Ti2Ni相对Ti-31合金焊缝金属性能的影响

Ti2Ni相是脆硬的金属间化合物,在Ti-31合金焊缝金属中析出Ti2Ni相,将明显地降低其冲击韧性.Ti2Ni相的自然腐蚀电位要负于Ti-31合金及其焊缝金属,在电化学上Ti2Ni相属阳极相,故在Ti-31合金焊接接头中Ti2Ni相将成为牺牲阳极.     

放电等离子合成Ti3AlC2-TiB2复合材料的相形成研究

采用放电等离子烧结工艺,以Ti,Al,B4C,TiC为原料制备Ti3AlC2／TiB2复合材料。通过X射线衍射分析了从600℃到1300℃Ti3AlC2／TiB2系统反应过程的相形成规律。用扫描电镜观察了不同温度下试样的显微组织演变。结果表明,在900℃之前,主要的反应是Ti和Al反应生成Ti—Al金属间化合物,900℃之后,Ti—Al金属间化合物与TiC逐渐生成Ti3AlC2和TiB2相,形成致密Ti3AlC2／TiB2复合材料。     

Abrasive wear property of laser melting/deposited Ti2Ni/TiNi intermetallic alloy

A wear resistant intermetallic alloy consisting of TiNi primary dendrites and Ti2Ni matrix was fabricated by the laser melting deposition manufacturing process. Wear resistance of Ti2Ni/TiNi alloy was evaluated on an abrasive wear tester at room temperature under the different loads. The results show that the intermetallic alloy suffers more abrasive wear attack under low wear test load of 7, 13 and 25 N than high-chromium cast-iron. However, the intermetallic alloy exhibits better wear resistance under wear test load of 49 N. Abrasive wear of the laser melting deposition TiENi/TiNi alloy is governed by micro-cutting and plowing. Pseudoelasticity of TiNi plays an active role in contributing to abrasive wear resistance.     

层叠Ni/Ti热扩散形成金属间化合物的规律

选择Ni和Ti粉末及其机械合金化粉末制备Ni/Ti扩散偶,利用扫描电镜和X射线衍射等手段研究了Ni/Ti扩散偶在固相热处理作用下金属间化合物的形成及生长规律.随着热处理温度的提高,Ni3Ti,Ti2Ni和NiTi金属间化合物的数量增加明显;随热处理保温时间的增加,NiTi金属间化合物呈抛物线规律生长,而对Ni3Ti和Ti2Ni的生长影响不大.结果表明,金属间化合物在形成过程中,Ni3Ti和Ti2Ni优先形成,达到一定厚度后,NiTi金属间化合物开始形成并快速增长.     

Ti3SiC2、Ti3AlC2复相材料高温抗氧化行为的研究

以Ti粉、Si粉、铝粉、石墨为原料,在1600℃热压烧结制得试样,对不同配比Ti3SiC2、Ti3AlC2复相材料在1100～1500℃下恒温氧化20h的氧化行为进行研究.结果表明:热压法制备Ti3SiC2、Ti3AlC2复相材料在高温下具有比Ti3SiC2和Ti3AlC2更优良的高温抗氧化性能;由于试样氧化过程中产生了TiO2、SiO2、Al2TiO5和α-Al2O3,可有效提高试样的高温抗氧化能力.     

富钛的Ti51Ni47Si2形状记忆合金的马氏体相变

近等原子TiNi合金具有优异的形状记忆效应和超弹性,因此,在工程和医疗及牙科方面得到了广泛的应用。影响TiNi合金形状记忆性能的因素除了热循环、热处理、冷轧外,添加第三元素对其相变也有重要影响,如用钒、锆、铁及钴元素取代镍后,马氏体转变温度(Ms)降低,而用金、钯及铂部分取代镍后会显著增加Ms点。TiNiFe、TiNiAl及TiNiCo合金相变顺序为高温立方相B2→三角晶系中间相(R)→斜方晶系(B19);而对于TiNiCu、TiNiPd合金而言,相变顺序则为B2→B19→B19′(B19′为低温单斜晶系)。 采用射频溅射法制备的TiNi薄膜变形大,回复力强,被认…     

