High-temperature erosion resistance and aerodynamic oxidation mechanism of multi-layer MoSi2–CrSi2–Si/SiC coated carbon/carbon composites in a wind tunnel at 1873 K

The high-temperature erosion resistance of multi-layer MoSi₂–CrSi₂–Si/SiC coated carbon/carbon (C/C) composites was investigated in a wind tunnel. To study the aerodynamic oxidation mechanism and analyze the failure of the coated C/C composites, the shear force and bending moment distribution of the tested specimens in a wind tunnel were calculated. Flexural strengths and thermogravimetric analysis of the coated specimens were measured. These results show that the multi-layer MoSi₂–CrSi₂–Si/SiC antioxidation coating can protect the C/C composites from high-temperature erosion in a wind tunnel at 1873 K for more than 86 h. Due to the high viscosity of SiO₂, the multi-layer coating lacked effective oxidation resistance from 900 to 1500 K, resulting in extensive mechanical damage and the fracture of the tested specimens.     

TaB2–SiC–Si multiphase oxidation protective coating for SiC-coated carbon/carbon composites

To improve the oxidation resistance of the carbon/carbon (C/C) composites, a TaB₂–SiC–Si multiphase oxidation protective ceramic coating was prepared on the surface of SiC coated C/C composites by pack cementation. Results showed that the outer multiphase coating was mainly composed of TaB₂, SiC and Si. The multilayer coating is about 200 μm in thickness, which has no penetration crack or big hole. The coating could protect C/C from oxidation for 300 h with only 0.26 × 10^?2 g²/cm² mass loss at 1773 K in air. The formed silicate glass layer containing SiO₂ and tantalum oxides can not only seal the defects in the coating, but also reduce oxygen diffusion rates, thus improving the oxidation resistance.     

Ablation resistance of HfB2-SiC coating prepared by in-situ reaction method for SiC coated C/C composites

To improve the ablation resistance of SiC coating, HfB₂-SiC coating was prepared on SiC-coated carbon/carbon (C/C) composites by in-situ reaction method. Owing to the penetration of coating powders, there is no clear boundary between SiC coating and HfB₂-SiC coating. After oxyacetylene ablation for 60 s at heat flux of 2400 kW/m², the mass ablation rate and linear ablation rate of the coated C/C composites were only 0.147 mg/s and 0.267 µm/s, reduced by 21.8% and 60.0%, respectively, compared with SiC coated C/C composites. The good ablation resistance was attributed to the formation of multiple Hf-Si-O glassy layer including SiO₂, HfO₂ and HfSiO₄.     

MoSi2-based oxidation protective coatings for SiC-coated carbon/carbon composites prepared by supersonic plasma spraying

To protect carbon/carbon (C/C) composites against oxidation, MoSi₂-based oxidation protective coatings for SiC-coated carbon/carbon composites were prepared on them by supersonic plasma spraying. The MoSi₂-based coatings primarily consist of MoSi₂, Mo₅Si₃ and glassy SiO₂. Only a few pinholes and some microcracks are observed on the surface and no through-thickness cracks penetrate the cross-section. Weight loss of the MoSi₂-based coated specimens is only 1.14% after 400 h oxidation in air at 1773 K and the coated C/C composites remain intact after 11 thermal cycles between 1773 K and room temperature. The outstanding anti-oxidation ability is mainly attributable to the formation of SiO₂-based layer on the surface of MoSi₂-based coatings.     

Oxidation protection of carbon/carbon composites with SiC/indialite coating for intermediate temperatures

In order to improve the oxidation resistance of carbon/carbon composites at intermediate temperatures, a novel double-layer SiC/indialite coating was prepared by a simple and low-cost method. The internal SiC transition layer was prepared by pack cementation and the external indialite glass–ceramic coating was produced by in situ crystallization of ternary MgO–Al₂O₃–SiO₂ glass. The microstructures and morphologies of coating were determined by scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS). Oxidation resistance of the as-coated C/C composites was evaluated in ambient air at temperature from 800 °C to 1200 °C. Nearly neglectable mass loss was measured after 100 h isothermal oxidation test, indicating that SiC/indialite coating possesses excellent oxidation protection ability. The as-coated samples have a good thermal shock resistance and no obvious damage was found in the coating even after suffered more than 11 thermal cycles between test temperature and room temperature. The oxidation protection mechanism of this coating was also discussed.     

