Composition and corrosion resistance of cerium conversion films on 2195Al-Li alloy

The Ce conversion films on 2195Al-Li alloy without and with post-treatment were studied and the corrosion resistance was evalu-ated as well. The surface morphology was observed by scanning electron microscopy (SEM), and the chemical composition was characterized by X-ray photoelectron spectroscopy (XPS). The corrosion behaviors of 2195Al-Li alloy and conversion coating were assessed by means of potentiodynamic polarization curves. The experimental results indicated that after post-treatment the surface quality was improved signifi-cantly. According to XPS, the conversion coating after post-treatment was mainly composed of CeO2, Ce2O3, Ce-OH and a little MoO3 and MoO2. The results of potentiodynamic polarization curves revealed that the conversion coating with post-treatment possessed better corrosion resistance than bare alloy and Ce conversion coating without post-treatment.     

Corrosion behavior of rare earth cerium based conversion coating on aluminum alloy

The present paper focused on the use of the salt of rare earth cerium as corrosion inhibitor of aluminum by using cathodic electrolytic passivation method.The corrosion resistance and the microphology of the cerium passivation film were studied by the methods of electrochemical method,scanning electron microscopy(SEM),and energy dispersive spectroscopic analysis.From the results,it was shown that good corrosion resistance of cerium-based passive coating was obtained when the compositions were as follows:CeCl3·7H2O,0.05 mol/L;H2O2,30 ml/L;current density,1.1 mA/cm2;temperature,40 oC;time,9 min.SEM and EDS revealed that the cerium conversion coatings formed on the surface of aluminum alloy were related to cerium hydroxide/hydrated oxide depositions.     

回归加热速率对7050铝合金组织及抗腐蚀性能的影响

采用电导率、抗腐蚀性能测试及透射电镜观察等手段,研究了回归再时效处理过程中回归加热速率(340,57及4.3℃·min^-1)对7050铝合金组织与抗晶间腐蚀和应力腐蚀性能的影响.研究发现,回归加热速率对7050铝合金的抗腐蚀性能有显著的影响,在顾及合金的综合力学性能的情况下,中等回归加热速率能使合金具有较好的抗腐蚀性能.7050铝合金在中速(57℃·min^-1)回归加热条件下,经适当地回归再时效处理后,晶间腐蚀最大深度为50μm,等级为3级,比在340℃·min^-1和4.3℃·min^-1回归加热速率条件下具有更好的抗腐蚀性能,其晶界析出相为较粗大的非连续颗粒,并有较宽的无沉淀析出带.     

微弧氧化对7050铝合金腐蚀行为的影响

采用微弧氧化(MAO)技术在7050铝合金表面制备了陶瓷膜层,运用扫描电子显微镜(SEM)和能谱分析仪(EDS)表征陶瓷膜微观结构,采用动电位极化曲线、电化学阻抗谱(EIS)和慢应变速率拉伸试验(SSRT)研究了微弧氧化膜对7050铝合金在3.5%(质量分数) NaCl水溶液中腐蚀和应力腐蚀开裂(SCC)行为的影响.结果表明:微弧氧化膜层由表面疏松层与内部致密层组成,表面疏松层主要由Al₂O₃组成,内部致密层由氧化铝与铝烧结而成.微弧氧化膜层可以有效抑制7050铝合金表面的腐蚀萌生及明显降低腐蚀速率,且使7050铝合金的应力腐蚀敏感性出现显著下降.     

固溶温度对Al-Zn-Mg-Cu系铝合金组织与应力腐蚀的影响

对7B50铝合金热轧板在460～490℃范围内进行固溶处理、室温水淬及人工时效,通过室温力学性能测试、慢应变速率拉伸实验及电导率测试,结合光学显微镜,扫描电镜和能谱分析,研究固溶温度对Al-Zn-Mg-Cu铝合金组织与应力腐蚀的影响。结果表明,提高固溶温度能有效减少残留相,增加再结晶的体积分数。当固溶温度从460℃提高到490℃时,屈服强度(σ0.2)和抗拉强度(σb)分别提高20.9%和23.5%,固溶温度从480℃升高到490℃时,强度变化不大,但随着固溶温度升高,伸长率先提高后降低,抗应力腐蚀性能先升高后降低。当固溶温度为480℃时,应力腐蚀敏感性最低,综合性能较好。残留相增多和再结晶程度提高是引起应力腐蚀敏感性提高的主要原因。在腐蚀溶液中,应力腐蚀断口形貌为典型的沿晶断裂。     

