酶解玉米秸秆残渣制备聚氨酯硬质泡沫

以制备纤维乙醇得到的酶解玉米秸秆残渣为原料,采用碱性乙醇法提取木质素,然后用聚乙二醇/甘油溶液将木质素进行液化得到木质素基多元醇,并以此液化产物代替部分聚醚多元醇用于聚氨酯泡沫的合成。结果表明:碱性乙醇法得到的木质素提取率为93.5%,木质素质量分数达到94.1%;在PEG-400/丙三醇液化体系中,木质素液化率高达99.5%,液化产物羟值为360 mg KOH/g;在聚氨酯合成中,木质素液化溶液对聚醚多元醇的替代量可以达质量分数47%,所得聚氨酯泡沫产品的芯密度和压缩强度分别为48.6 kg/m3和212 k Pa,满足工业聚氨酯硬泡的国家标准。     

超软质聚氨酯泡沫的制备

概述了超软质聚氯酯泡沫的几种主要制备方法。     

Bi-phase flame-retardant effect of hexa-phenoxy-cyclotriphosphazene on rigid polyurethane foams containing expandable graphite

The flame-retardant rigid polyurethane (PU) foams with hexa-phenoxy-cyclotriphosphazene/expandable graphite (HPCP/EG) were prepared through box-foaming in our laboratory. The flame retardancy of PU foams was characterized using the limiting oxygen index and cone calorimeter. The results show that the incorporation of HPCP into the PU foams containing EG enhanced flame retardancy. The main degradation process of HPCP in PU foams was investigated by pyrolysis gas chromatography/mass spectroscopy. HPCP during combustion generated phenoxyl and PO₂ free radicals, which could quench the flammable free radicals produced by the matrix and hamper the free radical chain reaction of combustion. This observation shows that HPCP produced a gas-phase flame-retardant effect in this specimen. Additionally, micro-morphology, elemental composition and content of residual char of the flame-retardant PU foams after the cone calorimeter test were also characterized using scanning electron microscope and energy dispersive X-ray microanalyser. The results exhibit that the partial phosphorus from HPCP remained in the residual char, and HPCP significantly enhanced the strength and compatibility of the char layer formed by the PU foams containing EG. These results indicate the important function of HPCP in condensed phase. Thus, HPCP exhibited gas-phase and condensed-phase flame-retardant effects on the PU/EG foams.     

Bio-based flame-retardant rigid polyurethane foam with high content of soybean oil polyols containing phosphorus

Rigid polyurethane foam (RPUF) is prepared from petroleum-based polyols and isocyanate, which consumes a large amount of petroleum. To alleviate the consumption of petroleum, it is necessary to synthesize green and sustainable polyols. However, the greatest disadvantage of RPUF is its flammability. To reduce the risk of fire caused by RPUF, phosphorylated soybean oil polyol (Polyol-P) and phenyl phospho-soybean oil polyol (Polyol-PPOA) were synthesized by ring-opening reactions of epoxy soybean oil with phosphoric acid and phenylphosphonic acid, respectively. A flame-retardant RPUF was prepared via polymeric 4,4-diphenylmethane diisocyanate (p-MDI), which reacted after mixing Polyol-P and Polyol-PPOA with polyether polyol-330N in different proportions. Scanning electron microscopy (SEM) showed that the cell sizes of the RPUF-P and RPUF-PPOA increased first and then decreased and the cell number decreased first and then increased with the increase in the contents of Polyol-P and Polyol-PPOA. Mechanical property tests showed that the compressive strength of the RPUF-P4 reached 0.1 MPa, and the compressive strength of the RPUF-PPOA4 reached 0.07 MPa. The limiting oxygen index values of the RPUF-P4 and RPUF-PPOA4 were 20.9% and 24.3%, respectively. The UL 94 of the RPUFs indicated that the rating of the RPUF-PPOA3 was improved to V-1. The results showed that the flame-retardancy mechanism of the Polyol-P and Polyol-PPOA in the RPUF was based on the charred surface as a physical barrier, which slowed down the decomposition of RPUF and prevented heat and mass transfer between the gas and the condensed phase.     

