Fe—Cr—C—Si—B喷焊层的等离子弧重熔研究

本文首次开展了微束等离子弧的表面改性研究．采用２Ａ、３Ａ和４Ａ微束等离子弧，对Ｆｅ－Ｃｒ－Ｃ－Ｓｉ－Ｂ自熔合金喷焊层进行了表面扫描重熔，观察、分析了试样显微组织和成分分布，测定了扫描前后试样在１ＮＨ２ＳＯ４溶液中的极化曲线．由于试样的自淬火作用，微束等离子弧扫描细化了组织，减小了显微偏析，大大提高了喷焊合金的抗腐能力     

15CrMo钢及焊头氢蚀特性分析

对国产１５ＣｒＭｏ钢在高温高压氢中脱碳激活能和氢蚀激活能进行了测定．旨在研究国产１５ＣｒＭｏ钢的氢蚀机理，以达到在高温高压氢条件下更好地使用１５ＣｒＭｏ钢目的．另外，对１５ＣｒＭｏ钢自动焊焊头热影响区的氢蚀特性进行了研究，以积累１５ＣｒＭｏ钢焊头的氢蚀基本数据．碳化物分析表明，１５ＣｒＭｏ基材氢蚀前为单一Ｍ３Ｃ峰，氢蚀后有Ｍ２Ｃ峰存在，这说明氢蚀中Ｍ３Ｃ的分解过程为：Ｍ３Ｃ先分解为较稳定的Ｍ２Ｃ，然后再分解为Ｍ．１５ＣｒＭｏ焊接热影响区氢蚀前后都为Ｍ３Ｃ，说明焊接使Ｍ３Ｃ的分解过程发生了变化．     

GCr15钢纱锭底激光淬火初步研究

初步研究了ＧＣｒ１５钢纱锭底的激光硬化条件。在２５Ｗ／ｍｍ＾２激光功率密度下，和适当扫描速率下ＧＣｒ１５钢锭底硬度高达１２０５ＨＶ０．１且硬化层均匀。     

用正交试验法研究高温冲蚀磨损

介绍了正交试验法在高温冲蚀试验中的应用，通过正交试验法分析得出：对于等离子涂层来说，ＮｉＣｒＡｌ涂层最好，Ｘ４０（０．３）涂层其次；对于激光重熔层来说，４００℃时，Ｃｒ２Ｏ３涂层最好，ＷＴｉＣ２／ＮｉＣｒ涂层其次；７００℃时，Ｃｒ３Ｃ２／ＮｉＣｒ涂层最好，Ｘ４０（０．３）涂层其次。     

激光辐照镀铬钢合金化工艺与性能研究

用大功率ＣＯ２激光器对镀铬３０ＣｒＭｎＳｉ钢表面连续搭接式辐照处理，达到了在高含铬量的合金层和镀层与基体界面间获得高含铬量熔渗层两种不同的冶金效果，并实现镀层与基体间冶金结合，对此研究辐照前后耐磨性、阳极极化特性以及盐雾条件下的腐蚀行为。结果表明：激光辐照后耐磨性提高近一倍；激光合金化层耐蚀性明显提高；而熔渗工艺条件的电化学特性与原镀层相当，但原镀层穴蚀和龟裂的倾向得到克服，结合强度得到提高。     

激光重熔对氧化铝涂层的组织结构及性能的影响

用ＲＳ—１７００ＳＭ型轴流式ＣＯ２激光器对Ａｌ２Ｏ３涂层进行了重熔，降低了原始涂层中的孔隙，消除了涂层的层状结构，得到了致密均匀的涂层，使重熔层的显微硬度明显提高．高温氧化试验表明：激光表面重熔提高了Ａｌ２Ｏ３涂层的抗高温氧化性     

强束流Zr离子注入H13钢改善其耐磨性的研究

采用由金属蒸汽真空弧（ Ｍｅｔａｌ Ｖａｐｏｒ Ｖａｃｕｕｍ Ａｒｃ） 离子源引出的强束流脉冲Ｚｒ 、Ｚｒ ＋ Ｃ 离子对Ｈ１３ 钢进行了离子束表面处理。借助划痕仪和摩擦试验机分别测量了经表面处理的Ｈ１３ 钢的耐磨性和摩擦系数。研究结果表明： 经Ｚｒ、Ｚｒ＋ Ｃ 离子束处理的Ｈ１３ 钢的耐磨性有所提高、摩擦系数明显降低。采用卢瑟福背散射谱（ 简称ＲＢＳ） 、Ｘ 射线（ 简称ＸＲＤ） 分析了注入层的成分、结构及其影响其耐磨性的因素。     

