Highly conducting indium tin oxide (ITO) thin films deposited by pulsed laser ablation

Highly conducting and transparent indium tin oxide (ITO) thin films were prepared on SiO₂ glass and silicon substrates by pulsed laser ablation (PLA) from a 90 wt.% In₂O₃-10 wt.% SnO₂ sintered ceramic target. The growths of ITO films under different oxygen pressures (P_O2) ranging from 1×10⁻⁴–5×10⁻² Torr at low substrate temperatures (T_s) between room temperature (RT) and 200°C were investigated. The opto-electrical properties of the films were found to be strongly dependent on the P_O2 during the film deposition. Under a P_O2 of 1×10⁻² Torr, ITO films with low resistivity of 5.35×10⁻⁴ and 1.75×10⁻⁴ Ω cm were obtained at RT (25°C) and 200°C, respectively. The films exhibited high carrier density and reasonably high Hall mobility at the optimal P_O2 region of 1×10⁻² to 1.5×10⁻² Torr. Optical transmittance in excess of 87% in the visible region of the solar spectrum was displayed by the films deposited at Po₂≥1×10⁻² Torr and it was significantly reduced as the P_O2 decreases.     

Excited-state absorption at 1.57 μm in U:CaF2 and Co:ZnSe saturable absorbers

Appreciable excited-state absorption (ESA) in U²⁺:CaF₂ and Co²⁺:ZnSe saturable absorbers was measured at λ=1.573 μm by optical transmission versus light fluence curves of 30–40 ns long pulses. The ground- and excited-state absorption cross-sections obtained were (9.15±0.3)×10⁻²⁰ and (3.6±0.2)×10⁻²⁰ cm², respectively, for U²⁺:CaF₂, and (57±4)×10⁻²⁰ and (12.5±1)×10⁻²⁰ cm² for Co²⁺:ZnSe. Thus, ESA is not negligible in U²⁺:CaF₂ and Co²⁺:ZnSe, as previously estimated.     

Up-conversion dynamics in GdAlO3:Er single crystal fibre

Green fluorescence has been obtained under continuous laser excitation in the 780–860 nm range in GdAlO₃:Er³⁺. With the help of the Judd-Ofelt treatment we built a model based on population rate equations to describe its time evolution. We found the intensity parameters to be Ω₂ = 2.045 × 10⁻²⁰ cm², Ω₄ = 1.356 × 10⁻²⁰ cm² Ω₆ = 1. 125 × 10⁻²⁰ cm². Even if a two-photon absorption and a looping mechanism are necessary to well describe the dynamics, the main process responsible for up-conversion is energy transfer between erbium ions.     

Light emitting devices from organic charge transfer adduct thin films

For the first time, thin film devices of charge transfer adducts of tetrathiafulvalene (TTF) have been fabricated. A luminance of 5 cd m⁻² has been achieved for a device structure ITO/poly(aniline)/TTF(NO₃)_0.55/Al whose EL spectrum has a broad peak at 645 nm. The devices were fabricated by spin coating from solutions of the adducts. A luminous efficiency of 5×10⁻⁴ lm W⁻¹ has been obtained for these devices which is comparable to that of ITO/poly(aniline)/Alq₃/Al (5.2×10⁻⁴ lm W⁻¹) under same fabrication conditions. The single layer, mixed layer and double layer devices fabricated in this study fit the space charge limited model. Devices fabricated from the adduct [TTF–Alq₃] emit white light (40 cd m⁻²) with a luminous efficiency of 6.6×10⁻⁴ lm W⁻¹. The colour of light emitted appears to depend on the effective oxidation state of TTF in the adducts.     

