PP/PVC基竹塑复合材料的阻燃改性研究

为开发阻燃竹塑复合材料,选用聚丙烯接枝马来酸酐(PP-g-MAH)为相容剂,以聚丙烯(PP)/聚氯乙烯(PVC)不相容体系为基体,采用挤出-注塑工艺制备了PP/PVC基竹塑复合材料。研究了相容剂对共混复合材料力学性能的影响,并对复合材料体系的阻燃改性进行了研究。结果表明:增容剂PP-g-MAH能够明显改善PP/PVC共混体系的力学性能,当其用量为10份时体系的力学性能较好;添加三氧化二锑或磷酸三苯酯,能显著提高PP/PVC基竹塑复合材料的阻燃性能。     

填料改性充油SEBS／PP共混材料的摩擦学和力学性能研究

研究了不同种类填料对充油苯乙烯-乙烯/丁烯-苯乙烯(0-SEBS)/聚丙烯(PP)共混材料摩擦学和力学性能的影响以及滑石粉(Talc)粒径和用量对O-SEBS/PP/Talc体系各项性能的影响.结果表明:填料的加入能有效提高共混物的硬度,降低摩擦因数;在滑石粉用量相同时,滑石粉的粒径越小,材料的综合力学性能和摩擦学性能越优越;随着滑石粉用量的增大,材料的拉伸强度和硬度增大,摩擦因数下降,磨耗量略有上升.共混材料脆断面形貌表明:填料在O-SEBS/PP基体中发生了团聚或附聚现象;磨擦后,O-SEBS/PP磨损表面上有明显的黏着磨损痕迹,加人大量填料后共混材料磨损机制主要表现为磨粒磨损,同时共混材料的磨损性能下降.     

PP-g-MAH和SMAH增容PP/PA11的研究

分别用马来酸酐接枝聚丙烯(PP-g-MAH)和(苯乙烯/顺丁烯二酸酐)无规共聚物(SMAH)作增容剂,对聚丙烯(PP)／尼龙11(PA11)共混体系的拉伸性能、缺口冲击性能进行了研究。傅立叶转换红外光谱表明,SMAH的增容机理与PP-g-MAH不同。比较了两种增容体系的差示扫描量热曲线,PP-g-MAH增容体系中PP的熔融温度向更高温度移动。     

PP/SEBS/MH复合材料的制备及其性能研究

采用极限氧指数（LOI）和热重分析（TGA）研究了聚丙烯（PP）/氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物（SEBS）/氢氧化镁（MH）复合材料的阻燃性能和热降解行为;探讨了SEBS和MH分别对PP/SEBS共混体系和PP/SEBS/MH复合材料力学性能和熔体流动速率的影响。结果表明：PP/SEBS/MH复合材料的力学性能和加工流动性能随着MH的质量分数增加而降低;复合材料高温下的热稳定性得到提高,MH分解吸热降低材料的热降解速率;MH以吸热方式在凝缩相和气相中发挥阻燃作用,复合材料阻燃性能得到提高,当MH的质量分数为60%时,LOI可达26.3%。     

聚丙烯/聚氯乙烯共混物阻燃性能的研究

选用聚丙烯接枝马来酸酐(PP-g-MAH)为增容剂,以聚丙烯(PP)、聚氯乙烯(PVC)不相容体系为基体,采用双螺杆挤出机制备了PP/PVC共混物混合料。研究了不同PVC组分比及增容剂对PP/PVC共混体系阻燃性能的影响;并对PP/PVC体系的综合性能进行了研究。结果表明,随着PVC用量的增加,PP/PVC共混体系的阻燃性能逐渐变好,力学性能大幅下降。增容剂PP-g-MAH能够明显改善PP/PVC共混体系的力学性能,当其用量为4份时体系的力学性能较好。添加阻燃协效剂Sb2O3可以明显提高PP/PVC共混体系的阻燃性能。     

