冷轧压下率对无抑制剂取向硅钢初次再结晶退火的影响

对无抑制剂取向硅钢不同压下率下初次再结晶退火后的显微组织、宏观织构和微观织构进行了研究.结果表明,冷轧板织构主要为α取向线{001}＜110＞、{112}＜110＞和{111}＜110＞织构以及γ取向线{111}＜110＞织构.初次再结晶退火后,α取向线织构减弱,织构主要为γ取向线{111}＜112＞织构.随冷轧压下率的增加,冷轧和初次再结晶织构强度增加.当压下率为88％时,初次再结晶退火后 Goss 织构和{111}＜112＞织构强度最高,最有利于发生二次再结晶.EBSD 分析显示,Goss 取向晶粒大多与{111}＜112＞取向晶粒相邻.提高冷轧压下率,Goss取向晶粒和{111}＜112＞取向晶粒都增加,Goss 取向晶粒偏离理想取向角度减少.     

50W600 冷轧无取向电工钢退火过程组织和织构取向的演变

通过金相和电子背散射衍射法(EBSD)研究50W600冷轧无取向电工钢(0.003%～0.008%C、0.3%Si)在700～760℃3～360 s退火水冷时的组织和织构取向演变.结果表明,随退火温度的提高,钢的再结晶率和晶粒尺寸增大,740℃退火时,当保温时间由10 s增加至360 s,再结晶率由22.5%提高到100%,平均晶粒尺寸由3.08μm增大至17.17 μm.同时再结晶织构a线的取向密度下降,在15 8时{001}<110>、{112}<110>、{111}<110>、{110}<110>的取向密度均为1.5左右,y线上{111}<011>和{111}<112>的取向密度稳定在0.25左右.     

冷轧Ti-IF超深冲钢罩式退火机理及织构变化规律的研究

在480~750℃条件下,模拟罩式退火,利用光学显微镜、X射线衍射和金相显微硬度计研究了冷轧Ti-IF超深冲钢晶粒结构的变化,通过取向密度函数分析了再结晶过程织构演变规律。研究表明:冷轧Ti-IF超深冲钢的再结晶温度约为630℃,再结晶过程能够在660℃条件下2 h之内完成;冷轧后该钢主要有4种织构,分别是{001}〈110〉、{111}〈110〉、{111}〈112〉和{112}〈110〉;在退火再结晶过程中,{111}逐渐转变为γ-{111},当退火温度升至720℃时,{001}〈110〉和{112}〈110〉转变为纤维织构γ-{111},最终{111}〈110〉和{111}〈112〉成为主要织构类型。     

冷轧压下率对连续退火Ti-IF钢组织和织构的影响

以工业生产的Ti-IF钢热轧板为研究材料,结合连续热镀锌线的工艺特点,采用实验室冷轧、盐浴退火方法和金相、X射线织构测试等分析手段,研究了冷轧压下率对组织和织构的影响规律。试验结果表明,随着冷轧压下率从60%提高到90%,冷轧态α取向线上的取向密度不断增强,而且主要形成了{223}110和{114}110织构,γ线上的{111}110和{111}112织构亦有所增强;退火后铁素体晶粒尺寸从9.0级细化到10.5级;试验钢退火后仍具有较强的{223}110和{114}110织构,且随着冷轧压下率的提高,{111}织构有增强的趋势。要获得强的{111}织构,冷轧压下率需在80%以上。     

低温板坯加热取向硅钢形变和初次再结晶织构的演变规律

 采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明：一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。     

冷轧过程中IF钢的织构演变

以铁素体区热轧低温卷取的Ti-IF钢为研究对象,选择13%~75%的冷轧压下率,观察在冷轧过程中织构的演变。研究表明,压下率为46%是一个转折点,冷轧压下率较小(13%~35%)时,表面上取向变化为{110}001→{554}225→{111}112→{111}110→{223}110,{114}110转向{001}110;压下率达到46%时,{111}织构消失;继续增加压下率,{111}织构再次出现,并随压下率增加而增强。随着冷轧压下率的增加,中心面上的{111}织构强度先增加,压下率达到46%后又降低,最强组分先由{001}110向{223}110转动;压下率达46%时,又向反方向转动。     

半工艺无取向硅钢加临界变形的织构演变

测定了半工艺无取向电工钢热轧(终轧温度在Ar1以下)到成品各工序的织构,以取向分布函数(ODF)的形式对加临界变形的半工艺无取向硅钢的织构演变作了分析.发现其热轧板表层织构基本是典型的铁素体再结晶{111}组分,心部和1/4厚度处以铁素体剪切织构和轧制变形织构为主.冷轧变形后,心部和表层织构组分比较接近,{111}、{112}和{100}面织构都增加,但{111}组分增加最明显.软化退火后,{001}<110>与{112}<110>组分迅速降低,织构组分以γ纤维织构为主.通过增加临界变形,在最终去应力退火后,{111}不利面织构大量减少,高斯组分增加明显.Taylor因子可以表征不同取向晶粒对变形能的储存能力,从轧制变形时Taylor因子的分布可以解释该实验结果.     

