本文针对稠油油藏开发现状及存在问题,在前期研究的基础上,提出了"稠油高强度堵水技术研究",研制了一种耐高温暂堵剂,并在工艺上采用复合封堵技术,利用经济可行、技术合理的高、中温堵剂进行定时封堵,达到调整吸汽剖面的目的以抑制边底水侵入,提高稠油井开采效果。     

注水井暂堵酸化技术研究与应用

长庆油田鄂尔多斯盆地储层非均质性较强,不同储层渗透率差异明显。长期注水开发后,注水剖面严重不均匀。当井况恶化时,分层酸化受到限制。一般酸化过程中酸液容易进入高渗透储层。中、低渗透储层损害无法有效消除。相反,差异被放大了。通过室内试验,筛选出适合注水井酸化的暂堵剂和纤维。通过模拟试验,优化了暂堵酸化工艺参数。更有利于消除中低渗透伤害,改善吸水剖面,提高酸利用率。为非均质严重致密油藏低渗透层精细分层注水提供了新思路。现场试验1井次,技术成功率100%。     

油水井调堵双向治理技术研究

要高含水开发油田储层层间、层内矛盾日益突出,剩余油挖潜难度越来越大,单一措施的增产幅度逐年降低,为了充分挖掘高含水井组的剩余油潜力,本文提出综合应用目前较成熟的水井调剖技术和油井堵水技术,对高含水井组进行油水井调堵双向治理,进一步提高油田采出程度,为剩余油挖潜提供技术支持。     

暂堵酸化技术研究应用

文、卫油田属复杂断块油田,储层非均质性较严重,层间渗透率变异系数为0.73~0.87。由于断块碎小、难以形成完善注采井网、能量衰减快三大矛盾突出,致使注水剖面和产液剖面极为不均,严重影响了油田的开发水平。同时,井况恶化,卡封分层酸化受限,而笼统酸化只有少量酸液进入渗透率较低的层位,无法达到均匀布酸的目的,不能有效解除中低渗透层伤害。通过泵入暂堵剂在高、中渗透层形成低渗透滤饼,从而使酸液转向中、低渗透层,充分挖掘笼统酸化波及不充分的低渗透层的潜力,强化差层动用。经过室内评价与现场实验相结合,为满足中低渗透层酸液分布剖面调整需要,筛选出了颗粒型水溶性暂堵剂。通过完善施工工艺、调整酸液配方、分析污染堵塞原因、合理确定处理半径和暂堵剂类型等措施手段,提高了暂堵酸化的针对性和酸化堵效果。为非均质性严重油藏中低渗透层的精细注水开发提供了一条有效的工艺途径。现场应用5井次,工艺成功率100%,暂堵有效率87.3%。     

谈高温暂堵剂与普通暂堵剂的一点认识

修井作业时采用普通暂堵剂,由于不耐温打入目的层后,往往被降解,不能起到暂堵效果。一种新型的高强度高温聚合物暂堵剂,对一些吞吐(或汽驱)后的高渗透、大孔道的漏失地层具有较好的封堵效果,对地层无污染,且防喷、防窜、防漏。     

合水油田暂堵酸化技术研究与应用

非均质严重地层存在局部高渗透带,常规酸化解堵后易引起含水大幅度上升,通过预先挤注一定量转向剂对高渗带进行暂堵,然后酸化的工艺,使酸液尽可能进入含油饱和度较高的低渗层段,从而提高油井产能,抑制含水上升,达到提高酸化效果的目的。     

注堵剂工具的研制与应用

常规化学堵水管柱对高含水层段进行封堵时,存在注堵剂后反洗或候凝阶段堵剂返吐、影响封堵效果等问题。因此,开展注堵剂工具的研制,现场试验10口井,工艺成功率100%,与常规化学堵水管柱应用效果相比,增油降水效果明显,对提高油层动用状况,控制含水上升速度具有重要的意义。     

改善注水井工况的措施探讨

以深入研究注水欠注的原因为基础,制定出具有针对性的治理措施,从而对注水效率进行大幅提高。对于调配困难和层间差异大而产生的欠注层,主要运用调剖堵水和重分层的方法来解决;对于渗透率差异和油层物质性产生的欠注层,主要是运用酸化降压同时辅以单井增压的方法来解决;对于因为后期堵塞而产生的欠注层,由于堵塞类型的不同,从而分别采用缓硝酸酸化和常规酸化等一些化学解堵工艺以及水力压裂等一些物理解堵方法来解决。     

