赤泥是氧化铝冶炼工业生产过程中排放的固体废弃物,是一种严重的碱性污染源。实验采用不同温度（20、55、75、95 ℃）的水分别对强碱性赤泥进行洗涤。结果表明,首次洗涤所得洗涤液的质量浓度较高,6次洗涤液的平均质量浓度在2.44~2.72 g/L,其中冷水洗涤赤泥所得的溶液质量浓度最高。每次洗涤得到的洗涤液的pH变化不大。不同温度的水洗涤赤泥,回收碱的效率相差不大,前3次洗涤碱的回收量占总量的70%以上。其中,冷水洗涤赤泥回收碱的质量最多。经过6次洗涤后,每克赤泥中最终回收的氢氧化钠的质量最高达8.18 mg。     

赤泥的脱碱与贮存

０引言中国长城铝业公司氧化铝厂（下简称长铝公司）采用混联法生产氧化铝,每年外排赤泥约６０～８０万ｔ,由于目前尚没有找到有效的利用方法,不但占用大量的农田,而且严重污染环境。长铝公司外排赤泥中含有高达４３５%的Ｃ２Ｓ矿物,是生产普通水泥的很好原料。为了变废为宝,长铝公司水泥厂曾在１９６６年建了一套转鼓式真空过滤赤泥系统,由于赤泥粒度粗,赤泥浆在输送管道中经常出现沉淀现象,赤泥碱含量偏高,所以利用率也很低。为了找到一条有效的利用赤泥作原料生产水泥的途径,于１９９７年应用赤泥常压石灰脱碱技术,对赤泥进行了脱碱和贮…     

赤泥草酸脱碱实验研究

赤泥强碱性是影响环境和制约其综合利用的关键因素.本文提出了赤泥草酸脱碱的实验研究,考察了草酸用量,反应温度,液固比和反应时间对赤泥脱碱率的影响,同时对赤泥和脱碱渣进行了XRD物相分析.结果表明:在草酸用量为15％,反应温度为80℃,液固比为4 mL/g和反应时间为40 min条件下,赤泥脱碱率超过95％.草酸显著破坏了赤泥中钙霞石的结构,可以选择性地脱除赤泥中的钠,脱碱渣中氧化钠含量低于0.5％,而钛、钙和硅等元素含量略有提高.     

常压石灰法处理烧结法赤泥脱碱及其机理研究

采用石灰（CaO）作为脱碱剂处理烧结法赤泥,研究了反应温度、反应时间、脱碱剂添加量、液固比等因素对赤泥中钾、钠溶出率等碱脱除效果的影响,分析了石灰处理赤泥的脱碱机理。结果表明：温度升高、反应时间延长、石灰掺量增加以及液固比增大均能提高赤泥的脱碱效果,其中尤以反应时间和石灰掺量的影响效果更显著。添加石灰处理烧结法赤泥的脱碱机理是部分方钠石（Na₈Al₆Si₆O₂₄CO₃）中的2个Na⁺被1个Ca²⁺置换出,生成了更难溶的钙霞石［Na₆CaAl₆Si₆（CO₃）O₂₄·2H₂O］。     

赤泥脱碱方法及其机理研究进展

赤泥是氧化铝生产过程中产生的强碱性废弃物,其强碱性是制约自身大规模综合利用的重要因素。因此十分有必要对赤泥进行脱碱,以期实现赤泥的综合利用,保障铝工业可持续发展。论文综述了国内外赤泥脱碱方法,如水洗法、酸浸法、石灰法、盐类浸出法、CO₂法、生物法等;同时从自由碱和化学结合碱的角度分析了各种脱碱方法的特点及主要脱碱机理,总结出赤泥脱碱的原理主要是中和反应、沉淀反应及钠置换反应。最后剖析了各种脱碱方法存在的问题,并对赤泥脱碱的研究提出了建议,这将为赤泥脱碱技术的进步以及赤泥的综合利用提供参考。     

从拜耳法赤泥中提取钪

以拜耳法赤泥为原料,通过硫酸恒温浸出,真空过滤,回收赤泥中钪元素。并且考察温度、浸出剂浓度、浸出时间对其的影响。结果表明,温度升高可提高浸出率;硫酸浓度为4 mol/L时浸出率最高;浸出时间增加,浸出率增加,并在2 h后增加幅度减小。在T=363.15 K,硫酸浓度为4 mol/L,浸出2 h的条件下,钪的回收率最高,为85.8%。     

拜耳法赤泥脱碱研究现状

叙述了拜耳法赤泥脱碱的意义以及我国拜耳法赤泥的物理化学性质以及物相特点,结合国内外拜耳法赤泥脱碱研究现状,总结了目前拜耳法赤泥脱碱工艺存在的问题,并提出了拜耳法赤泥高效脱碱的建议和意见.     

