Preparation and study of the mechanical and optical properties of infrared transparent Y2O3–MgO composite ceramics

In this study, fine Y₂O₃–MgO composite nanopowders were synthesized via the sol–gel method. Dense Y₂O₃–MgO composite ceramics were fabricated by pre-sintering the green body in air at different temperatures for 1 h and then subjecting the sintered bodies to hot isostatic pressing at 1300°C for 1 h. The effects of pre-sintering temperature on the microstructural, mechanical, and optical properties of the resulting ceramics were studied. The average grain size of the ceramics was increased, whereas their hardness and fracture toughness were decreased with increasing pre-sintering temperature. A maximum fracture toughness of 1.42 MPa·m^1/2 and Vickers hardness of 10.4 GPa were obtained. The average flexural strength of the ceramics was 411 MPa at room temperature and reached 361 MPa at 600°C. A transmittance of 84% in the 3–5 µm region was obtained when the composite ceramics were sintered at 1400°C. Moreover, a transmittance of 76% in the 3–5 µm region was obtained at 500°C.     

Fabrication and thermoelectric properties of SrTiO3–TiO2 composite ceramics

The paper presents the results of preparing biphase SrTiO₃–TiO₂ ceramics as a promising system for n-type thermoelectrics using the features of a two-dimensional electron gas. Ceramics was obtained by reactive spark plasma sintering of SrCO₃ and TiO₂. The dynamics of phase transformations are shown; it is clarified that phase transformations are not the driving force of sintering. The mutual stabilization of the SrTiO₃ and TiO₂ phases is shown. Unique data on the assessment of the temperature gradient in the system have been obtained. A comparison of the thermoelectric characteristics of biphasic ceramics and its constituent phases allows concluding that the role of the two-dimensional electron gas is reduced to modulating the properties of bulk phases. Clear signs of size quantization were detected by the X-ray luminescence method, which is expressed in the blueshift of the luminescence spectrum by 22.3 ± 0.8 meV.     

Growth and optical properties of ZnO–In2O3 heterostructure nanowires

ZnO–In₂O₃ heterostructure nanowires were grown on a Si (111) substrate using the thermal evaporation method. Scanning electron microscopy results showed that the ZnO nanowires had spherical caps. The X-ray diffraction (XRD) pattern and energy-dispersive X-ray (EDX) spectrum indicated that these caps were In₂O₃. An analysis of the early growth process revealed that indium oxide might have played a self-catalytic role. Therefore, it was plausible that the vapor–liquid–solid mechanism (VLS) was responsible for the growth of the ZnO–In₂O₃ heterostructure nanowires. The optical properties of the products were characterized using a photoluminescence (PL) technique. The PL results for the ZnO–In₂O₃ heterostructure nanowires showed a strong peak in the ultraviolet region as a result of the near band emission and a negligible peak for the visible emissions that occurred as a result of the defects. Based on these PL results, it was found that the In₂O₃ nanostructures not only introduced the caps at the tips of the ZnO nanowires but also partially passivated the nanowire surfaces, leading to an improved near band edge emission and the suppression of the defect luminescence.     

Ion beam induced evolution of surface morphology and optical properties of SnO2–ZnO nanocomposite thin films

SnO₂–ZnO nanocomposite thin films, prepared by a simple carbothermal reduction based vapor deposition method, were irradiated with 8 MeV Si³⁺ ions for engineering the morphological and optical properties. The surface morphology of the nanocomposites was studied by atomic force microscopy (AFM), while the optical properties were investigated by photoluminescence spectroscopy (PL) and Raman spectroscopy. AFM studies on the irradiated samples revealed growth of nanoparticles at lower fluence and a significant change in surface morphology leading to the formation of nanosheets and their aggregates at higher fluences. A tentative mechanism underlying the observed ion induced evolution of surface morphology of SnO₂–ZnO nanocomposite is proposed. PL studies revealed strong enhancement in the UV emissions from the nanocomposite thin film at lower fluence, while a drastic decrease in the UV emissions along with a significant enhancement in the defect emissions has been observed at higher fluences.     

