热处理对SLM成形的Inconel 718合金组织的影响

研究了固溶+双级时效处理对激光选区熔化(SLM)工艺制备的Inconel 718高温合金微观组织形态和析出相的影响。结果表明,SLM沉积态合金为椭圆状晶组织,其由细小柱状晶组成。沉积态合金经固溶处理后转变成等轴细晶组织,且随固溶温度升高,晶粒尺寸增大。经固溶+双级时效处理后,合金会在晶界和晶内析出多种析出相,在940~1 020℃固溶过程中晶界析出短棒状δ相(Ni3Nb),在620~720℃时效过程中晶内析出针状δ、圆盘状γ″(Ni3Nb)和黑点状γ′相(Ni3Al,Ti)。     

α+β固溶处理对Ti65合金薄板的影响:硅化物析出、力学行为和新型{■}孪晶系（英文）

为应对航空领域对轻质和优异高温性能钛合金部件的迫切需求,对经不同热处理的新型高温钛合金Ti65合金薄板的显微组织演变、硅化物析出和力学行为进行系统研究。结果表明:在固溶空冷后的合金中析出亚微米级硅化物(Ti,Zr)₆Si₃,导致拉伸性能变差和剧烈波动。在950℃固溶炉冷后的合金中发现穿晶界(Ti,Zr)₅Si₃和近晶界(Ti,Zr)₆Si₃硅化物的共存。当固溶温度升高至1010℃时,(Ti,Zr)₃Si硅化物在位错附件出现。薄板固有尺寸效应与硅化物析出的协同效应导致拉伸性能的明显波动,塑性显著下降,甚至发生脆性断裂。硅化物析出受低温固溶处理的保温时间的影响较弱。此外,在990℃热轧获得的薄板中观察到新型{■}孪晶,其轴角对为65°<■>,仅存在于粗大的基面织构α晶粒中。     

固溶温度及冷却方式对00Cr40Ni55Al3Ti合金组织性能的影响

以热轧态00Cr40Ni55Al3Ti合金为研究对象,采取1150～1250℃固溶+水冷/空冷的试验方案,探究了固溶温度及冷却方式对显微组织与力学性能的影响规律。研究结果表明,在1150～1250℃范围内,合金晶粒及α-Cr相的尺寸随固溶温度升高而增加,超过1150℃后晶粒急剧长大,超过1200℃固溶并空冷后,α-Cr相在晶界片层状析出。合金的显微硬度随固溶温度的升高而下降,冲击吸收能量在1200℃达到峰值;水冷条件下α-Cr相和纳米级γ′相析出受到抑制,与空冷条件相比,硬度、冲击吸收能量分别降低和升高;拉伸性能受冷却方式的影响显著,空冷条件抗拉强度相对较高,1250℃固溶后空冷引起混晶及晶界粗大片层组织出现,导致伸长率与水冷相比下降了26.5%。     

热处理对铸态60NiTi合金第二相析出与硬度的影响

利用OM、XRD、SEM、EDS和DSC等分析测试手段研究了不同热处理方式对60NiTi合金中第二相析出,及其对马氏体转变和硬度的影响。结果表明:固溶后水淬处理能显著提高铸态60NiTi合金的硬度,但炉冷处理却显著降低合金的硬度。400℃时效略微降低固溶后水冷合金的硬度,但长时间时效对硬度的影响不大。Ni_3Ti相的大量固溶是固溶水冷处理显著提高铸态合金硬度的原因,而固溶后炉冷合金硬度下降则来源于更多Ni_3Ti相的析出。60NiTi合金的硬度取决于马氏体转变发生的难易程度。     

高硅镍铜合金NCu30-4-2-1热处理组织演变

采用高温显微镜、维氏显微硬度计、透射电子显微镜及差示扫描量热仪等手段研究了高硅镍铜合金NCu30-4-2-1热处理组织演变规律。结果表明,合金铸态组织由树枝状α-Ni基固溶体相以及枝晶间呈网状分布的α+β共晶相组成;固溶温度为850℃时,合金组织无明显变化;固溶温度为950℃保温2 h时,枝晶组织基本消失,合金中β强化相基本溶入固溶体基体中,形成单相过饱和固溶体基体组织;固溶温度为1050℃时,晶粒异常长大。在固溶处理950℃×2 h+时效处理600℃×8 h下,主要析出相为细小弥散分布的β'-Ni3Si相,与基体保持良好共格关系,合金硬度达到450 HV。     