Nanoclay reinforced rigid polyurethane foams

Clay was intercalated and exfoliated by neutralized dimethylol butanoic acid (DMBA) and used to fabricate rigid polyurethane foam (RPUF)/clay nanocomposites. Cream time, gel time, and tack‐free time increased with the addition and increasing amount of clay whereas foam density and compression strength decreased. Cell size, closed cell content, volume change upon heating and cooling, and thermal conductivity of the foam decreased with the addition and increasing amount of clay with a minimum at 2 pphp (parts per 100 polyol by weight). The glass transition and decomposition temperatures increased with increasing clay content due to the restricted motion of chains and barrier property of the clay platelets. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

低氟发泡聚醚多元醇

低氟(里昂)发泡聚醚多元醇是当代聚醚多元醇的新品种,它的问世为聚氯酯泡沫塑科生产中减少和最终完全替代CFC类物质创造了条件。本文介绍了低氟发泡聚醚多元醇结构设计原则、合成工艺及应用实例,建议在冰箱行业首先推广应用。     

Water-blown rigid and flexible polyurethane foams containing epoxidized soybean oil triglycerides

Both rigid and flexible water-blown polyurethane foams were made by replacing 0–50% of Voranol® 490 for rigid foams and Voranol® 4701 for flexible foams in the B-side of foam formulation by epoxidized soybean oil. For rigid water-blown polyurethane foams, density, compressive strength, and thermal conductivity were measured. Although there were no significant changes in density, compressive strength decreased and thermal conductivity decreased first and then increased with increasing epoxidized soybean oil. For flexible water-blown polyurethane foams, density, 50% compression force deflection, 50% constant force deflection, and resilience of foams were measured. Density decreased first and then increased, no changes in 50% compression force deflection first and then increased, increasing 50% constant force deflection, and decreasing resilience with increase in epoxidized soybean oil. It appears that up to 20% of Voranol® 490 could be replaced by epoxidized soybean oil in rigid polyurethane foams. When replacing up to 20% of Voranol® 4701 by epoxidized soybean oil in flexible polyurethane foams, density and 50% compression deflection properties were similar or better than control, but resilience and 50% constant deflection compression properties were inferior. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Continuous alcohol production from whey permeate using immobilised cell reactor systems

The present paper reports the performance of a bioreactor packed with alginate-entrapped Kluyveromyces marxianus NCYC179 for continuous fermentation of whey permeate to ethanol. A maximum ethanol productivity as 28.21 gl^?1 h^?1 was attained at D=0.42h^?1 and 75% lactose consumption (substrate feed rate in the inflowing medium was 200 g lactose I^?1). However, the higher dilution rates (0.6-1.Oh^?1) resulted in poor productivities and higher substrate washout in the effluent samples. The maximum specific ethanol production (qpi) and maximum specific lactose uptake (qsi) of the immobilised Kluyveromyces marxianus NCYC179 was found to be 3.88g ethanol/g immobilised cell/hx10^?2 and 8.75g lactose consumed/g immobilised cell/hx10^?2 respectively. A bead size of 2.5 mm in diameter and activation period of 24h of alginate beads in lactose solution (10%) prior to their packing in column reactor were found to support the efficient working of the bioreactor. The immobilised cell bioreactor system was operated continuously at a constant dilution rate of 0.15h^?1 and 10% lactose for 562 h without any significant change in the efficiency (varied from 84 to 88% of theoretical) and viability of the entrapped yeast cells (dropped from 84 to 81%).     

Desaminated glycolysis of water‐blown rigid polyurethane foams

Glycolysis reaction kinetics of methylene diphenyl diisocyanate‐based water‐blown polyurethane foams was examined by gel permeation chromatography. Glycolysates were reacted with butyl glycidyl ether to convert toxic aromatic amines to polyols, and their products were identified by ¹H‐NMR spectroscopy. To examine the quality of recycled polyol, polyurethane foams were reprepared using the virgin and recycled polyol mixtures with varying compositions. Cell structures and sizes of reprepared foams were similar to those of original ones when the recycled polyols were mixed up to 30 wt %. Density, thermal conductivity, and flexural strength of the reprepared foams were compared with those of the original ones, and no difference was observed below the recycled polyol concentration of 30 wt %. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 77: 2646–2656, 2000     

不同含量配比制备聚氨酯泡沫及其性能研究

采用一步法以异佛尔酮二异氰酸酯和聚醚多元醇为原料,选用A～D4种配比制备了聚氨酯泡沫材料,通过红外光谱仪、扫描电子显微镜、差示扫描量热仪、热重分析仪和噪声振动测试系统等对聚氨酯泡沫的泡孔结构、热稳定性及吸音隔音性能进行了测试.结果表明,聚醚多元醇的用量对聚氨酯泡沫成分未造成差异,聚氨酯泡沫中出现闭孔、半闭孔、开孔并存现...     