退火工艺及冷轧压下率对CSP工艺低碳冷轧板微观组织及织构演变规律的影响

以包钢CSP工艺生产的5.0 mm热轧板在实验室分别压下到1.75,1.25和0.75 mm冷硬板为原料,在实验室模拟了包钢罩式退火工艺,观察了不同压下率试样的显微组织.实验表明,通过观察罩式退火过程中试样的组织的变化,确定了再结晶开始温度在540℃左右,再结晶终了温度为700℃左右.并用X射线检测了试样在热轧和成品两个阶段的织构.结果表明,随着冷轧压下率的增大,再结晶进行的速度增:大,成品试样的织构密度增大,织构类型以{111}<110>和{111}<112>织构为主,但两者织构密度相差不大.     

无取向电工钢冷轧及退火织构的演变

运用不同冷轧、退火工艺的实验及ODF分析方法,分析了电工钢50W600的热轧织构、冷轧织构及再结晶织构的演变.研究表明:热轧带几乎是随机织构,α线非常弱;随着冷轧变形量的提高,晶粒在α线取向附近聚集程度不断提高,变形81%时,{001}《110》和{112}《110》取向密度分别为12和14.随退火温度升高和保温时间延长,α线的取向密度下降,{001}《110》和{112}《110》取向密度急剧降低,γ线{111}《112》密度显著增加,晶粒取向绝大多数聚集在γ线{111}《112》取向附近.通过控制冷轧及退火工艺,可有利于发展高{100}织构组分的冷轧无取向电工钢.     

再结晶阶段加热速度对低碳冷轧板罩式退火过程组织和织构的影响

在实验室条件下模拟CSP热轧板为基板生产的低碳冷轧板罩式退火过程,研究再结晶阶段加热速度对冷轧板罩式退火过程组织和织构的影响。结果表明,压下率83.3%的冷轧板,随着再结晶阶段加热速度的增加,会使试样再结晶温度降低,再结晶过程提前完成,{001}110织构变强,{111}110织构先减少后增加,{111}112织构先减少后增加出现峰值,当加热速度超过50℃/h时又减小。在加热速度30~40℃/h间变形织构{112}110有较低的密度值。再结晶阶段加热速度40℃/h的退火工艺成品组织为饼形晶粒,{001}110织构密度较低,{111}110和{111}112密度较强,密度值接近。     

Textures and Properties of Hot Rolled High Strength Ti-IF Steels

The texture evolution in a high strength Ti-IF steel during the processing of hot rolling, cold rolling, and annealing is studied. For comparison, both ferrite rolling and austenite rolling are employed. It is found that the texture type is the. same after ferrite rolling and austenite rolling, but the texture intensity is much higher in the ferrite rolled sample. Furthermore, texture characteristics at the surface are absolutely different from those at the mid sec tion in both ferrite rolled and austenite rolled samples, as well as under the cold rolled and annealed conditions. The shear texture { 110 } 〈001 〉 disappears and orientation rotates along { 110 } 〈001 〉→ { 554 } 〈 225 〉→ { 111 } 〈 112 〉→{111}〈110〉→{223}〈110〉 during cold rolling. Compared to the austenite rolled sample, the properties of the cold rolled and annealed sheet which is subjected to ferrite rolling are higher.     

CSP产线340 MPa级高强度无间隙原子钢开发

采用LF-RH双精炼工艺,在CSP流程上进行了340 MPa级冷轧IF高强钢的开发。试验材料达到成分设计要求,罩式炉退火后微观组织为细小等轴铁素体组织,晶粒度在10级左右,力学性能达到340 MPa级高强度无间隙原子钢要求。EBSD结果表明,试验材料退火织构由较强的γ织构（<111>∥ND）和一定强度的α织构（<110>//RD）组成,α取向中较高的{112}<110>和{001}<110>织构是导致试验材料r均值偏低和Δr小于0的主要原因。     

轧制-退火工艺制备超细晶D6 A钢的微观组织与织构

对D6 A钢热轧板进行了两相区轧制及退火处理,获得超细晶 D6 A 合金钢样品,微观结构特征为纳米尺寸的球粒状渗碳体弥散分布于亚微米尺寸的铁素体组织中.实验结果表明：随着退火温度由550℃升高至650℃,铁素体晶粒被拉长现象逐渐减弱直至消失,晶粒尺寸呈现先减小后增大的趋势,在550℃时达到最小尺寸400 nm;同时渗碳体尺寸逐渐由70增加至140 nm,其质量分数分数由9.6％降低至3.6％;随着退火温度升高,实验钢沿α和γ取向线分布的{112}＜110＞、{111}＜112＞和{001}＜110＞织构强度逐渐减弱,600℃退火后消失,{110}＜001＞与{112}＜111＞织构逐渐增强,硬度随退火温度升高由472 HV逐渐减小至423 HV.细晶强化、纳米尺寸渗碳体的析出强化,以及织构强化的共同作用是超细晶D6 A钢的主要强化机制.     

