e. 4.9 MPa), a low dielectric constant (i.e. 2.38) and low thermal conductivity (i.e. 0.168 W/(m K)). These results indicate that porous Yb₂SiO₅ ceramics are good candidates for ultra-high temperature broadband radome structures and thermal insulator materials.     

A novel method for the fabrication of porous calcium hexaluminate (CA6) ceramics using pre-fired CaO/Al2O3 pellets as calcia source

Herein, porous calcium hexaluminate ceramics that contain pores exhibiting multiple morphologies were fabricated via in situ reaction sintering using α-Al₂O₃ powders and pre-fired CaO/Al₂O₃ pellets. The results indicated that the composition of the pre-fired CaO/Al₂O₃ pellets significantly affected the pore morphology, reaction-diffusion mechanisms, sintering behaviour and properties of the porous CA₆ ceramics. For the specimens containing low CaO/Al₂O₃-ratio (0.37) pellets, the main reaction occurred by solid state diffusion, i.e. ion diffusion through the solid reactant phase, which resulted in a slow process and low CA₆ formation rate at an elevated sintering temperature. With higher CaO/Al₂O₃-ratio (0.57) pellets, large-sized pores were observed because of transient liquid phase diffusion during the sintering process. The transient liquid phase diffusion effect increased the porosity of the porous ceramics and promoted the formation of a large number of plate-like CA₆ grains in the walls of the pores, enhancing their mechanical properties and high-temperature performance. The porous CA₆ ceramics containing high CaO/Al₂O₃-ratio (0.57) pellets sintered at 1700 °C exhibited high open porosity (55.88%), low thermal conductivity and excellent high-temperature performance.     

Transient liquid phase sintering of high-purity mullite for high-temperature structural ceramics

High-purity mullite ceramics, promising engineering ceramics for high-temperature applications, were fabricated using transient liquid phase sintering to improve their high-temperature mechanical properties. Small amounts of ultrafine alumina or silica powders were uniformly mixed with the mullite precursor depending on the silica-alumina ratio of the resulting ceramics to allow for the formation of a transient liquid phase during sintering, thus, enhancing densification at the early stage of sintering and mullite formation by the reaction between additional alumina and the residual glassy phase (mullitization) at the final stage of sintering. The addition of alumina powder to the silica-rich mullite precursor resulted in a reaction between the glassy silica and alumina phases during sintering, thereby forming a mullite phase without inhibiting densification. The addition of fine silica powder to the mullite single-phase precursor led to densification with an abnormal grain growth of mullite, whereas some of the added silica remained as a glassy phase after sintering. The resulting mullite ceramics prepared using different powder compositions showed different sintering behaviors, depending on the amount of alumina added. Upon selecting an optimum process and the amount of alumina to be added, the pure mullite ceramics obtained via transient liquid phase sintering exhibited high density (approximately 99%) and excellent high-temperature flexural strength (approximately 320 MPa) at 1500 °C in air. These results clearly demonstrate that pure mullite ceramics fabricated via transient liquid phase sintering with compositions close to those of stoichiometric mullite could be a promising process for the fabrication of high-temperature structural ceramics used in an ambient atmosphere. The transient liquid phase sintering process proposed in this study could be a powerful processing tool that allows for the preparation of superior high-temperature structural ceramics used in the ambient processing atmosphere.     

Enhancing the thermal insulating properties of lanthanum zirconate porous ceramics via pore structure tailoring

The potentially useful role of lanthanum zirconate (La₂Zr₂O₇, LZO) porous bulk ceramics has been rarely explored thus far, much less the optimisation of its pore structure. In this study, LZO porous ceramics were successfully fabricated using a tert-butyl alcohol (TBA)-based gelcasting method, and the pore structures were tailored by varying the initial solid loading of the slurry. The as-prepared ceramics exhibited an interconnected pore structure with high porosity (67.9 %–84.2 %), low thermal conductivity (0.083–0.207 W/(m·K)), and relatively high compressive strength (1.56–7.89 MPa). The LZO porous ceramics with porosity of 84.2 % showed thermal conductivity as low as 0.083 W/(m·K) at room temperature and 0.141 W/(m·K) at 1200 °C, which is much lower than the counterparts fabricated from particle-stabilized foams owing to its unique pore structure with a smaller size, exhibiting better thermal insulating performance.     

Foam-gelcasting preparation,microstructure and thermal insulation performance of porous diatomite ceramics with hierarchical pore structures

Hierarchically pore-structured porous diatomite ceramics containing 82.9∼84.5% porosity were successfully prepared for the first time via foam-gelcasting using diatomite powder as the main raw material. Sizes of mesopores derived from the raw material and macropores formed mainly from foaming were 0.02∼0.1 μm and 109.7∼130.5 μm, respectively. The effect of sintering temperature, additive content and solid loading of slurry on pore size and distribution, and mechanical and thermal properties of as-prepared porous ceramics were investigated. Compressive strength of as-prepared porous ceramics increased with sintering temperature, and the one containing 82.9% porosity showed the highest compressive strength of 2.1 ± 0.14 MPa. In addition, the one containing 84.5% porosity and having compressive strength of 1.1 ± 0.07 MPa showed the lowest thermal conductivity of 0.097 ± 0.001 W/(m·K) at a test temperature of 200 ̊C, suggesting that as-prepared porous ceramics could be potentially used as good thermal insulation materials.     

