05CuPCrNi钢等离子弧焊焊接接头的组织与力学性能

 为了研究等离子弧焊在焊接薄板耐候钢时的优越性,对2 mm厚 05CuPCrNi耐大气腐蚀钢分别进行等离子弧焊与MAG焊(熔化极活性气体保护电弧焊)对接焊接,然后对焊接接头分别进行拉伸、弯曲、金相、硬度等试验,通过与MAG焊焊接接头的组织与力学性能对比,结果表明,与MAG焊相比,等离子弧焊时05CuPCrNi耐大气腐蚀钢焊接接头强度相对提高约6%,焊接接头组织为更均匀且细小的铁素体＋珠光体,并无MAG焊中出现的粗大块状铁素体及贝氏体,焊接热影响区较小,焊接接头弯曲性能良好,硬度值及硬度分布情况与MAG相近且无软化现象。     

Effect of Autogenous Arc Welding Processes on Tensile and Impact Properties of Ferritic Stainless Steel Joints

 The effect of autogeneous arc welding processes on tensile and impact properties of ferritic stainless steel conformed to AISI 409M grade is studied. Rolled plates of 4 mm thickness have been used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure, and fracture surface morphology of continuous current gas tungsten arc welding (CCGTAW), pulsed current gas tungsten arc welding (PCGTAW), and plasma arc welding (PAW) joints are evaluated and the results are compared. It is found that the PAW joints of ferritic stainless steel show superior tensile and impact properties when compared with CCGTAW and PCGTAW joints, and this is mainly due to lower heat input, finer fusion zone grain diameter, and higher fusion zone hardness.     

船用热轧钢板焊接性能研究

建立了热轧钢板焊接热影响区（HAZ）的连续冷却转变曲线（焊接CCT曲线）,以研究船用热轧钢板的焊接性能。根据所建立的焊接CCT曲线,选择了合理的焊接工艺对10mm厚的船用热轧钢板进行了手工电弧焊,并对焊后的焊接接头进行了宏观检验和X射线探伤、力学性能试验及冲击试验。借助金相显微镜和扫描电镜分析了CCT图中不同冷速条件下的显微组织和焊接接头的显微组织以及冲击断口形貌。试验结果表明：根据建立的焊接CCT曲线,所选择的手工电弧焊的焊接工艺是合理的,焊缝质量良好,焊接接头具有良好的综合性能。     

非调质低焊接裂纹敏感性(WDB620)钢的焊接

采用焊条电弧焊，气体保护焊，埋弧焊以及焊接热模拟的方法，研究了了WDB620钢焊接接头力学性能及抗冷裂性能，结果表明：当焊接热输小于35kJ/cm时，可以获得良好的焊接接头性能，非调质工艺生产的WDB620钢具有很低的焊接冷裂纹敏感性。     

Comparative Study on Processing Property Between CWW CO2 Gas Shielded Welding and SAW

 Cable welding wire (CWW) CO2 gas shielded welding is an innovative process arc welding with high efficiency, high quality and low consumption, in which cable wire is used as consumable electrode. CWW CO2 gas shielded welding and submerged arc welding (SAW) are used for contrast studies on processing property of high strength steel A36 used in ship structure. The results show that the shapes of weld seam, using CWW CO2 gas shielded welding and SAW, are good and no weld defect such as air hole, flaw, slag inclusion, incomplete fusion, lack of penetration and so on are found in the weld seam. Because the rotating of arc during CWW CO2 gas shielded welding process has a strong stirring effect on molten pool, the grain in the heat affected zone (HAZ) of the joints, using CWW CO2 gas shielded welding, is small. Tensile failure positions of joints by CWW CO2 gas shielded welding and SAW are all in the base metal, but tensile strength of CWW CO2 gas shielded welding joint is higher than that of SAW joint by an average of 2. 3%. The average impact energy of HAZ, using CWW CO2 gas shielded welding and SAW, is almost equal, but the average impact energy of the weld seam using CWW CO2 gas shielded welding is increased by 6%, and the average impact energy of the fusion line is increased by 7%. The 180° bending tests for the joints of CWW CO2 gas shielded welding and SAW are all qualified, and the joints hardness is all less than HV 355, but hardness of CWW CO2 gas shielded welding wire welding joint near the fusion line is obviously lower. It can be concluded that the properties of CWW CO2 gas shielded welding are better than those of the SAW joint, and CWW CO2 gas shielded welding is suitable for welding high strength steel A36 used in ship structure.     

