Effective nanoconfinement of 2LiBH4–MgH2 via simply MgH2 premilling for reversible hydrogen storages

To improve nanoconfinement of LiBH₄ and MgH₂ in carbon aerogel scaffold (CAS), particle size reduction of MgH₂ by premilling technique before melt infiltration is proposed. MgH₂ is premilled for 5 h prior to milling with LiBH₄ and nanoconfinement in CAS to obtained nanoconfined 2LiBH₄–premilled MgH₂. Significant confinement of both LiBH₄ and MgH₂ in CAS, confirmed by SEM–EDS–mapping results, is achieved due to MgH₂ premilling. Due to effective nanoconfinement, enhancement of CAS:hydride composite weight ratio to 1:1, resulting in increase of hydrogen storage capacity, is possible. Nanoconfined 2LiBH₄–premilled MgH₂ reveals a single–step dehydrogenation at 345 °C with no B₂H₆ release, while dehydrogenation of nanoconfined sample without MgH₂ premilling performs in multiple steps at elevated temperatures (up to 430 °C) together with considerable amount of B₂H₆ release. Activation energy (E_A) for the main dehydrogenation of nanoconfined 2LiBH₄–premilled MgH₂ is considerably lower than those of LiBH₄ and MgH₂ of bulk 2LiBH₄–MgH₂ (ΔE_A = 31.9 and 55.8 kJ/mol with respect to LiBH₄ and MgH₂, respectively). Approximately twice faster dehydrogenation rate are accomplished after MgH₂ premilling. Three hydrogen release (T = 320 °C, P(H₂) = 3–4 bar) and uptake (T = 320–325 °C, P(H₂) = 84 bar) cycles of nanoconfined 2LiBH₄–premilled MgH₂ reveal up to 4.96 wt. % H₂ (10 wt. % H₂ with respect to hydride composite content), while the 1st desorption of nanoconfined sample without MgH₂ premilling gives 4.30 wt. % of combined B₂H₆ and H₂ gases. It should be remarked that not only kinetic improvement and B₂H₆ suppression are obtained by MgH₂ premilling, but also the lowest dehydrogenation temperature (T = 320 °C) among other modified 2LiBH₄–MgH₂ systems is acquired.     

Effect of SWNTs on the reversible hydrogen storage properties of LiBH4–MgH2 composite

Single-walled carbon nanotubes (SWNTs) were mechanically milled with LiBH₄/MgH₂ mixture, and examined with respect to its effect on the reversible dehydrogenation properties of the Li–Mg–B–H system. Experimental results show that the addition of SWNTs results in an enhanced dehydriding rate and improved cyclic stability of the LiBH₄/MgH₂ composite. For example, the LiBH₄/MgH₂ composite with 10 wt% purified SWNTs additive can release nearly 10 wt% hydrogen within 20 min at 450 °C, with an average dehydriding rate over 2 times faster than that of the neat LiBH₄/MgH₂ sample. Based on the results of phase analysis and a series of designed experiments, the mechanism underlying the observed property improvement was discussed.     

Processing analysis of the ternary LiNH2–MgH2–LiBH4 system for hydrogen storage

In this article, we investigate the ternary LiNH₂–MgH₂–LiBH₄ hydrogen storage system by adopting various processing reaction pathways. The stoichiometric ratio of LiNH₂:MgH₂:LiBH₄ is kept constant with a 2:1:1 molar ratio. All samples are prepared using solid-state mechano-chemical synthesis with a constant rotational speed, but with varying milling duration. Furthermore, the order of addition of parent compounds as well as the crystallite size of MgH₂ are varied before milling. All samples are intimate mixtures of Li–B–N–H quaternary hydride phase with MgH₂, as evidenced by XRD and FTIR measurements. It is found that the samples with MgH₂ crystallite sizes of approximately 10 nm exhibit lower initial hydrogen release at a temperature of 150 °C. Furthermore, it is observed that the crystallite size of Li–B–N–H has a significant effect on the amount of hydrogen release with an optimum size of 28 nm. The as-synthesized hydrides exhibit two main hydrogen release temperatures, one around 160 °C and the other around 300 °C. The main hydrogen release temperature is reduced from 310 °C to 270 °C, while hydrogen is first reversibly released at temperatures as low as 150 °C with a total hydrogen capacity of ∼6 wt.%. Detailed thermal, capacity, structural and microstructural properties are discussed and correlated with the activation energies of these materials.     

