Synthesis and properties of novel copolymers of poly(ether ketone ether ketone ketone) and poly(ether ketone ketone ether ketone ketone) containing 1,4‐naphthylene moieties

A new monomer, 1,4‐bis(4‐phenoxybenzoyl)naphthalene (BPOBN), was conveniently synthesized via a simple synthetic procedure from readily available materials. A series of novel copolymers of poly(ether ketone ether ketone ketone) and poly(ether ketone ketone ether ketone ketone) containing 1,4‐naphthylene moieties were prepared by the Friedel‐Crafts acylation solution copolycondensation of terephthaloyl chloride (TPC) with a mixture of BPOBN and 4,4′‐diphenoxybenzophenone (DPOBPN), over a wide range of BPOBN/DPOBPN molar ratios, in the presence of anhydrous AlCl₃ and N‐methylpyrrolidone in 1,2‐dichloroethane. The copolymers with 10–40% BPOBN are semicrystalline and had remarkably increased T_gs over the conventional PEEK and PEKK due to the incorporation of 1,4‐naphthylene moieties in the main chains. The copolymers with 30–40 mol% BPOBN had not only high T_gs of 176–177°C, but also moderate T_ms of 332–338°C, which are suitable for the melt processing. These polymers had tensile strengths of 101.5–104.7 MPa, Young's moduli of 2.49–2.65 GPa, and elongations at break of 13.3–15.7% and exhibited high thermal stability and excellent resistance to organic solvents. POLYM. ENG. SCI., 56:566–572, 2016. © 2016 Society of Plastics Engineers     

Synthesis and properties of novel copolymers of poly(ether ketone diphenyl ketone ether ketone ketone) and poly(ether amide ether amide ether ketone ketone)

New monomers, 4,4′‐bis(4‐phenoxybenzoyl)diphenyl (BPOBDP) and N,N′‐bis(4‐phenoxybenzoyl)?4,4′‐diaminodiphenyl ether (BPBDAE), were conveniently synthesized via simple synthetic procedures from readily available materials. Novel copolymers of poly(ether ketone diphenyl ketone ether ketone ketone) (PEKDKEKK) and poly(ether amide ether amide ether ketone ketone) (PEAEAEKK) were synthesized by electrophilic Friedel‐Crafts solution copolycondensation of isophthaloyl chloride (IPC) with a mixture of BPOBDP and BPBDAE, over a wide range of BPOBDP/BPBDAE molar ratios, in the presence of anhydrous AlCl₃ and N‐methylpyrrolidone (NMP) in 1,2‐dichloroethane (DCE). The copolymers obtained were characterized by different physico‐chemical techniques. The copolymers with 10–40 mol% BPBDAE are semicrystalline and had remarkably increased T_gs over commercially available PEEK and PEKK due to the incorporation of amide and diphenyl linkages in the main chains. The copolymers IV and V with 30–40 mol% BPBDAE had not only high T_gs of 185–188°C, but also moderate T_ms of 326–330°C, having good potential for the melt processing. The copolymers IV and V had tensile strengths of 101.7–102.3 MPa, Young's moduli of 2.19–2.42 GPa, and elongations at break of 13.2–16.6% and exhibited high thermal stability and excellent resistance to organic solvents. POLYM. ENG. SCI., 54:1757–1764, 2014. © 2013 Society of Plastics Engineers     

Preparation and characterization of chloromethylated/quaternized poly(phthalazinone ether sulfone ketone) for positively charged nanofiltration membranes

