原位生成TiC对Al-8Fe合金显微组织的影响

通过XRD，SEM，TEM等手段研究了Al-8Fe常规铸态合金原位生成不同TiC粒子含量时相组成及显微组织的变化，以及Ti同α（Al）基体及Al3Fe相之间的界面关系。结果表明：随着TiC含量的增加，Al-8Fe合金中Al3Fe相及缩松的形貌及尺寸明显发生了变化，TiC与α（Al）基体之间界面干净，而与Al3Fe之间则存在一过渡层。     

快速凝固Al-2.5Ti-2.5Fe合金显微组织及热稳定性的研究

采用单辊旋铸技术制备Al-2.5Ti-2.5Fe合金薄带，利用DSC分析、X射线衍射和透射电镜来分析该合金的急冷态和退火态组织，测定了合金在 同温度下退火10h后的显微硬度。结果表明，快速凝固Al-2.5Ti-2.5Fe合金稳冷态组织中存在两种初生相：Al3Ti相和Al5Ti2相；而经300℃退火10h后，将发生亚稳相Al5Ti向稳定相Al3Ti 的转变；经400℃退火10h后，组织中出现了平衡稳定相Al13Fe4，且在热处理过程中弥散析出Al3Ti相。     

快速凝固Al—Ti—Fe系合金的组织演化

采用单辊旋铸技术制备Al-2.5Ti-2.5Fe,Al2.5Ti-2.5Fe-2.5V和Al-2.5Ti-2.5Fe-2.5Cr(at%，下同）合金薄带，利用X射线衍射（XRD）和透射电镜（TEM）分析了这些合金的急冷态和退火态组织。结果表明：快速凝固Al-2.5Ti-2.5Fe合金急冷态组织中存在Al3Ti和Al5Ti2两种初生相，快凝合金经400℃退火10h后，组织中出现了Al13Fe4相，在450℃退火，组织中析出了弥散Al3Ti相；快速凝固Al-2.5Ti-2.5Fe-2.5V合金急冷态组织中存在Al11V相和Al80V20相，400℃退火10h后，初生Al11V相转变为Al80V20相，且固溶在α-Al基体中的Ti,Fe以Al23Ti9相和Al13Fe4相的形式析出；快速凝固Al-2.5Ti-2.5Fe-2.5Cr合金急冷态组织中存在Al3Ti和Al13Cr2两种初生相，快凝合金经300℃退火10h后，组织中析出了Al13Cr2和Al3Ti两种弥散相，400℃退火10h时后组织中出现了Al13Fe4相。     

快速凝固Fe—C—Sn合金的显微组织

研究了经激光表面熔化处理的Fe-4％C-10％Sn合金的显微组织,发现在激光熔化区上部存在一种非晶相,而在其底部存在由α-Fe和一种bct相组成的显微组织,在熔化区其它区域存在含细小孪晶的马氏体。     

原位生成TiC对快凝Al—Fe—V—Si合金中“块状相”生成的影响

对含有原位生成TiC粒子的快凝Al-Fe-V-Si合金中的显微结构进行了电镜观察。结果表明：在Al6Fe相形成的温度范围内,TiC粒子消除了初生Al6Fe块状相,诱发了初生AlmFe相,AlmFe相以包裹TiC粒子的形成生长成类球状形貌,消除了边角效应。并用连续冷却方式下的形核理论对TiC粒子的原位生成对合金中各相的形核动力学影响进行了分析与计算,与试验结果有较好的吻合。     

快速凝固Al—20Si—5Fe合金的退火组织变化

利用ＸＲＤ、ＤＳＣ以及ＴＥＭ方法研究了快速凝固Ａｌ－２０Ｓｉ－５Ｆｅ合金退火态的微观组织、弥散相结构和相转变。结果表明,快凝Ａｌ－２０Ｓｉ－５Ｆｅ合金组织中存在两种弥散相,δ－Ａｌ４ＦｅＳｉ２和初生Ｓｉ相,退火温度低于３１０℃时,δ－Ａｌ４ＦｅＳｉ２相未明显粗化;当退火温度高于３１０℃时,亚稳相δ－Ａｌ４ＦｅＳｉ２转变成稳定相β－Ａｌ５ＦｅＳｉ,β－Ａｌ５ＦｅＳｉ相随退火温度的提高而明显粗化。高温     

快速凝固Al-Zr-Ti合金的组织结构

利用透射电子显微镜研究了快速凝固Al-Zr-Ti合金的组织结构。结果表明：快凝合金的显微硬度与其显微组织密切相关，快凝合金激冷态组织显示出单一相－过饱和Al基固溶体，此时显微硬度为220HV。快凝合金经420℃退火4h，具有立方结构的亚稳相L1-Al3(Zr,Ti) 析出，此时显微硬度达到峰值260HV。而经420℃退火20h，则L12相转变为DO23相，同时，显微硬度下降到150HV。     