Preparation of Pt-PtOx thin films as electrode for memory capacitors

Pt-PtO_x thin films were prepared on Si(100) substrates at temperatures from 30 to 700°C by reactive r.f. magnetron sputtering with platinum target. Deposition atmosphere was varied with O₂/Ar flow ratio. The deposited films were characterized by X-ray diffraction, X-ray photoelectron spectroscopy and scanning electron microscopy. Resistively of the deposited films was measured by d.c. four probe method. The films mainly consisted of amorphous PtO and Pt₃O₄ (or Pt₂O₃) below 400°C, and amorphous Pt was increased in the film as a deposition temperature increased to 600°C. When deposition temperature was thoroughly increased, (111) oriented pure Pt films were formed at 700°C. Compounds included in the films strongly depended on substrate temperature rather than O₂/Ar flow ratio. Electrical resistivity of Pt-PtO_x films was measured to be from the order of 10⁻¹ Ω cm to 10⁻⁵ Ω cm, which was related to the amount of Pt phase included in the deposited films.     

Al2O3 formation on Si by catalytic chemical vapor deposition

Catalytic chemical vapor deposition (Cat-CVD) has been developed to deposit alumina (Al₂O₃) thin films on silicon (Si) crystals using N₂ bubbled tri-methyl aluminum [Al(CH₃)₃, TMA] and molecular oxygen (O₂) as source species and tungsten wires as a catalyzer. The catalyzer dissociated TMA at approximately 600 °C. The maximum deposition rate was 18 nm min⁻¹ at a catalyzer temperature of 1000 °C and substrate temperature of 800 °C. Metal oxide semiconductor (MOS) diodes were fabricated using gates composed of 32.5-nm-thick alumina film deposited at a substrate temperature of 400 °C. The capacitance measurements resulted in a relative dielectric constant of 7.4, fixed charge density of 1.74×10¹² cm⁻², small hysteresis voltage of 0.12 V, and very few interface trapping charges. The leakage current was 5.01×10⁻⁷ A cm⁻² at a gate bias of 1 V.     

The optical and electrical properties of copper indium di-selenide thin films

Thin films of copper indium di-selenide (CIS) with a wide range of compositions near stoichiometry have been formed on glass substrates in vacuum by the stacked elemental layer (SEL) deposition technique. The compositional and optical properties of the films have been measured by proton-induced X-ray emission (PIXE) and spectrophotometry (photon wavelength range of 300–2500 nm), respectively. Electrical conductivity (σ), charge-carrier concentration (n), and Hall mobility (μ_H) were measured at temperatures ranging from 143 to 400 K. It was found that more indium-rich films have higher energy gaps than less indium-rich ones while more Cu-rich films have lower energy gaps than less Cu-rich films. The sub-bandgap absorption of photons is minimum in the samples having Cu/In ≈ 1 and it again decreases, as Cu/In ratio becomes less than 0.60. Indium-rich films show n-type conductivities while near-stoichiometric and copper-rich films have p-type conductivities. At 300 K σ, n and μ_H of the films vary from 2.15 × 10⁻³ to 1.60 × 10⁻¹ (Ω cm)⁻¹, 2.28 × 10¹⁵ to 5.74 × 10¹⁷ cm⁻³ and 1.74 to 5.88 cm² (V s)⁻¹, respectively, and are dependent on the composition of the films. All the films were found to be non-degenerate. The ionization energies for acceptors and donors vary between 12 and 24, and 3 and 8 meV, respectively, and they are correlated well with the Cu/In ratios. The crystallites of the films were found to be partially depleted in charge carriers.     

Physics of very thin ITO conducting films with high transparency prepared by DC magnetron sputtering

The preparation of very thin indium tin oxide (ITO) films with extremely high transparency and suitable resistivity, as well as resistivity stability for long term use, is described. In order to obtain these properties, amorphous suboxide films were first prepared and then annealed. Suboxide films with a thickness of 20 to 30 nm were prepared on PET film and glass substrates at a temperature of 60 °C using In₂O₃---SnO₂ targets with a SnO₂ content of 0 to 10 wt% by DC magnetron sputtering in a pure argon gas atmosphere. The films were annealed at a temperature of 150 °C for 1 to 100 h in air. The resistivity of films on PET films was, depending on the SnO₂ content, on the order of 10⁻³ ω cm. An average transmittance above 97% in the visible wavelength range and a resistivity of about 4 × 10⁻³ ω cm, as well as resistivity stability, were attained in ITO films with a SnO₂ content of about 1 wt% prepared on PET films by the low-temperature process. It is thought that these properties result from crystallization which occurred during the annealing, duration up to about 25 h.     

