纳米SiO_2掺杂改性聚酯亚胺浸渍漆的性能

为了改善聚酯亚胺无溶剂浸渍漆的介电性能,采用微乳化和超临界反应的方法制备纳米SiO_2,并制备了一系列纳米掺杂量不同的SiO_2改性聚酯亚胺浸渍漆。分别对试样进行TEM表征、介电强度测试、体积电阻率测试、介电常数测试和粘度测试,结果表明:纳米SiO_2与基体之间相容性较好;在掺杂质量分数为10%时击穿强度比纯漆提高5.79%,达到23.04k V/mm;体积电阻率基本保持不变;介电常数随掺杂量略有下降;随掺杂量增加粘度有较大幅度下降。     

C级单组分无溶剂绝缘浸渍漆的研究

以间苯二甲酸二烯丙酯(DAIP)为主体树脂，环氧丙烯酸酯(VE)为改性剂，合成了一种新型C级单组分无溶剂绝缘浸渍漆；利用差热分析(DSC)、傅立叶红外变换光谱分析(FTIR)、热失重分析(TG)等方法，系统表征了漆液及其固化产物的性能。结果证明，该漆液粘度低、贮存期长，固化产物耐热性高、电气绝缘性能好，是一种综合性能较高的新型C级单组分无溶剂绝缘浸渍漆。     

SRN—M系列耐高温液浸变压器

中电电气集团在消化吸收国外先进技术的基础上自行研制生产的SRN—M系列耐高温液浸变压器．是集干式变压器和油浸式变压器优点为一体的配电设备。该产品采用了杜邦Nomex纸为基础的绝缘系统和Beta油相配合，经VPI真空加压设备多次浸渍H级无溶剂浸渍漆技术．提高了耐热等级和机械强度；在结构上设计为全密封．采用气垫式和压力释放阀保护。     

纳米复合粉体提高传统有机绝缘漆性能研究

研究了纳米复合粉体提高绝缘性能的方法．采用高频老化实验对变频漆的耐变频性能进行测定，结果表明，纳米复合绝缘材料在变频电机中使用寿命比普通绝缘材料提高7倍以上，且纳米颗粒分散工艺对材料性能影响较大．还对纳米材料提高绝缘材料耐变频性能的机理作了初步探讨，研究了氧化锌阀片侧面纳米复合绝缘漆的耐大电流冲击绝缘性能，结果表明，经纳米改性的传统侧面绝缘漆的耐大电流冲击性能超过1EC-60099-4国际标准．     

桐油-亚胺H级绝缘浸渍漆的研制

以顺丁烯二酸酐与二元胺为原料合成的中间体双马来酰亚胺,是既含有耐热性的酰亚胺环又具有高反应活性双键的低分子化合物。它与各种含不饱和双键的化合物或含活性氢的化合物反应,可获得不同大分子结构的改性聚双马来酰亚胺。本工作研制的H级绝缘浸渍漆,即是以含共轭三烯的桐油与双马来酰亚胺及其衍生物为主要原料,首先经     

磷系阻燃改性聚酯的流变性能

为探究 2-羧乙基苯基次磷酸(CEPPA)作为阻燃剂改性合成的阻燃聚酯的可纺性，分别用 DSC、TG、毛细管流变仪、旋转流变仪对阻燃改性聚酯进行热稳定性和流变性能测试。结果表明：阻燃聚酯的熔融温度、初始降解温度略微降低，残碳率提高，说明阻燃聚酯的加工温度可降低且成碳效果变好。阻燃聚酯是典型的非牛顿流体，其剪切黏度随着剪切速率的增加而降低，随温度的升高而降低，相比普通聚酯，改性后的阻燃聚酯黏度更低，流动性更好；阻燃改性聚酯的非牛顿指数n均小于1，且随着剪切速率的增加而减小；其黏流活化能随着剪切速率的增加而降低，反映了阻燃聚酯随着剪切速率的增加而对温度的敏感性变小。该研究结果可为阻燃聚酯纤维的制备工艺和参数调整提供参考。     

亚胺-环氧H級滴浸型无溶剂漆的研制

无溶剂浸渍漆目前有滴浸型与沉浸型两种。从使用情况分析,滴浸型更能充分体现无溶剂漆的优越性,尤其是快速固化的特点,更有利于实现生产自动化,还可以克服无溶剂漆贮存期短的缺点。近几年来,我国无溶剂漆发展迅速,E、B级无溶剂漆已在微电机及中小型电机上推广应用,F级无溶剂漆亦已研制成功,但H级无溶剂漆则为急待填补的空白。     