TiNi合金中Ti2Ni3析出物的相变和晶体结构

在富锦的TiNi合金中，通过时效热处理可出现TiNi3,Ti2Ni3和Ti3Ni4等析出物．它们对合金的形状记忆效应和超弹性有严重影响．日本学者采用电子衍射（ED）、会聚束衍射（CBED）、高分辨电于显微束（HREM）和X射线衍射Rielvod分析方法分析了The拆出物的相变和晶体结构．用于分析样品是用红弧炉熔炼的成分为48T－52N（8％）钮扣锭．样品真空密封在石英管中，于1刀3K下周溶处理！h，然后打破石英管水淬．后在973K下进行不同时间的时效处理，产生Tde；沉锭，时放处理后冰水淬火．金相观察表明，在50h之内，随时效时间增长，析出量增多…     

Ti49.2Ni50.8合金在等径角挤压过程中Ti3Ni4析出相的演化规律

采用透射电子显微镜研究Ti49.2Ni50.8合金中Ti3Ni4析出相在等径角挤压及中间退火过程中的演化规律.固溶态Ti49.2Ni50.8合金在450℃时效处理10～60 min以获得尺寸为37～75 nm的Ti3Ni4析出相.在450℃等径角挤压处理1道次后,时效处理10 min和30 min试样中Ti3Ni4析出...     

Ni75Al21.5Ti3.5合金时效行为的微观相场计算

应用微观相场方法计算了Ni75Al21.5Ti3.5合金873K时效时的沉淀行为.利用原子演化图、长程序参数和成分序参数的演化、有序相颗粒的平均直径、颗粒数目及合金原子在α、β位置占位几率的演化等研究手段,讨论了Al、Ti原子的有序化和原子簇聚过程;有序相的形核机制及粗化行为;原子的择优占位行为.结果表明:有序相颗粒的形核机制为失稳分解机制,Al原子基本达到有序排列,同时存在Ni-Al原子反位,Ti原子未达到完全有序排列,在γ'有序相中择优占据Al位,且有序相生成过程中,前期的生长动力学指数为1/2,后期的生长动力学指数为2/5.     

PATTERN RECOGNITION APLLIED TO STABILITY OF FILLED Ti_2Ni PHASES

Pattern recognition method is used for the investigation of stability,region of filled Ti_2Niphases in multi-dimensional bond-parameter space.The filling of C,N and O atoms intoT_6 octahedra consisting of atoms of earhy-transition elements makes the expansion of thestability region of Ti_2Ni phase,and the relative stability of AI_2Cu and MoSi_2 type com-pounds decreases after the introduction of non-metallic elements such as C,N and O.     

模式识别在金属大气腐蚀预测中的应用

运用模式识别技术,通过对影响金属大气腐蚀主要因素的聚类分析,初步研究了运用典型地区金属大气腐蚀数据预测和评价有关地区大气环境腐蚀性.     

燃烧合成Ti_3AlC_2及其热稳定性

采用燃烧合成技术,通过改变Ti、Al和C 3种粉末的比例制备出高纯度的Ti_3AlC_2块体材料,并对其在氩气中的高温热稳定性进行了研究.X射线衍射(XRD)表明合成产物除了含有Ti_3AlC_2外,还含有少量TiC和Ti-Al金属间化合物,经k值法计算得Ti_3AlC_2最高含量为96.7%.耦合等离子-原子发射光谱(ICP-AES)结果表明最高纯度的合成产物中Ti、Al质量分数分别为74.2%和13.7%,与Ti_3AlC_2中Ti和Al含量十分接近.利用SEM对燃烧产物断口进行了观察,发现明显的层片状结构.热重-差热(TG-DTA)结果表明燃烧合成的高纯Ti_3AlC_2在加热过程中没有明显的热效应,说明合成的产物处于近似平衡状态.Ti_3AlC_2的分解温度在1370 ℃左右,同时由于氧化作用而导致试样质量略有增加.     

