Effect of heat treatment temperature on dissimilar welded joint

The dissimilar metals 1Crl8Ni9 and 16MnR are welded by shielded metal arc welding process using electrode A312. The corrosion experiments are carried out on welded joint samples, which is as-welded and post-weld heat treatment at 650 ℃, 750 ℃ and 850 ℃, for 2 h in 70% sodium hydroxide solution. EDS and X-ray diffraction analysis are carried out on the samples after corrosion. Average corrosion rate calculation and microhardness measurement are conducted on both as- welded and post-weld heat treatment samples. The results indicate that average corrosion rate of as-welded joint metal is smaller than that of post-weld heat treatment joint metal. Compared with that of post-weld heat treatment at 750 ℃ and 850 ℃ for 2 h, the average corrosion rate of welded joint after post-weld heat treatment at 650 ℃ for 2 h increases greatly.     

不同退火条件下304L不锈钢埋弧焊接头组织及性能分析

采用埋弧焊方法,进行了304L不锈钢厚板的对接试验研究.通过对焊接接头处的组织观察,并结合焊接接头的-196 ℃冲击韧性以及不同退火条件下残余应力测试,分析了埋弧焊304L不锈钢焊接接头组织和性能. 结果表明,热影响区组织为奥氏体,焊缝区则为奥氏体与少量的铁素体的复相组织;采用残余应力盲孔释放测量方法对焊接接头进行测试,随着退火温度的升高,焊缝及热影响区的残余应力得到进一步的释放;冲击试验中,热影响区-196 ℃冲击吸收能量随退火温度的升高急剧下降,焊缝区-196 ℃冲击吸收能量则呈平稳下降趋势.     

Influence of post-weld heat treatment on microstructure and properties in heat-affected zone of KMN steel joint

The influence of temperature during post-weld heat treatment on the microstructure and properties of KMN steel joints was investigated. The results reveal that after heat treatment, the martensite transformed to tempered sorbite, causing the softening of the resultant joints. XRD test shows that the residual austenite content decreased obviously when the joint was heattreated at 550 ℃ and 580 ℃, which degraded the impact toughness of heat-affected zone （ HAZ）. When the heat treatment temperature increased further, the dispersion strengthening from the precipitation of alloying elements improved the impact toughness of HAZ. The aggregation and coarsening of carbide also contributed to the improvement of impact toughness of HAZ.     

热输入对T4003/Q450NQR1异种钢焊接接头组织及性能的影响

采用奥氏体焊材ER309LSi-G焊丝对T4003铁素体不锈钢与Q450NQR1耐候钢异种钢进行两种不同焊接热输入的MAG焊接,通过显微组织和力学性能等试验,对两种焊接接头性能进行研究。结果表明:两种焊接接头均未发现缺陷,焊接接头性能较好。与0.82 kJ/mm热输入比较,0.62 kJ/mm热输入下的焊接接头冲击韧性及硬度较好,熔合线较窄,晶粒度较为细小,拉伸数值较高,更加适用于T4003铁素体不锈钢与Q450NQR1耐候钢异种钢焊接。     

FSS/ASS厚壁异种钢“TIG冷焊 + UNGW”组合焊的接头组织与力学性能

为了有效解决铁素体不锈钢的焊接热影响区晶粒易粗化问题，以及奥氏体不锈钢焊接时在接头部分熔合区及其附近热影响区内因易形成蠕虫状δ铁素体而显著降低该区域耐腐蚀性的问题，提出了“TIG冷焊 + UNGW”的组合焊接工艺，并进行了1Cr17/1Cr18Ni9Ti厚壁异种不锈钢的焊接，同时对所得接头的显微组织、力学性能及耐腐蚀性进行了测试与分析. 结果表明，组合焊接头的1Cr17母材热影响区晶粒未发生粗化，并且1Cr18Ni9Ti母材部分熔合区及其附近热影响区内未形成蠕虫状δ铁素体；组合焊接头的抗拉强度优于1Cr17母材，并且1Cr17母材热影响区的冲击吸收能量与1Cr17母材相当；组合焊接头的熔敷层、1Cr18Ni9Ti母材、1Cr17母材、UNGW焊缝区及完整接头的耐腐蚀性呈依次下降的趋势.     

Gas dynamic control of properties of welded joints from high strength alloyed steels

Gas dynamic control in welding with consumable electrode in conditions of two-jet gas shielding and its impact on the processes in the welding area and properties of the welded joints from high strength alloyed steel 30HGSA is considered in the paper. The results of a comparative experimental study of controlling the properties of welded joints by changing the gas dynamics of the active shielding gas are given. The impact force of a shielding gas jet on the drop of the electrode metal is 12 times higher in conditions of two-jet gas shielding than in those of single jet shielding. It is found that gas dynamics of the active shielding gas jet determines the formation of the welded joints, their chemical properties and the properties of the welded joints from high strength alloyed steels. The consumable electrode welding method with two-jet gas shielding provides controlled dynamics in the welding area and allows controlling the transfer of the electrode metal, chemical composition of the weld, stabilizing the welding process, it ensures higher mechanical properties of the welded joints.     