Fabrication and properties of ZrB2–SiC–BN machinable ceramics

ZrB₂–SiC–BN ceramics were fabricated by hot-pressing under argon at 1800 °C and 23 MPa pressure. The microstructure, mechanical and oxidation resistance properties of the composite were investigated. The flexural strength and fracture toughness of ZrB₂–SiC–BN (40 vol%ZrB₂–25 vol%SiC–35 vol%BN) composite were 378 MPa and 4.1 MPa m^1/2, respectively. The former increased by 34% and the latter decreased by 15% compared to those of the conventional ZrB₂–SiC (80 vol%ZrB₂–20 vol%SiC). Noticeably, the hardness decreased tremendously by about 67% and the machinability improved noticeably compared to the relative property of the ZrB₂–SiC ceramic. The anisothermal and isothermal oxidation behaviors of ZrB₂–SiC–BN composites from 1100 to 1500 °C in air atmosphere showed that the weight gain of the 80 vol%ZrB₂–20 vol%SiC and 43.1 vol%ZrB₂–26.9 vol%SiC–30 vol%BN composites after oxidation at 1500 °C for 5 h were 0.0714 and 0.0268 g/cm², respectively, which indicates that the addition of the BN enhances oxidation resistance of ZrB₂–SiC composite. The improved oxidation resistance is attributed to the formation of ample liquid borosilicate film below 1300 °C and a compact film of zirconium silicate above 1300 °C. The formed borosilicate and zirconium silicate on the surface of ZrB₂–SiC–BN ceramics act as an effective barriers for further diffusion of oxygen into the fresh interface of ZrB₂–SiC–BN.     

Synthesis,processing and properties of TaC–TaB2–C ceramics

Multi-phase ceramics in the TaC–TaB₂–C system were prepared from TaC and B₄C mixtures by reactive pressureless sintering at 1700–1900 °C. The pressureless densification was promoted by the use of nano-TaC and by the presence of active carbon in the reaction products. The presence of TaB₂ inhibited grain growth of TaC and increased the hardness compared to pure TaC. If a coarse TaC powder was used, the compositions did not densify. In contrast, pure nano-TaC was pressureless sintered at 1800 °C by the addition of 2 wt.% carbon introduced as carbon black or graphite. The introduction of carbon black resulted in fully dense TaC ceramics at temperatures as low as 1500 °C. The grain size of nominally pure TaC ceramics was a strong function of carbon stoichiometry. Enhanced grain size in sub-stoichiometric TaC, compared to stoichiometric TaC, was observed. Additional work is necessary to optimize processing parameters and evaluate the properties of ceramics in the TaC–TaB₂–C system.     

Crystal structure,dielectric properties,and optical bandgap control in KNbO3–BiMnO3 ceramics

(1 − x)KNbO₃–xBiMnO₃ (0 ≤ x ≤ 0.25) ceramics were prepared by the solid-state reaction method. An X-ray diffraction analysis combined with Raman spectroscopy showed the co-solubility of Bi and Mn in the orthorhombic structure to be less than 5% BiMnO₃. Orthorhombic and pseudocubic symmetries coexist in the 0.05 ≤ x ≤ 0.15 region, coinciding with a bimodal grain size distribution. This coexistence of crystal symmetries is further corroborated by several anomalies in the dielectric behavior, which can be ascribed to structural phase transitions. For x ≥ 0.20, only one dielectric anomaly is detected around 100°C, which is commensurate with in situ Raman spectroscopy analysis. This work also shows that Bi/Mn co-doping can be employed to tailor the bandgap of KNbO_3, which narrows continuously with increasing x, resulting in ∼1-eV narrowing for single-phase x = 0.25. This may offer the possibility to employ this ferroic material in photoresponsive technologies.     

Characterisation of SnO2–CoO–MnO–Nb2O5 ceramics

Varistors based on SnO₂ have attracted increasing interest in recent years. However, the combined effect of CoO–MnO on SnO₂ ceramics is still unclear. In this study, the non-Ohmic behaviour of the 98.95 mol%SnO₂–0.5 mol%CoO–0.5 mol%MnO–0.05 mol%Nb₂O₅ system, the microstructures and the influence of sintering temperature were investigated. The samples were prepared by the mixed oxide route, and were sintered at temperatures in the range 1250–1450 °C. SEM observation and EDS analysis revealed that the ceramics have a two-phase microstructure comprising SnO₂ primary grains and a Mn, Co rich secondary phase of small particles. The sintered density of the samples increased with the increase in sintering temperature. The maximum non-linear coefficient (α = 10) was obtained at a sintering temperature of 1350 °C.     