热处理对NCu30-4-2-1合金组织与性能的影响

本文采用差示扫描量热仪及透射电子显微镜研究了热处理工艺对NCu30-4-2-1合金组织及性能的影响。结果表明,固溶温度为850 ℃时,合金组织变化不明显;随着固溶温度的提高,枝晶间共晶组织逐渐溶解,当固溶温度为950 ℃时,枝晶组织基本消失,合金中β强化相基本溶入固溶体基体中,形成单相过饱和固溶体组织;继续提高固溶温度至1050 ℃时,晶粒异常长大。增加时效温度和时间,合金硬度值先增大,达到峰值后趋于平稳。合金经时效处理600 ℃×8 h,主要析出相为细小弥散分布的β´-Ni₃Si相,并与基体保持良好共格关系,合金强度硬度最大,断后伸长率较高。     

固溶温度对FGH95镍基合金持久断裂机制的影响

通过对不同温度固溶处理的FGH95合金进行组织形貌观察及持久性能测试,研究了组织结构对合金持久性能及其断裂机制的影响。结果表明:经1150℃固溶和时效处理后,合金中有粗大γ′相在较宽的边界区域不连续分布,其周围存在γ′相贫化区;经1160℃固溶及时效处理后,合金中粗大γ′相完全溶解,在晶内弥散分布高体积分数的γ′相,并有粒状(Nb,Ti)C碳化物在晶内及沿晶界不连续析出;经1165℃固溶和时效后,合金的晶粒尺寸明显长大,并有硬而脆的碳化物膜沿晶界连续析出。在650℃/1034MPa条件下,经1160℃固溶和时效的合金,由于在晶界处不连续析出的粒状碳化物对晶界具有钉扎作用,可有效阻碍晶界滑移,使合金具有较好的抗蠕变性能。合金蠕变后期的变形特征是晶内发生单取向和双取向滑移,随着蠕变进行,滑移迹线增多,并在晶界处引起应力集中,致使裂纹在晶界处萌生及扩展并最终导致断裂。     

Ti49.2Ni50.8合金在等径角挤压过程中Ti3Ni4析出相的演化规律

采用透射电子显微镜研究Ti49.2Ni50.8合金中Ti3Ni4析出相在等径角挤压及中间退火过程中的演化规律.固溶态Ti49.2Ni50.8合金在450℃时效处理10～60 min以获得尺寸为37～75 nm的Ti3Ni4析出相.在450℃等径角挤压处理1道次后,时效处理10 min和30 min试样中Ti3Ni4析出...     

FGH95镍基合金的蠕变行为及影响因素

通过蠕变曲线测定和组织形貌观察,研究FGH95合金的蠕变行为及影响因素。结果表明:经1150℃固溶和时效处理后,在晶界处有粗大γ′相不连续分布,其周围存在γ′相贫化区;经1165℃固溶和时效后,合金的晶粒尺寸明显长大,并在晶界形成连续的碳化物膜;经1160℃固溶后,合金中无粗大γ′相,在晶内弥散析出细小γ′相,其中,有粒状(Nb,Ti)C相在晶内及沿晶界不连续析出,可提高合金的晶界强度,抑制晶界滑移,是使合金具有较好蠕变抗力的主要原因。蠕变期间,合金的变形机制是位错剪切或绕过γ′相,蠕变后期,在晶内发生单取向和双取向滑移,并引起应力集中,致使裂纹在晶界处萌生及扩展是合金的蠕变断裂机制。     

Ti—40阻燃钛合金中的第二相

研究了Ti-40(Ti-25V-15Cr-0.2Si)阻燃钛合金中的第二相及其对合金性能的影响。研究结果表明：固溶温度升高,Ti40合金析出第二相的趋势增大;低于850℃固溶,合金中没有第二相析出,高于850℃固溶,合金中析出棒状α相和少量Ti5Si3相;910℃固溶＋600℃时效,合金存在第二相有α和Ti5Si3相;860℃固溶＋600℃时效,合金仅存在Ti5Si3相,固溶时效态存在的第二相对合金的性能没有明显影响,540℃,100h热暴露,合金中存在的各种形态的α相和Ti5Si3析出物,明显降低合金的热稳定性能。     