Study of microstructures and of domestic X70 properties for girth welding pipeline steels

With the development of domestic pipeline steels, it is necessary to develop suitable welding technology which can improve the properties of the welded pipeline. In this paper, the microstructures and mechanical properties of domestic XTO pipeline steels and welded joints are discussed. The welding consumables of BOHLER E6010 and HOBART 81N1 are matched for girth welding. The following characteristics in heat-affected zone（ HAZ） are indicated that microstructures of intercritical HAZ（ ICHAZ） is finer and more uniform, the grain sizes of fine-grain HAZ （ FGHAZ） and subcritical HAZ （ SCHAZ） are smaller than that of coarse-grain HAZ（ CGHAZ）. The hardness, tensile strength and toughness of welded joints come up to the standard. The micrographs of impact specimens in welded joints are cleavage, quasi-cleavage and dimple which shows there is typical ductile rupture.     

Research on the properties of MAG welded joint of X65 pipeline steel

With the worldwide pipeline construction boom, the pipeline welding technology has rapidly developed. Considering the needs of some projects, many tests of mechanical properties of X65 pipeline steel metal active-gus （MAG） welded joint have been carried out, and so do the analysis of metallographic structure characteristics and the impact fracture appearance of joint. The results show that, using MAG welding, the test data of mechanical properties of their girth welded joint are in conformity with the relevant technical standards （ API1104 ）. MAG welding with COz protection has the characteristics of low hydrogen, energy-saving and environmental protection. Therefore, it should be noted to develop the welding materials and equipments vigorously for this welding method.     

焊后热处理对1Cr18Ni9Ti与2Cr13钢焊接接头组织和性能的影响

通过钨极氩弧焊方法,对1Cr18Ni9Ti与2Cr13钢实施焊接,并对焊接接头整体进行焊后热处理。采用OM、SEM对2Cr13与1Cr18Ni9Ti钢热处理前后的焊接接头组织进行分析,利用显微硬度计、电子万能拉伸机测量了焊接接头的力学性能。结果表明,1Cr18Ni9Ti和2Cr13钢焊接接头热处理前焊缝组织为典型的柱状晶,组织为板条马氏体+残留奥氏体+碳化物;热处理后焊缝组织为回火索氏体,而且碳化物析出量也明显增多。拉伸时,热处理前后焊接接头断裂的部位都发生在奥氏体不锈钢热影响区一侧,热处理前后焊接接头的抗拉强度分别约为635.56、649.44 MPa;焊缝区的显微硬度分别约为276、222 HV0.5,热处理后焊接接头的整体显微硬度比热处理前的明显降低。     

Microstructure and properties of Nd:YAG laser welded AZ31B magnesium alloy

Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of 1 mm in thickness were successfully joined by Nd ： YAG laser welding. The microstructure and properties of the welded joint were investigated. The result shows that the welded joint is characterized by a narrow heat-affected zone, finer grains and a large number of precipitates distribute in the matrix in the weld. Microhardness of the weld is significantly improved to 72 HV 0. 05 as compared to 55 HV 0. 05 of the base metal. Tensile strength of butt-welded joint is 180. 24 MPa, which is 76. 8% that of the base metal. The electrochemical corrosion experiment shows that the corrosion resistance of laser welded joint is significantly improved in a 3.5 wt. % NaCl solution.     

不同热处理制度下1Cr11Ni2W2MoV闪光对焊接头的组织与性能

针对1Cr11Ni2W2MoV不锈钢开展闪光对焊试验,研究不同焊后热处理制度对其焊接接头组织和力学性能的影响。结果表明:采用闪光对焊方法焊接1Cr11Ni2W2MoV,能够获得优质的焊接接头。1Cr11Ni2W2MoV闪光焊焊态下焊缝组织为马氏体和少量的δ铁素体组织,焊接接头具有较好的拉伸性能,但塑性和韧性较差。经过淬火+回火热处理后组织表现为回火索氏体组织,焊接接头的抗拉强度、塑性和韧性等性能均得到改善。在1000℃油淬+570℃回火状态下,焊接接头具有良好的综合力学性能。     

超纯铁素体Cr30Mo2钢焊接接头的组织和力学性能

利用自制的焊接工作台,在ＴＩＧ焊基础上,对Ｃｅ３０Ｍｏ２超纯铁素体不锈施焊。焊接中对焊缝和热影响区附加拖罩和背;衬的Ａｒ气延续保护。对焊接接头质量进行宏观坶检验;借助金相显微镜、扫描电镜（ＳＥＭ）、透射电镜（ＴＥＭ）分析焊缝组织特征一冲击断口形貌;按国家标准测试焊接接头的力学性能。华发头上未发现任何焊接缺陷,焊接缝质量良好;其强度、延性和韧性均达到母材水平,特别是在焊缝和热影响区未出现脆化现象,冲     

Microstructure and mechanical properties of laser welded joints of pure copper and 304 stainless steels

A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the copper side of the butt joints. In process of laser welding, effects of processing primary parameters on tensile strength of the joints were investigated. The interfacial characterizations of the joints were investigated by metallographic microscope, scanning electron microscope （SEM） and energy dispersive X-ray spectroscope （EDS）. The results showed that the element diffusion and solution occur and metallurgical bonding was achieved between pure copper and 304 stainless steel. The maximum tensile strength of the joints was 209 MPa when the laser power of welding was 2. 4 kW and welding speed was 12 mm/s.     