Synthesis of aminophosphonate polyols and polyurethane foams with improved fire retardant properties

Aminophosphonated polyols with flame retardant properties are synthesized by ring opening polymerization using diethyl-N,N-bis(2-hydroxyethyl) aminomethyl phosphonate (Fyrol-6) as initiator. The influence of the catalyst type and its concentration on the polymerization rate are studied. The catalyst system formed by potassium methoxide (MeOK) in DMSO as a solvent presents the highest polymerization rate and allows reducing the polydispersity. The thermal resistance of the synthesized polyols is confirmed by the char residues formation. Finally, PU foams are synthesized containing up to a 50 pph of PFyCs[1:1], preserving good cellular structure up to a 25 pph content and improving the fire resistance by increasing the char residue from 7.79 to 22.13 wt % and decreasing the PHRR and the smoke production according to TGA and cone calorimeter tests, respectively. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47780.     

Preparation and application of glycolysed polyurethane integral skin foams recyclate from automotive wastes

Summary Glycolysis of isocyanate derived foams with glycol and amine mixture is a simple and economically attractive chemical recycling process. A mixture of diethylene glycol (DEG) and diethanol amine (DEA) is used as solvent system and sodium hydroxide as the catalyst. The obtained polyols can be completely reused in the formulation of integral skin foams in blend with virgin polyol.     

Sustainable rigid polyurethane foams based on recycled polyols from chemical recycling of waste polyurethane foams

The preparation and characteristics of rigid polyurethane foams (RPUFs) based on recycled polyol obtained by glycolysis of waste RPUF scraps from end-of-life refrigerators were investigated. To deactivate the amine adducts derived from isocyanates, the recycled product obtained after depolymerization was chemically modified via addition polymerization of propylene oxide. Two kinds of recycled polyols with different hydroxyl values and viscosity were blended with conventional virgin polyether polyol to prepare the RPUFs. The effects of the recycled polyols on the physical properties of RPUFs such as cell structures, compressive strength, thermal conductivity, and limiting oxygen index were discussed. It was found that the RPUFs from recycled polyols showed superior compressive strength, thermal insulation property, and self-extinguishing property compared with conventional control foam. The results of this study reveal that the recycled polyols could be used as feedstock for RPUFs with superior performance. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47916.     

Rigid polyurethane foams from a soybean oil-based Polyol

Polyurethane (PU) rigid foams were synthesized by substituting a polypropylene-based polyol with soybean oil-based polyol (SBOP). All the soy-based foams maintained a regular cell structure and had even smaller average cell size than the control foams. The density of soy-based foams was within 5% of the controls, except that the density of foams from 100% SBOP was 17% higher. Soy-based foams also had comparable initial thermal conductivity (k value) and closed cell content, higher T_g and compressive strength. However, while foams from 50% SBOP showed similar increase in k value to the 0% SBOP foams, under accelerated aging conditions, the 100% SBOP foams aged faster. Gas permeation tests performed on PU thin films showed higher N₂ permeation for PU thin films made from SBOP which is believed to be the cause of accelerated thermal aging.     

Physical properties of water‐blown rigid polyurethane foams from vegetable oil‐based polyols

Fifty vegetable oil‐based polyols were characterized in terms of their hydroxyl number and their potential of replacing up to 50% of the petroleum‐based polyol in waterborne rigid polyurethane foam applications was evaluated. Polyurethane foams were prepared by reacting isocyanates with polyols containing 50% of vegetable oil‐based polyols and 50% of petroleum‐based polyol and their thermal conductivity, density, and compressive strength were determined. The vegetable oil‐based polyols included epoxidized soybean oil reacted with acetol, commercial soybean oil polyols (soyoils), polyols derived from epoxidized soybean oil and diglycerides, etc. Most of the foams made with polyols containing 50% of vegetable oil‐based polyols were inferior to foams made from 100% petroleum‐based polyol. However, foams made with polyols containing 50% hydroxy soybean oil, epoxidized soybean oil reacted with acetol, and oxidized epoxidized diglyceride of soybean oil not only had superior thermal conductivity, but also better density and compressive strength properties than had foams made from 100% petroleum polyol. Although the epoxidized soybean oil did not have any hydroxyl functional group to react with isocyanate, when used in 50 : 50 blend with the petroleum‐based polyol the resulting polyurethane foams had density versus compressive properties similar to polyurethane foams made from 100% petroleum‐based polyol. The density and compressive strength of foams were affected by the hydroxyl number of polyols, but the thermal conductivity of foams was not. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