Chloromethylated poly(phthalazinone ether sulfone ketone) (CMPPESK) as a novel membrane material was successfully prepared from poly(phthalazinone ether sulfone ketone), with concentrated sulfuric acid as the solvent and catalyst, and chloromethyl octyl ether with lower toxicity as the chloromethylated regent. The effects of the reaction conditions on the preparation of CMPPESKs with different degrees of chloromethylation were examined. The quantity of chloromethyl groups per repeated unit (DCM) of CMPPESK was determined by the method of analysis of the chlorine element, and structures were characterized by ¹H‐NMR spectroscopy. The introduction of chloromethyl groups into the polymer chains led to a decrease in the decomposition temperature. With increasing DCM, the initial degradation temperature declined. CMPPESK had good solubility and was soluble in N‐methyl‐2‐pyrrolidone (NMP), N,N‐dimethylacetamide (DMAc), and chloroform. However, quaternized poly(phthalazinone ether sulfone ketone) (QAPPESK) had excellent solvent resistance, was only partly soluble in sulfuric acid (98%), and was swollen in N,N‐dimethylformamide. QAPPESK nanofiltration (NF) membranes had about 90% rejection for MgCl₂, and the performance of the NF membrane prepared with DMAc as the solvent was superior to that of the NF membrane prepared with NMP as the solvent. In addition, the rejection to the different salt solutions followed the following sequence: MgCl₂ > MgSO₄ > NaCl > Na₂SO₄. Furthermore, the thermotolerance of the QAPPESK NF membrane was examined, and the results show that when the solution temperature rose from 11 to 90°C, the water flux increased more than threefold with stable salt rejection. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis and thermotropic liquid‐crystalline behaviour of novel main‐chain poly(ether ether ketone ketone)s containing a lateral tert‐butyl group

The synthesis of novel poly(ether ether ketone ketone)s containing a lateral group via the random copolymerization of 4,4′‐biphenol, tert‐butylhydroquinone and 1,4‐bis(p‐fluorobenzoyl)benzene is described. The copolymers were characterized by differential scanning calorimetry (DSC), wide‐angle X‐ray diffraction (WAXD) and polarized optical microscopy (POM) observation. The results showed that the thermotropic liquid‐crystalline properties were achieved in the copolymers containing 30 mol% and 50 mol% tert‐butylhydroquinone, which have relatively lower melting temperatures due to the copolymerization effect. Both the crystalline–liquid‐crystalline transition (T_m) and the liquid‐crystalline–isotropic phase transition (T_i) were observable in the DSC thermograms, while the biphenol‐based poly(aryl ether ketone) has only one melting transition. The hydroquinone‐based polymer was shown to be amorphous. Thermogravimetric analysis (TGA) results showed that these copolymers are all high‐temperature resistant with higher glass transition temperature between 147 and 149 °C, and higher decomposition temperature T_d in the range 480–520 °C. © 2000 Society of Chemical Industry     

Synthesis and properties of poly(aryl ether ketone)s containing both biphenylene moieties and sulfone linkages in the main chain

Two monomers, 4,4′‐bis(4‐phenoxybenzoyl)biphenyl (BPOBBP) and 4,4′‐diphenoxydiphenyl sulfone (DPODPS), were conveniently synthesized via simple synthetic procedures from readily available materials. A series of novel poly(aryl ether ketone)s containing both biphenylene moieties and sulfone linkages in the main chain were synthesized by the modified electrophilic Friedel‐Crafts acylation copolycondensation of isophthaloyl chloride (IPC) with a mixture of BPOBBP and DPODPS, over a wide range of BPOBBP/DPODPS molar ratios. The resulting polymers were characterized by Fourier transform infrared spectroscopy (FT‐IR), wide‐angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA), etc. The results indicated that the copolymers with 30 to 35 mol% DPODPS were semicrystalline and had remarkably increased glass transition temperatures (T_gs) over the conventional poly(ether ether ketone) (PEEK) and poly(ether ketone ketone) (PEKK) due to the incorporation of biphenylene units and sulfone linkages in the main chain. The copolymers with 30 to 35 mol% DPODPS had not only high T_gs of 176 to 177°C, but also moderate melting temperatures (T_ms) of 334 to 337°C, having good potential for the melt processing. The semicrystalline copolymers II to V had tensile strengths of 99.8 to 103.1 MPa, Young's moduli of 2.26 to 2.79 GPa, and elongations at break of 16.8 to 26.5% and exhibited outstanding thermal stability and good resistance to organic solvents. POLYM. ENG. SCI., 55:2140–2147, 2015. © 2015 Society of Plastics Engineers     

Synthesis and properties of copolymers of poly(ether ketone ketone) and poly(ether amide ether amide ether ketone ketone)

