Silver nanoparticles: Large scale solvothermal synthesis and optical properties

Silver nanoparticles have been successfully synthesized by a simple and modified solvothermal method at large scale using ethanol as the refluxing solvent and NaBH₄ as reducing agent. The nanopowder was investigated by means of X-ray diffraction (XRD), transmission electron microscopy (TEM), dynamic light scattering (DLS), UV-visible and BET surface area studies. XRD studies reveal the monophasic nature of these highly crystalline silver nanoparticles. Transmission electron microscopic studies show the monodisperse and highly uniform nanoparticles of silver of the particle size of 5 nm, however, the size is found to be 7 nm using dynamic light scattering which is in good agreement with the TEM and X-ray line broadening studies. The surface area was found to be 34.5 m²/g. UV-visible studies show the absorption band at ∼425 nm due to surface plasmon resonance. The percentage yield of silver nanoparticles was found to be as high as 98.5%.     

Synthesis, characterization and fluorescence property of CdS/P(N-iPAAm) nanocomposites

A novel nanocomposite in which CdS nanoparticles were embedded in poly(N-isopropylacrylamide) (P(N-iPAAm)) matrix have been fabricated. The particle size of CdS nanoparticles ranged from 10 nm to 40 nm could be adjusted with the varying of the inorganic contents. The nanocomposites have been characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), thermo-gravimetric analysis (TGA), high resolution transmission electron microscope (HRTEM), UV-vis absorption and fluorescence spectra (FLS) measurements. The cell volume of CdS nanoparticles embedded in polymer matrix was smaller than the standard value and the nanocomposites with 12.0% inorganic content showed a good fluorescence property.     

Size-controlled synthesis, microstructure and magnetic properties of Ni nanoparticles

Ni nanoparticles with different mean diameters of 15-83 nm were synthesized by solution reduction process. The size of Ni nanoparticles can be controlled by varying the concentration of NiCl₂·6H₂O and synthesis temperature. The samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), infrared spectroscopy (IR) and X-ray photoelectron spectroscopy (XPS). Results show that the synthesized particles are single-phased Ni with a face-centered cubic crystal structure. Magnetic measurements indicate that Ni nanoparticles are ferromagnetic. The lattice constants and coercivities of the samples are size-dependent.     

Microwave-hydrothermal synthesis of γ-Fe2O3 nanoparticles and their magnetic properties

Nanosized γ-Fe₂O₃ is synthesized by the microwave-hydrothermal method. Powder X-ray diffraction and transmission electron microscopic studies showed that the average particle size is 10 nm. Magnetic studies reveal that the γ-Fe₂O₃ nanoparticles are superparamagnetic at room temperature, with a superparamagnetic blocking temperature of 200 K. The magnetic characteristics of the nanoparticles indicate their strongly interacting nature.     

Ultrasonic-assisted synthesis and magnetic studies of iron oxide/MCM-41 nanocomposite

Iron oxide nanoparticles were stabilized within the pores of mesoporous silica MCM-41 amino-functionalized by a sonochemical method. Formation of iron oxide nanoparticles inside the mesoporous channels of amino-functionalized MCM-41 was realized by wet impregnation using iron nitrate, followed by calcinations at 550 °C in air. The effect of functionalization level on structural and magnetic properties of obtained nanocomposites was studied. The resulting materials were characterized by powder X-ray diffraction (XRD), high-resolution transmission electron microscopy and selected area electron diffraction (HRTEM and SAED), vibrating sample and superconducting quantum interface magnetometers (VSM and SQUID) and nitrogen adsorption–desorption isotherms measurements. The HRTEM images reveal that the most of the iron oxide nanoparticles were dispersed inside the mesopores of silica matrix and the pore diameter of the amino-functionalized MCM-41 matrix dictates the particle size of iron oxide nanoparticles. The obtained material possesses mesoporous structure and interesting magnetic properties. Saturation magnetization value of magnetic iron oxide nanopatricles stabilized in MCM-41 amino-functionalized by in situ sonochemical synthesis was 1.84 emu g⁻¹. An important finding is that obtained magnetic nanocomposite materials exhibit enhanced magnetic properties than those of iron oxide/MCM-41 nanocomposite obtained by conventional method. The described method is providing a rather short preparation time and a narrow size distribution of iron oxide nanoparticles.     

Extracellular synthesis of silver nanoparticles using the leaf extract of Coleus amboinicus Lour.

In the present investigation, Coleus amboinicus Lour. leaf extract-mediated green chemistry approach for the synthesis of silver nanoparticles was described. The nanoparticles were characterized by ultraviolet-visible (UV-Vis) spectroscopy, X-ray diffraction (XRD), energy dispersive X-ray analysis (EDAX), Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM). The influence of leaf extract on the control of size and shape of silver nanoparticles is reported. Upon an increase in the concentration of leaf extract, there was a shift in the shape of nanoparticles from anisotrophic nanostructures like triangle, decahedral and hexagonal to isotrophic spherical nanoparticles. Crystalline nature of fcc structured nanoparticles was confirmed by XRD spectrum with peaks corresponding to (1 1 1), (2 0 0), (2 2 0) and (3 1 1) planes and bright circular spots in the selected-area electron diffraction (SAED). Such environment friendly and sustainable methods are non-toxic, cheap and alternative to hazardous chemical procedures.     