合金元素对6063铝型材腐蚀性能的影响

本文从分析合金元素的作用机理入手,详细叙述了元素Mg、Si、Fe、Zn、和Cu对6063铝型材腐蚀性能的影响,并在分析实验数据的基础上,总结出了较为合理的工艺参数。     

6005A铝合金的表面损伤对其耐海水腐蚀性能的影响

以6005A铝合金商品实际产生的表面少缺陷、多缺陷试样,以及作为比较的完全去除商品表面膜的人工磨制的三种不同表面状态试样为研究对象,研究铝合金商品表面的实际损伤对其耐海水腐蚀性能的影响及其腐蚀电化学行为.通过场发射扫描电镜和激光共聚焦扫描显微镜对具有不同表面状态的6005A铝合金表面形貌和粗糙度进行了表征,表明铝合金商品实际产生的表面缺陷主要为划伤,体现在随着表面缺陷的增多,表面粗糙度Ra明显增大,表面粗糙度Ra大小可以定量描述表面损伤的严重程度. 6005A铝合金在NaCl质量分数3.5%的模拟海水溶液中发生全面腐蚀和点蚀,表面缺陷越多,粗糙度越大,耐蚀性越差;电化学测试结果表明,表面缺陷越多,粗糙度越大,腐蚀电位越低,腐蚀电流密度越大,耐蚀性越差. 6005A铝合金表面损伤对其耐海水腐蚀性能产生影响的原因为：表面损伤造成铝合金商品原表面膜被破坏,表面缺陷越多,粗糙度越大,表面膜的破坏和表面塑性变形越严重,铝元素会因为被活化而迅速溶解,有着更高的腐蚀速率,而缺陷较少表面有较为均匀致密的氧化膜,对基体有着较好的保护性.     

工业海洋大气环境下阳极氧化6061铝合金的电偶腐蚀行为

在青岛典型的工业海洋大气环境下,进行硼硫酸阳极氧化6061铝合金与不同表面状态的30CrMnSiNi2A结构钢偶接件的户外大气暴露试验,通过电化学测试、腐蚀产物分析、力学性能检测、断口分析等,研究了偶接件中阳极氧化6061铝合金的腐蚀规律与机理.结果表明:经1 a户外大气暴露试验后,与镀镉钛结构钢偶接的6061阳极氧化铝合金力学性能最优,其强度σ_b和延伸率δ分别比原始试样下降6.45%和4.39%,远优于与结构钢裸材偶接的阳极氧化6061铝合金试样(分别下降10%和62.28%),略优于未偶接试样(分别下降6.77%和10.74%).沿晶腐蚀和表面点蚀是导致阳极氧化6061铝合金力学性能下降的主要原因,最严重的沿晶腐蚀裂纹深度达150 μm.青岛大气中的硫化物不仅会侵蚀试样表面形成硫酸铝,还会浸入到晶界促进沿晶腐蚀.     

7A04铝合金在薄液膜下腐蚀行为

采用薄液膜装置研究了7A04铝合金在1mol·L^-1硫酸钠溶液(pH=5)中的腐蚀行为,用扫描电镜(SEM)观察了腐蚀产物的微观形貌,用光电子能谱分析了腐蚀产物的组成,测试了试样在不同液膜厚度下腐蚀不同时间的交流阻抗曲线.结果表明:7A04铝合金在薄液膜下腐蚀不均匀,中心部位腐蚀轻微,而边沿腐蚀相对严重;腐蚀产物主要为Al(OH)₃和硫酸铝;电化学阻抗谱显示在腐蚀前期(0~96h),110μm液膜下7A04铝合金的腐蚀速率最大,而在腐蚀后期(96~168h),材料在本体溶液中腐蚀速率最大.     

耐腐蚀摩托艇ADC12-0.5La铝合金微观组织及制备

为改善ADC12铝合金的耐腐蚀性能,通过超声熔铸法制备ADC12-0.5La铝合金,并利用光学显微镜、扫描电镜、能谱分析仪、硬度计、浸泡腐蚀试验和电化学工作站研究了T6热处理和稀土La改性对ADC12铝合金的微观组织、硬度和耐腐蚀性能的影响。结果表明,T6态ADC12-0.5La铝合金微观组织明显细化,α-Al尺寸减小,形貌变圆整,共晶Si相和AlFeMnSi相细化为短棒状。相比于ADC12铝合金,T6态ADC12-0.5La铝合金硬度达到117.7HV,提高了26.8%,腐蚀电流密度降低了10.7%,腐蚀电位上升了64.4%,腐蚀速率降低了54.4%,腐蚀表面平坦且光滑,表现为较轻微的晶间腐蚀。T6态ADC12-0.5La铝合金提高了腐蚀电位,Al-La-Cu稀土相阻碍了电子移动,铝合金的耐腐蚀性能得到大幅度提高。     

