Ce0.9Gd0.1O19.5纳米粉的合成研究

分别采用柠檬酸一硝酸盐法,甘氨酸一硝酸盐法,碳酸盐共沉淀法制备了Ce0.9Gd0.1O19.5粉体。利用XRD、TG-DTA和FI-IR对粉体进行了表征,探讨了合成方法和烧结温度对掺杂CeO2米粉体粒径的影响。结果表明,烧结温度对粉体的粒径大小有较大的影响,采用碳酸盐共沉淀法合成的样品于500℃下焙烧2h后合成的掺杂CeO2粉体的颗粒最小。     

超细羽绒粉体/天然橡胶共混膜的制备及力学性能研究

采用γ-巯基丙基三甲氧基硅烷（KH590）、苯基异氰酸酯（PI）和十八烷基异氰酸酯（ODI）对超细羽绒粉体进行表面疏水化改性,制备了不同羽绒粉体含量的超细羽绒粉体/天然橡胶弹性体共混膜。分析了粉体含量及不同改性剂对天然橡胶共混膜吸水性能和拉伸力学性能的影响。结果表明：粉体的添加提高了共混膜的吸水率,与未改性粉体相比,PI和ODI对粉体改性可降低共混膜的吸水率,并提高了共混膜的断裂强度和断裂伸长率。共混膜的弹性模量随粉体含量的影响较大。     

金属陶瓷复合粉体的制备及其应用

介绍了金属陶瓷复合粉体的制备方法,并对采用该复合粉体制备的新型陶瓷材料的性能进行了初步研究。研究表明陶瓷粉体的活化是获得金属陶瓷复合粉体的关键环节。利用该粉体制备的Al2O3 Ti Co材料具有较高的断裂韧性和抗磨损性能。     

Sol-Gel法制备金云母/羟基磷灰石复合材料的研究

以熔融法制备可加工生物玻璃陶瓷的基础配方及分相机理为基础，采用溶胶-凝胶法分别制备了金云母和羟基磷灰石粉体，并由复合工艺制备了金云母／羟基磷灰复合材料。通过DTA、XRD、SEM等对粉体及材料进行了分析，结果表明：采用溶胶-凝胶法可制备出以钠金云母为主晶相的粉体，将该粉体与溶胶-凝胶法制备的羟基磷灰石粉体进行混合可制备出可加工性生物活性材料。     

不同光源下TiO2-ZnO改性粉体光催化性能研究

采用水热合成法对自制的TiO2—ZnO复合粉体进行了Pb、F单元素改性和Pb、F双元素改性,以样品对水中罗丹明B的降解性能为评价指标,对样品的光催化性能进行了评价。结果表明,改性TiO2—ZnO复合粉体在紫外光源下的光催化性能优于在日光灯光源下;在紫外光源下,Pb改性使TiO2—ZnO复合粉体的光催化性能降低,在日光灯光源下,Pb改性使粉体的光催化性能提高,最佳掺杂量为0.4%;F改性使TiO2—ZnO复合粉体的光催化性能提高;Pb、F双元素改性粉体的光催化性能比Pb改性粉体好,而比F改性粉体差。     

金属陶瓷复合粉体的制备及其应用

介绍了金属陶瓷复合粉体的制备方法，并对采用该复合粉体制备的新型陶瓷材料的性能进行了初步研究。研究表明陶瓷粉体的活化是获得金属陶瓷复合粉体的关键环节。利用该粉体制备的Al2O3-Ti-Co材料具有较高的断裂韧性和抗磨损性能。     

改性果酸粉体的大分子明胶法制备及其缓释作用

采用大分子明胶制备改性果酸粉体,比较了不同干燥方式下得到的果酸粉体的缓释作用,并用红外光谱对不同干燥方式下得到的果酸粉体进行了表征.结果表明,经过明胶改性后制得的果酸粉体,能够有效延长果酸粉体的果酸释放时间.喷雾干燥得到的果酸粉体,其缓释作用优于真空干燥和冷冻干燥得到的果酸粉体.当喷雾干燥的进口温度为140℃,出口温度为110℃时,制得的果酸粉体缓释作用较好.经过大分子明胶改性,通过不同干燥方式得到的果酸粉体,并没有改变果酸的化学结构,不会影响果酸的使用效果.     