暂堵酸化技术在姬塬油田三叠系的应用

一般土酸酸化只能使高渗层、大孔道或裂缝得到进一步酸化,加大储层之间的渗透率差异,造成出水孔道与出油孔道的相互沟通,从而使油井酸化后的采出液中,含水上升,增油效果不显著。暂堵酸化技术是把聚丙烯酰胺溶液携带暂堵剂先打入地层封堵高渗透大孔道地层或裂缝,在高渗层及部分中渗层中形成低渗透滤饼,再向地层中挤入土酸使低渗及堵塞油层得到有效酸化,由于暂堵剂具有酸不溶、水不溶、油溶的特性,可以从根本上改变油水两相渗透率,达到增产增油的目的。     

暂堵剂应用于压裂施工中的实验研究

水溶性压裂暂堵剂用于压裂封堵老裂缝,造新缝,改善油流通道;该剂在1%的水溶液及压裂液破胶液中在50℃、80℃、120℃均可溶解,溶解速度随温度增加而加快;室温20℃下,在压裂液中可分散并稳定;与压裂液及添加剂配伍;暂堵剂粒径对暂堵效果有影响,不同粒径组合比单一粒径暂堵压力高。     

耐高温高盐水平井堵水剂的研究与应用

研发了一种适合水平井先期堵水的堵水剂体系,以丙烯酰胺基-甲基丙磺酸为单体,亚甲基双丙烯酰胺为交联剂,甲醛合次硫酸钠-过硫酸铵为引发剂,考察了单体浓度、交联剂浓度、引发剂浓度、温度以及矿化度对堵剂体系性能的影响。结果表明,适合水平井先期堵水的堵水剂体系为8%单体丙烯酰氨基-甲基丙磺酸+0. 08%交联剂亚甲基双丙酰胺+0. 08%引发剂甲醛合次硫酸钠-过硫酸铵的复合聚合物,该堵剂体系具有较好的堵水性能,可以实现水平井段脚跟部堵水,适用矿化度可达10 000 mg/L,耐温性可达160℃,突破压力梯度可达9. 65 MPa/m,180℃以上完全破胶。现场实验表明,井日产液量从35. 2 m3下降到18 m3,日产油量从0. 5 t上升到4. 5 t,综合含水从98%下降到75%,目前累积增油达3 212 t,取得了比较好的结果。     

水杨酸生产技术进展

<正> 水杨酸是一种重要的中间体,在制药、染料、橡胶、树脂、火药等工业中,均有广泛的用途。在我国目前水杨酸仍属短线产品。水杨酸生产已有近百年的历史,工艺成熟,采用Schmidt-Kolbe法。即在压力温度下,由酚钠和二氧化碳反应,生成水杨酸钠,而后用硫酸酸析,得粗品水杨酸。经精制,可得到高纯度的药用水杨酸或工业水杨酸。随着石油化学工业的发展,大家都在寻求生产水杨酸的新方法。     

水膨性暂堵剂的制备及表征

以丙烯酰胺、丙烯酸钠为聚合单体,膨润土为填充剂,聚乙二醇二丙烯酸酯、N,N'-亚甲基双丙烯酰胺为交联剂、过硫酸钾与亚硫酸钠为氧化还原引发剂,制备了环保的可降解水膨性暂堵剂并研究了其性能。采用水溶液聚合法,通过改变膨润土、淀粉、交联剂、引发剂量,考察各因素对暂堵剂的性能影响。结果表明,当反应温度50℃,交联剂用量占单体的0.02%,引发剂用量占单体的0.6%,膨润土添加量5%(占总质量的百分数),该条件下合成的暂堵剂韧性较好,吸水率达184 g/g,19 h完全降解。在原有配方中分别加AMPS、淀粉以提高暂堵剂降解速度,并通过SEM对暂堵剂进行表征。     

A polyacrylamide hydrogel for application at high temperature and salinity tolerance in temporary well plugging

In addition to conventional approach to ensure the successful application of polymer hydrogels in maintaining temporary well plugging, exact analysis of gel formation and gel strength properties in wellbore are necessary. In this work, bottles and rheology tests are used to investigate the polymer hydrogel gelation time and cross-linking kinetics of sol–gel systems which consist of polyacrylamide and chromium acetate hydroxide as a cross-linker. The effects of temperature of 90 °C and pressure of 3000 psi (typical Iranian oil well condition) were studied in relation to gelation time, strength and the mechanical properties of the hydrogel. The average molecular weight of the polymer chains between cross-link ties was evaluated using an oil-well laboratory system and compressive strength test. Differential scanning calorimeter (DSC) analysis of dried gel and the effect of temperature on the kinetics of the gel swelling in different solutions such as distilled water, tap water, formation water and oil were studied. The results showed that the number of tie points between each entanglement has not much reduced under pressure. Therefore, the prepared hydrogel can maintain its chemical structure under the Iranian oil well pressure and can be proposed to field studies. The degree of sol–gel reaction of prepared hydrogel and the activation energy based on the Arrhenius equation were calculated to be 1.5 and 274 kJ/mol, respectively.     