稀土对热浸Al－3Si合金镀层影响的研究

本文对在Ａｌ─３Ｓｉ合金浴中加入０．０５～０．７９％ＲＥ后获得的热浸铝合金镀层的组织和耐腐蚀性性能进行了研究。研究结果表明，微量（≤０．３５％）ＲＥ能改善铝合金浴的流动性和镀层与钢基的结合，并提高镀层的耐盐雾腐蚀和耐３％ＮａＣｌ盐水浸泡腐蚀性能；而过量ＲＥ则由于在镀层中形成明显的ＲＥ富集区而降低镀层的耐腐蚀性能。     

Effect of cerium on microstructure,mechanical properties and corrosion properties of Al-Zn-Mg alloy

The effects of trace Ce on the microstructure,mechanical properties and corrosion resistance of Al-Zn-Mg alloy were studied by means of metallographic analysis,scanning electron microscopy(SEM),mechanical tensile test,slow strain rate tensile test,cyclic polarization curve test,electrochemical impedance spectroscopy test and anodic oxidation test.The results show that the addition of trace Ce has little effect on the strength of Al-Zn-Mg alloy,but can significantly improve the corrosion resistance of the alloy;The mechanical properties and corrosion resistance of the alloys decrease significantly with the addition of excessive Ce;the addition of 0.04 wt%Ce can reduce significantly the self-corrosive current density of AlZn-Mg alloy and increase obviously passivation film resistance of the alloy.The stress corrosion sensitivity index decreases from 0.612 to 0.219,which improves the corrosion resistance properties significantly.     

Study on solid solution and aging process of AZ91D magnesium alloy with cerium

The influence of Ce on solid solution and aging process of AZ91D magnesium alloy was analyzed.The results showed that the decomposition of β-Mg17Al12 phase in AZ91D magnesium alloy at 420 ℃ could be completed within 12 h,while this process in the Ce-containing alloy required more time.In subsequent aging process at 175 ℃,Ce obviously delayed the aging process of AZglD.It was inferred that the influence of Ce on process of solid solution and aging was relative to the Ce that existed in β-Mg17Al12 phase of original structure in the form of solid solution,and the interaction of the Ce and Al was an important factor to get process of solution and aging slowly.     

二氧化硫复合盐雾环境下2024-T351铝合金应力腐蚀开裂

通过SO₂复合盐雾试验模拟工业污染海洋大气环境,结合有限元模拟分析、扫描电镜/能谱仪、光电子能谱分析等技术研究2024-T351铝合金在弹性应力区间的应力腐蚀开裂行为.结果表明:应力腐蚀开裂行为优先发生在2024-T351铝合金C型环的顶部应力集中区域;疏松的腐蚀产物层的形貌经历了由细棒状、团絮状到板块状的变化;试验6 h就可以监测到裂纹,进行到480 h的时候有贯穿裂纹形成,720 h的时候试样完全断裂;裂纹为穿晶和沿晶混合机制,主裂纹以穿晶机制沿C型环法线扩展,二次裂纹沿晶界扩展.     

Zn及热处理制度对2056铝合金力学性能及局部腐蚀行为的影响

通过拉伸性能测试、晶间腐蚀(IGC)、剥落腐蚀(EXCO)实验、极化曲线测试及透射电镜(TEM)分析,研究Zn元素和不同热处理制度对2056铝合金室温常规力学性能、抗晶间腐蚀性能、抗剥落腐蚀性能及微观组织的影响。结果表明,微量Zn均匀存在于合金的各个位置,可促进S′相的析出和提高合金强度;减小晶内与晶界的电化学腐蚀动力,使晶界析出的S相数量减少并不连续分布,无沉淀析出带(PFZ)变窄,提高合金的抗晶间腐蚀性能和抗剥蚀性能。与T6处理态相比,经T8处理后,晶内析出的S′相数量增加、尺寸减小、分布均匀,合金的强度显著提高,塑性降低;同时,沿晶界析出的S相数量减少,PFZ变窄,合金的抗晶间腐蚀和抗剥落腐蚀能力提高。在3.5%的NaCl溶液中进行的极化曲线测试也表现出相同的结果。     