水热法制备ZnO∶Sb粉体结构及光学性质

采用水热法在石英衬底上以ZnCl2和SbCl3水溶液为源溶液,在较低温度下制备了Sb掺杂的ZnO粉体。采用X射线衍射(XRD)和EDS能谱仪对所生长ZnO粉体的晶体结构和元素成分进行了表征,考察了Sb掺杂对ZnO微观结构和发光性能的影响。结果表明:Sb掺杂的ZnO粉体呈六方纤锌矿结构。室温光致发光(PL)谱检测显示,Sb掺杂ZnO粉体具有很强的近带边紫外发光峰,而与深能级相关的缺陷发光峰则很弱。     

锆瓷口腔修复材料用复合粉体的研制

采用不同粒度、纯度的原料 ,根据不同的配方 ,采用沉淀包裹法、共沉淀法和混合法等制粉方法制备出了锆瓷口腔修复材料用复合粉体 ,对不同方法制备的复合粉体性能进行了综合比较 .研究发现 :采用沉淀包裹可以制得 t- Zr O2 含量较高的复合粉体 ,采用沉淀包裹法制备的复合粉体比共沉淀和混合法综合效果好 .     

光催化TiO2纳米粉体的水热合成

以硫酸钛为原料，采用水热法制备了陶瓷载体用的光催化二氧化钛粉体。通过XRD等测试分析对TiO2粉体进行表征，研究了TiO2粉体的光催化活性。结果表明，所制得的TiO2粉体均训锐钛矿型TiO2，晶粒尺寸均达纳米级，具有良好的光催化活性。     

微波内氧化法制备Al2O3/Cu复合材料

CuO—Al混合粉末微波加热至一定温度下可发生内氧化反应,用X射线衍射仪对反应后的复合粉末进行成份分析,确定CuO-Al混合粉末发生内氧化反应的最佳温度与时间。在此条件下采用常规烧结方法制备Al2O3/Cu复合材料。SEM分析表明,微波内氧化法可以有效制备Al2O3／Cu复合材料,细小的Al2O3增强相弥散分布在Al2O3／Cu复合材料中。     

EVA边角料/NR/胶粉复合发泡材料的制备及其性能

以废弃工业乙烯-乙酸乙烯酯（EVA）泡沫边角料、天然橡胶（NR）和废旧胶粉等为原料,通过共混模压制备EVA边角料/NR/胶粉复合发泡材料。研究了交联剂、发泡剂等助剂的种类与含量对EVA边角料/NR/胶粉复合发泡材料的发泡性能和力学性能的影响。结果表明,偶氮二甲酰胺、过氧化二异丙苯、N550炭黑、轻质碳酸钙含量分别为4 phr（每百克份数）、0.8 phr、5 phr、10 phr时,复合发泡材料的发泡质量及力学性能较好。差示扫描量热、X射线衍射测试数据表明,在复合发泡材料体系中,EVA和NR的相容性良好,且填充胶粉后,共混体系的结晶能力下降。     

TiO_2/ZnO/Ni_(0.5)Zn_(0.5)Fe_2O_4磁载光催化剂的制备及其光催化性能

采用均匀沉淀法制备了镍锌铁氧体、纳米TiO2-ZnO复合粉体和镍锌铁氧体负载纳米TiO2-ZnO复合粉体,并用XRD对所制粉体进行了表征。发现所制得的纳米TiO2为锐钛矿型、镍锌铁氧体为尖晶石型。以甲基橙溶液为模拟废水,考察了纳米TiO2-ZnO复合粉体和镍锌铁氧体负载纳米TiO2-ZnO复合粉体的光催化活性。研究还发现镍锌铁氧体负载纳米TiO2-ZnO粉体后仍具有良好的磁性能,可通过增加外磁场进行分离。     