赤泥水浸脱碱实验及动力学研究

赤泥是一种碱性污染物,强碱性是制约其综合利用的关键因素。进行了拜耳法赤泥水浸脱碱实验及动力学研究,实验结果表明：赤泥在水浸次数为4次、液固体积质量比为9 mL/g、反应温度为90 ℃和反应时间为60 min的条件下,赤泥的脱碱率可达71%。采用未反应收缩核模型对水浸脱碱数据进行线性拟合,动力学分析表明：活化焙烧后赤泥的水浸脱碱过程受扩散步骤控制,线性相关系数大于0.97,表观活化能为11.72 kJ/mol。     

烧结法赤泥脱碱过程

采用适当的工艺流程对烧结法赤泥进行脱碱处理．研究了脱碱剂用量、赤泥粒度、液－固比、温度、时间对脱碱结果的影响．结果表明：使用该脱碱工艺,可使脱碱后赤泥中碱含量１％．     

拜耳法赤泥的湿法碳化脱碱工艺研究

利用二氧化碳对具有强碱性的拜耳法赤泥进行湿法碳化脱碱实验,研究了在CO2气流量为0.3 L/min条件下,液固比、反应温度、反应时间、CO2压力对拜耳法赤泥脱碱效果的影响并确定了适宜的脱碱条件.研究表明,在反应温度50℃,液固比为7,CO2压力为4 MPa,反应时间2h条件下,拜耳法赤泥的脱碱率达到50％以上.脱碱后赤泥碱含量大幅降低,有助于减轻对土壤及地下水源的危害.     

硼泥活化焙烧-浸取综合回收硅、镁有价组分

以硼化工行业固体废物--硼泥为原料,在TG-DSC热分析基础上,采用马弗炉和微波炉对其进行活化焙烧,再将焙烧产物进行碱浸和酸浸综合回收硅、镁有价组分。研究了两种焙烧方式对硼泥中SiO₂和MgO浸出率的影响。采用化学分析、X射线衍射和扫描电镜对焙烧产物以及白炭黑和氧化镁制品的化学成分、物相组成和微观形貌进行表征分析。结果表明：两种焙烧方式均可提高硼泥活性,促进硼泥中硅、镁组分的浸取。其中,马弗炉最佳焙烧条件为600℃、30 min,此时硼泥中SiO₂和MgO浸出率分别为97.65%和98.81%;微波炉最佳焙烧条件为500℃、10 min,此时SiO₂和MgO浸出率分别为98.03%和98.83%。白炭黑制品中SiO₂含量为92.20%,颗粒多呈近球状,粒径100～200 nm。氧化镁制品中MgO含量为93.05%,晶粒呈圆片状,粒径约2 mm。     

Dissolution kinetics of cerium from red mud

Leaching kinetics of rare earth element (REE) cerium (Ce) from red mud was investigated using different shrinking core models. The effect of various pertinent parameters such as acid concentration, liquid–solid ratio (LS), average particle size (PS), temperature and leaching time on the leaching efficiency was studied. The maximum recovery of 70.32% was obtained for 2 M HCl solution and an LS of 20:1 v/v. It was observed that the leaching process was limited by diffusion within the porous ash layer of the solid, thus making it ash diffusion controlled. The apparent activation energy was 11.38 kJ/mol, and the Arrhenius constant was 3.36 min?1.     

Waste-bearing foamed ceramic from granite scrap and red mud

Using granite scrap and red mud as raw materials, SiC as foaming agent, powder sintering method was used to prepare closed-pore foamed ceramic. The effects of the ratio of red mud and granite scrap, foaming agent content, sintering temperature and holding time on the crystalline phase, pore structure, and performance of foamed ceramic were systematically studied. The results showed that, when the content of red mud was 10 wt%, together with 1.0 wt% SiC addition, the heating rate was 5°C/min, the foamed ceramic sintered at 1130°C for 30 min exhibited optimal properties, including bulk density of 483.11 kg/m³, porosity of 77.27%, compressive strength of 1.62 MPa and water absorption of .49%. Based on these properties, it possessed broad potential application prospects in the fields of sound and thermal insulation, lightweight construction materials. In this study, the utilization ratio of industrial solid waste was 100%, realized the comprehensive utilization of granite scrap and red mud, and provided a new idea to realize their low-cost utilization by preparing foamed ceramic with associated economic and environmental benefits.     

逆流浸取法回收赤泥中的碱

赤泥脱碱现有的方法不足主要表现在：酸法或碱法脱碱会耗费大量的酸或碱,使脱碱成本偏高;简单水洗法脱碱时,副产品中碱浓度较低,不能实现赤泥与碱的综合利用。本文以阴离子型聚丙烯酰胺为絮凝剂,水为浸取剂,采用五级逆流浸取法对赤泥中碱的回收利用进行研究,考察了温度、液固比、浸取速度等因素对碱的浸出率及浓度的影响,得出碱的浸出率与浓度随温度、液固比、浸取速度等因素的变化规律,确定最佳浸取条件为：温度70℃,液固比3∶1,浸取速度15mL/min,在此条件下赤泥中碱的浸出率达89.18%,浓度达到20.38g/L。此方法不仅能将赤泥中的碱有效脱除,同时得到浓度较高的碱溶液,实现赤泥与碱的综合利用。     

Cyclohexanethiol separation from kerosene oil by red mud

The transfer of cyclohexanethiol from kerosene oil to unconventional adsorbent, red mud and the influence of variation in agitation rate, concentration and temperature on separation by adsorption technique has been investigated. The maximum transportation of sulfur compound from oil containing 730.67 mg dm^?3 (0.025% by weight sulfur) of cyclohexanethiol was noted at 45°C. The adsorption follows first order kinetics and is a diffusion controlled process. The applicability of Langmuir isotherm indicates monolayer coverage of sulfur on the outer interface of red mud. Calcination of red mud and thermodynamic parameters suggest the favorable separation of cyclohexanethiol from kerosene oil by adsorption.     

利用赤泥制备琉璃瓦的研究

利用广西平果铝厂产出的工业废弃物—赤泥制备琉璃瓦,研究琉璃瓦坯料的配料比及坯料的可塑度,以及釉料的组成,为赤泥的开发利用开辟了一条新途经。