PTT/PP共混物的性能研究

通过熔融共混制备了聚对苯二甲酸丙二酯/聚丙烯(PTT/PP=75/25)及其马来酸酐接枝PP(PP-g-MAH)增容共混物,研究了PTT/PP及其增容共混物的结晶性能、力学性能、流变性能和结晶形态。研究结果表明,PTT与PP共混能提高PP、PTT组分的结晶温度;对于增容共混物,随PP-g-MAH用量的增加,PP和PTT的结晶温度基本不变。加入PP使PTT拉伸强度降低,冲击强度提高;PP-g-MAH增容使共混物的拉伸和冲击强度都提高。增容共混物的熔体粘度明显降低,存在明显的剪切变稀现象,但熔体粘度与PP-g-MAH用量无关。在一定用量范围内,随PP-g-MAH用量的增加,PP分散相的尺寸变小。     

增容PP/回收PET共混物的力学性能

采用熔融挤出法制备了聚丙烯(PP)/增容剂/回收聚对苯二甲酸乙二酯(r-PET)共混物,研究了r-PET、不同增容剂和混合增容剂对PP/r-PET共混物力学性能的影响.r-PET提高了PP的拉伸强度、弯曲强度及其模量,但降低了冲击强度;采用马来酸酐接枝聚丙烯(PP-g-MAH)增容,可提高PP/r-PET共混物的拉伸强度、弯曲强度及其模量,但使冲击强度稍有降低;马来酸酐接枝乙烯-辛烯共聚物(POE-g-MAH)增容或PP-g-MAH/POE-g-MAH混合增容可提高PP/r-PET共混物的冲击强度,且对共混物的拉伸和弯曲强度影响不大.     

PP/PS/SBS共混物的性能研究

通过添加聚苯乙烯(PS)、热塑性弹性体苯乙烯-丁二烯-苯乙烯共聚物(SBS),以改善聚丙烯(PP)的性能。先采用熔融法制备PP/PS共混物,在确定PP,PS最佳配比的基础上,再添加SBS制备PP/PS/SBS共混物,确定了PP,PS及SBS的最佳配比。研究了PP/PS,PP/PS/SBS共混物的力学性能、热性能及熔体流动行为。结果表明,当PP与PS的质量比为70∶30时,PP/PS共混物的性能最好,其拉伸强度为28.5 MPa,拉伸弹性模量为1 214 MPa,弯曲弹性模量为1 752 MPa,冲击强度为14.0 kJ/m2,断裂应变为130%,维卡软化温度为143.9℃。当PP,PS及SBS的质量比为70∶30∶10时,PP/PS/SBS共混物的性能最好,其拉伸强度为23.2 MPa,拉伸弹性模量1 040 MPa,断裂应变为260%,冲击强度为18.0 kJ/m2,弯曲强度为36.5 MPa,弯曲弹性模量为1 297 MPa,定挠度弯曲应力为36.1 MPa,弯曲破坏应力为36.5 MPa,熔体流动速率为8.94 g/(10 min),维卡软化温度为139.0℃。     

PP-g-MAH增容PP/PA66共混物的形态结构和性能

用固相接技法制备了马来酸酐接枝改性聚丙烯(PP-g-MAH),研究了PP-g-MAH增容PP/PA66共混物的形态结构和性能。结果表明,未用PP-g-MAH增容的PP/PA66共混物是热力学不相容的海岛型两相结构,而用PP-g-MAH增客的PP/PA66共混物虽是两相结构,但分散相粒子尺寸大大减小,PP-g-MAH对PP/PA66共混物实现了反应性增容。与不含PP-g-MAH的PP/PA66共混物相比,PP-g-MAH增容的PP/PA66共混物的拉伸强度提高约10 MPa,弯曲强度提高约10 MPa,弯曲模量增加10％,缺口冲击强度和伸长率保持不变。     

成核剂与增容剂调控聚乳酸/聚丙烯复合材料的结晶与力学性能研究

通过熔融共混法制备聚丙烯/聚乳酸(PP/PLA)复合材料,研究成核剂癸二酸二苯基二酰肼(TMC-300)和增容剂聚丙烯接枝马来酸酐(PP-g-MAH)对PP/PLA复合材料的结晶行为、热学性能、力学性能的影响。结果表明,TMC-300能够显著提高PP/PLA共混物的结晶速率和结晶度,降低球晶尺寸,并改善复合材料的力学性能。当TMC-300添加量为0.5%时,共混物的熔点从163.9℃提高到168.6℃,结晶度达到44.2%,比纯PP/PLA提高25.6%,拉伸强度和冲击强度分别增加了13.33%,49.86%。当增容剂与成核剂并用时,增容剂可改善PLA链段运动能力,并提供更多的成核位点,进一步促进PLA的结晶性能,且结晶的分布由海岛式结构变为双连续相结构,复合材料的拉伸强度比纯PP/PLA提升了19.25%。     