Poly(aryl ether ketone)s (PAEKs) are a class of high‐performance engineering thermoplastics known for their excellent combination of chemical, physical and mechanical properties, and the synthesis of semicrystalline PAEKs with increased glass transition temperatures (T_g) is of much interest. In the work reported, a series of novel copolymers of poly(ether ketone ketone) (PEKK) and poly(ether amide ether amide ether ketone ketone) were synthesized by electrophilic solution polycondensation of terephthaloyl chloride with a mixture of diphenyl ether and N,N′‐bis(4‐phenoxybenzoyl)‐4,4′‐diaminodiphenyl ether (BPBDAE) under mild conditions. The copolymers obtained were characterized using various physicochemical techniques. The copolymers with 10–35 mol% BPBDAE are semicrystalline and have markedly increased T_g over commercially available poly(ether ether ketone) and PEKK due to the incorporation of amide linkages in the main chain. The copolymers with 30–35 mol% BPBDAE not only have high T_g of 178–186 °C, but also moderate melting temperatures of 335–339 °C, having good potential for melt processing. The copolymers with 30–35 mol% BPBDAE have tensile strengths of 102.4–103.8 MPa, Young's moduli of 2.33–2.45 GPa and elongations at break of 11.7–13.2%, and exhibit high thermal stability and good resistance to organic solvents. Copyright © 2010 Society of Chemical Industry     

Physical and electrochemical behaviors of directly polymerized sulfonated poly(arylene ether ketone sulfone)s proton exchange membranes with different backbone structures

Sulfonated poly(ether ether ketone sulfone) (SPEEKS) and sulfonated poly(ether ether ketone ketone sulfone) (SPEEKKS) copolymers with different degree of sulfonation (DS) were synthesized by aromatic nucleophilic polycondensation of disodium 3,3′‐disulfonate‐4,4′‐dichloro‐diphenylsulfone (SDCDPS), tertbutylhydroquione, and 4,4′‐difluorobenzophenone or 1,4′‐bi(4‐fluorobenzoyl) benzene. Prepared sulfonated copolymers were characterized by Fourier transform infrared spectra, thermogravimetric analysis, and differential scanning calorimetry. The transmission electron microscope was used to investigate the microstructure of membranes. The different distance between two adjacent sulfonic groups in two series of membranes resulted in different physical and electrochemical properties between two kinds of membranes with the same DS. The proton conductivity, ionic exchange capacity and water uptake of SPEEKS membranes were higher than those of SPEEKKS membranes while the mechanical strength of SPEEKS membranes was lower than that of SPEEKKS membranes at the same DS. Moreover, the SPEEKKS membranes with DS equals to 0.8 showed a good combination of a high proton conductivity (0.046 S/cm at 25°C, 0.061 S/cm at 80°C), acceptable water uptake (33–65 wt %), excellent mechanical strength (tensile strength reached 49.7 MPa), and good thermal properties (T_g above 250°C, T_d5% above 300°C). It suggested that this could be a promising membrane for proton exchange membrane fuel cell application. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and characterization of organo‐soluble poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing pendant pentadecyl chains

Poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing pendant pentadecyl chains were synthesized by polycondensation of each of the two bisphenol monomers viz, 1,1,1‐[bis(4‐hydroxyphenyl)‐4′‐pentadecylphenyl]ethane and 1,1‐bis(4‐hydroxyphenyl)‐3‐pentadecyl cyclohexane with activated aromatic dihalides namely, 4,4′‐difluorobenzophenone, and 1,3‐bis(4‐fluorobenzoyl)benzene in a solvent mixture of N,N‐dimethylacetamide and toluene, in the presence of anhydrous potassium carbonate. Polymers were isolated as white fibrous materials with inherent viscosities and number average molecular weights in the range 0.70–1.27 dL g^?1 and 76,620–1,36,720, respectively. Poly(ether ether ketone)s and poly(ether ether ketone ketone)s were found to be soluble at room temperature in organic solvents such as chloroform, dichloromethane, tetrahydrofuran, and pyridine and could be cast into tough, transparent, and flexible films from their solutions in chloroform. Wide angle X‐ray diffraction patterns exhibited a broad halo at around 2θ = ～ 19° indicating that the polymers containing pentadecyl chains were amorphous in nature. In the small‐angle region, diffuse reflections of a typically layered structures resulting from the packing of pentadecyl side chains were observed. The temperature at 10% weight loss, obtained from TG curves, for poly(ether ether ketone)s and poly(ether ether ketone ketone)s were in the range 416–459°C, indicating their good thermal stability. A substantial drop in glass transition temperatures (68–78°C) was observed for poly(ether ether ketone)s and poly(ether ether ketone ketone)s due to “internal plasticization” effect of flexible pendant pentadecyl chains. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and characterization of poly(ether amide ether ketone)/poly(ether ketone ketone) copolymers