快速凝固二元Al－Cr合金的退火组织及显微硬度

研究了快速凝固Ａｌ－Ｃｒ合金的微观组织及显微硬度，确定了α－Ａｌ过饱和固溶体在退火过程中沉淀析出相为θ－Ａｌ７Ｃｒ，析出开始温度取决于过饱和度和沉淀位置．     

外加法和原位法生成Al-8Fe/TiC复合材料显微组织的研究

通过外加法和原位生成法制备了常规凝固Al-8Fe/TiC复合材料材料,通过OM和TEM等手段研究了两种材料的显微组织,发现外加法制备的合金中TiC粒子比较粗大,而且TiC粒子容易产生聚集,在TiC颗粒与α-Al基体界面处有过渡层存在.而原位法生成的合金中TiC粒子细小,均匀分布于基体之上,而且和α-Al基体在界面处接合紧密,没有污染相和其它反应产物的生成.     

原位TiC颗粒对喷射沉积7093铝合金微观组织的影响

采用喷射沉积及原位反应喷射沉积方法制备7093铝合金及7093+TiC铝合金,研究试验合金420℃热挤压及不同固溶处理后的微观组织和力学性能。探索原位TiC颗粒对喷射沉积7093铝合金组织的影响。结果表明,原位TiC颗粒能够提高喷射沉积7093铝合金的再结晶温度10℃,当固溶温度达到490℃时,7093+TiC铝合金中的富Cu颗粒基本溶解,但并未出现过烧现象。采用450℃×3h+480℃×3h+120℃×24h的制度处理后,7093+TiC铝合金的抗拉强度达754 MPa,伸长率达7.1%。     

原位TiC颗粒含量对近液相线铸造7075铝合金二次加热组织的影响

采用原位反应近液相线铸造法制备具有不同原位TiC颗粒含量的TiC_p/7075铝基复合材料,在7075铝合金固-液两相区间(477～635 ℃)的580和600 ℃进行二次加热并保温20 min,水淬固定其半固态组织,应用Image Pro Plus软件测量平均晶粒尺寸及形状因子,研究原位TiC颗粒含量对该合金二次加热组织的影响.结果表明:当原位TiC颗粒质量分数为0～4.4%时,随着原位TiC颗粒质量分数增加,合金铸态组织直接转变为等轴晶组织,且在二次加热过程中,原位TiC颗粒对晶粒的长大行为具有明显的抑制作用;在相同的二次加热条件下,4.4%TiC_p/7075铝基复合材料的平均晶粒尺寸比7075基体合金的减少30～40 μm,更加适合于半固态触变成形.     

Morphology and microstructure of rapidly solidified tin-lead alloy powders

Sn60Pb40 al oy powders were fabricated using the planar flow casting （PFC） atomization process. By using OM, SEM and EPMA, the characteristics of the morphologies and microstructures of the powders have been investigated. It is observed that the environment of ambient gas in the atomization box has great effects on the morphology of the al oy powders. The microstructures of Sn60Pb40 al oy powders produced by the PFC atomization process are completely composed of eutectic, which is made up of both oversaturated αsolid solution and β solid solution. The microstructures of smal size powders are extraordinarily undeveloped dendritic eutectic, in which the large majority of the α phase appears nearly spherical, evidently since the cooling rate is higher and the under-cooling is larger. As for the large size powders, since the cooling rate and undercooling are relatively low, lamel ar α phase apparently increases in the eutectic microstructures of these powders, and there is even typical lamellar eutectic structure clearly observed in some micro-areas. After remelting tests by DTA, the microstructures of smal size powders are transformed, which become composed of large crumby α phase and eutectic （α＋β）, while those of large size powders change into classical tin-lead structures of primary α phase plus lamellar eutectic （α＋β）. By studying the microstructures of tin-lead alloy powders, a model has been proposed to predict the microstructure formation of Sn60Pb40 al oy powders.     

