纯棉厚重织物的一浴法前处理工艺

采用精练酶881和去蜡剂对纯棉厚重织物纱卡进行退、煮、漂一浴法处理,探讨了精练酶881用量、去蜡剂用量、双氧水用量、汽蒸时间和稳定剂硅酸钠用量对处理后棉织物性能的影响。通过试验得出最佳工艺条件为：精练酶881用量25 g/L,去蜡剂8 mL/L,双氧水12 mL/L,硅酸钠8 g/L,在100 ℃条件下汽蒸60 min。精练酶881一浴法前处理工艺简单,对纤维损伤小,处理后的棉织物各项性能指标均优于常规法前处理工艺。     

多功能精练粉TF-120EB

多功能精练粉TF 120EB集碱剂、渗透、精练、螯合及双氧水稳定剂功能于一体,与常规多功能精练粉一样,适用于全棉织物长车碱氧一浴汽蒸工艺。用其对全棉纱卡进行碱氧一浴汽蒸前处理的优化工艺为：精练粉TF 120EB 30~40 g/L,100%双氧水8~15 g/L,汽蒸时间40~90 min。与市售同类产品相比,TF 120EB具有更优异的渗透性和双氧水稳定性以及与棉用增白剂良好的同浴复配稳定性。     

棉织物的复合茶皂素前处理

采用复合茶皂素(卜公茶皂素)对棉织物进行前处理,优化的卜公茶皂素汽蒸退煮漂一浴工艺为:茶皂素40 g/L,渗透剂JFC 5 g/L,精练剂YS198 6 g/L,双氧水稳定剂GJ-101 4g/L,浸轧(多浸多轧,50 ℃)→汽蒸(95～100 ℃,50～60 min)→热水洗(100℃)→冷水洗→烘干.结果表明,采用卜公茶皂素对棉织物进行退煮漂一浴前处理的效果好于常规碱氧工艺.     

精练酶T115I在纯棉织物练漂工艺中的应用

探讨了精练酶T115 I用于纯棉织物练漂一浴法前处理的工艺条件。确定了最佳工艺为:处理浴浴比1∶20;精练酶T115 I 1.5g/L;双氧水5mL/L;加热至100℃煮漂50m in。经此工艺处理后的棉织物,其毛效为10.3 cm,白度为80.3,经向撕破强力为656.0N。     

简化的棉织物一浴连续前处理工艺

通过正交试验,确定了简化的棉织物一浴连续轧蒸前处理的最佳工艺条件:30％双氧水35 g/L、精练剂YJ 15 g/L、配套助剂KX-10 42g/L、轧余率80％、汽蒸时间20 min.该前处理工艺不用烧碱,工艺流程短、效率高,对环境有利,处理效果与传统工艺相近.     

棉织物阳离子化改性/双氧水漂白-浴工艺

探讨棉织物用自制阳离子改性剂WLS与双氧水进行同浴改性和漂白的可行性,优化-浴法改性漂白工艺,即改性剂WLS20g/L,碳酸钠9g/L,硅酸钠2g/L,30％双氧水15g/L,漂白改性处理60 min.结果表明,改性剂WLS对双氧水漂白效果影响不大,用一浴法漂白改性的棉织物活性染料染色性能显著提高,耐摩擦色牢度和耐皂洗色牢度有所改进.     

纯棉织物练漂一浴法精练酶T115I的应用

选用精练酶T115I代替烧碱对纯棉织物进行练漂一浴法处理.讨论了精练酶T115I用量、双氧水用量、煮漂时间和煮漂温度对处理后织物性能的影响;确定了工艺条件,即浴比1：20,精练酶T115I 1.5g/L,双氧水5 Ml/L,100℃煮漂50 min.酶精练工艺处理时间短,对纤维损伤小,处理后织物白度为80.3,毛效为10.3 cm/30 min,强力为656.0 N.     

棉织物退煮漂和改性一浴工艺

采用自制改性剂对棉织物进行退煮漂和改性一浴加工,分析了氢氧化钠用量、硅酸钠用量、双氧水用量、温度、时间和改性剂用量对棉织物染色效果的影响.结果表明,优化的棉织物退煮漂和改性一浴工艺为:氢氧化钠20 g/L,硅酸钠3 g/L,30％双氧水24 mL/L,改性剂20 g/L,温度80℃,时间70 min.棉织物经退煮漂和改性一浴处理后,可实现活性染料无盐染色,其耐水洗色牢度及干摩擦色牢度优异,但湿摩擦色牢度有待进一步改进.     

棉织物的高效短流程练漂工艺

研究了一浴精练剂ZS和双氧水用量,以及精练温度和时间对棉织物精练效果的影响,优化了棉织物精练剂ZS一浴短流程练漂工艺。结果表明,一浴练漂法最佳工艺为:精练剂ZS 3~3.5 g/L,双氧水8 m L/L,精练温度95~100℃,精练时间60 min。采用该工艺练漂的织物白度达到80%以上,毛效13 cm/30 min以上。添加适量的有渗透作用的表面活性剂,可以进一步提升棉织物的毛效。     

棉织物生物酶精练漂白技术研究

研究棉织物生物酶精练漂白工艺配方及技术。测试了复合精练酶用量、双氧水浓度、活化剂浓度对棉织物白度、芯吸高度、强力的影响情况,通过试验优化复合酶精练棉织物的工艺配方为复合精练酶6 m L/L,双氧水(30%)7 g/L,活化剂4 g/L。试验结果表明:采用优化后的复合酶精练工艺配方活化漂白处理后的棉织物白度值在72%左右,芯吸高度大于12 cm,强力均值在500 N左右。认为采用复合精练酶精练漂白棉织物可以达到较好的漂白效果。     