Destabilization of LiBH4 by nanoconfinement in PMMA–co–BM polymer matrix for reversible hydrogen storage

Destabilization of LiBH₄ by nanoconfinement in poly (methyl methacrylate)–co–butyl methacrylate (PMMA–co–BM), denoted as nano LiBH₄–PMMA–co–BM, is proposed for reversible hydrogen storage. The onset dehydrogenation temperature of nano LiBH₄–PMMA–co–BM is reduced to ∼80 °C (ΔT = 340 and 170 °C as compared with milled LiBH₄ and nanoconfined LiBH₄ in carbon aerogel, respectively). At 120 °C under vacuum, nano LiBH₄–PMMA–co–BM releases 8.8 wt.% H₂ with respect to LiBH₄ content within 4 h during the 1st dehydrogenation, while milled LiBH₄ performs no dehydrogenation at the same temperature and pressure condition. Moreover, nano LiBH₄–PMMA–co–BM can be rehydrogenated at the mildest condition (140 °C under 50 bar H₂ for 12 h) among other modified LiBH₄ reported in the previous literature. Due to the hydrophobicity of PMMA–co–BM host, deterioration of LiBH₄ by oxygen and humidity in ambient condition is avoided after nanoconfinement. Although the interaction between LiBH₄ and the pendant group of PMMA–co–BM leads to a reduced hydrogen storage capacity, significant destabilization of LiBH₄ is accomplished.     

Effects of MoS2 addition on the hydrogen storage properties of 2LiBH4–MgH2 systems

A 2LiBH₄–MgH₂–MoS₂ composite was prepared by solid-state ball milling, and the effects of MoS₂ as an additive on the hydrogen storage properties of 2LiBH₄–MgH₂ system together with the corresponding mechanism were investigated. As shown in the TG–DSC and MS results, with the addition of 20 wt.% of MoS₂, the onset dehydrogenation temperature is reduced to 206 °C, which is 113 °C lower than that of the pristine 2LiBH₄–MgH₂ system. Meanwhile, the total dehydrogenation amount can be increased from 9.26 wt.% to 10.47 wt.%, and no gas impurities such as B₂H₆ and H₂S are released. Furthermore, MoS₂ improves the dehydrogenation kinetics, and lowers the activation energy (E_a) 34.49 kJ mol⁻¹ of the dehydrogenation reaction between Mg and LiBH₄ to a value lower than that of the pristine 2LiBH₄–MgH₂ sample. According to the XRD test, Li₂S and MoB₂ are formed by the reaction between LiBH₄ and MoS₂, which act as catalysts and are responsible for the improved hydrogen storage properties of the 2LiBH₄–MgH₂ system.     

Interface effects in NaAlH4–carbon nanocomposites for hydrogen storage

For practical solid-state hydrogen storage, reversibility under mild conditions is crucial. Complex metal hydrides such as NaAlH₄ and LiBH₄ have attractive hydrogen contents. However, hydrogen release and especially uptake after desorption are sluggish and require high temperatures and pressures. Kinetics can be greatly enhanced by nanostructuring, for instance by confining metal hydrides in a porous carbon scaffold. We present for a detailed study of the impact of the nature of the carbon–metal hydride interface on the hydrogen storage properties. Nanostructures were prepared by melt infiltration of either NaAlH₄ or LiBH₄ into a carbon scaffold, of which the surface had been modified, varying from H-terminated to oxidized (up to 4.4 O/nm²). It has been suggested that the chemical and electronic properties of the carbon/metal hydride interface can have a large influence on hydrogen storage properties. However, no significant impact on the first H₂ release temperatures was found. In contrast, the surface properties of the carbon played a major role in determining the reversible hydrogen storage capacity. Only a part of the oxygen-containing groups reacted with hydrides during melt infiltration, but further reaction during cycling led to significant losses, with reversible hydrogen storage capacity loss up to 40% for surface oxidized carbon. However, if the carbon surface had been hydrogen terminated, ∼6 wt% with respect to the NaAlH₄ weight was released in the second cycle, corresponding to 95% reversibility. This clearly shows that control over the nature and amount of surface groups offers a strategy to achieve fully reversible hydrogen storage in complex metal hydride-carbon nanocomposites.     