增容剂对PP/PP-g-MAH/CaCO_3复合材料性能与形态的影响

采用熔融混合法制备了PP/PP-g-MAH/CaCO3复合材料,并利用万能试验机、差示扫描量热仪(DSC)和扫描电子显微镜(SEM)分析了PP-g-MAH含量对PP/PP-g-MAH/CaCO3复合材料力学性能、结晶性能与界面形态的影响。结果表明:随着增容剂PP-g-MAH含量的增加,PP/PP-g-MAH/CaCO3复合材料的拉伸强度从25.7 MPa增加到32.0 MPa,弯曲强度从34.7 MPa增大到41.2 MPa;结晶温度则先增大后逐渐减小,当PP-g-MAH含量为2%时结,晶温度为123.9℃,结晶度为44.7%;而断裂伸长率和冲击强度逐渐减小。     

Surface modification of magnesium hydroxide and its application in flame-retardant oil-extended styrene–ethylene–butadiene–styrene/polypropylene composites

Magnesium hydroxide (MH) was modified with triethoxysilane and polymethyl–vinyl silicone rubber and used to prepare flame-retardant oil-extended styrene–ethylene–butadiene–styrene (O-SEBS)–polypropylene (PP) composites. The water contact angle of modified magnesium hydroxide (MMH) reached 141°; this indicated that MMH possessed excellent hydrophobic properties. The samples (1.6 mm) passed the UL-94 V-0 rating during vertical burning tests when the loading amount of MH or MMH was 70 wt %. This indicated the modification did not decrease the flame-retardant properties of MH. The tensile strength and elongation at break values of the MMH–O-SEBS–PP composites increased by 20.4 and 88.9%, respectively, compared with those of the MH–O-SEBS–PP composites. The modification of MH enhanced the interfacial compatibility between the flame retardant and the matrix; thus, the mechanical performance was enhanced. Moreover, MMH was scarcely extracted after water treatment for 168 h at 70 °C. As a result, the mechanical properties and flame retardancy of the MMH–O-SEBS–PP composites were well maintained after the water treatment. The modification of the MH endowed the O-SEBS–PP composites with an excellent compatibility and water-resistant performance. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47129.     

热致性液晶共聚酯／聚丙烯共混物

通过熔融共混制备了不同配比的（ＰＨＢ／ＰＥＴ）／ＰＰ共混物，研究表明，共混物的弯曲弹性模量，弯曲强度及拉伸强度均比ＰＰ有所提高，当液晶含量为１５％，ＰＰ－ｇ－ＭＡＨ为２０％时，（ＰＨＢ／ＰＥＴ）（ＰＰ－ｇ－ＭＡＨ）／ＰＰ三元共混物弯曲弹性模量最大，ＰＰ－ｇ－ＭＡＨ作为两相界面相容剂，改善了两相间的亲合性。ＤＳＣ分析表明，共混物中ＰＰ相的结晶温度有较大幅度的提高，（ＰＨＢ／ＰＥＴ）共聚酯起了ＰＰ结晶     

聚丙烯/环氧树脂复合材料的制备及其性能研究

在聚丙烯(PP)基体中加入环氧树脂(EP)、固化剂、马来酸酐接枝聚丙烯(PP-g-MAH),通过动态固化制备了PP/EP复合材料,并对其相容性、力学性能、结晶性能等进行了研究。结果表明:PP/EP为不相容体系,PP-g-MAH作为反应性增容剂对体系的刚性和模量影响较大;通过EP和PP-g-MAH的接枝反应,增强了两相间的界面作用力,降低了EP分散相的尺寸,改善了PP/EP复合材料的力学性能。力学性能测试结果表明,EP与PP-g-MAH的最佳配比为1:1;等温结晶的偏光照片和DSC数据表明,EP阻碍了PP的结晶,使其球晶微细化、结晶度降低。     

复配增容剂增容PPO/PP/GF研究

研究复配增容剂(SEPS/PP-g-MAH)对玻璃纤维(GF)增强聚苯醚(PPO)/聚丙烯(PP)力学性能、熔体流动性以及耐热性能的影响,并用扫描电子显微镜观察了不同共混体系的形态结构.结果表明,复配增容剂改善了PPO/PP/GF共混体系的相容性,提高了共混体系的拉伸强度、弯曲强度、冲击强度和熔体流动速率,但同时降低了...     