Fabrication of W@Cu composite powders by direct electroless plating using a dripping method

A direct electroless copper (Cu) coating on tungsten powders method requiring no surface treatment or stabilizing agent and using glyoxylic acid (C₂H₂O₃) as a reducing agent was reported. The effects of copper sulfate concentration and the pH of the plating solution on the properties of the prepared W@Cu composite powders were assessed. The content of Cu in the composite powders was controlled by adjusting the concentration of copper sulfate in the electroless plating solution. A uniform, dense, and consistent Cu coating was obtained under the established optimum conditions (flow rate of C₂H₂O₃ = 5.01 mL/min, solution pH = 12.25 and reaction temperature 45.35 °C) by using central composite design method. In addition, the crystalline Cu coating was evenly dispersed within the W@Cu composite powders and Cu element in the coating existed as Cu0. The formation mechanism for the W@Cu composite powders by electroless plating in the absence of surface treatment and stabilizing agent was also proposed.     

玻璃粉/尼龙1010复合材料摩擦学性能研究

将玻璃粉碎成微米级颗粒，作为增强材料，用硅烷偶联剂KH-550对玻璃粉进行表面处理，充填尼龙1010．制备了玻璃粉／尼龙1010复合材料，在环一块磨损试验机上研究了复合材料的摩擦学性能，使用邵氏硬度计测量了复合材料的硬度．借助SEM进行摩擦表面分析．试验结果表明：玻璃粉充填尼龙1010能降低复合材料的摩擦系数，础（玻璃粉）为25％时摩擦系数最小；w（玻璃粉）为20％时，磨损率仅为尼龙的18％．玻璃粉在一定含量的范围内能提高复合材料硬度．     

铜粉表面化学镀银及表征

铜-银复合粉末具有良好的抗氧化性、热稳定性及高电导性,在电子浆料、导电填料等众多领域具有广阔的应用前景.利用化学镀的方法,采用氯化亚锡为敏化剂,甲醛为还原剂,合成了用于电子浆料的铜-银复合粉末.用X射线衍射、扫描电镜表征了复合粒子的晶型和形貌结构,研究了敏化剂氯化亚锡、反应温度、还原剂及镀液的pH值对材料晶型和形貌的影响.结果表明：采用甲醛为还原剂,经过敏化处理后,当镀液pH值为10时,在50℃下,合成的银包铜粉电接触材料有较好的形貌.     

金红石TiO_2-CNTs粉体的制备及光催化性能

利用微波等离子体技术,对钛铁矿进行了还原并获得金红石型TiO2-CNTs复合粉体.通过XRD和SEM分析了不同制备条件对产物的影响,研究了不同条件下制备的复合粉体对甲基橙光降解效率.结果表明,该方法制备出的复合粉体在可见光和紫外光下都具有较强的光催化效果,纳米碳管的结构和含量对光催化效率有较强的影响.     

稀土元素镧和锶对镍基钎焊料焊接性能的影响

碳化钨(WC)复合涂层是一种高温下使用的有效耐磨蚀保护涂层.在BNi-2钎料粉末中添加稀土粉末,用机械合金化技术制备了改进的BNi-2钎料粉末,并在Q235钢基体上制备了碳化钨复合涂层;采用SEM观察了涂层显微组织,分析了稀土元素La和Ce对钎料焊接性能的影响规律.结果表明,在BNi-2合金中分别加入0.1 Wt.%稀土元素La,0.05 Wt.%稀土元素Ce,并采用机械合金化制备的粉状镍基焊料,与母材润湿性良好,焊接性能有所提高.采用此焊料及渗透钎焊技术可以制备出界面结合良好的WC复合涂层.     

Self-Propagating High-Temperature Reductive Synthesis of TiB_2-Al_2O_3 Composite Powders

TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis(SHS) method with reductive process from B2O3-TiO2-Al system. X-ray diffraction(XRD) and scanning electron microscopy(SEM) analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy (TEM) and high resolution electron microscopy (HREM) observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.