Study on the hydrogen storage properties and reaction mechanism of NaAlH4–MgH2–LiBH4 ternary-hydride system

In this paper, we report the hydrogen storage properties and reaction mechanism of NaAlH₄–MgH₂–LiBH₄ (1:1:1) ternary-hydride system prepared by ball milling. It was found that during ball milling, the NaAlH₄/MgH₂/LiBH₄ combination converted readily to the mixture of LiAlH₄/MgH₂/NaBH₄ and there is a mutual destabilization among the hydrides. Three major dehydrogenation steps were observed in the system, which corresponds to the decomposition of LiAlH₄, MgH₂, and NaBH₄, respectively. The onset dehydrogenation temperature of MgH₂ in this system is observed at around 275 °C, which is over 55 °C lower from that of as-milled MgH₂. Meanwhile, NaBH₄-relevant decomposition showed significant improvement, starts to release hydrogen at 370 °C, which is reduced by about 110 °C compared to the as-milled NaBH₄. The second and third steps decomposition enthalpy of the system were determined by differential scanning calorimetry measurements and the enthalpies were changed to be 61 and 100 kJ mol⁻¹ H₂ respectively, which are smaller than that of MgH₂ and NaBH₄ alone. From the Kissinger plot, the apparent activation energy, E_A, for the decomposition of MgH₂ and NaBH₄ in the composite was reduced to 96.85 and 111.74 kJ mol⁻¹ respectively. It is believed that the enhancement of the dehydrogenation properties was attributed to the formation of intermediate compounds, including Li–Mg, Mg–Al, and Mg–Al–B alloys, upon dehydrogenation, which change the thermodynamics of the reactions through altering the de/rehydrogenation pathway.     

Improved reversible dehydrogenation properties of 2LiBH4–MgH2 composite by milling with graphitic carbon nitride

The 2LiBH₄–MgH₂ reactive hydride composite is a promising hydrogen storage system due to the combined high hydrogen capacity and relatively moderate reaction enthalpy. However, the sluggish de/rehydrogenation kinetics severely impedes its practical applications. In this study, graphitic carbon nitride (C₃N₄) as a metal-free additive was added to the 2LiBH₄–MgH₂ composite and examined with respect to the promoting effect on the hydrogen storage properties of the composite. Our study found that mechanically milling with small amount of C₃N₄ additive can eliminate the incubation period between two dehydrogenation steps and thus markedly enhance the dehydrogenation kinetics of the LiBH₄–MgH₂ composite. Further cyclic study found that the composite with C₃N₄ additive exhibits improved cyclic dehydrogenation property although it also shows capacity loss upon cycling, particularly in the second cycle. Combined dehydrogenation property, phase analysis and a series of designed experiments suggested that the C₃N₄ additive could react with both LiBH₄ and MgH₂ in heating process, and the resulting products may improve the reversible dehydrogenation property of the composite system.     

Improved reversible dehydrogenation properties of LiBH4–MgH2 composite by tailoring nanophase structure using activated carbon

In this study, activated carbon (AC) was added to the 2LiBH₄–MgH₂ composite and examined with respect to its effect on the hydrogen storage properties of the system. Our study found that AC is an effective additive for promoting the reversible dehydrogenation of the 2LiBH₄–MgH₂ composite. A series of control experiments were carried out to optimize the sample preparation method, milling time and addition amount of AC. In comparison with the neat LiBH₄–MgH₂ system, the LiBH₄–MgH₂–AC composite prepared under optimized conditions exhibits enhanced dehydrogenation kinetics, improved cyclic stability and particularly, eliminated incubation period between the two dehydrogenation stages. A combination of phase/microstructure/chemical state analyses has been conducted to gain insight into the promoting effect of AC on the reversible dehydrogenation of the 2LiBH₄–MgH₂ system. Our study found that AC exerts its promoting effect via tailoring nanophase structure of the 2LiBH₄–MgH₂ composite.     