Foam gel-casting preparation of SiC bonded ZrB2 porous ceramics for high-performance thermal insulation

Lightweight SiC-ZrB₂ porous ceramics is of great potential as thermal insulation material used in aerospace, chemical and energy industries. In this work, a series of SiC bonded ZrB₂ (SiC_b-ZrB₂) porous ceramics with porosity high up to 86.9% were prepared by a simple foam gel-casting method. The SiC_b-ZrB₂ porous ceramic prepared at 1573 K exhibited a low thermal conductivity of 0.280 W/(m?K) and a reasonable compressive strength of 0.52 MPa. It could maintain the original geometric shape and microstructure after a secondary heat treatment at 1473 K in inert atmosphere. When heating the samples with thickness of 30 mm for 12 min with an alcohol spray lamp (～1273 K), the temperatures of the cold sides of SiC_b-ZrB₂ ceramics were all lower than 432 K, demonstrating their exceptional insulation capabilities. The present work provides a simple route to produce robust and thermally-insulating non-oxide porous ceramics for use under high temperature.     

Effective conductivity of porous ceramics in a radiative environment

The knowledge of the effective thermal conductivity, taking into account conduction and radiation, is crucial for the accurate prediction of the thermal behavior of porous foams, especially in an environment where radiation is dominating. We present a combined experimental-numerical method for the quantification of the temperature-dependent effective thermal conductivity of porous ceramics. The experiments include transient and spatially-resolved temperature measurements of ceramic foam samples with porosities between 75% and 92%, exposed to high radiative fluxes (peak of 1500 kW.m⁻²). Maximum surface temperatures of 1900K for high purity alumina samples and of 1500K for alumino-silicate (AS) samples were measured, and nonlinear temperature profiles through the sample along the main temperature gradient direction were measured. A 3D numerical model based on an OpenFOAM toolbox was developed and used to determine the thermal conductivity, using the experimental temperature measurements as input. We quantified the effective thermal conductivities (ETCs) in a temperature range of 288–1473K and showed that the ETC of AS samples can significantly increase in the presence of incoming and internal radiation. Alumina with 2 to 5 times smaller typical pore sizes (80 μm vs 190 μm, 230 μm, and 400 μm) exhibited an ETC dominated by conduction and relatively unaffected by radiation. This work illustrates that the ETC of porous materials exposed to radiative fluxes do not only depend on material properties or morphology but also on the operational conditions.     

Porous anorthite ceramics with ultra-low thermal conductivity

Porous anorthite ceramics with an ultra-low thermal conductivity of 0.018 W/m K have been fabricated by hydrous foam-gelcasting process and pressureless sintering method using γ-alumina, calcium carbonate and silica powders as raw materials. Microstructure and phase composition were analyzed by SEM and XRD respectively. Properties such as porosity, pore size distribution and thermal conductivity were measured. High porosity (69–91%) and low thermal conductivity (0.018–0.13 W/m K) were obtained after sintering samples with different catalyst additions at 1300–1450 °C. Porosity, pore size, pore structure and grain size had obvious effect on heat conduction, resulting in the low thermal conductivity. The experimental thermal conductivity data of porous anorthite ceramics were found to be fit well with the computed values derived from a universal model.     

Estimating thermal conductivities and elastic moduli of porous ceramics using a new microstructural parameter

Porous ceramics are numerically constructed based on the convexity of the void phase: microstructures with convex pores are representative of isolated or randomly overlapping spherical pores, while particulate materials with non-convex pores are composed of randomly overlapping, partial overlapping or partially sintered solid spheres. Finite element simulations show that, given the porosity, thermal conductivities and elastic moduli for convex porosity are larger than the values for non-convex pores. These conditions are not well described by solely porosity. By contrast, this study proposes a new microstructural parameter, <lp2>/(<ls2>+<lp2>), to estimate thermal conductivities and elastic moduli for both convex and non-convex pores. <ls2> and <lp2> are respectively mean-square solid chord length and mean-square pore chord length of cross-sections, which can be conveniently extracted from SEM images combined with chord length distributions of solid and void.     

The preparation and properties of high-strength porous mullite ceramics by a novel non-toxic gelcasting process

A novel approach to fabricate porous mullite ceramics with homogeneous pore size and high-strength using green non-toxic and cost-effective poly-γ-glutamic acid (γ-PGA) gelling system was reported for the first time. Effect of γ-PGA addition, additive amount and solid loading on rheological behavior of the slurries, and microstructure and properties of samples were investigated systematically. By optimizing the solid loading of mullite samples, we are able to get the sample with small pores (< 200 µm) dominating (93.3% of the total pores), and compressive strength of the sample reaches up to 26.62 MPa. In addition, the mullite ceramics exhibited high porosity of 75.7% with low thermal conductivity of 0.279 W/(m·K) at room temperature. This study not only provides a green and non-toxic gelling system but also offers porous mullite ceramics with low thermal conductivity and excellent mechanical strength as an energy-saving thermal insulation material.