TiAl－V－Si合金中Ti_（5）Si_3析出相与基体相的取向关系

通过电子显微分析，发现在热等静压的ＴｉＡｌ－Ｖ－Ｓｉ合金中有大量的硅化物沿层状结构的相界面析出，这些硅化物为Ｔｉ_５Ｓｉ_３相，通常为近六角形的薄片．Ｔｉ_５Ｓｉ_３相与层状结构基体相（α_２和γ相）间具有如下的固定取向关系［０００１］_（Ｔｉ_５Ｓｉ_３）／／［０００１］_（Ｔｉ_３Ａｌ），（３１２０）_（Ｔｉ_５Ｓｉ_３），／／（１０１０）_（Ｔｉ_３Ａｌ）［０００１］_（Ｔｉ_５Ｓｉ_３）／／［１１１］_（ＴｉＡｌ），（４１５０）_（Ｔｉ_５Ｓｉ_３）／／（１１０）_（ＴｉＡｌ）     

模式识别─人工神经网络在改善汽车发动机缸体铸件力学性能方面的应用

利用模式识别技术对影响汽车发动机缸体铸件抗拉强度和硬度的铁水化学成分以及浇注工艺参数进行了分析,给出了影响铸件抗拉强度和硬度的主要因素的优化范围．利用经已知样本集训练的人工神经网络对铸件抗拉强度和硬度进行了预报,预报结果与实测值符合较好．     

模式识别—人工神经网络在改善汽车发动机缸体铸件力学性能方面的 …

利用模式识别技术对影响汽车发动机缸体铸件抗拉强度和硬度的铁水化学成分以及浇注工艺参数进行了分析给出了影响铸件抗拉强度和硬度的主要因素的优化范围,利用经已知样本集训练的人工神经网络对铸件抗拉强度和硬度进行了预报,预报结果与实测值符合较好。     

高强耐蚀Ni-Co-Cr高温合金的组织稳定性

利用SEM，TEM及X射线衍射分析技术观察了高强耐蚀Ni-Co-Cr高温合金不同温度（704，750，849℃）长期时效1000h及700℃长期时效至5008h过程中的组织演变过程。结果表明，700℃即使长期时效5008h，γ‘相粗化缓慢，而且没有发现TCP相（如σ相）的析出。当温度升高到750℃，γ‘相迅速长大。晶界上碳化物析出增多，并析出片状的η相。导致合金冲击性能下降。温度达到849℃时，析出大量的η时。甚至形成魏氏组织形貌。由此可见，该合金在700℃时具有较好的组织稳定性。     

基于模糊模式识别的金属材料海水腐蚀形貌诊断系统

采用图像扫描方法获得了碳钢、低合金钢实海试片的腐蚀形貌图像,并对图像进行预处理及灰度分析;将所得样本的灰度值分布和对应的腐蚀形貌作为知识库的标准样本,用模糊模式识别理论建立了腐蚀形貌诊断系统,可以由扫描灰度值分布判断金属的表面腐蚀形貌．     

Ti合金化Mg2Ni氢化物能量和电子结构的第一性原理研究

采用基于密度泛函理论的第一性原理赝势平面波方法,计算Ti掺杂Mg2Ni储氢合金及其氢化物的能量和电子结构。计算结果表明:在掺杂浓度为0≤x≤0.5的情况下,Ti优先占据Mg(II)位,Ti的掺杂使Mg2Ni合金稳定性降低,且随着掺杂浓度的升高,对稳定性的削弱效果逐渐增强。六方结构的固溶体合金Mg(2-x)TixNi(0≤x≤0.5)相对于立方结构的Mg3TiNi2化合物呈现热力学不稳定性,极易分解为Mg3TiNi2和Mg2Ni组成的复合相。Ti的掺杂使低能级区域的成键电子数减少,削弱了H-Ni的成键作用,提高了Mg2Ni氢化物的解氢能力。     

分子轨道理论在分析合金相稳定性方面的应用

应用分子轨道理论分析了面心立方过渡族金属三元合金的固溶度,采用特征点成分平均法计算了三元合金相图的不同等温截面的43个γ/(γ+σ),γ/(γ+μ),和γ/(γ+γ′)相界线的临界■_d值■_(dc)。得到了γ/(γ+μ)相变的■_(dc)值与温度的关系式,并对分析的准确度进行了讨论发现存在着临界平均键合级次■_(oc),它可以和■_(dc)一道用来分析合金相的稳定性。