Improved hydrogen storage performance of the LiNH2–MgH2–LiBH4 system by addition of ZrCo hydride

Significant improvements in the hydrogen absorption/desorption properties of the 2LiNH₂–1.1MgH₂–0.1LiBH₄ composite have been achieved by adding 3wt% ZrCo hydride. The composite can absorb 5.3wt% hydrogen under 7.0 MPa hydrogen pressure in 10 min and desorb 3.75wt% hydrogen under 0.1 MPa H₂ pressure in 60 min at 150 °C, compared with 2.75wt% and 1.67wt% hydrogen under the same hydrogenation/dehydrogenation conditions without the ZrCo hydride addition, respectively. TPD measurements showed that the dehydrogenation temperature of the ZrCo hydride-doped sample was decreased about 10 °C compared to that of the pristine sample. It is concluded that both the homogeneous distribution of ZrCo particles in the matrix observed by SEM and EDS and the destabilized N–H bonds detected by IR spectrum are the main reasons for the improvement of H-cycling kinetics of the 2LiNH₂–1.1MgH₂–0.1LiBH₄ system.     

Comprehensive hydrogen storage properties and catalytic mechanism studies of 2LiBH4–MgH2 system with NbF5 in various addition amounts

In the present work, the role of NbF₅ addition amount in affecting the comprehensive hydrogen storage properties (dehydrogenation, rehydrogenation, cycling performance, hydrogen capacity) of 2LiBH₄–MgH₂ system as well as the catalytic mechanism of NbF₅ have been systematically studied. It is found that increasing the addition amount of NbF₅ to the 2LiBH₄–MgH₂ system not only results in dehydrogenation temperature reduction and hydriding–dehydriding kinetics enhancement but also leads to the de/rehydrogenation capacity loss. Compared with other samples, 2LiBH₄–MgH₂ doping with NbF₅ in weight ratios of 40:4 exhibits superior comprehensive hydrogen storage properties, which can stably release ∼8.31 wt.% hydrogen within 2.5 h under 4 bar H₂ and absorb ∼8.79 wt.% hydrogen within 10 min under 65 bar H₂ at 400 °C even up to 20 cycling. As far as we know, this is the first time that excellent reversibility as high as 20 cycles without obvious degradation tendency in both of hydrogen capacity and reaction rate has been achieved in the 2LiBH₄–MgH₂ system. The further experimental study reveals that the highly catalytic effects of NbF₅ on the 2LiBH₄–MgH₂ system are derived from the reaction between NbF₅ and LiBH₄, which provides a fundamental insight into the catalytic mechanism of NbF₅.     

Catalytic effect of carbon nanostructures on the hydrogen storage properties of MgH2–NaAlH4 composite

The present investigation describes the hydrogen storage properties of 2:1 molar ratio of MgH₂–NaAlH₄ composite. De/rehydrogenation study reveals that MgH₂–NaAlH₄ composite offers beneficial hydrogen storage characteristics as compared to pristine NaAlH₄ and MgH₂. To investigate the effect of carbon nanostructures (CNS) on the de/rehydrogenation behavior of MgH₂–NaAlH₄ composite, we have employed 2 wt.% CNS namely, single wall carbon nanotubes (SWCNT) and graphene nano sheets (GNS). It is found that the hydrogen storage behavior of composite gets improved by the addition of 2 wt.% CNS. In particular, catalytic effect of GNS + SWCNT improves the hydrogen storage behavior and cyclability of the composite. De/rehydrogenation experiments performed up to six cycles show loss of 1.50 wt.% and 0.84 wt.% hydrogen capacity in MgH₂–NaAlH₄ catalyzed with 2 wt.% SWCNT and 2 wt.% GNS respectively. On the other hand, the loss of hydrogen capacity after six rehydrogenation cycles in GNS + SWCNT (1.5 + 0.5) wt.% catalyzed MgH₂–NaAlH₄ is diminished to 0.45 wt.%.     