高温皂碱练与酶制剂练精干绵性能比较

通过测试比较，分析了酶制剂练、高温皂碱练由精练方法不同而造成纤维在微观、外观、机械、吸湿及电学等方面的异同点。提出酶制剂练对提高纤维梳折、提高成纱品质、提高劳动生产率、降低工人劳动强度等方面均优于高温皂碱练，是精练工程改造方向之一。     

精练剂HS-200conc

高效浓缩型精练剂HS-200conc为阴/非离子复合物,具有高耐碱性能.通过试验其耐碱稳定性和耐碱渗透性,并考察了其用量对煮练和轧蒸效果的影响,结果表明,精练剂HS-200conc具有优良的耐碱稳定性和耐碱渗透性,根据不同工艺,当其用量分别为0.3g/L(煮练)和3.0g/L(轧蒸)时,可获得良好的精练效果,织物毛效和白度较高.     

Optimization of Scouring Alpaca Wool by Ultrasonic Technique

This paper presents a new method of scouring wool in small batches using ultrasonic techniques. Alpaca wool because of the variety of colors and delicate structure requires scouring in small batches (sorted colors) and mild conditions. Scouring of alpaca wool in industrial washers used for sheep wool results in strong loop entanglement of wool and makes its further processing impossible. The study on parameters and conditions of the scouring of alpaca wool was carried out on a specially prepared scouring unit developed on the basis of ultrasonic cleaner. Ultrasonic scouring equipment used in the study prevented displacements of wool in the bathtubs and the reaction of metal on the fiber. As the changing conditions, i.e., the scouring parameters, such as the sample mass, scouring time, and detergent concentration affecting the quantity of removed impurities were considered. As a result, the study determined the optimal conditions of the scouring of alpaca wool. The use of ultrasound technology reduces water and detergents consumption and it shortens the time of scouring. The most important result is the obtaining of the scouring wool without damages and entanglements.     

煮练酶在纯棉粗厚织物前处理中的应用

通过对比实验发现：煮练酶SKD-301堆置工艺较传统前处理更有助于纯棉机织物强力的保护及失重率控制,但对于棉纱质量较差的粗厚织物,尚需借助碱氧煮漂工艺完成PVA浆及棉籽壳的退除。     

生物酶在大麻织物精练中的应用

分别采用精练酶、果胶酶和纤维素酶对大麻织物进行精练处理,通过分析酶用量、处理温度、时间以及pH对处理后织物毛效和抗弯刚度的影响,得出3种酶较优的处理工艺.对比3种酶单独处理和两两复配处理对大麻织物毛效和抗弯刚度的影响,结果为:纤维素酶与果胶酶复配处理的综合效果较好,毛效为16.8 cm,抗弯刚度为213 mg·mm.     

棉低温练漂的研发与应用

研究成功了低温练漂剂QR-2010、QR-2011、QR-2020。以不同比例进行棉的双氧水煮练、漂白同浴练漂,可以使练漂温度降低到80℃以下,或使冷轧堆练漂的堆置时间缩短到4-6h。阐述了该低温练漂的基本原理、大生产应用工艺及其应用效果。该工艺具有节能显著、排污减少、半制品质量优异、减少绉印和略降低加工成本的特点。     

氨纶精练剂TF-109的应用性能

采用氨纶精练剂TF-109对锦/氨纶织物进行精练,通过单因素分析和正交试验,以探讨精练工艺条件对织物精练效果的影响.结果表明,精练剂TF-109浓度是影响精练效果的主要因素;较佳工艺条件为:TF-109浓度6g/L,精练温度80℃,精练时间20min,浴比为1:30.     

脱胶细菌在亚麻粗纱煮练中的初步应用

对假单胞菌DA10(CGMCC No.3851)在亚麻粗纱煮练中的应用进行了研究。通过试验研究了发酵液用量、初始pH值、煮练温度和处理时间对细菌煮练的影响。试验表明：当发酵液用量150mL,初始pH值9,煮练温度40℃,时间7.5h左右时,细菌煮练可以获得较好的效果。但细菌煮练的作用较柔和,在细菌煮练前引入预处理可以明显改善细菌煮练效果,提高纤维分裂程度和纤维强度,其中以低浓度碱煮-细菌联合煮练的效果为最优。同时,也使用扫描电镜对胶质的去除情况进行分析,结果表明：经细菌煮练后的纤维虽获得了分裂但纤维上仍有胶质,而碱煮-细菌联合煮练后纤维上的胶质去除较彻底。     

ZS-1丝素保护快速精炼剂

ZS-1型丝素保护快速精练剂是一种含有丝素保护剂的多种表面活性剂的混合物。在起泡性、润湿性、分散性和净洗能力等性能上均能满足精练真丝绸的技术要求,可以保护各类真丝绸在94～98℃、pH值11.2～11.6的条件下快速精练不受损伤。完全可代替Miltopan SE用于平幅连续精练。     

绢纺原料自控精练技术的小试研究

通过对各类绢纺原料的自控精练技术小试研究，使精练工艺和设备的全自动控制得以可能，为生产自控精练设备及其网络控制系统的设计研制提供了可靠的技术依据。本文对自控精练工艺、自控精练设备、工艺试验情况等作了介绍。