高氧TC4/TC17线性摩擦焊接头组织与显微硬度研究

对高氧TC4和TC17钛合金进行了线性摩擦焊试验,利用光学显微镜与扫描电镜对焊接接头的微观组织进行了分析,并研究了热处理对接头组织及显微硬度的影响。结果表明,焊态下高氧TC4侧焊缝比TC17侧窄,焊缝界面处生成共生晶粒,界面两侧发生动态再结晶。高氧TC4侧,靠近焊缝边缘的部分热力影响区形成大量的亚晶粒,部分区域发生动态再结晶形成细小的等轴β晶粒,冷却后晶粒内析出马氏体α'相。TC17侧,β晶粒以及α晶界被拉长形成变形带,在靠近焊缝处、形成许多细小的等轴β晶粒。经过焊后热处理,高氧TC4的TMAZ亚稳态马氏体α'相分解,高度变形的β相中析出片层状α相;TC17侧TMAZ组织为细小的针状α相。焊缝中心的共生晶粒组织不均匀,由相互交错的大小α片层组成。焊态下焊缝中心硬度最高;热处理后,TC17侧焊缝及热力影响区硬度大幅度增加。     

钛合金线性摩擦焊接头动态再结晶规律研究

针对TC4/TC17异种钛合金进行了线性摩擦焊试验,利用光学显微镜与扫描电镜对焊接接头各区域的微观组织进行了分析,并采用透射电镜分析了钛合金线性摩擦焊接头焊合区的动态再结晶规律。结果表明:在焊接升温的过程中,TC4/TC17钛合金线性摩擦焊焊缝区已经达到β转变温度。在热和力的作用下,焊缝中心处金属发生动态再结晶,生成了细小的等轴晶粒。由于焊合区在共生晶粒形成之后又经历了强塑性变形,焊合区的晶粒内部产生了高密度的位错。位错运动形成亚晶界,焊合区形成亚晶粒,并以亚晶粒为形核核心,发生动态再结晶过程。     

摩擦压力对异质钛合金线性摩擦焊接头界面组织的影响

选用不同摩擦压力对TC11/TC17异质钛合金进行了线性摩擦焊试验.焊后利用扫描电镜对焊接接头微观组织进行了分析.结果表明,摩擦压力越大,摩擦界面获得的焊接热输入量越大,产生的飞边越大.焊缝区宽度随摩擦压力的增大而减小.热机影响区组织变形严重,由被拉长的α相及破碎的β相组成,靠近焊缝附近有明显的再结晶现象.线性摩擦焊接过程中界面温度超过β相转变温度,在焊后冷却过程中β相发生再结晶,产生细小的针状组织.焊缝中的再结晶晶粒随着摩擦压力的增大而变得更加细小.     

高氧TC4/TC17钛合金线性摩擦焊接头组织特征及力学性能

对高氧TC4/TC17异质钛合金进行线性摩擦焊试验,研究了焊接接头各区域组织特征、焊接界面合金元素扩散行为及力学性能. 结果表明,焊接过程中焊缝区发生了相变及动态再结晶,形成细小的等轴晶粒. 高氧TC4侧焊缝区形成针状马氏体,TC17侧形成亚稳定β相;两侧热力影响区晶粒均发生了破碎,沿着振动方向拉长. 焊后冷却阶段在焊合线附近出现合金元素扩散现象,扩散区域狭窄. 焊缝中心处显微硬度值最高达到420 HV,高氧TC4侧显微硬度随着靠近母材而逐渐降低;TC17侧显微硬度随着远离焊缝中心迅速升高. 拉伸性能测试结果表明,接头抗拉强度与高氧TC4母材相当.     

热处理对异质钛合金线性摩擦焊接头组织和显微硬度的影响

研究焊后热处理对TC4和TC17异质钛合金线性摩擦焊接头显微组织的影响。焊态条件下焊缝组织为完全再结晶组织,表明线性摩擦焊接过程中,摩擦界面温度超过β相变点温度,其中TC4侧焊缝组织主要为具有马氏体组织结构的α′相,TC17侧焊缝组织主要为单一的β相。TC4与TC17侧热力影响区组织为严重的变形组织,且具有明显的方向性,但在该区各相的体积分数未发生变化。热处理后,TC4侧焊缝组织中α′转变为针状的α＋β相,且随着热处理温度的升高,针状α相粗化,长大现象明显,并导致该区的显微硬度下降。TC17侧焊缝组织热处理后从晶界和β晶粒内部析出了细小的α相,导致该区显微硬度明显提高。     

异质钛合金线性摩擦焊接头微观组织与显微硬度分析

选用优化的工艺参数对TC4/TC17异质钛合金进行线性摩擦焊及测温试验.焊后利用光学显微镜、扫描电镜及显微硬度仪等对接头微观组织及显微硬度进行分析.结果表明,线性摩擦焊接过程中界面温度超过1 200℃、超过β相变温度,在焊后冷却过程中发生再结晶,产生细小针状组织.界面混合区再结晶组织有等轴化甚至球化现象.TC4侧热力影响区由被拉长的α相及破碎的β相组成,TC17侧热力影响区的α相和β相被拉长细化.TC4侧热力影响区组织发生应变强化,TC17侧热力影响区靠近焊缝侧发生一定的软化现象,靠近母材侧强化现象明显.     