Material properties and empirical rate equations for hydrogen sorption reactions in 2 LiNH2–1.1 MgH2–0.1 LiBH4–3 wt.% ZrCoH3

2 LiNH₂–1.1 MgH₂–0.1 LiBH₄–3 wt.% ZrCoH₃ is a solid state hydrogen storage material with a hydrogen storage capacity of up to 5.3 wt.%. As the material shows sufficiently high desorption rates at temperatures below 200 °C, it is used for a prototype solid state hydrogen storage tank with a hydrogen capacity of 2 kWh_el that is coupled to a high temperature proton exchange membrane fuel cell. In order to design an appropriate prototype reactor, model equations for the rate of hydrogen sorption reactions are required. Therefore in the present study, several material properties, like bulk density and thermodynamic data, are measured. Furthermore, isothermal absorption and desorption experiments are performed in a temperature and pressure range that is in the focus of the coupling system. Using experimental data, two-step model equations have been fitted for the hydrogen absorption and desorption reactions. These empirical model equations are able to capture the experimentally measured reaction rates and can be used for model validation of the design simulations.     

Improved hydrogen storage performance of MgH2–NaAlH4 composite by addition of TiF3

In a previous paper, it was demonstrated that a MgH₂–NaAlH₄ composite system had improved dehydrogenation performance compared with as-milled pure NaAlH₄ and pure MgH₂ alone. The purpose of the present study was to investigate the hydrogen storage properties of the MgH₂–NaAlH₄ composite in the presence of TiF₃. 10 wt.% TiF₃ was added to the MgH₂–NaAlH₄ mixture, and its catalytic effects were investigated. The reaction mechanism and the hydrogen storage properties were studied by X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry (DSC), temperature-programmed-desorption and isothermal sorption measurements. The DSC results show that MgH₂–NaAlH₄ composite milled with 10 wt.% TiF₃ had lower dehydrogenation temperatures, by 100, 73, 30, and 25 °C, respectively, for each step in the four-step dehydrogenation process compared to the neat MgH₂–NaAlH₄ composite. Kinetic desorption results show that the MgH₂–NaAlH₄–TiF₃ composite released about 2.4 wt.% hydrogen within 10 min at 300 °C, while the neat MgH₂–NaAlH₄ sample only released less than 1.0 wt.% hydrogen under the same conditions. From the Kissinger plot, the apparent activation energy, E_A, for the decomposition of MgH₂, NaMgH₃, and NaH in the MgH₂–NaAlH₄–TiF₃ composite was reduced to 71, 104, and 124 kJ/mol, respectively, compared with 148, 142, and 138 kJ/mol in the neat MgH₂–NaAlH₄ composite. The high catalytic activity of TiF₃ is associated with in situ formation of a microcrystalline intermetallic Ti–Al phase from TiF₃ and NaAlH₄ during ball milling or the dehydrogenation process. Once formed, the Ti–Al phase acts as a real catalyst in the MgH₂–NaAlH₄–TiF₃ composite system.     

Mg2FeH6–LiBH4 and Mg2FeH6–LiNH2 composite materials for hydrogen storage

Two composite hydrogen storage materials based on Mg₂FeH₆ were investigated for the first time. The Mg₂FeH₆–LiBH₄ composite of molar ratio 1:5 showed a hydrogen desorption capacity of 5.6 wt.% at 370 °C, and could be rehydrogenated to 3.6 wt.% with the formation of MgH₂, as the material was heated to 445 °C and held at this temperature. The Mg₂FeH₆–LiNH₂ composite of 3:10 molar ratio exhibited a hydrogen desorption capacity of 4.3 wt.% and released hydrogen at 100 °C lower then the Mg₂FeH₆–LiBH₄ composite, but this mixture could not be rehydrogenated. Compared to neat Mg₂FeH₆, both composites show enhanced hydrogen storage properties in terms of desorption kinetics and capacity at these low temperatures. In particular, Mg₂FeH₆–LiNH₂ exhibits a much lower desorption temperature than neat Mg₂FeH₆, but only Mg₂FeH₆–LiBH₄ re-absorbs hydrogen.     