用烟籽油代替桐油制酚醛、酯胶树脂漆

本文报道采用烟籽油代替桐油制酚醛、酯胶树脂漆的研究成果。用价廉、来源广的烟籽油造漆,不但可节省桐油,而且工艺稳定,质量好,经济效益和社会效益显著。但烟籽油碘值低、颜色深、酸值高,难于聚合,因此造漆难度大,本研究用自制的CKD-1强力催化剂和采用新的聚合方法,解决了上述问题,提高了制漆性能,开发了造漆的新油源,降低了成本。该漆广泛用于涂刷门窗、地板、金属防锈、木材防腐、纸箱防潮以及作为电气绝缘涂料等,效果良好。     

新型共聚酯PETG的热性能及结晶性能

用差示扫描量热法(DSC)、和广角X衍射(WAXD)分析了新型共聚酯PETG的热性能与结晶性能.DSC的研究结果表明: PETG共聚酯的玻璃化转变温度随着CHDM含量的增加而升高;当EG/CHDM投料比为85/15、80/20和75/25时,共聚酯没有结晶峰和熔融峰,即处于一种完全无定形状态.X-衍射表明,DSC中不能结晶的样品即使经过热处理后仍不能结晶,共聚酯的结晶能力总是随着CHDM含量的增加先降低,经过一个最低点后再逐渐升高.     

环境友好磷系阻燃聚酯性能的研究

用红外光谱表征了环境友好磷系阻燃聚酯的结构,研究了环境友好磷系阻燃聚酯的特性粘数、DSC、氧指数、可纺性等性能。结果表明,磷系阻燃单体分子中的柔性链段亦被引入大分子主链中,使磷系阻燃聚酯的玻璃化温度(gθ)、熔点(θm)相应降低;磷系阻燃聚酯具有良好的阻燃性,当磷系阻燃单体质量分数4.5%时,磷系阻燃聚酯氧指数为32.8%。但由于侧基的空间体积较大也使磷系阻燃聚酯的结晶性有所降低,导致拉伸强度降低,实验结果表明磷系阻燃聚酯纤维的物性指标能够满足后加工要求。     

不饱和树脂绝缘阻燃漆的合成与性能研究

通过在环氧树脂中引入双键合成不饱和环氧树脂,加入稀释剂苯乙烯制备无溶剂型绝缘漆,通过电阻率和介电损耗对其绝缘性能进行表征.研究不同阻燃剂对绝缘漆体系的阻燃性能、电性能和力学性能的影响.通过DSC研究绝缘漆体系的固化工艺条件.实验结果表明,绝缘漆体系中当三聚氰胺磷酸盐（MP）质量分数为30%时,体系的阻燃性能达到UL0-94 V-0级,绝缘阻燃漆的电阻为7.8×10^13Ω,电阻率为4.36×10^15Ω.·cm,介电损耗为0.014 5,此时拉伸强度为3.34MPa,冲击强度为0.71 kJ/m^2.     

电机绕组烘干过程的实时监控

介绍了一种在工业现场实时监控电机绕组浸渍绝缘漆后烘干过程的原理和实现方法。该方法利用对绝缘漆的介质系数进行实时监测、处理，能对漆膜烘干程度作出准确的判断和对电机部件在烘房中所需时间进行控制。从而有效地避免了烘漆时间过程引起的产品质量问题和烘漆时间过长所造成的电能浪费。     

600 mesh silicon carbide corona protection varnish with epoxy/OMMT nano-composite adhesive

A new corona protection varnish was prepared by using epoxy/montmorillonite nano-composite and pure epoxy resin as adhesives respectively. The adhesive with different amounts of organic montmorillonite (OMMT) was mixed with 1200 mesh silicon carbide (SiC) by different weight ratios. The surface states of the varnishes with various adhesives were observed by powerful optical microscope. Some properties of the varnishes were analyzed during the enduring time under 5kV/cm DC, such as the relation of change in nonlinear coefficient, natural surface resistivity, and surface temperature variation. The results showed that the amounts of OMMT had little effect on the natural surface resistance of the varnish but had important influence on the nonlinear property of the varnish. When the range of the OMMT content was 2wt% to 6wt%, the nonlinear coefficient of all materials with epoxy/OMMT nano-composite adhesive was higher than that with pure epoxy resin adhesive. The surface temperature of the varnish with epoxy/OMMT nanocomposite adhesive was all lower than that with the pure epoxy resin adhesive under high electrical field strength.     

