含硼铁精矿添加剂改善烧结矿质量的工业试验

 以含硼铁精矿作为烧结添加剂,在本钢炼铁厂生产条件下,研究了含硼铁精矿对烧结矿质量的影响。工业试验表明：含硼铁精矿是一种良好的烧结原料,烧结配加含硼铁精矿可提高烧结矿强度,降低烧结矿粉化率,改善烧结矿粒度组成和还原性,同时对烧结矿TFe含量无明显影响。     

Roasting Properties of Pellets With Iron Concentrate of Complex Mineral Composition

 Investigation was conducted on roasting properties of pellets with an iron concentrate of complex mineral composition. The results indicated that the pellets of complex mineral composition concentrate required higher preheating temperature and longer preheating time than that of single magnetite concentrate. Therefore, it is difficult for preheated pellets to withstand the mechanical collision in the roasting process in rotary kiln. It was found that after the iron concentrate being subjected to high pressure roll grinding, the specific surface area reached 2029.1 cm2/g. Consequently, the preheating and roasting temperature of pellets were decreased by 70 and 50 ℃ and preheating and roasting time were decreased by 2 and 4 min, respectively. Meanwhile, the compression strength of preheated and roasted pellets were increased by 200 N for a pellet and 220 N for a pellet, respectively. The mechanism lied in that the increase of specific surface area activated thermal reaction and promoted formation of iter-grain bridge.     

K和Na对白云鄂博铁精矿烧结连晶特性的影响

通过微型烧结试验,研究了氟的质量分数为0.5%时,不同K、Na含量对白云鄂博铁精矿烧结连晶特性的影响。结果表明,在氟含量较低时,烧结过程中不易生成低强度枪晶石,随着铁精矿中K、Na含量的增加,烧结矿中液相量和硅酸盐玻璃相增加,致使气孔分布不均匀,阻碍了赤铁矿连晶的发展,导致烧结矿连晶强度降低。     

配加高镁铁精粉的烧结配料结构优化

为了在烧结生产中配加低价、低品位的高镁铁精粉替代南非进口粉,淮钢烧结厂运用了烧结生产配料理论测算和成本分析等手段并结合高镁铁精粉烧结工业试验进行了配料结构优化,达到了降本增效的目的。     

白云石强化含氟铁精矿球团的研究

 研究了配加白云石粉提高MgO含量对含氟铁精矿球团质量的影响。试验结果表明：提高球团矿中MgO含量对生球质量的影响不大。当球团MgO含量从0.83%增加到2.0%时,成品球抗压强度显著提高,强度从3555 N/个提高到了5050 N/个。但由于白云石的分解产生CO2增加了球团的孔隙率,使得提高球团矿中MgO含量会降低预热球抗压强度,通过延长预热时间来完成Fe3O4的氧化即可以提高预热球抗压强度也可以提高成品球抗压强度。在较高的焙烧温度下,MgO大多赋存于铁相中稳定了磁铁矿和含镁矿物的晶格,这些矿物与Fe2O3、铁酸钙等互连和紧密胶结,相互熔蚀,有利于球团抗压强度的提高。     

改善武钢铁矿粉烧结强度的配矿试验

烧结生产中某一铁矿粉质量分数在20%以上时,对烧结矿指标有较大的影响。研究表明,在高比例使用同化温度高、粒度细、成球性差的铁矿粉后,烧结矿的强度明显下降,燃耗增加;在高比例使用流动性好的铁矿粉后,烧结矿强度和利用系数均会降低。利用铁矿粉的烧结基础特性指导烧结杯配矿研究的试验表明,使用25%左右A粉,30%左右C粉,15%左右E粉以及碱度为2.0左右的铁矿粉烧结,可以较大程度地提高转鼓强度,综合烧结指标较好。     

包钢烧结混合料中配加巴润精矿的试验研究

文章通过烧结杯试验,研究了包钢炼铁厂烧结生产中利用巴润精矿替代一部分外购精矿后,烧结各项技术指标的变化。考察烧结利用巴润精矿的可行性及合理性。为烧结配加巴润精矿生产提供依据。     

Mechanism of Strength Improvement of Magnetite Pellet by Adding Boron-bearing Iron Concentrate

The mechanism of improving compressive strength of magnetite pellet by adding boron-bearing iron concentrate was studied. Boron-bearing iron concentrate and magnetite were mixed, pelletized and roasted under differ ent roasting conditions. Then, compressive strength of pellets was tested, and polished sections of the roasted pellets were analyzed from the perspective of mineralogy. Finally, the effects of different proportions, roasting temperatures and roasting time of boron-bearing iron concentrate on the compressive strength of magnetite pellets were investigated and explained.     

润磨强化镜铁精粉烧结特性的研究

巴西镜铁精粉难制粒反应性差,通过润磨单一镜铁矿或其与石灰石的混合料可改善其表面性质和高温反应性能.测定润磨预处理前后巴西镜铁矿的润湿热、粒度组成及变形温度等指标,揭示其作用机理.并通过烧结杯试验,考察润磨预处理强化烧结的效果.研究结果表明,润磨改善了巴西镜铁矿的润湿热,表面亲水性得到改善;降低了变形温度,提高了巴西镜铁矿的高温反应性能.巴西镜铁矿预处理后,烧结矿产量和质量得到大幅度改善,成品率增加了3.7%,转鼓强度提高了3.33%,固体燃耗降低了约4 kg/t ,利用系数提高22.4%,烧结矿质量完全能满足高炉生产的需要.     

几种典型铁矿石烧结基础特性的实验与评价

引入了铁矿石烧结基础特性的新概念,并对几种典型铁矿石的烧结基础特性进行了测试与评价,包括铁矿石的同化性、流动性、粘结相强度、连晶性能及铁酸钙生成性能.在此研究基础上给出了烧结与球团互补性配矿建议.     