海洋平台用S355G10+M厚钢板的焊接性研究

按照EN10225标准要求,对75 mm厚度规格海洋平台用S355G10+M钢板进行了堆焊硬度试验(BOP)、可控热拘束试验(CTS)以及热输入50 k J/cm埋弧焊对接接头系列力学性能试验,研究了钢板焊接热影响区(HAZ)的淬硬倾向、HAZ冷裂纹敏感性、焊接接头各部位抗拉强度、冲击韧性和裂纹尖端张开位移(CTOD)值的变化情况。结果显示S355G10+M厚钢板的HAZ最高硬度、焊接钢板冷裂纹、埋弧焊对接接头抗拉强度、低温冲击功均值、CTOD值等各项性能指标良好,满足海洋平台的焊接生产要求。     

Effect of Welding Processes on Tensile and Impact Properties, Hardness and Microstructure of AISI 409M Ferritic Stainless Joints Fabricated by Duplex Stainless Steel Filler Metal

The effect of welding processes such as shielded metal arc welding, gas metal arc welding and gas tungsten arc welding on tensile and impact properties of the ferritic stainless steel conforming to AISI 409M grade is studied. Rolled plates of 4 mm thickness were used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure and fracture surface morphology of the welded joints have been evaluated and the results are compared. From this investigatio.n, it is found that gas tungsten arc welded joints of ferritic stainless steel have superior tensile and impact properties compared with shielded metal are and gas metal arc welded joints and this is mainly due to the presence of finer grains in fusion zone and heat affected zone.     

Effect of welding processes on tensile, impact, hardness and microstructure of AISI 409M ferritic stainless joints fabricated using duplex stainless steel filler metal

 The present investigation is aimed at to study the effect of welding processes such as shielded metal arc welding, gas metal arc welding and gas tungsten arc welding on tensile and impact properties of the ferritic stainless steel conforming to AISI 409M grade. Rolled plates of 4 mm thickness were used as the base material for preparing single pass butt welded joints. Tensile and impact properties, micro hardness, microstructure and fracture surface morphology of the welded joints have been evaluated and the results are compared. From this investigation, it is found that gas tungsten arc welded joints of ferritic stainless steel showed superior tensile and impact properties compared with shielded metal arc and gas metal arc welded joints and this is mainly due to the presence of finer grains in fusion zone and heat affected zone.     

Evaluation of automatic girth weldability of pipeline in special conditions

To meet the requirements of pipeline consumers abroad, in this study, an automatic gas metal arc welding type of girth welding was performed with a heat input of no more than 0.25 kJ/mm and high-strength solid-wire matching for an X70 M large-diameter UOE pipeline.An integral evaluation of the X70 M pipeline girth weldability was performed with respect to the girth-weld cold-cracking sensitivity during the welding process and the strengthening, hardening, and embrittlement of the girth weld joint after girth welding in especially rigorous welding conditions with accelerated failure characteristics.The performance of the above girth weld joint with joints welded using the main construction-field girth welding procedure was compared to ensure the good girth weldability of the X70 M pipeline.The results of this study have important supervisory significance for field-construction girth welding.Finally, the girth weldability of the X70 M pipeline was found to satisfy the field construction requirements even when the welding conditions are especially rigorous.     

Microstructural and Mechanical Characterization of as Weld and Aged Conditions of AA2219 Aluminium Alloy by Gas Tungsten Arc Welding Process

In this article, Welding of AA2219 aluminium alloy using Gas tungsten arc welding process (GTAW) and evaluation of metallurgical, mechanical and corrosion properties of the joints are discussed. The weld samples were subjected to ageing process at the temperature range of 195°C for a period of 5 h to improve the properties. AA2219 aluminium plates of thickness of 25 mm were welded using gas tungsten arc welding (GTAW) process in double V butt joint configuration. The input parameters considered in this work are welding current, voltage and welding speed. Tensile strength and hardness were measured as performance characteristics. The variation in the properties were justified with the help of microstructures. The same procedures were repeated for post weld heat treated samples and a comparison was made between as weld condition and age treated conditions. The post weld heat samples had better tensile strength and hardness values on comparing with the as weld samples. Fracture surface obtained from the tensile tested specimen revealed ductile mode of failure.     