热处理对TC17(α+β)/TC17(β)线性摩擦焊接头组织及力学性能的影响

针对热处理前后TC17(α+β)/TC17(β)钛合金线性摩擦焊接头组织和性能进行了对比分析. 结果表明,焊态时焊缝区组织发生动态回复和再结晶,两侧的热力影响区组织均被不同程度地拉长,热处理后焊缝中的亚稳相分解析出弥散的α和β相,TC17(α+β)侧热力影响区的初生α相有所长大. 焊态接头焊缝区显微硬度比母材低,接头的抗拉强度和屈服强度略低于母材,分别达到母材的91.9%,96.2%,接头拉伸性能试件断裂位置均在焊缝区;经过热处理,母材显微硬度未发生明显变化,焊缝区显微硬度显著提高,接头抗拉强度和屈服强度达到与母材相当,与焊态相比分别提高11.9%,8.2%,接头拉伸性能试件断于母材区.     

异质钛合金线性摩擦焊接头形成过程及组织特征

对TC4和TC17异质钛合金线性摩擦焊接头形成及接头组织特征进行分析,并测量了动态平衡阶段的界面温度.结果表明,在摩擦初期界面容易产生大的磨损颗粒,摩擦过渡阶段两侧基体材料产生大的塑性变形,大的磨损颗粒被细化,摩擦界面开始产生高温粘塑性金属;动态平衡摩擦阶段高温粘塑性金属被均匀的挤出界面形成飞边,焊后界面两侧组织被细化.测温结果显示,摩擦过程中界面温度超过1 200℃,高于两基体材料的相变温度,TC17侧焊缝中形成再结晶β晶粒,TC4侧形成典型的魏氏组织,焊缝两侧的热力影响区产生明显的变形,组织均被拉长.     

TC17(α + β)/TC17(β)钛合金线性摩擦焊接头相组成及织构分析

利用电子背散射衍射技术对TC17(α+β)/TC17(β)钛合金线性摩擦焊接头测试并分析,对接头各区域进行相鉴定和织构分析.结果表明,与母材相比,焊态接头两侧热力影响区α相减少,β相增多.由于焊缝区冷却迅速快,焊态焊缝处发生动态再结晶,生成了大量的亚稳定β相晶粒. TC17(β)侧母材及热力影响区的织构分布密度比TC17(α+β)侧强,且焊态焊缝区产生(5 4 6)[■]织构,轧面与(1 1 1)近似平行.经过610℃热处理后,焊缝区亚稳定β相发生分解,形成细小的次生α相和β相.与焊态焊缝相比,热处理后焊缝区晶体稍有转动,焊缝区织构强度较焊态有较大增强,形成(5 5 7)[■]织构.热处理前后的焊缝区晶体取向都存在着ND方向与[1 1 1]靠近,轧面与(111)接近平行的择优取向.     

异质TC17线性摩擦焊接头焊后时效处理组织与性能

线性摩擦焊是制造航空发动机整体叶盘的关键技术. 通过光学显微镜、扫描电镜、电子式万能试验机及显微硬度仪对比分析了TC17(α + β)/TC17(β)钛合金线性摩擦焊接头焊态及不同时效温度下接头的组织与性能. 结果表明,焊态下焊合区及附近区域的微观组织为过冷β细晶,硬度最低;经焊后时效处理,析出了细小针状α相,硬度升高. 焊后时效温度为400 ℃时,焊合区及附近区域的硬度值明显提高,焊接区脆化. 焊后时效温度为630 ℃时,接头弯曲角度最高,但强度降低. 综合焊接接头的硬度、弯曲与拉伸性能优化出的焊后时效温度为550 ℃. 接头弯曲角度和抗拉强度分别达到母材的36%和95%. TC17(α + β)侧热力影响区( thermal-mechanical affected zone,TMAZ)受力后微观塑性变形更均匀,其强塑性能均优于TC17(β)侧TMAZ. 接头的弱化区对应于TC17(β)侧TMAZ硬度变化梯度及组织梯度最大的区域. 相比母材,接头的塑性损失比强度损失要大得多.     

Microstructural evolution characterization of friction stirring welded AZ31 magnesium alloy

A friction stirring welding to joint 5 mm rolled AZ31 magnesium had been developed. The microstructures in various regions including the weld nugget, thermo-mechanically affected zone (TMAZ) and heat affected zone (HAZ) were investigated and compared with unaffected parent metal using optical microscopy. The results showed that the heat and mechanical process had great effect on the microstructure evolution. In weld nugget, the heat was enough to produce sufficient superplastic material flow and the mechanical effect was greatest, and the dynamic recrystallization was completed thoroughly. In TMAZ, the mechanical effect was indirectly affected by the welding tool and only some grains had undergone dynamic recrystallization. The various regious were studied in detail to better understand the microstructural evolution during friction stirring welding (FSW). The cross section near the ““““key hole““““ showed clear onion rings because the material was stirred only by the rotation of the probe and materials rotated with the probe and did not move along welding direction and in vertical direction, there was no material flow and the flow movement can be regarded as two dimensional layer flow.     