高比例精矿粉对烧结的影响分析及强化措施探讨

太钢吕梁铁矿投产,烧结铁料中自产铁矿的配比超过了85%,且自产铁精矿粒度很细,其中吕梁铁精矿不超过0.045mm的比例占到了96%以上。要在730mm左右的料层高度条件下,为4350m3高炉生产优质烧结矿,难度较大。会使混合料制粒效果变差,而且自产精粉比例较大,配矿结构调整余地很小,不利于烧结过程的进行和烧结矿质量的改善。为了给烧结配用自产资源提供技术支持,摸清高比例精矿粉对烧结造成的影响,在技术中心进行了烧结杯试验。试验结果表明：随着精粉率的提高,烧结矿的产、质量指标变差,当精粉率超过70%时,烧结过程变得缓慢,特别是全精粉烧结时,控制不好,会出现烧结熄火,烧结过程停滞的现象。为此,要采取强化制粒、优化燃料粒度、提高碱度等有效措施。     

烧结矿中MgO配加方式的改进试验

对济钢烧结矿 Mg O的几种不同带入方式进行了工业试验和生产实践。指出在济钢目前生产条件下 ,在烧结生产中配加高 Mg O铁精粉和高 Mg O熔剂 ,是确保铁前系统稳定、优化高效的有效途径     

铜精矿中铁含量的快速测定

论述铜精矿中铁含量的快速检测方法,对试样分解、还原、滴定、测定范围、共存元素影响、方法的准确度和精密度等作了详细研究。方法的相对标准偏差为0.14%-0.40%,样品加标回收率为96.4%-103.5%,方法适用于铜精矿中0.5%以上铁的测定。     

2009年铁精矿粉采购思路分析

采购成本是企业经营成本中最大的一部分,降低成本是企业生存发展之路。2008年以来,钢铁行业经历了先盈利后亏损的局面,采购成本的变化是一个主要因素。主动把握市场变化趋势,积极应对,理清2009年铁精矿粉的采购思路,对包钢的生存发展有积极意义。     

提高铁精矿品位的实践

为了提高铁精矿品位，金岭铁矿选矿厂对原工艺流程和设备进行改进，采取了降低入磨粒度和合理配矿以提高球磨机磨矿细度、更换磁聚机提高磁选流程处理能力、改造过滤机增加其吸附面积、应用永磁干式磁选机替代原电磁磁滑轮、改造尾矿泵等一系列措施，使铁精矿品位由65．54％提高到66．37％，年增效益160余万元。     

含铁氰渣磁化焙烧回收铁精矿

以铁含量为35%的氰渣为研究对象,研究了焙烧温度、焙烧时间及碳氧比对煤基磁化焙烧过程的影响,并采用化学分析、XRD、SEM、热重分析等分析手段对含铁氧化物的转变过程进行表征。随着焙烧温度的提高,铁氧化物的物相转变过程为Fe₂O₃→Fe₃O₄→FeO。随着磁化焙烧焙烧时间的延长,尾渣中的Fe₂O₃首先被C还原为Fe₃O₄,还原得到的Fe₃O₄可被空气中的O₂重新氧化为Fe₂O₃。碳氧比较低时,磁化率接近2.33;当碳氧比超过3时,过量的煤与尾渣混合,Fe₂O₃还原反应不完全;在焙烧温度645℃、焙烧时间45 min、碳氧比3的优化焙烧条件下,得到焙烧矿的磁化率为2.34。     

铁精矿烧结新工艺研究

以近北庄为主的磁铁精矿的球团烧结进行了较全面的实验室探索，结果表明，球团烧强工艺可以用普通粒度结燃料和全部磁铁精矿生产出碱度不同的优质烧结矿。     

鞍钢自产铁精矿合理使用研究

对鞍钢常用4种铁精矿的烧结基础特性进行了试验研究,在此基础上,采用最优试验设计方法,建立了烧结合理配矿的统计模型,给出了烧结获得最佳和最差烧结指标值时的各种矿的定量搭配关系,提出了鞍钢烧结合理配矿方案.优化配矿工业试验结果表明:烧结技术经济指标有不同程度改善,尤其是烧结矿的粒度组成改善、固体燃耗降低;提出并确定了球团配加铁精矿A的优越性,配加铁精矿A后,皂土配比降低8.69%,转鼓强度提高0.35个百分点.     

钒钛烧结矿和普通烧结矿显微力学性能对比

采用维氏压痕法对钒钛烧结矿与普通烧结矿中常见矿物的显微硬度进行测定,对比分析不同矿物的显微硬度值及压痕裂纹的萌生与扩展。研究发现,两种烧结矿中常见矿物的显微硬度从高到低依次为:钙钛矿-钛赤铁矿-铁酸钙-交织熔蚀结构-钛磁铁矿-硅酸盐;赤铁矿-交织熔蚀结构-铁酸钙-磁铁矿-硅酸盐。总体上钒钛烧结矿的显微硬度高于普通烧结矿,但部分矿物压痕裂纹多,且延伸较长,钙钛矿和钛赤铁矿断裂韧性差、易碎。烧结矿中减少板块状赤铁矿,多发展铁酸钙和交织熔蚀结构有利于提高烧结矿的显微硬度,改善烧结矿的质量。     

烧结法生产中铁矿物的行为及[F/A]的控制方法

介绍了烧结法生产氧化铝工艺中,铁矿物的行为变化及对工艺过程的影响,以及为改善生产作业条件控制[F／A]值的工业方法。指出低[F／A]条件下进行熟料烧结是进一步吸收强化烧结技术、优化湿法车间工艺技术指标的重要手段之一。