Influence of welding heat input on the HAZ of hot-rolled high strength steel

When welding the hot-rolled high strength steel manufacture by thermal-mechanical controlled process（TMCP）,there has a soften zone in the heat affected zone（HAZ）.Evaluate the welding quality though the research on the influence of softened zone’s width,hardness,strength by the different heat input. Take the 8mm thickness QSTE700TM that produced by Baosteel as an example and used the gas metal arc welding（GMAW,the CO₂ and Ar as the shield gas） welding method choose the high strength welding wire ER76-G（GB）、ER110S-G（AWS） as the welding consumer.Adjust the welding heat input range from 6.8 kJ/cm to 43.6 kJ/cm and found that as the heat input increased the tensile strength,fatigue strength of the welding structure and the hardness of the HAZ will decreased.But when using the lower heat input the quality of the welding structure can fulfil the usage request splendidly.And give the advise to increased the welding quality in detail:when keep the heat input in the scope of Q =6.8 -20 kJ/cm the good welding quality can be achieved successful.And the further research approve that when usage the lower strength welding consumer such as the ER50-6（GB）、ER70S-G（AWS） the welding structure can also achieved high quality for which the tensile strength can get about 700 MPa when use the lower welding heat input.Thus not only keep the welding quality,but also decreased the cost.     

耐火耐候钢焊接性能及焊接材料的研究

重点介绍了武钢技术中心高层办公大楼用WGJ510C2耐火耐候钢(14 mm 、25 mm)2种规格钢板与WQ-1埋弧焊丝匹配试验研究.按照工程提出的焊接技术条件,对武钢二热轧生产的WGJ510C2钢进行了埋弧焊对接性能试验,内容包括接头常规力学性能试验、高温拉伸性能试验、金相组织与硬度试验、电化学腐蚀性能试验.试验结果表明,采用WQ-1焊丝加CHF101焊剂匹配焊接WGJ510C2钢2种规格试板,接头常温拉伸强度和高温拉伸强度均满足WGJ510C2钢技术条件要求.焊缝、熔合线和热影响区低温冲击功大于140 J,接头各区电化学腐蚀电位相近,具有优良耐腐蚀性能,焊接接头综合性能指标完全满足高层建筑用钢焊接技术要求.     

超低碳微合金X100管线钢CO2焊焊接接头的组织和性能

 采用CO2焊接方法焊接X100管线钢,分析了不同焊接工艺下焊接接头组织和性能的变化特征。随着焊接热输入的增加,焊接接头的屈服强度和抗拉强度降低,焊缝和热影响区处的冲击吸收功呈现先增大后减小的变化趋势,而焊缝组织均以针状铁素体（AF）为主。焊接热输入为1.17 kJ/mm时,粗晶区的显微组织主要是贝氏体铁素体（BF）,强韧匹配性最为优异;当热输入增加至1.91 kJ/mm时,粗晶区的组织除了BF外,还出现了粒状贝氏体（GB）,强韧水平明显降低。综合考虑,可将1.17 kJ/mm作为X100管线钢CO2焊接时的最佳热输入。     

热输入对DP600激光焊组织和力学性能的影响

摘要：为了研究DP600钢的焊接性能,采用5种不同的激光焊接工艺进行焊接试验。结果表明,焊接接头表面成形质量良好,随着热输入的增加,上下熔宽逐渐增大;熔融区均为板条状马氏体组织,当热输入高于33J/mm时热影响区组织为马氏体、铁素体和少量的回火马氏体;当热输入低于33J/mm时,热影响区组织为马氏体和铁素体。在低热输入条件下,回火时间很短,马氏体未发生分解;在高的热输入条件下,回火时间较长,马氏体分解显著,热影响区中出现M3C型碳化物,碳化物形貌以球状和片状为主。从熔融区到母材,显微硬度值逐渐降低;焊接接头静态拉伸失效位置均在母材,拉伸断口为韧性断口,DP600钢激光焊接接头不存在软化现象。     

大型原油储罐用高强钢焊接性能研究

采用实物焊接和热模拟的方法研究了大型原油储罐用610MPa级高强度钢板大热输入焊接性能。结果表明,试验钢具有良好的抗大热输入量焊接的能力,原因是钢板中存在大量细小、弥散分布的TiN复合粒子,在焊接热循环的高温阶段,TiN粒子通过有效钉轧奥氏体晶界和促进铁素体晶内形核,抑制了焊接热影响区组织粗化;采用气电立焊和埋弧横焊焊接后,焊接对接接头的拉伸强度、低温冲击和冷弯性能优良,性能指标富余量大,试验钢板完全可以应用于10万m3及以上大型石油储罐的建造。     