固溶处理及时效对镍钛形状记忆合金组织演化及力学性能的影响

将镍钛形状记忆合金Ni50.9Ti49.1（摩尔分数）在1123 K固溶处理2 h,然后分别在573、723和873 K时效2h。采用透射电镜、高分辨率透射电镜、扫描电镜和压缩实验,系统研究固溶处理和时效对镍钛合金组织演化及力学性能的影响。结果表明：固溶处理有助于消除原始镍钛样品中的Ti2Ni相,但不能消除TiC相。固溶处理导致镍钛合金中原子排列的有序畴界。在所有时效镍钛样品中,Ni4Ti3析出相、R相和B2奥氏体相共存于室温下的镍钛基体上,然而在873 K时效的镍钛样品中,可以观察到马氏体孪晶。在573和723 K时效的镍钛样品中,细小密集的Ni4Ti3相均匀分布在镍钛基体上,而且与B2基体保持共格关系。然而,在873 K时效的镍钛样品中, Ni4Ti3相尺寸非常不均匀,和B2基体保持共格、半共格和非共格关系。在723 K时效的条件下,细小均匀的Ni4Ti3相阻碍位错运动,导致最大的位错滑移临界分切应力,因此镍钛样品表现出最高的屈服强度。     

双晶体NiTi形状记忆合金在无/有应力作用时效下的Ni_4Ti_3相沉淀行为模拟(英文)

运用相场方法研究双晶体NiTi形状记忆合金分别在无应力和有应力作用下时效过程中Ni4Ti3相的沉淀行为,模拟研究两种不同初始过饱和度(Ni含量分别为51.5%和52.5%,摩尔分数)的NiTi基体并考虑外加应力的影响。模拟结果表明,在无应力作用的体系中,当体系Ni原子初始浓度相对较低(51.5%Ni)时,Ni4Ti3相以非均匀的方式析出,其中晶界上存在大量的Ni4Ti3变体,晶界内大部分区域无变体;当体系Ni原子初始浓度较高(52.5%Ni)时,Ni4Ti3在整个双晶体系中均匀析出。在所研究的两种初始浓度下,一定大小的外加应力将直接导致Ni4Ti3变体在整个模拟体系中均匀析出,而两晶粒中变体的类型分布有所不同。     

多相V-Ti-Ni氢分离合金显微组织与力学性能

研究了多相V_(100-2x)-Ti_x-Ni_x(x=10,15,20)系列氢分离合金的显微组织、硬度和拉伸性能。V_(100-2x)-Ti_x-Ni_x合金铸锭显微组织均由枝晶相V基固溶体和枝晶间相NiTi和NiTi_2组成。随着合金中Ti和Ni的含量增加,枝晶间相在合金中体积占比增大,形成连续网状,阻止枝晶臂的连接。在室温下,合金整体硬度、抗拉强度、延伸率和断面收缩率均随Ti、Ni含量增加而升高。V基固溶体和NiTi_2相是影响3种合金的整体硬度的主要因素。3种合金在室温下均属于脆性材料。合金中NiTi相含量对合金的延伸率有较大影响。     

Microstructure and mechanical properties of laser melting deposited Ti2Ni3Si/NiTi Laves alloys

Two Ti2Ni3Si/NiTi Laves phase alloys with chemical compositions ofNi-39Ti-11Si and Ni-42Ti-8Si （%, mole fraction, the same below）, respectively, were fabricated by the laser melting deposition manufacturing process, aiming at studying the effect of Ti, Si contents on microstructure and mechanical properties of the alloys. The Ni-39Ti-llSi alloy consisting of Ti2Ni3Si primary dendrites and Ti2Ni3Si/NiTi eutectic matrix is a conventional hypereutectic Laves phase alloy while the Ni-42Ti-8Si alloy being made up of NiTi primary dendrites uniformly distributed in Ti2Ni3Si/NiTi eutectic is a new hypoeutectic alloy. Mechanical properties of the alloys were investigated by nano-indentation test. The results show that the decrease of Si and the increase of Ti contents change the microstructures of the alloys from hypereutectic to hypoeutectic, which influences the mechanical properties of the alloys remarkably. Corrosion behaviors of the alloys were also evaluated by potentiodynamic anodic polarization curves.     