阻燃聚氨酯软泡的研究进展

介绍了聚氨酯软质泡沫塑料阻燃的必要性及国内外对阻燃泡沫的研究情况,大多数国家对聚氨酯泡沫塑料都提出了阻燃要求并制定出相应的阻燃标准。研究了软质泡沫塑料中常用的阻燃剂,阐述了阻燃剂的阻燃机理,并展望阻燃聚氨酯泡沫塑料的发展前景。     

Effect of ingredient ratios of rigid polyurethane foam on foam core panels properties

One‐step manufacturing process (in‐situ foaming) provide great potential for the production of foam core panels. Polyurethane (PU) foam showed good applicability for use for in‐situ foaming. Here, the effect of ingredient ratios of rigid PU foam on foam performance and panel properties is investigated. It was observed that the isocyanate (ISO) content and polyols (PO) type and content significantly change the foam and panel properties. Foam cell density, as the most important factor influencing the foam characteristics, was higher in foams with higher ISO and polyether content. Bending strength, internal bond and screw withdrawal resistance of the foam core panels were significantly enhanced when the ISO and polyether content was increased in the foam formulation. Varying the ISO content had no influence on panel properties with higher content of polyester (60%) in the PO blend. Varying the foam ingredient ratios did not change the thickness swelling, while the water absorption was dependent on the foam components ratios. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44722.     

软质聚氨酯泡沫塑料无卤阻燃技术研究进展

软质聚氨酯泡沫(FPUF)是聚氨酯材料的主要产品之一,由于其较低的密度和热传导率而易燃,在燃烧过程中会放出大量烟雾和有毒气体,对FPUF进行阻燃处理尤为重要。卤系阻燃剂由于存在潜在的毒性和环境问题而受到限制,因此FPUF的无卤阻燃技术是今后主要的研究方向。本文综述了近年有关软质聚氨酯泡沫无卤阻燃技术的研究进展,包括添加型无卤阻燃剂法、反应型无卤阻燃剂法、层层组装涂层法。指出开发高相对分子质量、含多种阻燃元素的有机添加型阻燃剂和膨胀型阻燃剂以及复配型阻燃剂,解决层层组装涂层法的组装慢等问题将是FPUF无卤阻燃技术的发展趋势。     

基于环三磷腈磷氮阻燃剂的合成及其在聚氨酯泡沫的应用

以六氯环三磷腈、对羟基苯甲醛、苯胺及亚磷酸二乙酯等原料,成功合成阻燃剂六（4-苯胺基次甲基苯氧基-亚磷酸二乙酯基）环三磷腈（HADPPCP）,用于阻燃基于苹果酸多元醇的聚氨酯硬泡。HADPPCP具有良好的热稳定性和成炭性,氮气气氛下的初始分解温度为191.9℃,700℃时的残炭量高到46.8%（质量）。HADPPCP的加入可以改善聚氨酯硬泡的热稳定性、阻燃性能和燃烧行为。添加25%(质量)的HADPPCP可以将聚氨酯泡沫的氧指数从18%提高到25%,最大热释放速率和总热释放量分别从230 kW/m²和20.1 MJ/m²降低至213 kW/m²和16.6 MJ/m²,总产烟量从10.5 m²下降到5.3 m²。     

Enhanced flame-retardant performance of rigid polyurethane foam by using APTES-MMT and ATH mixed intumescent coatings

The design of environment-friendly fireproof rigid polyurethane foams (RPUFs) that completely prevent ignition or the spread of fires is important for energy conservation and emission reductions. In this paper, an intumescent flame-retardant coating was prepared and coated onto the surface of a RPUF to improve its flame retardancy. Vertical combustion experiments (UL-94) showed that, compared with the pure RPUF, a RPUF coated with the expansion coating successfully self-extinguished without a droplet formed after ignitor removal. Thermogravimetric analyses showed that the expanded coating effectively increased the rate of carbon residue formation. Cone calorimetry showed that when the pigment-to-binder ratio was 3.5:1, with 5% modified montmorillonite, 6% aluminum hydroxide, and 4% titanium dioxide, the intumescent coating effectively reduced the heat release rate and total heat release of the RPUF. Remarkably, the smoke release rate and total exhaust gas volume showed that the expanded coating provided obviously enhanced smoke suppression. Therefore, the flame retardancy and toxic smoke suppression provided by the RPUF thermal insulation material is essential and very useful for healthy development of human society and the environment.