Preparation and properties of porous SiC–Al2O3 ceramics using coal ash

In this paper, we first reported that porous SiC–Al₂O₃ ceramics were prepared from solid waste coal ash, activated carbon, and commercial SiC powder by a carbothermal reduction reaction (CRR) method under Ar atmosphere. The effects of addition amounts of SiC (0, 10, 15, and 20 wt%) on the postsintering properties of as-prepared porous SiC–Al₂O₃ ceramics, such as phase composition, microstructure, apparent porosity, bulk density, pore size distribution, compressive strength, thermal shock resistance, and thermal diffusivity have been investigated. It was found that the final products are β-SiC and α-Al₂O₃. Meanwhile, the SEM shows the pores distribute uniformly and the body gradually contacts closely in the porous SiC–Al₂O₃ ceramics. The properties of as-prepared porous SiC–Al₂O₃ ceramics were found to be remarkably improved by adding proper amounts of SiC (10, 15, and 20 wt%). However, further increasing the amount of SiC leads to a decrease in thermal shock resistance and mechanical properties. Porous SiC–Al₂O₃ ceramics doped with 10 wt% SiC and sintered at 1600°C for 5 hours with the median pore diameter of 4.24 μm, room-temperature compressive strength of 21.70 MPa, apparent porosity of 48%, and thermal diffusivity of 0.0194 cm²/s were successfully obtained.     

Effect of adding Y2O3 on structural and mechanical properties of Al2O3–ZrO2 ceramics

The effects of adding 1–8 wt% Y₂O₃ on phase formation and fracture toughness of Al₂O₃–xZrO₂–Y₂O₃(AZY) ceramics were studied. Phase formations of the samples were characterized by the X-ray diffraction (XRD) technique. It was found that the major phase was rhombohedral-Al₂O₃, while the minor phase consisted of the monoclinic-ZrO₂, tetragonal-ZrO₂ and monoclinic-Y₂O₃. It was found that Y₂O₃ contents did not clearly influence grain shape of AZY ceramics. The results obtained from the microhardness test could be used to evaluate the fracture toughness. It was found that the smaller grains had high fracture toughness. The maximum fracture toughness of 4.827 MPa m^1/2 was obtained from 4 wt% Y₂O₃. Refinement of lattice parameters using Rietveld analysis revealed the quantitative phases of AZY ceramics. This shows that under adding Y₂O₃ conditions the proportion of tetragonal-ZrO₂ phase plays an important role for the mechanical properties of AZY ceramics.     

Microstructural evolution and enhanced mechanical properties of 95Al2O3–Yb/Mg/Si ceramics by optimizing sintering temperature

Designed component of 0.95Al₂O₃–0.015Yb₂O₃–0.01MgO–0.025SiO₂ (95Al₂O₃–Yb/Mg/Si) ceramics were prepared by the traditional mixed-oxide method in the sintering temperature range of 1450–1700 °C. The influence of sintering temperature on the crystal structure, densification, microstructure, mechanical, friction and wear properties of 95Al₂O₃-YbMgSi ceramics were systematically investigated. XRD and SEM analysis results revealed that the increase in sintering temperature was very beneficial to eliminate the pores, increase the density and grain size, which obeys the common grain growth law. Both the flexural strength and hardness of obtained samples were increased almost linearly when the sintering temperature increased from 1450 °C to 1700 °C. The ceramics sintered at 1650 °C showed the optimum properties: H_v = 1812.3, σ = 151.3 MPa, μ = 0.41, ρ = 3.72 g/cm³ and K_c = 8.06e^?5 mm³/N·m, respectively. Furthermore, the results of friction and wear experiments suggested that the 95Al₂O₃–Yb/Mg/Si ceramic prepared at the optimizing sintering process exhibited more stable friction state and lower wear degree under non-lubricated conditions. The enhanced mechanical properties could be attributed to their structure densification, pore elimination and gain growth with the increase of sintering temperature.     

Structural modification and evaluation of dielectric and ferromagnetic properties of Ce-modified BiFeO3–BaTiO3 ceramics