Raman spectroscopic observation of dehydrogenation in ball-milled LiNH2–LiBH4–MgH2 nanoparticles

In situ Raman spectroscopy was used to monitor the dehydrogenation of ball-milled mixtures of LiNH₂–LiBH₄–MgH₂ nanoparticles. The as-milled powders were found to contain a mixture of Li₄BN₃H₁₀ and Mg(NH₂)₂, with no evidence of residual LiNH₂ or LiBH₄. It was observed that the dehydrogenation of both of Li₄BN₃H₁₀ and Mg(NH₂)₂ begins at 353 K. The Mg(NH₂)₂ was completely consumed by 415 K, while Li₄BN₃H₁₀ persisted and continued to release hydrogen up to 453 K. At higher temperatures Li₄BN₃H₁₀ melts and reacts with MgH₂ to form Li₂Mg(NH)₂ and hydrogen gas. Cycling studies of the ball-milled mixture at 423 K and 8 MPa (80 bar) found that during rehydrogenation of Li₄BN₃H₁₀ Raman spectral modes reappear, indicating partial reversal of the Li₄BN₃H₁₀ to Li₂Mg(NH)₂ transformation.     

Reversible hydrogen storage behavior of LiBH4–Mg(OH)2 composites

The dehydrogenation/hydrogenation properties of LiBH₄-xMg(OH)₂ were systematically investigated. The results show that the LiBH₄-0.3Mg(OH)₂ composite possesses optimal dehydrogenation properties: approximately 9.6 wt% of hydrogen is released via a stepwise reaction with an onset temperature of 100 °C. In the range of 100–250 °C, a chemical reaction between LiBH₄ and Mg(OH)₂ first occurs to give rise to the generation of LiMgBO₃, MgO and H₂. From 250 to 390 °C, the newly developed LiMgBO₃ reacts with LiBH₄ to form MgO, Li₃BO₃, LiH, B₂O₃ and Li₂B₁₂H₁₂ with hydrogen release. From 390 to 450 °C, the decomposition of LiBH₄ and Li₂B₁₂H₁₂ proceeds to release additional hydrogen and to form LiH and B. A further hydrogenation experiment indicates that the dehydrogenated LiBH₄-0.3Mg(OH)₂ sample can take up 4.7 wt% of hydrogen at 450 °C and 100 bar of hydrogen with good cycling stability, which is superior to the pristine LiBH₄.     

Improved reversible dehydrogenation of LiBH4–MgH2 composite by the synergistic effects of Al and MgO

In this paper, we report a novel method of improving the reversible dehydrogenation properties of the 2LiBH₄–MgH₂ composite. Our study found that mechanically milling with small amount of Al powder can markedly shorten or even eliminate the problematic incubation period that interrupts the dehydrogenation steps of the 2LiBH₄–MgH₂ composite. But the resulting composite showed serious kinetics degradation upon cycling. In an effort to solve this problem, we found that combined usage of small amounts of Al and MgO enabled the 2LiBH₄–MgH₂ composite to rapidly and reversibly deliver around 9 wt% hydrogen at 400 °C under 0.3 MPa H₂, which compares favorably with the dehydrogenation performance of the composites with transition-metal additives. A combination of phase/microstructural analyses and series of control experiments has been conducted to gain insight into the promoting effects of Al and MgO. It was found that Al and MgO additives act as precursor and promoter for the formation of AlB₂ heterogeneous nucleation sites, respectively.     

Remarkable hydrogen storage properties and mechanisms of the shell–core MgH2@carbon aerogel microspheres

Carbon aerogel (CA) microspheres with highly crumpled graphene–like sheets surface and network internal structure have been successfully prepared by an inverse emulsion polymerization routine, subsequently ball milled with Mg powder to fabricate Mg@CA. The Mg change into MgH₂ phases, decorating on the surface of the CA forming MgH₂@CA microspheres composite after the hydrogenation process at 400 °C. The MgH₂@CA microspheres composite displays MgH₂–CA shell–core structure and shows enhanced hydrogenation and dehydrogenation rates. It can quickly uptake 6.2 wt% H₂ within 5 min at 275 °C and release 4.9 wt% H₂ within 100 min at 350 °C, and the apparent activation energy for the dehydrogenation is decreased to 114.8 kJ mol^?1. The enhanced sorption kinetics of the composite is attributed to the effects of the in situ formed MgH₂ NPs during the hydrogenation process and the presence of CA. The nanosized MgH₂ could reduce the hydrogen diffusion distance, and the CA provides the sites for nucleation and prevents the grains from agglomerating. This novel method of in situ producing MgH₂ NPs on zero–dimensional architecture can offer a new horizon for obtaining high performance materials in the hydrogen energy storage field.