A mullite/SiC oxidation protective coating for carbon/carbon composites

To protect carbon/carbon (C/C) composites against oxidation, a mullite coating was prepared on SiC precoated C/C composites by a hydrothermal electrophoretic deposition process. The phase composition, microstructure and oxidation resistance of the prepared mullite/SiC coatings were investigated. Results show that hydrothermal electrophoretic deposition is an effective route to achieve crack-free mullite coatings. The mullite/SiC coating displays excellent oxidation resistance and can protect C/C composites from oxidation at 1773 K for 322 h with a weight loss rate of only 4.89 × 10^?4 g/cm² h. The failure of the multi-layer coatings is considered to be caused by the volatilization of silicate glass layer, the formation of microholes and microcracks on the coating surface and the formation of penetrative holes between the SiC bonding layer and the C/C matrix at 1773 K. The corresponding high temperature oxidation activation energy of the coated C/C composites at 1573–1773 K is calculated to be 111.11 kJ/mol.     

Ablation mechanism of WC-SiC double layer coating under oxyacetylene torch test

A WC-SiC double-layer coating was prepared on C/C composites to improve their anti-ablation property. The WC outer layer was designed to withstand high heat flux by its high mechanical strength, the SiC inner layer could transform into SiO₂ to block oxygen by its good anti-oxygen permeability. During ablation process, amounts of SiO₂ filled into the pores and cracks of WC outer layer, forming a steadily self-filling and cooling structure. As a result, the mass and linear ablation rates of WC-SiC coated C/C composites were 0.013 mg s⁻¹ cm² and −1.61 µm/s, respectively. Compared with single SiC coated and single WC coated C/C composites, the linear ablation rates decreased by 46.3% and 27.3%, respectively, indicating that WC-SiC coating has a remarkable effect to resist chemical and mechanical ablation.     

A SiC–Si–ZrB2 multiphase oxidation protective ceramic coating for SiC-coated carbon/carbon composites

In order to improve the oxidation protective ability of SiC-coated carbon/carbon (C/C) composites, a SiC–Si–ZrB₂ multiphase ceramic coating was prepared on the surface of SiC-coated C/C composite by the process of pack cementation. The microstructures of the coating were characterized using X-ray diffraction and scanning electron microscopy. The coating was found to be composed of SiC, Si and ZrB₂. The oxidation resistance of the coated specimens was investigated at 1773 K. The results show that the SiC–Si–ZrB₂ can protect C/C against oxidation at 1773 K for more than 386 h. The excellent oxidation protective performance is attributed to the integrity and stability of SiO₂ glass improved by the formation of ZrSiO₄ phase during oxidation. The coated specimens were given thermal shocks between 1773 K and room temperature for 20 times. After thermal shocks, the residual flexural strength of the coated C/C composites was decreased by 16.3%.     

Design of an inlaid interface structure to improve the oxidation protective ability of SiC–MoSi2–ZrB2 coating for C/C composites

To improve the oxidation protective ability of SiC–MoSi₂–ZrB₂ coating for carbon/carbon (C/C) composites, pre-oxidation treatment and pack cementation were applied to construct a buffer interface layer between C/C substrate and SiC–MoSi₂–ZrB₂ coating. The tensile strength increased from 2.29 to 3.35 MPa after pre-oxidation treatment, and the mass loss was only 1.91% after oxidation at 1500 °C for 30 h. Compared with the coated C/C composites without pre-oxidation treatment, after 18 thermal cycles from 1500 °C and room temperature, the mass loss was decreased by 30.6%. The improvements of oxidation resistance and mechanical property are primarily attributed to the formation of inlaid interface between the C/C substrate and SiC–MoSi₂–ZrB₂ coating.     

