Bimodal microstructure ZrB2-MoSi2 coating prepared by atmospheric plasma spraying for carbon/carbon composites against long-term ablation

To protect carbon/carbon composites against long-term ablation, a bimodal microstructure ZrB₂-MoSi₂ coating, consisting of an outer ZrB₂-MoSi₂ layer modified by Y₂O₃ and an inner basal ZrB₂-MoSi₂ layer, was prepared by atmospheric plasma spraying. The microstructure, phase composition and ablation resistance of the proposed coating were investigated in detail. Results showed that the bimodal coating maintained integrity in structure except for phase composition. There was no visible interlayer between the inner ZrB₂-MiSi₂ layer and the outer modified one. Mass ablation rate of the bimodal microstructure ZrB₂-MoSi₂ coated C/C composites was −2.02 × 10⁻³ g/s under an oxyacetylene flame ablation at 1873 K for 600 s, which exhibited better ablation resistance than a single ZrB₂-MoSi₂ coating. The excellent ablation resistance was ascribed to the positive effect of Y₂O₃, which not only pined in the glassy phase and alleviated the volatilization of SiO₂ glass phase by reacting with SiO₂ to form high viscosity of Y₂SiO₅, but also stabilized ZrO₂ and promoted its recrystallization and growth.     

Ultra-high temperature ceramic coating for carbon/carbon composites against ablation above 2000 K

To improve the ablation resistance of carbon/carbon composites at the temperature above 2000 K, a ZrB₂-SiC-ZrC ultra-high temperature ceramic coating was prepared by combination of supersonic atmosphere plasma spray (SAPS) and reaction melt infiltration. The micro-holes in ZrB₂-Si-ZrC coating prepared by SAPS were effectively filled and the compactness and interface compatibility between the coating and C/C composites was improved through the reaction melt infiltration process. The ultra-high temperature ceramic coating exhibited good ablation resistance under oxyacetylene torch ablation above 2000 K. After ablation for 120 s, the mass and linear ablation rates of the ZrB₂-SiC-ZrC coated C/C samples were only ?0.016 × 10^?3 g/s and 1.30 µm/s, respectively. Good ablation resistance of the ultra-high temperature ceramic coating is mainly attributed to the dense coating structure and the improvement of interface compatibility between the coating and C/C composites.     

Ablation resistance of HfB2-SiC coating prepared by in-situ reaction method for SiC coated C/C composites

To improve the ablation resistance of SiC coating, HfB₂-SiC coating was prepared on SiC-coated carbon/carbon (C/C) composites by in-situ reaction method. Owing to the penetration of coating powders, there is no clear boundary between SiC coating and HfB₂-SiC coating. After oxyacetylene ablation for 60 s at heat flux of 2400 kW/m², the mass ablation rate and linear ablation rate of the coated C/C composites were only 0.147 mg/s and 0.267 µm/s, reduced by 21.8% and 60.0%, respectively, compared with SiC coated C/C composites. The good ablation resistance was attributed to the formation of multiple Hf-Si-O glassy layer including SiO₂, HfO₂ and HfSiO₄.     

Design of an inlaid interface structure to improve the oxidation protective ability of SiC–MoSi2–ZrB2 coating for C/C composites

To improve the oxidation protective ability of SiC–MoSi₂–ZrB₂ coating for carbon/carbon (C/C) composites, pre-oxidation treatment and pack cementation were applied to construct a buffer interface layer between C/C substrate and SiC–MoSi₂–ZrB₂ coating. The tensile strength increased from 2.29 to 3.35 MPa after pre-oxidation treatment, and the mass loss was only 1.91% after oxidation at 1500 °C for 30 h. Compared with the coated C/C composites without pre-oxidation treatment, after 18 thermal cycles from 1500 °C and room temperature, the mass loss was decreased by 30.6%. The improvements of oxidation resistance and mechanical property are primarily attributed to the formation of inlaid interface between the C/C substrate and SiC–MoSi₂–ZrB₂ coating.     