M2＋4B喷涂层及激光涂覆层的组织与磨损特性

本文对Ｍ２＋４Ｂ微晶粉末的喷涂层和激光涂覆层的组织与耐磨性进行了研究。结果表明，喷涂层和激光涂覆层均有各自独特的组织特征，两者的耐磨性均匀为ＧＣｒ１５钢的６．５倍以上。     

W18Cr4V钢激光表面淬火工艺参数的选择

对Ｗ１８Ｃｒ４Ｖ钢激光表面淬火工艺参数进行了试验研究，试验结果表明，激光表面淬火工艺参数ｄ＝１．５ｍｍｑ＝１２４Ｗ／ｍｍ＾２，ｖ＝１８ｍｍ／ｓ时，激光淬火加热温度处于Ａｃ－Ｔ熔范围之内，可以得到无表面熔化的淬火层，淬火层深度０．２５ｍｍ，淬火层组织为细针状马氏体＋碳物＋残余奥氏体，显微硬度ＨＶ０．１９５０－１０５０。     

25Cr2MoV钢变温快速深层离子氮化工艺的研究

采用显微硬度计和ｘ射线衍射仪等手段，研究了２５Ｃｒ２ＭｏＶ钢经普通离子氮化和变温快速深层离子氮化新工艺处理后，其氮化层的性能及相组成，结果表明：在相同氮化时间内，变温快速深层离子氮化新工艺能显著地增加材料的有效氮化层深和总氮化层深，提高材料的表面硬度．     

激光强化40Cr合金钢表面磨损的实验研究

采用CO2激光器在不同的激光强化参数下对40Cr钢进行表面强化，并钭其与热轧Q235钢组成磨擦副，在干摩擦条件下进行摩擦磨损实验，旨在确定合理的激光强化参数，为提高矫直辊耐磨性提供实验依据。通过对实验结果和定量分析提出，激光强化可以提高40Cr钢的耐磨性，采用扫描电镜对激光强化后的40Cr钢表面和磨损表面进行分析，发现激光强化后40Cr钢的金相组织主要是致密的马氏体，而且磨损表面比正常淬火的40Cr钢的表面光滑，仅产生一些微裂纹。     

激光熔覆Ni+Cr_2O_3复合涂层的耐蚀性

研究了激光搭接熔覆Ni+Cr2 O3复合涂层在 0 .5mol/LH2 SO4 +0 .5mol/LNaCl水溶液中的电化学行为 .试验表明Cr2 O3粒子在激光熔池中发生了完全溶解 ,涂层具有胞状枝晶组织特征 .激光熔覆Ni+Cr2 O3复合涂层比单一熔覆Ni合金涂层和 2Cr13马氏体不锈钢基材具有更低的维钝电流密度和更宽的钝化区范围 ,明显改善了在该腐蚀介质中的抗点蚀能力 .     

Microstructure and performance of laser cladding TiB2 and Nickel-coated graphite composite coating on stainless steel 9Cr18

Stainlesssteel9Cr18withhighhardnessandanti wearpropertyiswidelyusedinthefieldsofbothna tionaldefenseandciviluse,especiallyapplicationintheaero enginebearingsandnationaldefenseaccoutre ments.Thetechnologyoflasercladdinghighhardness,antiwearandantifrictionc…     

Dry wear behaviors of wear resistant composite coatings produced by laser cladding

Using different proportional mixtures of Ni-coated MoS2, TiC and pure Ni powders, new typical wear resistant and selflubricant coatings were formed on low carbon steel by laser cladding process. The microstructures and phase composition of the composite coatings were studied by SEM and XRD. The typical microstructure of the composite coating is composed of multisulfide phases including binary element sulfide and ternary element sulfide, γ-Ni, TiC and Mo2C. Wear tests were carried out using an FALEX-6 type pin-on-disc machine. The friction coefficient and mass loss of three kinds of MoS2/TiC/Ni laser clad coatings are lower than those of quenched 45 steel, and the worn surfaces of the laser cladding coatings are very smooth. Because of high hardness combined with low friction, the laser cladding composite coating with a mixture of 70% Ni-coated MoS2, 20%TiC and 10% pure Ni powder presents better wear behaviors than the composite coating with other powder blends. The composition analysis of the worn surface of GCr15 bearing steel shows that the transferred film from the laser cladding coating to the opposite surface of GCr15 bearing steel contains an amount of sulfide, which can change the micro-friction mechanism and lead to a reduced friction coefficient.     