A MoSi2-SiOC-Si3N4/SiC anti-oxidation coating for C/C composites prepared at relatively low temperature

In this study, SiC coating for C/C composites was prepared by pack cementation method at 1773 K, and MoSi₂-SiOC-Si₃N₄ as an outer coating was successfully fabricated on the SiC coated samples by slurry method at 1273 K. The microstructure and phase composition of the coatings were analyzed. Results showed that a porous β-SiC inner coating and a crack-free MoSi₂-SiOC-Si₃N₄ coating are formed. Effect of Si₃N₄ content on the oxidation resistance of the coated C/C composites at 1773 K in air was also investigated. The weight loss curves revealed that introducing the appropriate proportion of Si₃N₄ could improve the oxidation resistance of coating. The MoSi₂-SiOC/SiC coated C/C sample had an accelerated weight loss after oxidation in air for 20 h. However, the coating containing 45% Si₃N₄ could protect C/C composition from oxidation for 100 h with a minute weight loss of 0.63%.     

Oxidation behavior and microstructure evolution of SiC-ZrB2-ZrC coating for C/C composites at 1673 K

To protect carbon/carbon (C/C) composites against oxidation, a SiC-ZrB₂-ZrC coating was prepared by the in-situ reaction between ZrC, B₄C and Si. The thermogravimetric and isothermal oxidation results indicated the as-synthesized coating to show superior oxidation resistance at elevated temperatures, so it could effectively protect C/C composites for more than 221 h at 1673 K in air. The crystalline structure and morphology evolution of the multiphase SiC-ZrB₂-ZrC coating were investigated. With the increase of oxidation time, the SiO₂ oxide layer transformed from amorphous to crystalline. Flower-like and flake-like SiO₂ structures were generated on the glass film during the oxidation process of SiC-ZrB₂-ZrC coating, which might be ascribed to the varying concentration of SiO. The oxide scale presented a two-layered structure ~130 µm thick after oxidation, consisting of a SiO₂-rich glass layer containing ZrO₂/ZrSiO₄ particles and a Si-O-Zr layer. The multiphase SiC-ZrB₂-ZrC ceramic coating exhibited much better oxidation resistance than monophase SiC, ZrB₂ or ZrC ceramic due to the synergistic effect among the different components.     

A double layer nanostructure SiC coating for anti-oxidation protection of carbon/carbon composites prepared by chemical vapor reaction and chemical vapor deposition

A double layer nanostructure SiC coating was prepared by chemical vapor reaction and chemical vapor deposition to protect carbon/carbon composites from oxidation. The obtained dense coating reveals a typical crystalline structure and combines well with the substrate. The outer layer of the coating consists of SiC nanocrystals and nanowires, whereas the inner layer is mainly composed of SiC microcrystals, nanocrystals and nanowires. The oxidation and cyclic thermal shock test performed at 1400 °C in air demonstrates that the prepared dense nanostructure coating has excellent anti-oxidation behavior and thermal shock resistance at high temperature. After 400 h oxidation and 34 cycles of thermal shock from 1400 °C to room temperature, the weight loss of the coated sample is only 1.67%. In the oxidation process, the amorphous silica formed at the beginning of the oxidation crystallizes to cristobalite as oxidation time increased. The formation of cristobalite resulted in micro-cracks formed along grain boundaries in the cyclic thermal shock test. As only cracks are formed on the coating surface, it can be concluded that the formation of the penetration cracks may be the reason for the weight loss of the SiC coated composite.     

HfC nanowires to improve the toughness and oxidation resistance of Si-Mo-Cr/SiC coating for C/C composites

To improve the oxidation resistance of carbon/carbon (C/C) composites, a dense HfC nanowire-toughened Si-Mo-Cr/SiC multilayer coating was prepared by chemical vapor deposition (CVD) and pack cementation. The microstructure, thermal shock and isothermal oxidation resistance of the coating were investigated. HfC nanowires could improve the toughness of the coating and suppress the coating cracking. After incorporating HfC nanowires in the coating, both of the thermal shock and isothermal oxidation resistance of the coating were obviously improved. The multilayer coating with HfC nanowires could effectively protect C/C composites at 1773 K for 270 h, whose weight loss is only 0.19%. The good oxidation resistance is mainly attributed to the formation of a compound glass layer containing SiO₂ and Cr₂O₃.     