PP-g-(MAH/VAc)接枝物对PP/PA6体系的增容作用

通过扫描电镜、差示扫描量热仪和力学性能测试等方法研究了聚丙烯接枝马来酸配和酷酸乙烯酷(PP-g-MAH/VAc)对聚丙烯康酸胺6(80/20}共混体系的增容效果。结果表明,PP-g-(MAH/DAc)用于PP/PA6共混体系,分散相PA6的微区尺寸可以减小到5μm以下,相应地提高了共混物的断裂伸长率、拉伸强度和冲击强度。使用接枝率为5.3%的PP-g-(MAH/VAc)作为相容剂,当用量为8%时,体系的拉伸强度为60.88MPa,断裂伸长率为558%,冲击强度为5.28KJ/㎡.DSC分析表明,PP/PA6共混体系各组分相互促进成核,结晶度降低。FTIR结果表明,PP-g-(MAH/VAc)中的MAH上的酸配基团与PA6中的酸胺键发生了化学反应从而改善了体系的相容性。     

PP-g-MAH增容改性木粉/PP复合材料的性能研究

以马来酸酐接枝聚丙烯 (PP-g-MAH) 为相容剂,聚丙烯 (PP) 为基体,通过熔融共混法制备了木粉/PP复合材料。研究了 PP-g-MAH 用量对复合材料力学性能及吸水性能的影响; 采用扫描电镜 (SEM) 观察了复合体系的冲击断面形貌。结果表明: 当 PP-g-MAH 的质量分数为 4%时,可以提高添加 35 份木粉复合材料体系的拉伸强度及弯曲强度,比未添加相容剂的分别提高了 49.4%和 16%,而缺口冲击强度仅下降了 9%。SEM 观察证实: PP-g-MAH 的加入有利于提高木粉与 PP 基体的界面相互作用。从吸水率来看,木粉/PP 复合材料的吸水率保持在 0.22% 以下,远低于纯木材。     

An investigation on the influence of filler loading and compatibilizer on the properties of polypropylene/marble sludge composites

In this article, polypropylene reinforced marble sludge (PP/MS) was prepared, and the effects of MS loading and polypropylene-g-maliec anhydride (PP-g-MAH) as compatibilizer on density, melt flow index (MFI), and mechanical properties of PP/MS composite were investigated. Our studies show that tensile strength, flexural strength and tensile modulus increased with increasing the MS loading but tensile strength increased till 30 pph of MS further addition of MS in PP composites decreased the strength. The % elongation at break and Izod Impact Strength decreased with increasing of MS loading. Studies revealed that PP/MS composites containing PP-g-MAH enhance the properties compared to without compatibilizer.     

复合型相容剂的制备及其对PP／煤共混体系的增容作用

采用固相接枝和力化学改性的方法制备了复合型相容剂PP－g-MAH(AM)－煤，采用FTIR，毛细管流变仪，SEM及力学性能测试对相容剂的增容作用进行研究，发现随着相容剂含量的增加，材料的断裂类型由脆性转为韧性，对于煤含量为15％的共混材料，添加本相容剂后拉伸强度由12．981MPa提高到31．051MPa，且新型相容剂较常规相容剂对PP／煤共混材料有更好的增容效果。     

聚丙烯/纳米黏土复合材料抗熔垂性能的研究

在双螺杆挤出机上制备了聚丙烯/纳米黏土复合材料;考察了其结构对其抗熔垂性能的影响。X射线衍射分析结果表明,实验得到了插层结构聚丙烯/纳米黏土复合材料,不同的聚丙烯基体和相容剂用量影响材料的插层结构。抗熔垂性能研究发现,不同的插层结构,抗熔垂性能不同。其中,黏土片层插层结构的层间距与材料抗熔垂性能存在一定关联,插层结构中黏土片层层间距过大或过小都不利于抗熔垂性能的改善,层间距为2.90-3.00 nm的插层结构的聚丙烯/纳米黏土复合材料具有较好的抗熔垂性能。