Characterization of indium zinc oxide thin films prepared by pulsed laser deposition using a Zn3In2O6 target

Using a Zn₃In₂O₆ target, indium-zinc oxide films were prepared by pulsed laser deposition. The influence of the substrate deposition temperature and the oxygen pressure on the structure, optical and electrical properties were studied. Crystalline films are obtained for substrate temperatures above 200°C. At the optimum substrate deposition temperature of 500°C and the optimum oxygen pressure of 10⁻³ mbar, both conditions that indeed lead to the highest conductivity, Zn₃In₂O₆ films exhibit a transparency of 85% in the visible region and a conductivity of 1000 S/cm. Depositions carried out in oxygen and reducing gas, 93% Ar/7% H₂, result in large discrepancies between the target stoichiometry and the film composition. The Zn/In (at.%) ratio of 1.5 is only preserved for oxygen pressures of 10⁻²–10⁻³ mbar and a 93% Ar/7% H₂ pressure of 10⁻² mbar. The optical properties are basically not affected by the type of atmosphere used during the film deposition, unlike the conductivity which significantly increases from 80 to 1400 S/cm for a film deposited in 10⁻² mbar of O₂ and in 93% Ar/7% H₂, respectively.     

Reactions in Au/Nb bilayer thin films

The interdiffusion and intermetallic compound formation of Au/Nb bilayer thin films annealed at 200–400 °C have been investigated. The bilayer thin films were prepared by electron beam deposition. The Nb film was 50 nm thick and the Au film was 50–200 nm thick. The interdiffusion of annealed specimens was examined by measuring the electrical resistance and depth-composition profile and by transmission electron microscopy. Interdiffusion between the thin films was detected at temperatures above 325 °C in a vacuum of 10^-4 Pa. The intermetallic compound Au₂Nb₃ and other unknown phases form during annealing at over 400 °C. The apparent diffusion constants, determined from the penetration depth for annealing at 350 °C, are 3.5 × 10⁻¹⁵ m² s⁻¹ for Nb in Au and 8.6 × 110^7minus;15 m² s⁻¹ for Au in Nb. The Au surface of the bilayer films becomes uneven after annealing at over 400 °C due to the reaction.     

Sintering behavior and microwave dielectric properties of Bi3(Nb1−xTax)O7 solid solutions

Solid solutions of Bi₃(Nb_1−xTa_x)O₇ (x = 0.0, 0.3, 0.7, 1) were synthesized using solid state reaction method and their microwave dielectric properties were first reported. Pure phase of fluorite-type could be obtained after calcined at 700 °C (2 h)⁻¹ between 0 ≤ x ≤ 1 and Bi₃(Nb_1−xTa_x)O₇ ceramics could be well densified below 990 °C. As x increased from 0.0 to 1.0, saturated density of Bi₃(Nb_1−xTa_x)O₇ ceramics increased from 8.2 to 9.1 g cm⁻³, microwave permittivity decreased from 95 to 65 while Q_f values increasing from 230 to 560 GHz. Substitution of Ta for Nb modified temperature coefficient of resonant frequency τ_f from −113 ppm °C⁻¹ of Bi₃NbO₇ to −70 ppm °C⁻¹ of Bi₃TaO₇. Microwave permittivity, Q_f values and τ_f values were found to correlate strongly with the structure parameters of fluorite solid solutions and the correlation between them was discussed in detail. Considering the low densified temperature and good microwave dielectric proprieties, solid solutions of Bi₃(Nb_1−xTa_x)O₇ ceramics could be a good candidate for low temperature co-fired ceramics application.     

Atomic layer deposition growth of zirconium doped In2O3 films

Zirconium doped indium oxide thin films were deposited by the atomic layer deposition technique at 500 °C using InCl₃, ZrCl₄ and water as precursors. The films were characterised by X-ray diffraction, energy dispersive X-ray analysis and by optical and electrical measurements. The films had polycrystalline In₂O₃ structure. High transparency and resistivity of 3.7×10⁻⁴ Ω cm were obtained.     