A new monomer, N,N′‐bis(4‐phenoxybenzoyl)‐m‐phenylenediamine (BPPD), was prepared by condensation of m‐phenylenediamine with 4‐phenoxybenzoyl chloride in N,N‐dimethylacetamide (DMAc). A series of novel poly(ether amide ether ketone) (PEAEK)/poly(ether ketone ketone) (PEKK) copolymers were synthesized by the electrophilic Friedel‐Crafts solution copolycondensation of terephthaloyl chloride (TPC) with a mixture of diphenyl ether (DPE) and BPPD, over a wide range of DPE/BPPD molar ratios, in the presence of anhydrous AlCl₃ and N‐methylpyrrolidone (NMP) in 1,2‐dichloroethane (DCE). The influence of reaction conditions on the preparation of copolymers was examined. The copolymers obtained were characterized by different physicochemical techniques. The copolymers with 10–25 mol % BPPD were semicrystalline and had remarkably increased T_gs over commercially available PEEK and PEKK due to the incorporation of amide linkages in the main chains. The copolymers III and IV with 20–25 mol % BPPD had not only high T_gs of 184–188°C, but also moderate T_ms of 323–344°C, having good potential for the melt processing. The copolymers III and IV had tensile strengths of 103.7–105.3 MPa, Young's moduli of 3.04–3.11 GPa, and elongations at break of 8–9% and exhibited outstanding thermal stability and good resistance to organic solvents. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and characterization of soluble poly(arylene ether ketone)s with high glass transition temperature based on 3,6‐bi(4‐fluorobenzoyl)‐N‐alkylcarbazole

3,6‐bi(4‐fluorobenzoyl)‐N‐methylcarbazole and 3,6‐bi(4‐fluorobenzoyl)‐N‐ethylcarbazole were synthesized and used to prepare poly(arylene ether ketone)s (PAEKs) with high glass transition temperatures (T_g) and good solubility. High molecular weight amorphous PAEKs were prepared from these two difluoroketones with hydroquinone, phenolphthalein, 9,9‐bis(4‐hydroxyphenyl)fluorene and 4‐(4‐hydroxylphenyl)‐2,3‐phthalazin‐1‐one, respectively. All these polymers presented high thermal stability with glass transition temperatures being in the range 239–303 °C and a 5% thermal weight loss temperature above 460 °C. Compared with the T_g of phenolphthalein‐based PAEK (PEK‐C), fluorene‐based PAEK (BFEK) and phthalazinone‐based PAEK (DPEK) not containing a carbazole unit, these polymers presented a 30–50 °C increase in T_g. Meanwhile, PAEKs prepared from N‐ethylcarbazole difluoroketone showed good solubility in ordinary organic solvents, and all polymers exhibited excellent resistance to hydrochloric acid (36.5 wt%) and sodium hydroxide (50 wt%) solutions. In particular, phthalazinone‐based PAEK bearing N‐ethylcarbazole afforded simultaneously a T_g of 301 °C with good solubility. Tensile tests of films showed that these polymers have desirable mechanical properties. The carbazole‐based difluoroketones play an important role in preparing soluble PAEKs with high T_g by coordinating the relationship between chain rigidity resulting from the carbazole unit and chain distance from the side alkyl. © 2014 Society of Chemical Industry     

Soluble and crosslinkable poly(phthalazinone ether ketone)s with pendent terminal ethynyl groups: synthesis,characterization and click modification