Bimodal microstructure ZrB2-MoSi2 coating prepared by atmospheric plasma spraying for carbon/carbon composites against long-term ablation

To protect carbon/carbon composites against long-term ablation, a bimodal microstructure ZrB₂-MoSi₂ coating, consisting of an outer ZrB₂-MoSi₂ layer modified by Y₂O₃ and an inner basal ZrB₂-MoSi₂ layer, was prepared by atmospheric plasma spraying. The microstructure, phase composition and ablation resistance of the proposed coating were investigated in detail. Results showed that the bimodal coating maintained integrity in structure except for phase composition. There was no visible interlayer between the inner ZrB₂-MiSi₂ layer and the outer modified one. Mass ablation rate of the bimodal microstructure ZrB₂-MoSi₂ coated C/C composites was −2.02 × 10⁻³ g/s under an oxyacetylene flame ablation at 1873 K for 600 s, which exhibited better ablation resistance than a single ZrB₂-MoSi₂ coating. The excellent ablation resistance was ascribed to the positive effect of Y₂O₃, which not only pined in the glassy phase and alleviated the volatilization of SiO₂ glass phase by reacting with SiO₂ to form high viscosity of Y₂SiO₅, but also stabilized ZrO₂ and promoted its recrystallization and growth.     

Ablation behavior and mechanism of C/C–ZrC–SiC composites under an oxyacetylene torch at 3000 °C

C/C–ZrC–SiC composites with continuous ZrC–SiC ceramic matrix were prepared by a multistep technique of precursor infiltration and pyrolysis process. Ablation properties of the composites were tested under an oxyacetylene flame at 3000 °C for 120 s. The results show that the linear ablation rate of the composites was about an order lower than that of pure C/C and C/C–SiC composites as comparisons, and the mass of the C/C–ZrC–SiC composites increased after ablation. Three concentric ring regions with different coatings appeared on the surface of the ablated C/C–ZrC–SiC composites: (i) brim ablation region covered by a coating with layered structure including SiO₂ outer layer and ZrO₂–SiO₂ inner layer; (ii) transition ablation region, and (iii) center ablation region with molten ZrO₂ coating. Presence of these coatings which acted as an effective oxygen and heat barrier is the reason for the great ablation resistance of the composites.     

SiC nanowire-toughened MoSi2-WSi2-SiC-Si multiphase coating for improved oxidation resistance of C/C composites

To improve the oxidation resistance of carbon/carbon (C/C) composites at high temperature, a SiC nanowire-toughened MoSi₂-WSi₂-SiC-Si multiphase coating was prepared by chemical vapor deposition (CVD) and pack cementation. The microstructure, mechanical properties and oxidation resistance of the coating were investigated. After the introduction of SiC nanowires, the elastic modulus, hardness, and fracture toughness of the MoSi₂-WSi₂-SiC-Si coating were increased by 25.48%, 4.09% and 45.03%, respectively. The weight loss of the coated sample with SiC nanowires was deceased from 4.83–2.08% after thermal shock between 1773 K and room temperature for 30 cycles and the weight loss is only 3.24% after isothermal oxidation at 1773 K in air for 82 h. The good oxidation resistance of the coating is mainly attributed to that SiC nanowires can effectively inhibit the propagation of cracks in the coating by the toughening mechanisms including bridging and pull-out.     