航空Al-Cu-Mg合金剥落腐蚀行为

采用TEM、电化学等分析方法和手段,对在剥落腐蚀溶液中浸泡不同时间的Al-Cu-Mg合金的剥蚀敏感性及电化学阻抗(EIS)进行研究,分析剥落腐蚀的动力学过程.实验结果表明,2524-T4态合金具有良好的耐剥落腐蚀性能,高Cu含量的第二相粒子是影响合金剥蚀行为的主要因素,合金浸泡2d后才可见明显的点蚀,浸泡4d后局部出现剥蚀现象.根据EIS及EIS等效电路的拟合分析合金的剥蚀行为,发现其动力学过程主要由点蚀的诱导形成、点蚀发展及轻微的剥蚀形成三个阶段组成,而腐蚀的界面反应依次经历氧化膜的溶解、表面腐蚀产物的形成、吸附及脱落的一系列过程.     

插套用导电CuSn合金耐腐蚀性能提升研究

用半连续铸造法制备5种合金。通过力学性能测试、盐雾腐蚀失重实验和直观颜色对比,优化出新耐腐蚀插套用导电CuSn合金成分。结果表明,若考虑综合力学性能、电性能、中性盐雾腐蚀失重率、制造成本等因素,合金成分控制范围为(质量分数)：Sn为0.8%～1.2%、Ni为0.8%～1.2%、Al为0.4%～0.6%、Zn为0.5%、Si为0.15%、Zr为0.05%,其余是Cu和不可避免的杂质元素。     

EDTA滴定法测定稀土铝中间合金中稀土总量

准确测定稀土铝中间合金中稀土总量,对于有效控制稀土铝中间合金的生产技术和产品质量具有重要意义。用400g/L氢氧化钠溶液溶解试样,此时,稀土与氢氧化钠反应生成氢氧化稀土沉淀,而铝与氢氧化钠反应后以偏铝酸根的形式留在了试液中,过滤,实现了铝与稀土元素的分离;用盐酸溶解沉淀,加入氢氟酸,此时稀土和氢氟酸反应生成氟化稀土沉淀,而铁与氢氟酸反应形成络合物留在溶液中,过滤,实现了干扰元素铁与稀土元素的分离;加入盐酸和高氯酸溶解沉淀,用抗坏血酸还原残留铁(Ⅲ),乙酰丙酮溶液掩蔽残留的少量干扰元素铝,控制pH 5.5,以二甲酚橙作指示剂,用EDTA标准溶液滴定至溶液由红紫色变为亮黄色即为终点,建立了EDTA滴定法测定稀土铝中间合金中稀土总量的方法。将实验方法用于稀土铝中间合金(镧铝、钐铝、铒铝、钇铝)试样中稀土总量的测定,并在试样中分别加入不同量的于950℃马弗炉中灼烧过的高纯氧化镧、高纯氧化钐、高纯氧化铒和高纯氧化钇试剂进行加标回收试验,结果的相对标准偏差(RSD,n=11)不大于0.30%,加标回收率为99.6%～100.4%。选取镧铝、钐铝试样,按照实验方法测定其中稀土总量,并采用国标GB/T...     

高温电热合金铁铬铝冶金工艺研究

针对铁铬铝电热合金的钢种特点,开发了精炼过程硅含量控制、VOD真空精炼铝合金化、连铸工艺及保护渣等关键技术.通过实践表明:可将铁铬铝合金中硅质量分数控制在0.15％ 以下,VOD真空条件下完成铝质量分数5％ ～6％ 的合金化,VOD精炼时间控制在60～70 min,铝收得率提高至94.5％.通过钢包稀土合金化,稀土合金...     

Investigation of Formation and Inhibition Mechanism of Cerium Conversion Films on Al 2024 Alloy

To study the mechanism of formation and inhibition of Ce conversion films on A1 2024-T3 alloy, scanning microreference electrode technique (SMRE) is used to probe the potential map on A1 2024-T3 in CeC13 solution, the localized corrosion of A1 alloy decreases with immersion time and disappears finally, which results from the competition of Cl^- aggression and Ce^3 inhibition on alloy surface. The results of X-ray photoelectron spectroscopy (XPS) indicate that the Ce conversion films consist of Al2O3, CeO2 and Ce2O3 (Ce(OH)3), and CeO2/Ce2O3 ratio decreases with the immersion time. When a critical pH for Ce(OH)3 formation was reached, Ce(OH)3 will precipitate on the micro cathodic area on alloy surface. Consequently, H2O2, the product of the catholic reaction will oxidize a part of Ce(OH)3 to CeO2, which appears a better corrosion resistance for Al alloys.