Optically active Er–Yb codoped Y2O3 films produced by pulsed laser deposition

Optically active Er³⁺:Yb³⁺ codoped Y₂O₃ films have been produced on c-cut sapphire substrates by pulsed laser deposition from ceramic Er:Yb:Y₂O₃ targets having different rare-earth concentrations. Stoichiometic films with very high rare-earth concentrations (up to 5.5 × 10²¹ at cm^− 3) have been achieved by using a low oxygen pressure (1 Pa) during deposition whereas higher pressures lead to films having excess of oxygen. The crystalline structure of such stoichiometric films was found to worsen the thicker the films are. Their luminescence at 1.53 μm and up-conversion effects have been studied by pumping the Yb³⁺ at 0.974 μm. The highest lifetime value (up to 4.6 ms) is achieved in films having Er concentrations of ≈ 3.5 × 10²⁰ at cm^− 3 and total rare-earth concentration ≈ 1.8 × 10²¹ at cm^− 3. All the stoichiometric films irrespective of their rare-earth concentration or crystalline quality have shown no significant up-conversion.     

(Fe,Ti) 16N2 films with high saturation magnetization prepared by facing target sputtering

(Fe,Ti)-N films with a Ti concentration of 10 at.% were prepared on Si(100) and NaCl substrates by facing targets sputtering. The effects of the nitrogen pressure (P_N) and the substrate temperature (T_s) on the formation of various (Fe,Ti)-N phases and their microstructures were investigated in detail. X-ray diffractometer and transmission electron microscope provided complete identification of the phases present in the films and the characterization of their microstructures. Films deposited at a lower P_N = 1 3 × 10⁻² Pa or a lower T_s = RT consist of mainly -phase. Films deposited at a higher P_N = 1.3 2 × 10⁻¹ Pa or a higher T_s = 200 °C contain a great many γ' and Fe₂N phases with a higher nitrogen content. When P_N = 4 7 × 10⁻² Pa and T_s = 100 150 °C, it is advantageous to the formation of ′' phase. These films exhibit a high saturation magnetization (M_s) up to the range of 2.3 2.5 T, which is larger than that of pure iron.     

Zinc oxide thin films by the spray pyrolysis method

Undoped and In-doped ZnO thin films have been prepared on glass substrates from solutions of Zn(CH₃CO₂)₂2H₂O in a mixture of deionized water and isopropyl alcohol by spray pyrolysis. Their optical, morphological and structural qualities have been studied and the effect of the preparation conditions discussed. It was shown that the main factors determining the parameters of ZnO films are the growth temperature and the indium concentration. The growth temperatures of 625–675 K, indium doping levels of 1–1.5 at.% and precursor concentrations of 0.1–0.2 mol 1⁻¹ are preferable to achieve ZnO films with optical and structural qualities as required for solar cell applications.     

Characterization of fluorine-doped silicon dioxide film by Raman spectroscopy

We have measured Raman spectra of fluorine-doped SiO₂ (SiOF) films and quartz glass. From a comparison between Raman spectra of the SiO₂ film and quartz glass, it has been found that the SiO₂ film is under compressive stress and that it has more threefold ring defects than quartz glass. Raman bands from threefold and fourfold ring defects in SiOF films become week as the fluorine/oxygen (F/O) ratio increases and as the stress decreases. The decrease of intensities of these Raman bands shows that ring defects in SiOF films decrease as the F/O ratio increases and as the stress decreases. The triply degenerated ω₄ mode at 460 cm⁻¹ becomes sharp as the F/O ratio increases and as the stress decreases. Furthermore, the peak-frequency of ω₁ mode around 820 cm⁻¹ decreases with a decrease of stresses whereas that of ω₃ mode around 1065 cm⁻¹ increases. These results can be well understood in terms of a decrease of O-Si-O bonding angle caused by relaxation of stresses.     