Pulsed TIG welding-brazing butt joints of aluminum-stainless steel thin plates with different fillers

Aluminum and stainless steel plates with 1.5 mm thickness are joined by pulsed TIG welding-brazing process with ER1100, ER4043 and ER2319 fillers, separately. Good weld formation can be obtained by adjusting appropriate pulse parameters. The effects of the fillers on that the thickness of the intermetallic compound （ IMC ） and tensile strength of the joints are investigated. SEM results indicate layer with ER2319 filler is about 2 ~m, which is thinner than 2. 5 p~m of ER1100 filler and 3.5 txm of ER4043 filler. Moreover, the element distribution in both IMCs and welded seams with three fillers are different because of the different compositions of fillers. The results of mechanical property tests suggest that the joint strength with ER2319 filler is the highest, while the joint impact energy is the lowest. The joint with ERllOO filler exhibits the best comprehensive mechanical pet.formanee.     

TIG welding-brazing joint of aluminum to stainless steel with hot wire

TIG welding-brazing process with high frequency induction hot wire technology was presented to create joints between 5A06 aluminum alloy and SUS32! stainless steel using ER1100 filler wire with different temperature. The joints were evaluated by mechanical test and microstructural analyses. The welding procedure using hot fiUer wire （400 ℃ ） significantly increases strength stability by 71% and average value of tensile strength by 30. 8 % of the joints, compared with cold wire. The research of microstructures in interfaces and welded seams reveals that using 400 ℃ hot filler wire can decrease the thickness of intermetallic compounds （ IMCs ） from 6 to 3.5 txm approximately, which is the main reason of mechanical property improvement.     

城市输水用Q235B+304不锈钢复合管环焊焊接工艺

不锈钢复合管内侧为具有耐腐蚀性能的不锈钢,外侧为具有一定强度的碳钢,成为新一代环保型输水管。为了研究8 mm+2 mm厚城市输水用Q235B+304不锈钢复合钢管的环焊焊接工艺,试验选用合理的焊接材料及坡口形式等,获得了复合板与复合板、复合板与碳钢板的焊接接头。通过拉伸、冲击、弯曲试验评价两种焊接接头的力学性能;通过检测接头不锈钢焊道化学成分,评估复合管焊接接头内侧不锈钢焊道的耐晶间腐蚀性能。结果表明,所采用的焊接工艺获得的接头力学性能满足技术要求且富余量较大,复合管接头不锈钢焊缝获得了A+(5%~10%)δ组织,耐晶间腐蚀性能优异。     

Study on process of roll bonding stainless and carbon steel under non-vacuum condition

The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the base materials, the microstructure of nickel cladding is observed by scanning electron microscopy （SEM） at high, and room temperature, and the results show that the nickel cladding on base material can be protected from oxidation in the high temperature. Non-vacuum roll bonding tests of nickel plating on base materials are done by the roll bonding equipment, and the roll bonding plates of stainless/carbon steel are obtained. The microstructure and the elements distribution of non-vacuum roll bonding interface are analyzed by optical microscope （OM） and SEM. The results reflect that the nickel plating layer and the base materials bond well.     

304不锈钢三元保护气体MAG焊工艺及其接头组织和力学性能

采用MAG焊在对接接头形式下,分别选用二元保护气体(Ar+O2)和不同比例的三元保护气体(Ar+CO2+O2),在4mm厚的304不锈钢板上进行焊接工艺试验。焊后观察并测量焊接接头,比较不同保护气体下的焊缝外观成形质量,测量焊缝合金元素及氧的含量,并测试了焊接接头的硬度、拉伸、弯曲以及低温冲击性能。     

中低温热处理对SUS304不锈钢TIG焊接接头组织及力学性能的影响

轨道交通车辆在冲击振动试验后,部分设备SUS304不锈钢焊接件出现断裂失效现象.为了提升SUS304不锈钢焊后机械性能,采用金相显微镜、扫描电镜、硬度测试及拉伸试验等方法,研究了中低温热处理工艺对2 mm厚SUS304不锈钢板TIG焊接接头的组织及力学性能的影响.研究发现,经400℃热处理30 min及焊接后未处理态焊...     

热处理工艺对0Cr13Ni5Mo钢焊接接头组织和性能的影响

对马氏体不锈钢0Cr13Ni5Mo焊接接头经过1000℃油淬后,分别进行了600℃,620℃+600℃,400℃回火。通过显微组织分析、拉伸试验、冲击试验和硬度检测对3种焊接接头的组织和力学性能进行了研究。结果表明,3种焊接接头中焊缝组织粗大,硬度最高;焊接接头的韧性低于相应热处理状态下母材的韧性;随着回火温度的降低,韧性下降,强度提高。二次回火比一次回火组织更加细小,强度和韧性更好;620℃+600℃二次回火后焊接接头具有比较理想的综合力学性能。