An investigation on Rare earth constituent Ce incorporated BiFeO₃–BaTiO₃ ceramics has been focused in the present study. The ceramic samples of (Bi₀.₇Ba_0.3)_1-xCe_x(Fe₀.₇Ti_0.3)O₃ (x = 0–0.12) were formulated adopting the cost-effective solid-state sintering method. The influence of aliovalent Ce ions on the structural, microstructural, dielectric, ferromagnetic, and optical properties of BiFeO₃–BaTiO₃ was evaluated in this paper. The coexistence of the Tetragonal and the Rhombohedral phases was established by the Rietveld refinement process. The refined crystallographic parameters showed maximum cell volume (V_cell) and the highest percentage of the Rhombohedral phase for x = 0.06; and consequently, the ceramic exhibited the topmost dielectric constant of 946 at x = 0.06. The scanning electron microscopy of the samples revealed the manifestation of polygonal grain morphology. Besides, remarkably improved ferromagnetic properties were evinced for Ce doped ceramics. The magnitude of saturation (M_s) and remnant (M_r) magnetizations were boosted from 0 emu/g and 0.0019 emu/g to 0.9186 emu/g and 0.3745 emu/g respectively with increasing x from 0 to 0.12. Additionally, the optical band gaps of all the samples were evaluated and found to be in the range of 2.941–3.077 eV.     

Mechanical properties and microstructure of porous BN–SiO2–Si3N4 composite ceramics

Porous silicon nitride (Si₃N₄) ceramics incorporated with hexagonal boron nitride (h-BN) and silica (SiO₂) nanoparticles were fabricated by pressureless-sintering at relatively low temperature, in which stearic acid was used as pore-making agent. Bending strength at room and high temperatures, thermal shock resistance, fracture toughness, elastic modulus, porosity and microstructure were investigated in detail. The mechanical properties and thermal shock resistance behavior of porous Si₃N₄ ceramics were greatly influenced by incorporation of BN and SiO₂ nanoparticles. Porous BN–SiO₂–Si₃N₄ composites were successfully obtained with good critical thermal shock temperature of 800 °C, high bending strength (130 MPa at room temperature and 60 MPa at 1000 °C) and high porosity.     

The structure and properties of 0.95MgTiO3–0.05CaTiO3 ceramics co-doped with ZnO–ZrO2

The (Mg_0.93Ca_0.05Zn_0.02)(Ti_1?xZr_x)O₃ ceramics were prepared by conventional solid-state route. The dielectric properties and structure of (Mg_0.93Ca_0.05Zn_0.02)(Ti_1?xZr_x)O₃ ceramics were investigated. It has been found that MgTiO₃ and CaTiO₃ are the main phases and a second phase CaZrTi₂O₇ appeared in 95MCT ceramics co-doped with Zn–Zr. With Zn–Zr additive, the sintering temperature of 95MCT ceramics can be reduced to 1300 °C, and adjust the temperature coefficient of dielectric constant. With the increasing of Zr content, dielectric constant ?_r decrease from 22.6 to 19.91 and the temperature coefficient of dielectric constant α_c from 5.93 to 2.52 ppm/°C when x = 0.01, 0.02, 0.03 and 0.04 mol respectively. The 95MCT ceramics with x = 0.02 has a dielectric constant ?_r of 22.02, a dielectric loss of 2.78 × 10^?4 and a temperature coefficient of dielectric constant α_c value of 2.98 ppm/°C.     

Charge compensation and electrical characteristics of Ta2O5–doped SnO2–CoO ceramics

We investigated the effect of pentavalent donor dopant Ta₂O₅ on microstructure development, electric and dielectric characteristics of SnO₂–CoO based ceramics. Already low additions of Ta₂O₅ (0.05 mol%) effectively reduce the porosity, improve densification and dielectric permittivity and trigger a 3–fold increase in SnO₂ growth rate. Rietveld analysis shows that the amount of Co₂SnO₄ spinel phase drops with the addition of Ta₂O₅ due to incorporation of Co²⁺ and Ta⁵⁺ into SnO₂ structure. With higher additions, however, Ta₂O₅ segregates to the grain boundaries and hinders SnO₂ grain growth, which in turn improves electrical properties. TEM/EDS analysis shows that above 0.5 mol% of Ta₂O₅ the Co:Ta ratio in SnO₂ grains is constant 1:2, which means that a twice lower amount of Ta⁵⁺ is incorporated in the SnO₂ structure compared to the Nb₂O₅-doped SnO₂–CoO system. Accordingly, the following charge compensation mechanism is proposed: 3 Sn(IV)_S^˟_{n (IV)} ⇋ Co(II)_Sn ̎_(IV) + 2 Ta(V)˙_{Sn (IV)}.     