A SiC–Si–ZrB2 multiphase oxidation protective ceramic coating for SiC-coated carbon/carbon composites

In order to improve the oxidation protective ability of SiC-coated carbon/carbon (C/C) composites, a SiC–Si–ZrB₂ multiphase ceramic coating was prepared on the surface of SiC-coated C/C composite by the process of pack cementation. The microstructures of the coating were characterized using X-ray diffraction and scanning electron microscopy. The coating was found to be composed of SiC, Si and ZrB₂. The oxidation resistance of the coated specimens was investigated at 1773 K. The results show that the SiC–Si–ZrB₂ can protect C/C against oxidation at 1773 K for more than 386 h. The excellent oxidation protective performance is attributed to the integrity and stability of SiO₂ glass improved by the formation of ZrSiO₄ phase during oxidation. The coated specimens were given thermal shocks between 1773 K and room temperature for 20 times. After thermal shocks, the residual flexural strength of the coated C/C composites was decreased by 16.3%.     

TaB2–SiC–Si multiphase oxidation protective coating for SiC-coated carbon/carbon composites

To improve the oxidation resistance of the carbon/carbon (C/C) composites, a TaB₂–SiC–Si multiphase oxidation protective ceramic coating was prepared on the surface of SiC coated C/C composites by pack cementation. Results showed that the outer multiphase coating was mainly composed of TaB₂, SiC and Si. The multilayer coating is about 200 μm in thickness, which has no penetration crack or big hole. The coating could protect C/C from oxidation for 300 h with only 0.26 × 10^?2 g²/cm² mass loss at 1773 K in air. The formed silicate glass layer containing SiO₂ and tantalum oxides can not only seal the defects in the coating, but also reduce oxygen diffusion rates, thus improving the oxidation resistance.     

UHTC–carbon fibre composites: Preparation,oxyacetylene torch testing and characterisation

Current generation carbon–carbon (C–C) and carbon–silicon carbide (C–SiC) materials are limited to service temperatures below 1800 °C and materials are sought that can withstand higher temperatures and ablative conditions for aerospace applications. One potential materials solution is carbon fibre-based composites with matrices composed of one or more ultra-high temperature ceramics (UHTCs); the latter are intended to protect the carbon fibres at high temperatures whilst the former provides increased toughness and thermal shock resistance to the system as a whole. Carbon fibre–UHTC powder composites have been prepared via a slurry impregnation and pyrolysis route. Five different UHTC compositions have been used for impregnation, viz. ZrB₂, ZrB₂–20 vol% SiC, ZrB₂–20 vol% SiC–10 vol% LaB₆, HfB₂ and HfC. Their high-temperature oxidation resistance has been studied using a purpose built oxyacetylene torch test facility at temperatures above 2500 °C and the results are compared with that of a C–C benchmark composite.     

Effect of the surface microstructure of SiC inner coating on the bonding strength and ablation resistance of ZrB2-SiC coating for C/C composites

The present study has been conducted in order to investigate the effect of the surface morphology of SiC inner coating on the bonding strength and ablation resistance of the sprayed ZrB₂-SiC coating for C/C composites. The microstructure of SiC inner coatings prepared by chemical vapor deposition and pack cementation at different temperatures were analyzed by X-ray diffraction, scanning electron microscopy, and 3D Confocal Laser Scanning Microscope. Tensile bonding strength and oxyacetylene ablation testing were used to characterize the bonding strength and ablation resistance of the sprayed ZrB₂-SiC coating, respectively. Results show that SiC inner coating prepared by chemical vapor deposition has a smooth surface, which is not beneficial to improve the bonding strength and ablation resistance of the sprayed ZrB₂-SiC coating. SiC inner coating prepared by pack cementation at 2000 °C has a rugged surface with the roughness of 72.15 µm, and the sprayed ZrB₂-SiC coating with it as inner layer exhibits good bonding strength and ablation resistance.     