New poly(phthalazinone ether ketone)s (PPEKs) with pendent terminal ethynyl groups were synthesized by the aromatic nucleophilic substitution (S_NAr) polycondensation reaction of a new bisphenol monomer, 2‐(3‐ethynylphenyl)hydroquinone, with 4‐(4′‐hydroxyphenyl)phthalazin‐1(2H)‐one and 4,4′‐bis(4‐fluorophenyl) ketone, followed by click modification reaction with 1‐azidopyrene. Fourier transform infrared and NMR spectral data of the model compound indicated that the terminal ethynyl groups were stable in S_NAr reaction conditions, thus allowing the synthesis of the desired polymers. The PPEKs obtained with glass transition temperature (T_g) in the range 152–245 °C were amorphous, characterized by wide‐angle X‐ray diffraction, and dissolved in organic solvent to cast into transparent and flexible films. Differential scanning calorimetry results indicated that the curing reaction of the terminal ethynyl groups of the copolymers took place upon heating to 250 °C. The T_g of cured PPEKs was increased to about 260 °C. They also exhibited excellent thermal stability with 5% weight loss temperatures ranging from 448 to 527 °C in various atmospheres. The PPEKs with pendent terminal ethynyl groups were subsequently functionalized with pyrene through click reaction. A dilute chloroform solution displayed a red‐shifted emission profile. © 2014 Society of Chemical Industry     

Synthesis of novel poly(ether ketone diphenyl ketone ether ketone ketone)s by electrophilic Friedel–Crafts solution polycondensation

4,4′‐Bis(4‐phenoxybenzoyl)diphenyl was prepared by the Friedel–Crafts reaction of 4‐bromobenzoyl chloride and diphenyl followed by condensation with potassium phenoxide. Novel aromatic poly(ether ketone diphenyl ketone ether ketone ketone)s were obtained by the electrophilic Friedel–Crafts solution copolycondensation of 4,4′‐bis(4‐phenoxybenzoyl)diphenyl with a mixture of isophthaloyl chloride and terephthaloyl chloride over a wide range of isophthaloyl chloride/terephthaloyl chloride molar ratios in the presence of anhydrous aluminum chloride and N‐methylpyrrolidone in 1,2‐dichloroethane. The influence of the reaction conditions on the preparation of the copolymers was examined. The copolymers were characterized with different physicochemical techniques. Because of the incorporation of diphenyl, the resulting copolymers exhibited outstanding thermal stability. The glass‐transition temperatures were above 174°C, the melting temperatures were above 342°C, and the 5% weight loss temperatures were above 544°C in nitrogen. All these copolymers were semicrystalline and insoluble in organic solvents. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Copolymers of poly(arylene sulfide sulfone)/poly(ether sulfone): Synthesis,structure, and rheology properties

In order to overcome the poor flowability of poly(arylene sulfide sulfone) (PASS), we introduced ether bonds into the polymer main chain. A series poly(arylene ether sulfide sulfone) copolymers (PAESS) containing different proportion of ether bonds were synthesized with 4,4′‐dichlorodiphenyl sulfone (DCDPS), sodium sulfide (Na₂S·xH₂O), and 4,4′‐dihydroxydiphenyl ether (DHDPE). The copolymers were characterized by Fourier transform infrared (FTIR), ¹H‐nuclear magnetic resonance (NMR), differential scanning calorimetry, dynamic mechanical analysis (DMA), and rheometer. The results of FTIR and ¹H‐NMR indicate the copolymers are synthesized successfully. PAESS were found to have excellent thermal properties with glass transition temperature (T_g) of 175.7–219.1 °C and 5% weight lost temperature were all above 420 °C. The tensile and DMA test indicates that these resultant copolymers have good mechanical properties with tensile strength of 60 MPa and storage modulus of 1.5 GPa. From the results of rheology properties testing, we found that the melt stability and melt flowability of PASS were improved distinctly from 25,470 Pa s down to 355 Pa s with the incorporation of ether bonds. That will be quite beneficial to the processing of PASS, especially for the thermoforming of precision products. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46534.     