Effect of yttria substitution on structure,optical and mechanical properties of (Gd,Y)2O3–MgO nanocomposite ceramics

A citrate-nitrate combustion method was applied to synthesize fine composite Gd_2-xY_xO₃-MgO (x = 0, 0.02, 0.2, 0.3, 0.4, 0.6) nanopowders. Y₂O₃ substitution inhibited Gd₂O₃ phase transition from cubic structure to monoclinic structure during sintering, thereby stabilizing its cubic structure to room temperature. This approach led to nanocomposite ceramics with a grain size of about 190 nm and increased the transmittance to 85% over the 3–5 μm wavelength range when x = 0.3. However, the addition of Y₂O₃ weakened the mechanic properties of the nanocomposite ceramics.     

Microstructure and properties of CaO–ZrO2–SiO2 glass–ceramics prepared by sintering

For the development of a new wear resistant and chemically stable glass-ceramic glaze, the CaO–ZrO₂–SiO₂ system was studied. Compositions consisting of CaO, ZrO₂, and SiO₂ were used for frit, which formed a glass-ceramic under a single stage heat treatment in electric furnace. In the sintered glass-ceramic, wollastonite (CaSiO₃) and calcium zirconium silicate (Ca₂ZrSi₄O₁₂) were crystalline phases composed of surface and internal crystals in the microstructure. The internal crystal formed with nuclei having a composition of Ca_1.2Si_4.3Zr_0.2O₈. The CaO–ZrO₂–SiO₂ system showed good properties in wear and chemical resistance because the Ca₂ZrSi₄O₁₂ crystals positively affected physical and mechanical properties.     

Influence of Ge and GeO2 on the microstructure and varistor properties of TiO2–Ta2O5–CaCO3 ceramics

This study investigated the effect of elemental crystal Ge or/and GeO₂ doping on the microstructure and varistor properties of TiO₂–Ta₂O₅–CaCO₃ varistor ceramics, which were prepared via the traditional ball milling–molding–sintering process. X-ray diffraction, scanning electron microscopy, scanning transmission electron microscopy-energy dispersive X-ray spectroscopy, scanning electron microscopy-energy dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy demonstrated that co-doping with Ge and GeO₂ changed the microstructure of TiO₂–Ta₂O₅–CaCO₃ ceramics, thereby increasing the nonlinear coefficient and decreasing the breakdown voltage. The optimum doping concentrations of Ta₂O₅, CaCO₃, Ge, and GeO₂ exhibited the highest nonlinear coefficient (α=14.6), a lower breakdown voltage (E_B=18.7 V mm⁻¹), the least leakage current (J_L=10.5 μA cm⁻²), and the highest grain boundary barrier (Φ_B=1.05 eV). In addition, Ge and GeO₂ function as sintering aids, which reduce the sintering temperature because of their low melting points.     

Densification behavior and properties of alumina–chrome ceramics: Effect of TiO2

Highly dense alumina–chrome bodies with low porosity are usually used as corrosion and thermal resistant refractories. Alumina–chrome refractory with molar ratio 1:1 was developed using chemical grade hydrated alumina and chromium (III) oxide by conventional sintering route. Batch materials were attrition milled, isostatically pressed and sintered in the temperature range from 1000 °C to 1700 °C with 2 h soaking at peak temperature. Phase development of the sintered materials with temperature was studied by X-ray diffraction. Sintering temperature, sintering condition and addition of sintering aid (TiO₂) have immense effect on the densification of the alumina–chrome refractory. Highly dense alumina–chrome refractory with almost nil apparent porosity was developed at 1500 °C in reducing atmosphere. Flexural strength of the sintered materials at room temperature and at 1200 °C was also measured. 1 wt% TiO₂ gives the optimum result with respect to densification and flexural strength.     

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Zirconia ceramic is a significant structural material, but its use under some extreme circumstances is limited by its mechanical properties. In this work, SiC particles (SiCp) were added into alumina toughened zirconia ceramics to prepare ZrO₂–Al₂O₃-SiCp ceramics with high performance by using oscillatory pressure sintering (OPS). Results showed that the best OPS temperature of 1600 °C was obtained, and the optimal SiCp particle size and content were 200 nm and 10 vol% respectively. Under these conditions, the specimen exhibited higher mechanical properties including Vickers hardness of 15.43 GPa, bending strength of 1162 MPa and fracture toughness of 6.36 MPa m^1/2. Moreover, it was found that the atomic matching between ZrO₂/SiCp, Al₂O₃/SiCp, and ZrO₂/Al₂O₃ was much higher, showing the coherent interface relationship. Therefore, it was favorable for enhanced mechanical properties of as-prepared ZrO₂–Al₂O₃-SiCp ceramics.