Improved ablation resistance of C–C composites using zirconium diboride and boron carbide

Zirconium diboride and boron carbide particles were used to improve the ablation resistance of carbon–carbon (C–C) composites at high temperature (1500 °C). Our approach combines using a precursor to ZrB₂ and processing them with B₄C particles as filler material within the C–C composite. An oxyacetylene torch test facility was used to determine ablation rates for carbon black, B₄C, and ZrB₂–B₄C filled C–C composites from 800 to 1500 °C. Ablation rates decreased by 30% when C–C composites were filled with a combination of ZrB₂–B₄C particles over carbon black and B₄C filled C–C composites. We also investigated using a sol–gel precursor method as an alternative processing route to incorporate ZrB₂ particles within C–C composites. We successfully converted ZrB₂ particles within C–C composites at relatively low temperatures (1200 °C). Our ablation results suggest that a combination of ZrB₂–B₄C particles is effective in inhibiting the oxidation of C–C composites at temperatures greater than 1500 °C.     

High-temperature erosion resistance and aerodynamic oxidation mechanism of multi-layer MoSi2–CrSi2–Si/SiC coated carbon/carbon composites in a wind tunnel at 1873 K

The high-temperature erosion resistance of multi-layer MoSi₂–CrSi₂–Si/SiC coated carbon/carbon (C/C) composites was investigated in a wind tunnel. To study the aerodynamic oxidation mechanism and analyze the failure of the coated C/C composites, the shear force and bending moment distribution of the tested specimens in a wind tunnel were calculated. Flexural strengths and thermogravimetric analysis of the coated specimens were measured. These results show that the multi-layer MoSi₂–CrSi₂–Si/SiC antioxidation coating can protect the C/C composites from high-temperature erosion in a wind tunnel at 1873 K for more than 86 h. Due to the high viscosity of SiO₂, the multi-layer coating lacked effective oxidation resistance from 900 to 1500 K, resulting in extensive mechanical damage and the fracture of the tested specimens.     

ZrB2-based composites toughened by as-received and heat-treated short carbon fibers

In order to improve the fracture toughness of ZrB₂ ceramics, as-received and heat treated short carbon fiber reinforced ZrB₂-based composites were fabricated by hot pressing. The toughening effects of the fibers were studied by investigating the relative density, phase composition, microstructure and mechanical properties of the composites. It was found that the densification behavior, microstructure and mechanical properties of the composites were influenced by the fibers’ surface condition. The heat treated fiber was more appropriate to toughen the ZrB₂-based composites, due to the high graphitization degree, low surface activity and weak interfacial bonding. As a result, the fracture toughness of the composites with heat-treated fiber is 7.62 ± 0.12 MPa m^1/2, which increased by 10% as compared to the composites with as-received fiber (6.89 ± 0.16 MPa m^1/2).     

Oxidation behavior and microstructure evolution of SiC-ZrB2-ZrC coating for C/C composites at 1673 K

To protect carbon/carbon (C/C) composites against oxidation, a SiC-ZrB₂-ZrC coating was prepared by the in-situ reaction between ZrC, B₄C and Si. The thermogravimetric and isothermal oxidation results indicated the as-synthesized coating to show superior oxidation resistance at elevated temperatures, so it could effectively protect C/C composites for more than 221 h at 1673 K in air. The crystalline structure and morphology evolution of the multiphase SiC-ZrB₂-ZrC coating were investigated. With the increase of oxidation time, the SiO₂ oxide layer transformed from amorphous to crystalline. Flower-like and flake-like SiO₂ structures were generated on the glass film during the oxidation process of SiC-ZrB₂-ZrC coating, which might be ascribed to the varying concentration of SiO. The oxide scale presented a two-layered structure ~130 µm thick after oxidation, consisting of a SiO₂-rich glass layer containing ZrO₂/ZrSiO₄ particles and a Si-O-Zr layer. The multiphase SiC-ZrB₂-ZrC ceramic coating exhibited much better oxidation resistance than monophase SiC, ZrB₂ or ZrC ceramic due to the synergistic effect among the different components.     

Ablation resistance of HfC coating reinforced by HfC nanowires in cyclic ablation environment

To improve the ablation resistance of carbon/carbon composites in cyclic ablation environment, SiC/HfC ceramic coating reinforced by HfC nanowires was prepared. The microstructure, bonding strength, coefficient of thermal expansion and cyclic ablation resistance of the as-prepared coating were investigated. After incorporating HfC nanowires, the bonding strength between inner SiC coating and outer HfC coating was increased. HfC nanowires could relieve the coefficient of thermal expansion mismatch between inner and outer coating and improve the toughness of the outer coating. By introducing HfC nanowires, the coated sample’s cyclic ablation resistance was improved. After cyclic ablation under oxyacetylene flame for 60 s × 3, the mass and linear ablation rates of the coated sample with HfC nanowires were only 0.444 mg/s and −0.767 μm/s, respectively.     