Effect of co-deposited SiC nanowires and carbon nanotubes on oxidation resistance for SiC-coated C/C composites

To protect carbon/carbon composites (C/Cs) against oxidation, SiC coating toughened by SiC nanowires (SiCNWs) and carbon nanotubes (CNTs) hybrid nano-reinforcements was prepared on C/Cs by a two-step technique involving electrophoretic co-deposition and reactive melt infiltration. Co-deposited SiCNWs and CNTs with different shapes including straight-line, fusiform, curved and bamboo dispersed uniformly on the surface of C/Cs forming three-dimensional networks, which efficiently refined the SiC grains and meanwhile suppressed the cracking deflection of the coating during the fabrication process. The presence of SiCNWs and CNTs contributed to the formation of continuous glass layer during oxidation, while toughed the coating by introducing toughing methods such as bridging effect, crack deflection and nanowire pull out. Results showed that after oxidation for 45 h at 1773 K, the weight loss percentage of SiC coated specimen was 1.35%, while the weight gain percentage of the SiCNWs/CNTs reinforced SiC coating was 0.03052% due to the formation of continuous glass layer. After being exposed for 100 h, the weight loss percentage of the SiCNWs/CNTs reinforced SiC coating was 1.08%, which is relatively low.     

Microstructure and ablation behavior of SiC coated C/C–SiC–ZrC composites prepared by a hybrid infiltration process

In this study, C/C–SiC–ZrC composites coated with SiC were prepared by precursor infiltration pyrolysis combined with reactive melt infiltration. The pyrolysis behavior of the hybrid precursor was investigated using thermal gravimetric analysis-differential scanning calorimetry, X-ray diffraction, and scanning electron microscopy techniques. The microstructure and ablation behavior of the composites were also investigated. The results indicate that the composites exhibit an interesting structure, wherein a ceramic coating composed of SiC and a small quantity of ZrC covers the exterior of the composites, and the SiC–ZrC hybrid ceramics are partially embedded in the matrix pores and distributed around the carbon fibers as well. The composites exhibit good ablation resistance with a surface temperature of over 2300 °C during ablation. After ablation for 120 s, the mass and linear ablation rates of the composites are 0.0026 g/s and 0.0037 mm/s, respectively. The great ablation resistance of the composites is attributed to the formation of a continuous phase of molten SiO₂ containing SiC and ZrO₂, which seals the pores of the composites during ablation.     

Enhanced bonding strength and thermal cycling performance of MoSi2–CrSi2–SiC–Si coating for carbon/carbon composites by surface modification via blasting treatment

Before the preparation of MoSi₂–CrSi₂–SiC–Si coating, blasting treatment of carbon/carbon (C/C) composites, as a surface modification method, was conducted under oxyacetylene torch. MoSi₂–CrSi₂–SiC–Si coating was prepared on the treated C/C composites by pack cementation, where an interlock interface was formed between the coating and the C/C substrate. After blasting treatment, the thermal expansion coefficient mismatch between the coating and C/C substrate was alleviated efficiently, and the bonding strength of the coating was increased by 45.6% and reached 26.2 MPa. To simulate the real working condition, thermal cycling test was conducted under oxyacetylene torch from 1600 °C to room temperature to construct an environment of combustion gas erosion. Due to the improvement of bonding strength and the alleviation of thermal expansion coefficient mismatch between the coating and the C/C substrate, thermal cycling performance of MoSi₂–CrSi₂–SiC–Si coating was enhanced. After 25 thermal cycles, the mass loss of the coated C/C composites without blasting treatment was up to 2.4%, and the C/C substrate was partially exposed. In contrast, the mass loss of the coated C/C composites with blasting treatment was only 1.1%.     

In-situ synthesis of SiC nanofibers for improving the oxidation resistance of graphite

In order to improve the oxidation resistance of graphite, a SiC/ZrO₂-SiC nanofibers multiphase coating was developed on a graphite substrate using the pack cementation and slurry painting techniques. The microstructure of the coating was characterized by X-ray diffraction and scanning electron microscopy. The HSC chemistry software package was used for the thermodynamic calculations. The isothermal oxidation test of the coated samples was performed at 1773 K in air. A 500 µm thick gradient C–SiC transition layer was formed at the graphite-coating interface SiC nanofibers with the diameter in the range of 32–88 nm were observed on the coating whose growth was ascribed to the gas phase reaction of SiO with CO. The oxidation test results revealed that the SiC nanofibers and thermally stable phase ZrSiO₄ were the mainly effective tools protecting graphite from oxidation.