Ca及其含量对快速凝固Mg-Zn合金组织和性能的影响

采用雾化-双辊急冷法成功制备了快速凝固（RS）Mg-Zn-Ca合金薄片,分析了不同含量的Ca对RS Mg-Zn合金微观组织、物相种类和热稳定性的影响。结果表明,RS Mg-6Zn合金的组织细小,晶粒尺寸为6～10μm,其相组成为α-Mg、Mg51Zn20相及少量的MgZn2和Mg2Zn3相。随着Ca的加入及其含量的增加,合金的组织显著细化（达到3～5μm）、析出相的数量大幅度增加,同时低熔点的Mg51Zn20相逐渐被大量热稳定的Ca2Mg6Zn3和Mg2Ca相替代,有效地阻碍了高温下晶界的运动,从而有助于合金组织热稳定性的提高;其中,RS Mg-6Zn-5Ca合金最为显著。     

原位TiC颗粒对7075铝合金组织和磨损特性的影响

采用原位反应近液相线铸造法制备具有不同原位TiC颗粒含量的TIC/7075铝合金复合材料,在不同干摩擦条件下测试了复合材料磨损特性,研究TiC原位颗粒对材料的组织及磨损性能的影响.结果表明,原位TiC颗粒对7075基体铝合金的铸态组织具有细化和球化作用,随着TiC颗粒含量的增加,复合材料的铸态组织由蔷薇状组织逐渐转变为等轴晶组织.在转速和压力相同的条件下,复合材料的磨损量随TiC颗粒含量的增加而降低,增强相TiC的加入显著提高了材料的磨损性能.     

热处理对定向凝固Ti-45Al-8Nb-（W,B,Y）合金组织的影响

研究两种热处理制度对Bridgeman法制备的典型定向凝固Ti-45Al-8Nb-（W,B,Y）（摩尔分数,%）合金组织的影响。两种典型的定向凝固显微组织分别为胞状生长形貌全片层组织和枝晶状生长形貌块状组织,对其热处理发现：热处理1250℃,24h＋900℃,30min＋AC能有效消除其定向凝固合金中的B2相,并将快速定向凝固时产生的块状组织转变为片层组织,在胞状间及枝晶臂上分别获得了宽度为150-200μm和50-100μm的柱状晶。热处理1400℃,2h＋900℃,30min＋AC能同时消除B2相、块状组织及凝固偏析,但造成了晶粒的严重长大。热处理能有效改进定向凝固合金的显微组织。     

深冷处理时间对快凝过共晶Al-Si-Fe合金组织与性能的影响

在固溶时效的基础上研究了深冷处理时间对过共晶Al-Si-Fe合金组织与性能的影响。结果表明,随着深冷时间的延长,组织变化不大,合金的力学性能得到了很大的提高;最佳的处理工艺为固溶处理(520℃×3 h)+深冷处理(-196℃×48 h)+时效处理(120℃×10 h)。     

Variety of solidification structures in Al-2.89%Fe alloy solidified under high magnetic field

考察了冷却速率、磁场强度及高梯度磁场对Al-2.89%Fe(质量分数)过共晶合金中Al3Fe 相形貌及分布规律的影响. 结果表明, 在无磁场条件下, 初生Al3Fe相沉积在试样下部; 施加12 T强磁场后, 初生Al3Fe相所受磁力作用和重力作用相平衡, 在整个试样中均匀分布, 且沿着易磁化方向[121]发生定向排列, 其取向程度不受冷却速率的影响, 但随着磁场强度的增大而加强; 在高梯度磁场中, 初生Al3Fe相所受磁力作用大于重力作用而偏聚在试样的上部, 且多个针状初生Al3Fe相结合在一起, 形成近似星状聚合体. 此外, 对强磁场的作用机理进行了分析和探讨.     

Microstructures of rapidly solidified Al-In immiscible alloy

1　ＩＮＴＲＯＤＵＣＴＩＯＮＴｈｅｒｅａｒｅｍａｎｙｂｉｎａｒｙｉｍｍｉｓｃｉｂｌｅｓｙｓｔｅｍｓｗｉｔｈａｍｉｓｃｉｂｉｌｉｔｙｇａｐｗｈｉｃｈｈａｖｅｂｅｅｎｉｄｅｎｔｉｆｉｅｄａｓｄｅｓｉｒ ａｂｌｅｆｏｒｍａｎｙａｐｐｌｉｃａｔｉｏｎｓ ,ｓｕｃｈａｓｅｎｇｉｎｅｅｒｉｎｇａｎｄｅｌｅｃｔｒｏｎｉｃｍａｔｅｒｉａｌｓ ,ｈｉｇｈｔｅｍｐｅｒａｔｕｒｅｓｕｐｅｒｃｏｎｄｕｃ ｔｏｒｓ,ａｎｄｓｅｌｆ ｌｕｂｒｉｃａｔｉｏｎｂｅａｒｉｎｇｓ[1～ 3] .Ｈｏｗｅｖｅｒ ,ｔｈｅｆａｂｒｉｃａｔｉｏｎｏｆｓｕ…