TR-3型聚合物解堵剂的研究及应用

注聚合物对油田进行开发是一种常用的提高油田最终采收率的三次采油技术。随着聚合物注入量的增加，聚合物固体颗粒将沉积在孔隙中，这些附着物将会干扰聚合物的继续注入。因此我们研制了TR-3型聚合物解堵剂，我们应用研究的成果进行了现场试验，截止到2004年12月底，共应用解堵剂12吨，累计施工4井次，成功4井次，施工工艺成功率100％。平均单井增注2400m^3，平均单井增注聚合物母液1300m^3，对应油井增油420吨，取得了较好的经济效益。同时挤注解堵剂解堵后，平均降低注聚压力1．2MPa。     

新型抗高温水溶性暂堵剂实验研究

高温120℃下,使用不同分子量和水解度的聚丙烯酰胺与多种交联剂按照不同比例进行交联反应,得到高温暂堵剂体系,通过对暂堵剂的成冻时间、稳定时间和破胶时间等因素的研究,确定暂堵剂体系的聚合物为PAM1200,聚合物质量浓度为0.4%～0.55%;交联剂为G与YG107(2∶1)复配体,质量浓度为0.1%～0.2%,破胶剂质量浓度0.03%～0.05%。在120℃0,.5%PAM1200,0.1%交联剂G,0.2%交联剂YG107,0.03%破胶剂下,稳定性评价实验及岩心流动实验表明:暂堵剂对不同渗透率的岩心封堵率达92.75%,暂堵后渗透率恢复率高于83.19%,具有较好的破胶液化能力。     

淀粉基可降解暂堵剂制备及性能评价

以玉米淀粉和3种丙烯酸类单体为原料,通过接枝反应,在交联作用下聚合,同时混掺纳米碳酸钙,制备了一种环保型可降解暂堵剂STA-2。STA-2热稳定性优于淀粉,在土壤中可降解,吸水后具有变形虫的特点,对不同渗透率的岩心封堵性较强,具有自适应封堵特点,岩心渗透率恢复值可达85%以上。STA-2对水基钻井液流变性影响较小,可降低滤失量,改善储层保护效果。     

碎屑岩油藏YN-1水平井堵剂的性能评价与应用

根据碎屑岩油藏的特征,研制了能在地层中有效驻留,并能形成界面交结强度大、有效期长的YN-1水平井液凝化学堵剂,评价了凝胶体强度、耐温性、抗盐性、堵剂注入能力、堵塞能力等性能,并进行了堵水施工应用。结果表明,该堵剂的封堵降水效果明显,能够满足现场需要。     

油井堵水用高强度酚醛树脂预聚体封堵剂的合成

以苯酚、甲醛为原料,氢氧化钠为催化剂,采用两步碱催化方法合成了一种高强度酚醛树脂预聚体封堵剂。考察了甲醛与苯酚摩尔比、体系pH值、反应温度和反应时间等对酚醛树脂预聚体性能的影响。结果表明:当甲醛与苯酚摩尔比为3:1、体系pH值为9~10、反应温度为90℃、反应时间为30 min时,得到水溶性好、黏度较低的酚醛树脂预聚体,且该预聚体固化后,形成的固体强度高;封堵剂强度随酚醛树脂预聚体用量的增加而增大,当酚醛树脂预聚体的质量分数为50.0%时,填砂管模拟实验测得的突破压力梯度为40.65 MPa/m,具有很强的封堵能力。     

管外封窜剂的研究及应用

高强度管外封窜技术主要针对河南油田高压水井、稠油热采井管外窜的特点及对封窜工艺技术的要求,自主研发的高强度管外封窜剂及其配套工艺。高强度管外封窜剂具有强度高、抗拉伸性能好、与套管界面胶结强度高、封堵率高、体系粘度低、易泵注、施工安全简便等特点。河南油田先后开展了楼8201、楼3904、王EW40等80多井次的现场应用试验,工艺成功率100%,有效率100%,措施井阶段累计增油46158.3t,降水53156.1m3,该技术的成功应用,形成了适合河南油田高压水井、稠油热采井管外窜封堵的新技术。