正交试验法研究改性酚醛浸渍树脂

为了提高建筑木模板用酚醛浸渍树脂的性能,以氢氧化钡为催化剂、三聚氰胺为增强剂、聚乙烯醇为增韧剂,用二次升温缩聚的方法制备了改性钡酚醛浸渍树脂,并且利用正交试验法分析讨论了浸渍树脂的配方和合成工艺.结果表明,在最优合成条件(甲醛/苯酚摩尔比为1.8、三聚氰胺/苯酚摩尔比为0.09、低温(65 ℃)缩聚时间为45 min)下合成的改性钡酚醛树脂的聚合时间、弹性模量、静曲强度、抗冲击强度等性能均显著优于未改性钡酚醛树脂.该实验方法及结果可为提高浸渍树脂的性能和木模板的生产效率提供参考.     

环氧-酚醛-聚酰胺树脂掺混清漆

应用溶解度参数理论,通过对环氧树脂、聚酰胺树脂、酚醛树指３种树脂均相溶液的适当掺混,并对各种清漆配方性能测试比较,造反出附着力好、抗冲击强度好、耐酸耐碱等化学腐蚀性强等综合性能优良的溶剂型环氧－酚醛－聚酰胺树脂清漆。其适宜配方（ｗＢ）为：Ｅ－４４环氧树脂３０．５２％,低分子聚酰胺树脂１０．２６％,酚醛树脂１０．２７％,邻苯二甲酸二丁酯３．５１％,二甲苯／环乙酮（质量比１／１）８．９４％,二甲苯／正     

130级紫外光固化型漆包线用环保绝缘漆的制备与性能研究

针对现有溶剂型绝缘漆挥发性有机物质(VOC)含量高,使用中污染较大、能耗较高的问题,通过分子设计及专用树脂的合成,制备130级紫外光固化型环保绝缘漆,利用凝胶渗透色谱仪、旋转黏度计及相关专用仪器对树脂、漆料及所制漆包圆铜线性能进行分析测试。结果表明：所制备的环保绝缘漆专用树脂的数均分子量为1 125 g/mol,漆料的黏度为265 mPa·s(25℃下),有效固含量为99.2%,所制备漆包圆铜线的各项指标均达到或超过现行130级聚酯漆包线的性能指标。     

新型聚酯氨基汽车烘漆的研制

根据我国汽车市场发展的需要，以热固性饱和聚酯树脂为基质，采用三聚氰胺基树脂为交联剂，开发出了新一代的聚酯氨基汽车烘漆。该漆具有高装饰性、高防护性、耐候性等优点。与国内同类产品相比，该产品在配方及工艺方面均有所创新。其主要性能指标在国内居于领先地位。     

混纤纱热塑复合材料研究进展

以增强纤维和热塑纤维组成的混纤纱作为制作热塑复合材料的预浸料,提供了一种低成本加工连续纤维增强的热塑复合材料的方法.综述混纤纱热塑复合材料复合过程的理论模型和实验研究的进展,对树脂沿纤维束垂直方向一维流动的理论模型作了归纳和分析,介绍了关于纤维束结构参数以及复合工艺参数对复合材料性能影响的实验研究成果,并指出在这一领域的理论和实验研究方面需要进一步解决的问题.     

炭黑/环氧树脂复合材料的导电阈值现象

目的 研究炭黑/二氧化硅/环氧树脂复合材料中的导电阈值现象,寻找材料形成导电通路时炭黑的用量.方法 通过溶剂化过程,制备了炭黑/二氧化硅/环氧树脂复合材料,并测试了复合材料表面涂层的导电性能.结果 复合材料的导电特性可以用渗透理论来解释,其导电组分的阈值约为13.2%(体积分数).结论 复合材料的导电性受炭黑用量的影响.当炭黑用量低于阈值时,孤立的炭黑颗粒被绝缘的聚合物所包缚,材料中没有形成导电通路网,电导率较低:当炭黑用量高于阈值时,炭黑颗粒数量增加,间距变小,电子隧道效应增强,材料中形成了导电通路网,因而电导率增加.     

新型聚合物混凝土／玻璃钢复合结构装饰墙体

提出一种新型复合结构墙体,该墙体以聚合物混凝土为基层,以玻璃钢为保护层和装饰层,并由树脂渗透层将以上两层紧密结合起来。此复合结构适用于大型墙体装饰,并可达到与天然石材、壁纸、涂料几乎相同的装饰效果。介绍了各层形态及形成机理,并的 一套较为合理的选材方案及相关技术措施。