试样状态对线性摩擦焊接头组织及性能的影响

文中针飞机构件常用的TC4钛合金,分别研究了线切割表面、粗铣表面及磨制表面三种状态焊前试件状态对线性摩擦焊接头成形、显微组织、氧元素含量及力学性能的影响。结果表明三种状态试件接头成形良好。焊后的宏观组织均分为母材区、热力影响区、焊合区,其中热力影响区组织沿着受力方向被拉长并发生了初生α相溶解,焊合区发生了动态再结晶,晶粒内部为细小的片层组织。线切割及粗铣状态接头氧元素含量没有明显增加,与磨制状态接头相当。三种焊前状态接头的拉伸性能相当;K_t=1,R=0.06,550 MPa条件时三种接头的疲劳寿命相当。     

Cu-Cr-Zr合金连续驱动摩擦焊接头热力演变

采用热电偶—蓝牙技术测量了Cu-Cr-Zr合金连续驱动摩擦焊接头特征点的温度,并研究接头温度与组织演变的关系. 结果表明,各特征点温度均存在一定程度的滞后现象;沿工件径向, 2/3R区温度最高;沿工件轴向,摩擦界面处温度最高;旋转工件的温度略低于移动工件. 在热力耦合作用下,接头焊合区形成细小的等轴晶粒,热力影响区晶粒被不同程度拉长,呈塑性流线.从轴心到外径动态再结晶区的宽度增加,晶粒粗化,而与其相邻的热力影响区径向塑性流动的趋势减小. 此外,与旋转端相比,移动端接头具有较高的峰值温度和再结晶峰值宽度,所对应的焊合区晶粒也较为粗大.     

TC17钛合金嵌入式线性摩擦焊接头组织与性能

针对航空长形整体构件锻造与加工的难题,提出采用嵌入式线性摩擦焊方法进行分段组合制造,采用嵌入式线性摩擦焊技术开展了TC17钛合金试验件的焊接,针对所形成的V形接头,分析了接头塑性流动规律与接头形成机理、组织特征与力学性能.?结果表明,焊接过程中,金属流动规律与普通线性摩擦焊接头有显著区别,高温塑性金属随着楔块的移动逐渐...     

Study of microstructural evolution of friction taper plug welded joints of C–Mn steels

Abstract

This paper describes the microstructural evolution of friction taper plug welded joints of C–Mn steels. Experimental and numerical analyses included calculations based on Calphad and continuous cooling transformation curves, and characterisation techniques. The studied friction taper plug welded joint contains three macroregions: plug material, thermomechanically affected zone (TMAZ) and base material. The thermomechanical conditions imposed in the studied friction taper plug welded joint precluded the formation of a heat affected zone. However, seven subregions were identified within the TMAZ region and details are discussed. The interface zone is found in the TMAZ region, where the most relevant phase transformations take place. It is suggested that the phase transformations in TMAZ region depend on local conditions, such as chemical composition, deformation rate, thermal history and the previous thermomechanical history of the parent materials.     

Ti2AlNb金属间化合物惯性摩擦焊接头组织及性能分析

采用惯性摩擦焊接工艺对Ti₂AlNb金属间化合物进行了焊接试验研究，利用SEM观察了焊态及焊后热处理接头各区域显微组织，并分析了接头显微硬度变化趋势. 结果表明，Ti₂AlNb金属间化合物试验母材为α₂+B2+O三相组织，α₂相呈断续网状和块状分布于原B2相晶界，O相呈片状分布在B2相基体上；摩擦焊接头分区明显，WZ为单一B2相等轴晶粒，晶粒均匀细小，热力影响区(TMAZ)近焊缝区为B2+α₂相组织，α₂相沿摩擦方向呈定向分布，远焊缝区与热力影响区(HAZ)相近为B2+O+α₂三相组织；焊后热处理接头WZ为板条状B2+O双相组织，并伴有疑似孪晶出现，TMAZ为B2+O+α₂三相组织，近焊缝区原黑色条纹区B2相转变成了块状O相，其余B2相转变成B2+O相板条束，HAZ组织与母材相近，但具有厚度更细小的O+B2相板条；焊态及焊后热处理接头焊缝区显微硬度最高，随着向母材区过度，显微硬度逐渐降低.     

TC4线性摩擦焊接头微观特征

对TC4线性摩擦焊接过程中的接头微观结构形态特征进行了分析,研究了接头微观特征参数随时间的变化趋势.结果表明,焊接过程为接头界面融合过程,界面呈现完全焊合区、过渡区及完全未焊合区3个区域.完全焊合区内界面完全融合、晶粒细小,为动态再结晶组织.过渡区内界面部分融合,有微孔出现.完全未焊合区内两侧金属未接触,夹杂着金属碎渣,晶粒无变形.振动方向飞边与垂直振动方向飞边分离是导致接头出现三叉形貌特征的原因.摩擦压力及顶锻力有使三叉形貌枝叉"闭合"的趋势,而摩擦剪切力有使三叉形貌枝叉"张开"的趋势.