Synthesis and characterization of poly(ether ketone ether ketone ketone)/poly(ether ether ketone ketone) copolymers containing naphthalene and pendant cyano groups

2,6‐Bis(β‐naphthoxy)benzonitrile (BNOBN) was synthesized by reaction of β‐naphthol with 2,6‐difluorobenzonitrile in N‐methyl‐2‐pyrrolidone (NMP) in the presence of KOH and K₂CO₃. Poly(ether ketone ether ketone ketone)(PEKEKK) /poly(ether ether ketone ketone) (PEEKK) copolymers containing naphthalene and pendant cyano groups were obtained by electrophilic Friedel‐Crafts polycondensation of terephthaloyl chloride (TPC) with varying mole proportions of 4,4′‐diphenoxybenzophenone (DPOBP) and 2,6‐bis(β‐naphthoxy)benzonitrile (BNOBN) using 1,2‐dichloroethane (DCE) as solvent and NMP as Lewis base in the presence of anhydrous AlCl₃. The resulting polymers were characterized by various analytical techniques, such as FTIR, DSC, TG, and WAXD. The results indicated that the crystallinity and melting temperature of the polymers decreased with increase in concentration of the BNOBN units in the polymer, the glass transition temperature of the polymers increased with increase in concentration of the BNOBN units in the polymer. Thermogravimetric studies showed that all the polymers were stable up to 536°C in N₂ atmosphere. The copolymers have good resistance to acidity, alkali, and organic solvents. Because of the melting temperature (T_m) depression with increase in the BNOBN content in the reaction system, the processability of the resultant coplymers could be effectively improved. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and characterization of poly(ether ketone ketone) (PEKK)/sodium sulfonated poly(arylene ether ketone) (S‐PAEK) block copolymers

A series of well‐defined poly(ether ketone ketone) (PEKK)/sodium sulfonated poly(aryl ether ketone) (S‐PAEK) block copolymers of high molecular weights was prepared by direct nucleophilic polymerization of hydroquinone with sodium 5,5′‐carbonylbis(2‐fluorobenzene sulfonate) ( 1 ) and PEKK oligomer ( 2 ). Varying the ratio of 1 to 2 used in polymerization can be used to control the degree of polymer sulfonation, which correspondingly affects the polymer solubility in solvents. Increasing content of 1 in the copolymers, slightly decreases their thermal stability which is nevertheless thermally stable up to 400 °C. Two T_g values, or one broad T_g, were observed in the DSC measurements of the block copolymers, indicating the existence of phase separation, which was further proved by phase‐separated morphologies as shown in atomic force microscopy images. © 2001 Society of Chemical Industry     

Copolymerization and blending of poly(phthalazinone ether ketone)s to improve their melt processability

The melt processability of phthalazinone‐containing poly(aryl ether)s (PAEs) was improved through copolymerization and blending. Poly(phthalazinone ether ketone) (PPEK) copolymers containing phthalazinone and bisphenol‐A (BPA) moieties were synthesized through nucleophilic substitution polycondensation. The PPEK copolymers exhibited high glass transition temperatures, excellent thermooxidative properties, good mechanical properties and improved solubility, all of which can be tailored by changing the molar ratio of phthalazinone to bisphenol monomers. The rheological investigation indicated that the incorporation of the flexible BPA moiety into the main chain lowered the melt viscosity of the copolymers. To improve the melt processability further, polymer blends of a PPEK copolymer/polycarbonate (PC) were prepared. The results suggested that blending is an effective approach for improving the melt processability of phthalazinone‐containing PAEs. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 2575–2580, 2007     

Crystallization kinetics of novel poly(aryl ether ketone) copolymers containing 2,7‐naphthalene moieties

To increase the glass transition temperature (T_g) of poly(aryl ether ketone), and to decrease the melting temperature (T_m) and temperature of processing, a series of novel poly(aryl ether ketone)s with different contents of 2,7‐naphthalene moieties (PANEK) was synthesized. We focused on the influence of the naphthalene contents to the copolymer's crystallization. The crystallization kinetics of the copolymers was studied isothermally and nonisothermally by differential scanning calorimetry. In the study of isothermal crystallization kinetics, the Avrami equation was used to analyze the primary process of the crystallization. The study results of the crystallization of PANEK at cooling/heating rates ranging from 5 to 60°C/min under nonisothermal conditions are also reported. Both the Avrami equation and the modified Avrami–Ozawa equation were used to describe the nonisothermal crystallization kinetics of PANEK. The results show that the increase in the crystallization temperature and the content of 2,7‐naphthalene moieties will make the crystallization rate decrease, while the nucleation mechanism and the crystal growth of PANEK are not influenced by the increasing of the content of 2,7‐naphthalene moieties. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 2527–2536, 2006     

