老化条件对SiO2-TiO2复合气凝胶光催化性能的影响

采用溶胶-凝胶法,在常压干燥条件下,以离子液体1-己基-3-甲基咪唑溴盐为模板剂和老化液在低温下制备了SiO2-TiO2复合气凝胶,研究了老化温度和老化时间对SiO2-TiO2复合气凝胶制备的影响。采用XRD、TEM及N2吸附/脱附等方法对其结构进行了一系列表征。以活性艳蓝为模拟污染物,考察了样品的光催化性能。实验结果表明,在60℃的老化温度下老化5d,制得的气凝胶样品具备较高的催化活性和最佳的综合性能。     

医用SiO2气凝胶/壳聚糖复合材料的制备

用环境干燥法,通过静电作用制备了SiO2气凝胶/壳聚糖复合材料.SiO2气凝胶为基体,乙醇水溶液为分散介质,三聚磷酸钠为强电解质.采用扫描电镜、红外光谱仪分析其形貌和组成,并实验研究了此复合材料对药物庆大霉素（Gen）的担载能力.结果表明,这种SiO2气凝胶/壳聚糖复合材料对药物包覆率为17.32%.     

石墨烯/碳复合气凝胶的制备及其吸附性能

碳气凝胶具有高比表面积、高导电性等优异的性能,将碳气凝胶与具有同样优异性能的石墨烯相结合,通过溶胶-凝胶法制备得到石墨烯/碳(G/C)复合气凝胶,进一步提高其吸附性能.研究结果表明,G/C复合气凝胶为三维多孔结构,具有较高的比表面积643 m2/g、孔容积1.688 cm3/g、平均孔径13.50 nm.对水中模拟污染...     

棉纤维增韧SiO2气凝胶复合材料的性能

以棉纤维作为增强体,二甲基二乙氧基硅烷(DMDES)和甲基三乙氧基硅烷(MTES)为共前驱体,采用溶胶-凝胶法结合冷冻干燥工艺制备了柔性的棉纤维/SiO2气凝胶复合材料.利用扫描电镜、压汞仪、万能试验机及热导系数测试仪等对材料进行表征分析,研究了棉纤维质量分数对复合材料的微观结构及力学性能的影响.结果表明,棉纤维的添加...     

SiO_2含量对TiO_2/SiO_2吸附性能与光催化活性影响研究

采用溶胶凝胶法制备不同SiO_2摩尔含量的TiO_2/SiO_2复合光催化剂,以亚甲基蓝(MB)的物理吸附降解与光催化降解为探针反应,分别评价了TiO_2/SiO_2复合光催化剂的物理吸附性能和光催化性能,并采用XRD、BET对样品结果进行了表征。结果表明,适量的SiO_2引入可改善光催化剂的孔结构,一定程度上提高材料物理吸附能力,有效提高光催化性能,对亚甲基蓝的光降解率可达76%;而过高的SiO_2引入可显著提高材料的比表面积,平均孔径相对较小,但抑制TiO_2的结晶,晶型表现为无定型结构,对亚甲基蓝的降解主要表现为物理吸附降解而无光催化作用。     

TiO2/SiO2复合气凝胶的制备与传热特性

针对SiO2气凝胶红外遮光性能差的问题,以纳米二氧化钛作为掺杂剂,以正硅酸乙酯(TEOS)为原料,采用溶胶-凝胶工艺和非超临界干燥方法制备了不同TiO2掺杂量的纳米孔改性SiO2气凝胶复合材料,研究了pH值和乙醇含量对凝胶时间的影响,并采用SEM、TEM和BET方法分别对凝胶的表面形貌和孔结构进行了分析表征.结果表明,当pH为6时,乙醇/TEOS为8∶1(摩尔比)时,可得到掺杂均匀、完整的TiO2/SiO2凝胶;热处理后的复合气凝胶具有网状纳米孔结构;当掺杂量小于5％时,干凝胶平均孔径为20～50 nm,比表面积均大于1 000 m2/g.通过红外透过率及消光性能比较,TiO2掺杂SiO2干凝胶复合材料的红外光屏蔽功能较纯SiO2气凝胶提高了50％.     

SiO_2气凝胶/WO_x-TiO_2复合空气净化涂料的制备及性能

以常压干燥制备的SiO2气凝胶和水热合成法制备的WOx-TiO2复合光催化粒子为主要的功能性无机吸附/光催化剂添加相,合成制备了SiO2气凝胶/WOx-TiO2复合空气净化涂料。通过BET-BJH法分析了SiO2气凝胶的比表面积及孔容积,利用光催化降解罗丹明B的实验分析了WOx-TiO2复合光催化粒子的可见光催化活性,重点研究了SiO2气凝胶/WOx-TiO2复合空气净化涂料对罗丹明B和甲醛气体的吸附/光催化降解能力。吸附/光催化降解罗丹明B的实验表明,吸附/光催化剂占涂料质量分数为5.0%时,具有较稳定、较高的吸附/光催化降解率,达69.6%;吸附/光催化降解甲醛的实验表明,当吸附/光催化剂占涂料质量分数的5.0%并且纯SiO2气凝胶与WOx-TiO2复合光催化粒子质量比为1∶1时,3h内复合空气净化涂料对甲醛气体的吸附/光催化降解率可达到84.62%。     

热处理温度对TiO2-SiO2复合气凝胶形貌、结构与性能的影响

采用溶胶-凝胶法结合常压干燥技术,以钛酸丁酯和甲酰胺分别为钛源和化学干燥添加剂,在不同温度进行热处理制得了TiO2-SiO2复合气凝胶;利用XRD、SEM、EDS、BET、红外、TG-DTA分析等表征方法对样品的结构和形貌进行分析,并在紫外光照射下测试了样品对甲基橙溶液的光催化降解效率.结果表明:当热处理温度为700℃...     