60NiTi合金的热变形行为及本构方程

60NiTi合金具有强度高、耐磨性好等一系列优异的性能。但由于它难热成型,因此大大限制了在工业领域的广泛应用。为了确定60NiTi合金最优的热加工工艺,研究了铸态60NiTi合金在750～1 050℃,0.01～1 s^-1变形速率下的热变形行为,并采用包含Arrhenius项的Z参数法构建了高温变形本构方程。结果显示：仅在1 000℃、1 s^-1速率下高温变形时60NiTi合金发生了明显的动态再结晶,温度升高能提高60NiTi合金的热成型性能。在高温(1 050℃)大变形速率下(1 s^-1)加工60NiTi合金的热成型性能最好。     

固溶-时效处理对Ti-Ni-Cr形状记忆合金拉伸性能和显微组织的影响

用拉伸试验和透射电子显微镜研究了固溶时效处理对Ti-50.8Ni-0.3Cr形状记忆合金拉伸性能和显微组织的影响。800℃固溶淬火态合金的塑性优于时效态。随时效时间tag延长,300和400℃时效态合金的抗拉强度Rm300和Rm400先急剧增大后趋于稳定,且Rm300相似文献   

Influence of aging on microstructure,martensitic transformation and mechanical properties of NiTiRe shape memory alloy

Aging is an effective way to adapt the microstructure, phase transformation and consequently the mechanical properties of NiTi shape memory alloys. In the present study, Ni₅₂Ti_47.7Re_0.3 shape memory alloy was solution treated at 1000 °C for 24 h then aged at various temperatures of 300, 400, 500 and 600 °C for 3 h. The influence of aging treatment on microstructure, martensitic transformation and mechanical properties of Ni₅₂Ti_47.7Re_0.3 was investigated. The microstructure of the solution treated alloy was martensite as a matrix phase and precipitates of Ti₂Ni phase. The aged alloys had a microstructure as same as that of solution treated alloy in addition to the existence of other types of precipitates like Ni₄Ti₃ and Ni₃Ti. The martensitic — austenitic transformation during heating and cooling was going through one stage of transformation. The martensitic phase transformation temperature increased by the increase of aging temperature but still lower than that of solution treated alloy.     

Ni含量对Cu-xNi-3Ti-0.1Zr合金组织和性能的影响

采用真空熔炼并经均匀化退火、热轧、固溶、冷轧和时效处理工艺制备Cu-xNi-3Ti-0.1Zr(x=2、4、6)合金,通过X射线衍射仪、光学显微镜和扫描电镜对合金的析出相进行表征和分析。结果表明,Ni的加入能够显著提高合金的导电率,且对其硬度的影响也同样显著。Ni在Cu-xNi-3Ti-0.1Zr合金中主要以CuNiTi相存在;Ni的加入导致合金中大量CuNiTi相的析出,降低了基体中Ti的固溶度,使合金的晶格畸变程度降低,从而提高了合金的导电率。但随着Ti的析出,Ti对合金的强化效果减弱,从而导致合金的硬度降低。在本试验工艺下,Cu-xNi-3Ti-0.1Zr(x=2、4、6)合金在500 ℃时效的峰值硬度分别为295、231、201 HV0.5。     

Microstructure evolution and thermal stability of nanocrystalline Cu-Nb alloys during heat treatment

The microstructure evolution and high thermal stability of the mechanically-alloyed supersaturated nanocrystalline Cu-10%Nb alloy during subsequent heat treatment were investigated by X-ray diffractometry and transmission electron microscopy (TEM). The results show that no significant change of the microstructure of the solid solution can be detected after annealing at 300-400 ℃. The pronounced phase separation can be detected at 700 ℃. After annealing for 30 min at 900 ℃, almost all the Nb atoms precipitate from the solid solution, and the average Cu grain size is about 37 nm. As the solute atoms hinder the migration of fcc phase, at Cu grain boundaries, no significant grain growth occurs before large amount of Nb atoms precipitates from Cu matrix, and the decrease of internal strain and density of dislocation is small. Furthermore, the nanosized Nb precipitates can also help to reduce the Cu grains growth through precipitating pinning effect. Therefore, the mechanically-alloyed nanocrystalline Cu-Nb alloys have a high thermal stability. And the contaminations brought into the Cu matrix by milling can influence the phase formation and the thermal stability of Cu-Nb alloys during heat treatment.