Laser Welding of Ultra-Fine Grained Steel SS400

Steeliswidelyusedbecauseofitsgoodcompre hensive properties ,plentyofresourceandlowerprice .Thestrengthandtoughnessaretwoimpor tantpropertiesofsteels ,andpeoplemakeeffortstoincreasetheirvalues .Addingalloyingelementandcontrollingmicrostructurearetwobasicwaystoac complishtheaim .Therefinedmicrostructureob tainedbyprocessingtechniqueenablesthestrengthandtoughnessofsteeltobeincreasedwithoutaddingalloyingelementandtheratioofperformance costtobeincreased .Theultra finegrainedsteelshavefer ritegrains…     

14MnNbq钢超厚板(60 mm)焊接性能研究

重点介绍武钢首批试制的天兴洲大桥14MnNbq超厚板（60mm）与匹配的WQ系列桥梁钢埋弧焊丝研制进展情况。按照大桥局提出的焊接技术条件,对首批生产的14MnNbq钢（60mm）超厚板埋弧焊进行了大量的抗裂焊接工艺试验及接头性能试验。研究结果表明,14MnNbq钢超厚板（60mm）具有优良的抗冷裂纹性能及优良的接头综合性能。埋弧焊采用WQ系列焊丝匹配均达到了天兴洲大桥焊接技术条件,焊缝综合性能指标完全满足了大跨度大桥制造焊接技术的要求。     

铝硅焊片对异种铝合金电子束焊接焊缝组织性能的影响

采用电子束焊接技术,研究厚度为20 mm的AlCu0.5,AlSiCu,AlSi1三种高纯铝合金分别与6061铝合金的焊接效果。通过添加铝硅焊片来改善异种铝合金焊接的组织性能。对焊缝区域组织的分析表明,不同焊片添加量改变铝合金焊缝中的Si含量,从而对焊接的裂纹敏感性有显著的影响。当焊缝中Si含量在1%左右时容易产生裂纹缺陷,随着焊缝中Si含量的增高,焊缝中的裂纹逐渐减小,直至没有裂纹缺陷的产生。焊缝的硬度也随焊缝中Si含量的增高而变大。针对不同的高纯铝合金与6061的焊接,通过添加合适的铝硅焊片,能获取组织性能优异的焊缝。     

Effect of Welding Processes and Consumables on Tensile and Impact Properties of High Strength Quenched and Tempered Steel Joints

Quenched and tempered steels are prone to hydrogen induced cracking in the heat affected zone after welding. The use of austenitic stainless steel consumables to weld the above steel was the only available remedy because of higher solubility for hydrogen in austenitic phase. In this investigation, an attempt was made to determine a suitable consumable to replace expensive austenitic consumables. Two different consumables, namely, austenitie stain less steel and low hydrogen ferritic steel, were used to fabricate the joints by shielded metal are welding （SMAW） and flux cored arc welding （FCAW） processes. The joints fabricated by using low hydrogen ferritic steel consumables showed superior transverse tensile properties, whereas joints fabricated by using austenitic stainless steel consumables exhibited better impact toughness, irrespective of the welding process used. The SMAW joints exhibited superior mechanical and impact properties, irrespective of the consumables used, than their FCAW counterparts.     

Comparison of microstructure and properties between joints of FSW and TIG 316L austenitic stainless steel

FSW and TIG were conducted on 316L stainless steel.Variation during microstructure and properties in joints obtained by different welding methods was studied.The results show that the effect of severe mechanical stirring and intense plastic deformation creat a fine recrystallized grain in the welding joint during FSW.As for TIG,the temperature of welding joint exceeds the melting point of welded material itself.The entire welding process belongs to the solidification of a small molten pool;and the microstructure of the joint takes on a typical casting structure.When the welding parameters were selected appropriately,the average ultimate tensile strength of FSW joints can reach 493 MPa,which is 83.6%of base metal;the average elongation is 52.1%of base metal.The average ultimate tensile strength of TIG joints is 475 MPa, which is 80.5%of base metal;the average elongation is 40.8%of base metal.The tensile test of FSW joints is superior to the TIG joints.The microhardness of FSW joint compared to base metal and TIG joint having a significant improvement,which arel95.5 HV,159.7 HV and 160.7 HV,respectively;grain refinement strengthening plays an important role in enhancing the microhardness.The electrochemical corrosion tests show that the joint of FSW 316L austenitic stainless steel has a good corrosion resistance.