Ablation behaviour of a TaC coating on SiC coated C/C composites at different temperatures

To improve the ablation resistance of carbon/carbon (C/C) composites, a TaC coating was prepared by supersonic plasma spraying on SiC coated C/C composites. The microstructure and morphology of the coatings were characterised by Scanning Electron Microscopy and X-ray diffraction. The ablation properties were studied at different temperatures under oxyacetylene torch. At 2100 °C, the oxides were blown away and resulted in high ablation rates: 1.2×10^?2 mm/s and 3.9×10^?3 g/s. However, most oxides can remain in ablation centre and serve as a coating at low temperature (1900 and 1800 °C). Therefore, the TaC/SiC coated samples exhibited zero linear ablation rate and lower mass ablation rate.     

MoSi2-based oxidation protective coatings for SiC-coated carbon/carbon composites prepared by supersonic plasma spraying

To protect carbon/carbon (C/C) composites against oxidation, MoSi₂-based oxidation protective coatings for SiC-coated carbon/carbon composites were prepared on them by supersonic plasma spraying. The MoSi₂-based coatings primarily consist of MoSi₂, Mo₅Si₃ and glassy SiO₂. Only a few pinholes and some microcracks are observed on the surface and no through-thickness cracks penetrate the cross-section. Weight loss of the MoSi₂-based coated specimens is only 1.14% after 400 h oxidation in air at 1773 K and the coated C/C composites remain intact after 11 thermal cycles between 1773 K and room temperature. The outstanding anti-oxidation ability is mainly attributable to the formation of SiO₂-based layer on the surface of MoSi₂-based coatings.     

Heat conduction mechanisms in hot pressed ZrB2 and ZrB2–SiC composites

Thermal diffusivity and conductivity of hot pressed ZrB₂ with different amounts of B₄C (0–5 wt%) and ZrB₂–SiC composites (10–30 vol% SiC) were investigated experimentally over a wide range of temperature (25–1500 °C). Both thermal diffusivity and thermal conductivity were found to decrease with increase in temperature for all the hot pressed ZrB₂ and ZrB₂–SiC composites. At around 200 °C, thermal conductivity of ZrB₂–SiC composites was found to be composition independent. Thermal conductivity of ZrB₂–SiC composites was also correlated with theoretical predictions of the Maxwell–Eucken relation. The dominated mechanisms of heat transport for all hot pressed ZrB₂ and ZrB₂–SiC composites at room temperature were confirmed by Wiedemann–Franz analysis by using measured electrical conductivity of these materials at room temperature. It was found that electronic thermal conductivity dominated for all monolithic ZrB₂ whereas the phonon contribution to thermal conductivity increased with SiC contents for ZrB₂–SiC composites.     

Microstructure and ablation behavior of SiC coated C/C–SiC–ZrC composites prepared by a hybrid infiltration process

In this study, C/C–SiC–ZrC composites coated with SiC were prepared by precursor infiltration pyrolysis combined with reactive melt infiltration. The pyrolysis behavior of the hybrid precursor was investigated using thermal gravimetric analysis-differential scanning calorimetry, X-ray diffraction, and scanning electron microscopy techniques. The microstructure and ablation behavior of the composites were also investigated. The results indicate that the composites exhibit an interesting structure, wherein a ceramic coating composed of SiC and a small quantity of ZrC covers the exterior of the composites, and the SiC–ZrC hybrid ceramics are partially embedded in the matrix pores and distributed around the carbon fibers as well. The composites exhibit good ablation resistance with a surface temperature of over 2300 °C during ablation. After ablation for 120 s, the mass and linear ablation rates of the composites are 0.0026 g/s and 0.0037 mm/s, respectively. The great ablation resistance of the composites is attributed to the formation of a continuous phase of molten SiO₂ containing SiC and ZrO₂, which seals the pores of the composites during ablation.     