H3PW12O40-TiO2/SiO2的制备及光催化性能

以硅胶为载体,采用浸渍法制备了H3PW12O40-TiO2/SiO2催化剂.利用IR、TG-DTA、XRD、XPS对其结构进行表征.研究结果表明,催化剂中的活性组分二氧化钛为锐钛矿型,磷钨酸仍保持其Keggin结构的基本骨架,二氧化钛及磷钨酸二者均与载体之间存在着化学作用.通过对染料罗丹明B的超声光催化降解研究发现,含4gH3PW12O40的TiO2溶胶浸渍在11gSiO2上的催化效果最佳,且H3PW12O40可明显提高TiO2超声光催化降解罗丹明B的降解率.     

二氧化硅-木质素微球的水热法处理及对银离子的吸附

利用稻壳为原料制备了二氧化硅-木质素复合微球,并对微球进行了水热法处理。利用两种微球作为吸附剂对硝酸银溶液进行了吸附实验。通过SEM、TEM、XRD和TGA对微球的结构形貌和性能进行了表征,发现水热处理后的微球中木质素含量明显上升,壳层稳定性也有所改进,微球对银离子具有还原作用,吸附后微球表面有银单质生成。在银离子浓度为0.02mol/L时,90℃水浴条件下反应24h,未经水热法处理的微球吸附量为21.7mg/g,水热法处理后微球吸附量达到55.6mg/g。     

Preparation and photocatalytic performance of ZnO/ZnGa_2O_4 composite microspheres

ZnO/ZnGa_2O_4 composite microspheres with heterojunction were successfully synthesized by one-pot hydrothermal method.These samples were characterized by TG/DTA,XRD,TEM,HRTEM,UV-vis DRS,FL and BET techniques.The results indicated the as-prepared samples showed better degree of crystalline and large specific surface area.The photocatalytic activity was evaluated by degradation of methyl orange with the concentration of 50 mg/L under the irradiation of simulated sunlight.The effects of molar ratio of Zn to Ga and calcination temperature on the photocatalytic activity were investigated in detail.The results showed that the highest photocatalytic degradation efficiency was observed at the molar ratio of Zn to Ga of 1:0.5 in the starting materials and the calcination temperature of 400 °C.The maximum photocatalytic degradation rate of MO was 97.1% within 60 min under the simulated sunlight irradiation,which is greatly higher than that of ZnO and ZnGa_2O_4.     

以天然原料为模板剂制备SiO_2/TiO_2-WO_3介孔光催化材料

以细菌纤维素、银杏叶子、淀粉等天然原料为模板剂,通过简单的一步水热合成法制备SiO2/TiO2-WO3介孔光催化材料,并对其形貌、孔结构及吸附/光催化性能进行表征。结果表明,以细菌纤维素为模板所制备的SiO2/TiO2-WO3介孔光催化材料的比表面积、孔容积最高,分别为308.7 m2/g和0.92mL/g,在水中对罗丹明B具有最好的吸附/光催化降解效果;以叶子为模板的SiO2/TiO2-WO3介孔光催化材料,形成类似叶细胞的不规则的形貌,具有最快的吸附速率;以淀粉为模板的SiO2/TiO2-WO3介孔光催化材料呈现出较为规则的球状,具有较好的光催化性能。     

Preparation and photocatalytic activity of Cu^2＋-doped TiO2/SiO2

Cu2+-doped nanostructured TiO2-coated SiO2. (TiO2./SiO2) particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized by the sol-gel method using TiOSO4 as a precursor. The experimental results showed that TiO2 nanopowders on the surface of SiO2 particles were well distributed and compact. The amount of TiO2 increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550℃. The 2-layer coated TiO2 particles on the surface showed a higher degradation rate compared with all the dif-ferent-layer samples. The photocatalytic activity of Cu2+-doped TiO2/SiO2 was higher than that of undoped TiO2/SiO2. The optimum dopant content was about 0.10wt%.     

自支撑尼龙66/钼酸铋/碘化银复合纳米纤维的制备及其光催化性能

利用静电纺丝和溶剂热法制备了尼龙66/钼酸铋复合纳米纤维,在室温下利用沉积-沉淀法将碘化银沉积在尼龙66/钼酸铋复合纳米纤维表面,制备了具有可见光响应的自支撑尼龙66/钼酸铋/碘化银复合纳米纤维.通过X射线衍射、扫描电子显微镜、能谱扫描仪、紫外-可见漫反射、光电流等表征分析了晶型结构、表面形貌及其光学性能.以罗丹明B为...     

反向原子转移自由基法制备SiO_2/PMMA复合粒子

采用反向原子转移自由基法,制备了SiO2/PMMA复合粒子.用硅烷偶联剂γ-甲基丙烯酰氧基丙基三甲氧基硅烷对纳米SiO2进行表面改性,通过亲水亲油性实验,确定了硅烷偶联剂的最佳用量(质量分数为10%).通过红外光谱和热重分析,证明聚甲基丙烯酸甲酯是通过化学键合接枝到纳米SiO2粒子表面.用透射电镜观察了纳米SiO2和复合粒子在乙醇中的分散情况,表明复合粒子的分散效果更好.