Cr3C2对等离子钴基堆焊层组织及性能的影响

采用等离子堆焊技术在低碳钢表面制备钴基合金堆焊层(Co40)及添加质量分数20%和40%Cr3C2的钴基合金复合堆焊层(Co40+20%Cr3C2,Co40+40%Cr3C2)。利用光学显微镜、扫描电镜、X射线衍射仪以及磨损实验机等研究不同添加量的Cr3C2对钴基合金堆焊层组织和耐磨性能的影响。结果表明:Co40堆焊层由γ-Co和Cr23C6组成;添加Cr3C2粉末后,堆焊层出现未熔的Cr3C2和Cr7C3及Cr23C6相,且明显改变了其组织特征,Co40+20%Cr3C2堆焊层仍以亚共晶方式结晶,但其组织得到明显的细化和均匀化,而Co40+40%Cr3C2堆焊层转变为过共晶方式结晶,其组织由大量初生碳化物和枝晶组织组成;Co40+Cr3C2复合堆焊层的硬度和耐磨性较Co40堆焊层均得到显著提高,且随着Cr3C2添加量的增加而相应提高。     

P-C法涂覆中碳结构钢的表面耐蚀性

应用Ｐ－Ｃ法对中碳结构钢进行Ｃｒ－Ｓｉ－Ａｌ复合涂覆,用电子探针及扫描电镜测定了涂层的表面成分及Ｃｒ,Ｓｉ,Ａｌ在涂层中的分布,用Ｘ射线衍测定了涂层中的相结构,将涂覆后的试样在酸、碱、盐溶液中进行腐蚀试验,结果表明,中碳结构钢经Ｐ－Ｃ法复合涂履后,表面优良的抗多种介质腐蚀的能力。     

稀土添加剂在激光熔敷自熔合金上的应用

对以2Cr13钢为基材,表面激光熔敷钴基自熔合金涂层中稀土元素的添加方式及稀土对熔敷层组织及性能的影响进行了深入的研究。试验结果表明:采用Cr-Y,Co-Y中间合金的方式,将性质活泼的稀土元素钇加入到钴基自熔合金涂层中的方法是可行的,且以采用Cr-Y中间合金尤为合适。稀土元素钇的加入,改善了激光熔敷层的组织,使合金敷层的硬度、耐磨性等综合机械性能均有一定的提高。     

40Cr钢表面改性处理及磨损性能研究

目的为了改善矫直辊合金钢表面的耐磨性，提高钢筋矫直辊的使用寿命．方法采用激光和等离子弧淬火表面硬化技术对合金钢40Cr进行表面处理。并将其与Q235配副在销盘式摩擦试验机上进行了摩擦磨损试验。通过干摩擦和切削液润滑的对比试验，进一步研究在润滑条件下的磨损机理．结果激光硬化处理的表面耐磨性最好；等离子弧淬火能够有效地改善材料表面硬度和耐磨性，采用水基切削液润滑能够大大提高合金钢表面耐磨性能．结论采用等离子弧淬火技术处理的合金钢表面的耐磨性能略差于经激光硬化处理的表面，在干摩擦条件下平均磨损率是激光处理的2倍，但是优于常规淬火的情况．可以采用等离子弧淬火技术和水基切削液润滑可以提高40Cr合金钢表面的耐磨性能。     

浆料法制备Mo2FeB2金属陶瓷-钢覆层材料及其性能研究

以FeB，Mo，Fe等粉末为主要原材料，加入有机溶剂，制备出成型料浆，用料浆法在钢基体表面成型覆层坯体，采用真空液相烧结技术，制备了Mo2FeB2金属陶瓷-钢覆层材料，并对其性能进行了检测。结果表明，覆层主要由Mo2FeB2硬质相和α—Fe黏结相构成，Mo2FeB2金属陶瓷-钢覆层材料在界面存在一个从高硬度到低硬度的渐变过渡区。磨损试验表明，Mo2FeBe金属陶瓷-钢覆层材料具有比YG8硬质合金更好的耐磨性。腐蚀试验表明，Mo2FeB2金属陶瓷-钢覆层材料具有比2Crl3钢更好的耐腐蚀性。     

激光熔敷工艺对镍基合金的耐蚀性影响的研究

我国火电厂千瓦汽轮机末级叶片在特定工况下其进气边常常遭到腐蚀．我们对其进行了激光直接重熔和激光熔敷镍基合金处理,经形貌观察,物相分析及阳极极化曲线测定,结果表明,激光处理后其耐蚀性均比处理前提高．其中熔敷镍基Ｇ１１２合金的耐蚀性提高最大．若激光处理参数匹配恰当,三者比较,涂敷的镍基ＷＣ合金更易印化、耐蚀性最好．