Significance of hot pressing parameters and reinforcement size on sinterability and mechanical properties of ZrB2–25 vol% SiC UHTCs

The influences of hot pressing parameters and SiC particle size on the bulk density, the average ZrB₂ grain size and Vickers hardness of ZrB₂–25 vol% SiC ultrahigh temperature ceramic composites were investigated. In this paper, the Taguchi methodology (An L9 orthogonal array) was used to specify the contributions of four parameters: the hot pressing temperature, holding time, applied pressure and SiC particle size. The experimental procedure included nine tests for four parameters with three levels which were employed to optimize the process parameters. The statistical analyses recognized the hot pressing pressure and temperature as the most consequential parameters affecting the density and hardness of ZrB₂–SiC composites. The SiC particle size and holding time were specified as the most effective parameters on the average ZrB₂ grain size. The bulk density, average ZrB₂ grain size, Vickers hardness and fracture toughness of the sample, hot pressed at optimal conditions (1850 °C, 90 min, 16 MPa and 200 nm), reached about 5.36 g/cm³, 10.03 µm, ~17.1 GPa and 5.9 MPa m^1/2, respectively. The confirmation test, carried out under optimum conditions, showed that the experimental results were relatively equal to the predicted values from the Taguchi prediction model. Finally, the mechanisms of enhanced fracture toughness of the hot pressed ZrB₂–SiC ceramic composites were discussed.     

Dynamic oxidation and protection of the PAN pre-oxidized fiber C/C composites

Pre-oxidized fibers as reinforcement are candidates for reducing the overall cost of C/C composites with superior properties. This study investigated the dynamic oxidation and protection of the pre-oxidized fiber C/C composites (Pr-Ox-C-C). According to the Arrhenius equation, the oxidation kinetics of the Pr-Ox-C-C consisted of two different oxidation mechanism with the transition point was at about 700 °C. Scanning electron microscopy investigation showed that oxidation initiated from the fiber/matrix interface of composites, whereas the matrix carbon was easily oxidized. To improve the anti-oxidant properties of Pr-Ox-C-C, a ceramic powder-modified organic silicone resin/ZrB₂-SiC coating was prepared by the slurry method. The coated samples were subjected to isothermal oxidation for 320 h at 700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C with incurred weight losses of ? 1.6%, 0.77%, ? 1.28%, 0.68% and 1.19%, respectively. After 110 cycles of thermal shock between 1100 °C and room temperature, a weight loss of 1.30% was obtained. The Arrhenius curve presented four different phases and mechanisms for coating oxidation kinetics. The excellent oxidation resistance properties of the prepared coating could be attributed to the inner layer which was able to form B₂O₃-Cr₂O₃-SiO₂ glass to cure cracks, and the ZrB₂-SiC outer layer that could provide protective oxides to reduce oxygen infiltration and to seal bubbles.     

The ablation behavior and mechanical property of C/C-SiC-ZrB2 composites fabricated by reactive melt infiltration

In order to improve the ablation resistance of carbon/carbon (C/C) composites, SiC-ZrB₂ di-phase ceramic were introduced by reactive melt infiltration. The ablation properties of these composites were evaluated by oxyacetylene torch with a heat flux of 2.38 MW/m² for 60 s. Compared with the pure C/C composites, the C/C-SiC-ZrB₂ composites show a significant improvement in the ablation resistance, and the linear and mass ablation rates decreased from 10.28×10⁻³ mm/s to 6.72×10⁻³ mm/s and from 3.08×10⁻³ g/s to 0.61×10⁻³ g/s, respectively. After ablation test, the flexural strength retentions of the C/C and C/C-SiC-ZrB₂ composites near the ablated center region are 39.7% and 81.6%, respectively. The higher strength retention rate of C/C-SiC-ZrB₂ composites was attributed to the introduction of SiC-ZrB₂ ceramic phases, which have excellent ablation resistant property. During ablation test, an ‘embedding structure’ of Zr-O-Si glass layer was formed, which could act as an effective barrier for oxygen and heat. The oxide ceramic coating could protect the C/C-SiC-ZrB₂ composites from further ablation, and thus contribute to retaining the mechanical property of C/C-SiC-ZrB₂ composites after ablation.