Standing-wave solutions of the Enneper (sine-Gordon) equation

The present paper investigates the real solutions of the partial differential equations (∂²ω/∂u²) − (∂²ω/∂ν²) = sin ω (Enneper or sine-Gordon equation) that are of the FORM = F(|₁(u) · |₂(ν)). In the application of the Enneper equations to crystal physics such solutions may represent standing waves. A complete classification of these solutions and its degenerate cases is given.     

Underlying mechanisms for unique elastic properties of nanocrystalline Au

In order to get an insight into the grain boundaries (GBs) in nanocrystalline (n-) metal, we prepared the high-density n-Au with ρ/ρ₀>99% by the gas-deposition method and carried out the vibrating reed measurements, where ρ/ρ₀ is the relative density referring to the bulk density. The strain amplitude dependence (SAMD) of the resonant frequency (f) and the internal friction (Q⁻¹) was measured for the strain () amplitude between 10⁻⁶ and 2×10⁻³ and for temperature between 5 and 300 K. No plastic deformations are detected for the present strain range, where f decreases for up to 10⁻⁴ and then turns to increase, showing saturation for between 10⁻⁴ and 2×10⁻³. The low temperature irradiation by 2 MeV electrons or 20 MeV protons causes an increase in the Young’s modulus at 6 K, which is surmised to reflect a modification of the anelastic process in the GB regions. In contrast, the SAMD of f is hardly modified by irradiation, suggesting that it is indicative of a collective motion of atoms in n-Au.     

Effect of Al2O3 particles on mechanical properties of directionally solidified intermetallic Ti–46Al–2W–0.5Si alloy

The effect of Al₂O₃ particles on microhardness and room-temperature compression properties of directionally solidified (DS) intermetallic Ti–46Al–2W–0.5Si (at.%) alloy was studied. The ingots with various volume fractions of Al₂O₃ particles and mean ₂–₂ interlamellar spacings were prepared by directional solidification at constant growth rates ranging from 2.78×10⁻⁶ to 1.18×10⁻⁴ ms⁻¹ in alumina moulds. The ingots with constant volume fraction of Al₂O₃ particles and various mean interlamellar spacings were prepared by directional solidification at a growth rate of 1.18×10⁻⁴ ms⁻¹ and subsequent solution annealing followed by cooling at constant rates varying between 0.078 and 1.889 K s⁻¹. The mean ₂–₂ interlamellar spacing λ for both DS and heat-treated (HT) ingots decreased with increasing cooling rate according to the relationship λ∝ ^−0.46. In DS ingots, microhardness, ultimate compression strength, yield strength and plastic deformation to fracture increased with increasing cooling rate. In HT ingots, microhardness and yield strength increased and ultimate compression strength and plastic deformation to fracture decreased with increasing cooling rate. The yield stress increased with decreasing interlamellar spacing and increasing volume fraction of Al₂O₃ particles. A linear relationship between the Vickers microhardness and yield stress was found for both DS and HT ingots. A simple model including the effect of interlamellar spacing and increasing volume fraction of Al₂O₃ particles was proposed for the prediction of the yield stress.     

New transparent conducting MgIn2O4---Zn2In2O5 thin films prepared by magnetron sputtering

New materials for a transparent conducting oxide film are demonstrated. Highly transparent Zn₂In₂O₅ films with a resistivity of 3.9 × 10⁻⁴ Ω cm were prepared on substrates at room temperature using a pseudobinary compound powder target composed of ZnO (50 mol.%) and In₂O₃ (50 mol.%) by r.f. magnetron sputtering. MgIn₂O₄---Zn₂In₂O₅ films were prepared using MgIn₂O₄ targets with a ZnO content of 0–100 wt.%. The resistivity of the deposited films gradually decreased from 2 × 10⁻³ to 3.9 × 10⁻⁴ Ω cm as the Zn/(Mg + Zn) atomic ratio introduced into the films was increased. The greatest transparency was obtained in a MgIn₂O₄ film. The optical absorption edge of the films decreased as the Zn/(Mg + Zn) atomic ratio was increased, corresponding to the bandgap energy of their materials. It was found that the resistance of the undoped Zn₂In₂O₅ films was more stable than either the undoped MgIn₂O₄, ZnO or In₂O₃ films in oxidizing environments at high temperatures.