一次再结晶法取向硅钢超薄带的冷轧塑性变形行为北大核心CSCD

以市场上购买的取向硅钢成品板为原料,经不同压下率冷轧至0.23~0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量,利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征,分析了硅钢超薄带的塑性变形行为。结果发现,在平面压缩应力下,{112}<111>滑移系的取向因子较大。随冷轧压下率的增加,Goss织构的含量逐渐减少,{212}<141>织构组分的含量先增加后减少,{111}<112>织构组分的含量逐渐增加,织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶,其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。     

深冲板St15再结晶退火过程织构演变

运用电子背散射花样技术(EBSP)对本钢深冲板St15再结晶退火过程中的织构演变规律进行了研究.当加热速率为30℃/h时,深冲板St15再结晶开始温度在560℃左右,再结晶完成时间约为2h,最强织构组分为{100}<110>.随着温度的升高,深冲板St15的γ纤维织构,尤其是{111}<112>织构有所增强.当保温温度为700℃,随保温时间延长,深冲板St15的{111}<110>织构明显增强,4h后{111}<112>织构开始逐渐增强,到13h时,获得理想的退火织构.     

基于CSP工艺稀土冷轧板罩式退火中组织织构演变

 采用金相显微镜和X射线衍射仪对CSP(Compact Strip Production)稀土板热轧、冷轧及退火3个阶段的组织和织构进行了检测和分析,并结合文献讨论了稀土板组织织构的演变规律。结果表明：稀土冷轧板以{223}<110>、{001}<110>、{112}<110>为主要织构,退火后形成了以{223}<110>和{111}<110>为主的再结晶织构,织构密度均达8. 5以上,{223}<110>和{111}<110>取向差为10°。稀土板开始再结晶需要的温度较高,并且再结晶完成需要的时间较长。再结晶初期织构变化比后期小。试验稀土板退火后{111}/{001}值极大,{111}<011>织构与{111}<211>织构密度差约为6。     

连续退火温度对390 MPa级IF钢组织、织构和力学性能的影响

试验用390 MPa级IF钢(/%:0.005C,0.04Si,0.35Mn,0.095P,0.005S,0.030Nb,0.016Ti,0.036Alt)0.8 mm冷轧板由4 mm热轧板冷轧生产。研究了连续退火温度780~820℃对该IF钢组织、织构和力学性能的影响。结果表明,当连续退火温度由780℃提高至820℃时,IF钢的屈服和抗拉强度分别由282 MPa和432 MPa降至249 MPa和405 MPa,伸长率A₅₀和塑性应变比r_m分别从37.2%和1.45提高到41.7%和1.84,具有较好的深冲性能;但随退火温度升高,平面各向异性指数△r由0.44提高到0.65,铁素体晶粒尺寸增大,组织均匀变差,同时变形织构{112}<110>变弱,有利织构{111}<110>增强,{001}<110>变弱,综合考虑退火温度控制在820℃左右为宜。     

CSP流程DC04汽车板研制

 酒钢利用CSP流程与冷轧生产线匹配进行汽车板DC04的研制,采用提高钢质纯净度和优化热轧工艺及控制冷轧压下量等措施,研制的DC04汽车板碳含量可控制在50×10-6以下,罩式退火后为等轴铁素体组织,成品板晶粒度在ASTM7.5~8,获得了较强的{111}〈110〉{111}〈112〉织构,力学性能均达到IF钢标准。     

冷轧压下率和再结晶退火温度对Ti-IF钢织构和成型性能的影响

采用背散射衍射技术(EBSD)研究了3.13 mm热轧板的冷轧压下量(65%~80%)和再结晶退火温度(660~780℃)对0.64~1.10 mm Ti-IF钢冷轧板(/%:0.02C、0.01Si、0.10Mn、0.013P、0.011S、0.064 Ti、0.028Al、0.002 0N)的织构和成型性能应变硬化指数(n)、塑性应变比(r)的影响。结果表明,Ti-IF钢冷轧板在冷轧压下率为75%时{111}织构含量最大,成型性能最佳;在740℃以下再结晶退火时材料{111}<110>织构含量高,高于740℃时材料{111}<112>织构含量高;在660~780℃再结晶退火随温度增高,材料{111}织构含量增加,成型性能提高。