Properties and crystallization kinetics of poly(ether ether ketone)‐co‐poly(ether ether ketone ketone) block copolymers

A series of block copolymers composed of poly(ether ether ketone) (PEEK) and poly(ether ether ketone ketone) (PEEKK) components were prepared from their corresponding oligomers via a nucleophlilic aromatic substitution reaction. Various properties of the copolymers were investigated with differential scanning calorimetry (DSC) and a tensile testing machine. The results show that the copolymers exhibited no phase separation and that the relationship between the glass‐transition temperature (T_g) and the compositions of the copolymers approximately followed the formula T_g = T_g1X₁ + T_g2X₂, where T_g1 and T_g2 are the glass‐transition‐temperature values of PEEK and PEEKK, respectively, and X₁ and X₂ are the corresponding molar fractions of the PEEK and PEEKK segments in the copolymers, respectively. These copolymers showed good tensile properties. The crystallization kinetics of the copolymers were studied. The Avrami equation was used to describe the isothermal crystallization process. The nonisothermal crystallization was described by modified Avrami analysis by Jeziorny and by a combination of the Avrami and Ozawa equations. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 1652–1658, 2005     

Synthesis and properties of poly(aryl ether ketone ketone)/poly(aryl ether ether ketone ketone) copolymers with pendant cyano groups

2,6‐Diphenoxybenzonitrile (DPOBN) was synthesized by reaction of phenol with 2,6‐difluorobenzonitrile in N‐methyl‐2‐pyrrolidone in the presence of KOH and K₂CO₃. Poly(aryl ether ketone ketone)/poly(aryl ether ether ketone ketone) copolymers with pendant cyano groups were prepared by the Friedel–Crafts electrophilic substitution reaction of terephthaloyl chloride with varying mole proportions of diphenyl ether and DPOBN using 1,2‐dichloroethane as solvent and N‐methyl‐2‐pyrrolidone as Lewis base in the presence of anhydrous AlCl₃. The resulting polymers were characterized by various analytical techniques, such as FT‐IR, differential scanning calorimeter, thermal gravimetric analysis, and wide‐angle X‐ray diffraction. The crystallinity and melting temperature of the polymers were found to decrease with increase in concentration of the DPOBN units in the polymer. Thermogravimetric studies showed that all the polymers were stable up to 514°C in N₂ atmosphere. The glass transition temperature was found to increase with increase in concentration of the DPOBN units in the polymer when the molar ratios of DPOBN to DPE ranged from 10/90 to 30/70. The copolymers containing 30–40 mol % of the DPOBN units exhibit excellent thermostability at (350 ± 10)°C and have good resistance to acidity, alkali, and organic solvents. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 3601–3606, 2007     

Preparation,morphologies, and properties of positively charged quaternized poly(phthalazinone ether sulfone ketone) nanofiltration membranes

Positively charged quaternized poly(phthalazinone ether sulfone ketone) (QAPPESK) nanofiltration (NF) membranes were prepared from chloromethylated poly(phthalazinone ether sulfone ketone) by the dye/wet phase inversion method with N‐methyl‐2‐pyrrolidone (NMP) and N,N‐dimethylacetamide (DMAc) as solvents. The effects of the ratio of NMP to DMAc, the evaporation time, the evaporation temperature, and the coagulation temperature on membrane performance were evaluated by the orthogonal design method. The results showed that the optimal preparation conditions were an NMP/DMAc ratio of 2/8, an evaporation time of 5 min at 70°C, and a coagulation temperature lower than 5°C. The effects of the additive type and concentration on the QAPPESK NF membrane cross‐section morphology and performance were investigated in detail. Furthermore, QAPPESK NF membranes exhibited good thermal stability with stable membrane performance for 120 h at 60°C. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009