Hydrothermal fabrication of various morphological α-Fe2O3 nanoparticles modified by surfactants

Two kinds of various morphological α-Fe₂O₃ nanoparticles modified by anionic surfactant (sodium dodecylsulfonate, SDS) and cationic surfactant (hexadecyipyridinium chloride, HPC), respectively, have been synthesized via hydrothermal method, using simple inorganic salt (NH₄)₃Fe(C₂O₄)₃ and alkali NaOH as starting precursors. Meanwhile, α-Fe₂O₃ nanoparticles without surfactant are also fabricated under the same conditions for comparison. The resultant products were characterized by means of Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), transmission electron micrograph (TEM) combined with electron diffraction (ED) and magnetization measurements. It is interesting that the obtained α-Fe₂O₃ nanoparticles without surfactant are polyhedral with average particle size of 90 ± 35 nm; while the obtained α-Fe₂O₃ nanoparticles modified by SDS are ellipsoidal with mean particle size of major axis: ca. 420 nm; minor axis: ca. 205 nm and those modified by HPC are spherical with mean particle size of ca. 185 nm observed from TEM. In addition, magnetic hysteresis measurements reveal that the α-Fe₂O₃ nanoparticles modified by two surfactants show enhancement in coercivity (H_c) and the remanent magnetization (M_r) compared with those of the obtained α-Fe₂O₃ nanoparticles without surfactant at room temperature. The experimental results suggest that the surfactants not only significantly influence the size and shape of the particles, but also their magnetic properties.     

Synthesis and characterization of ZnO/SiO2 core/shell nanocomposites and hollow SiO2 nanostructures

In this paper, we prepared the ZnO nanoparticles by a simple hydrothermal method and fabricated the ZnO/SiO₂ core/shell nanostructures through a sol-gel chemistry process successfully. The hollow SiO₂ nanostructures were obtained by selective removal of the ZnO cores. The structure, morphology and composition of the products were determined by the techniques of X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDS) and transmission electron microscopy (TEM). The results indicated that the ZnO nanoparticles were sphere-like shape with the average size of 60 nm and belonged to hexagonal wurtzite crystal structure. With the coating of SiO₂, the vibration modes of Si-O-Si and Si-OH were found. Furthermore, the measurement results of optical properties showed that spectra of bare ZnO nanoparticles and ZnO/SiO₂ core/shell nanocomposites exhibited similar emission features, including a blue emission peak and an orange emission band.     

Synthesis, characterization and magnetic properties of NiS1+x nanocrystals from [bis(salicylidene)nickel(II)] as new precursor

[Bis(salicylidene)nickel(II)] was used as a precursor to prepare nickel sulfides nanoparticles of average size 20 nm by a chemical process in oleylamine. The products were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), ultraviolet-visible spectroscopy (UV-vis) and photoluminescence (PL) spectroscopy. Magnetization measurement indicates that both of the α-NiS and Ni₃S₄ nanoparticles show pramagnetism due to the size effect.     

Dendrigraft polymer-based synthesis of silver nanoparticles showing bright blue fluorescence

A novel method is reported here for the synthesis of optically clear and stable colloidal solutions of silver nanoparticles. According to size they show different colours depending upon their plasmonic absorption frequencies. The materials have been synthesized at room temperature by chemical reduction of silver ions (silver nitrate) coordinated with dendrigraft polymer, polyethyleneimine (PEI) using formaldehyde in aqueous medium. UV-vis absorption and transmission electron microscopy (TEM) studies show single-band absorption with peak maximum at 354 nm for ∼3 nm sized particles, whereas a side band at ∼400 nm was observed when the particle size increased to ∼20 nm. Highly narrow particle size distribution was observed in case of samples having ∼3 nm size silver particles and also the process of reduction could be completed within minutes. More interestingly, the 3-nm sized particles showed strong blue (474 nm) fluorescence under UV excitation. Thin films of all synthesized samples were prepared on silica substrate by fine spray coating technique.     

Temperature dependence of magnetic property and photocatalytic activity of Fe3O4/hydroxyapatite nanoparticles

Fe₃O₄/hydroxyapatite (HAP) nanoparticles have been developed as a novel photocatalyst support, based on the embedment of magnetic Fe₃O₄ particles into HAP shell via homogeneous precipitation method. The resultant nanoparticles were characterized by transmission electron microscope (TEM) and X-ray diffraction (XRD). These particles were almost spherical in shape, rather monodisperse and have a unique size of about 25 nm in diameter. The effect of calcination temperature on magnetic property and photocatalytic activity of Fe₃O₄/HAP nanoparticles was investigated in detail. The obtained results showed that the Fe₃O₄/HAP nanoparticles calcined at 400 °C possessed good magnetism and photocatalytic activity in comparison with that calcined at other temperatures.     

Nanoparticles of La0.8Ca0.2Fe0.8Ni0.2O3−δ perovskite for solid oxide fuel cell application

Polycrystalline samples of La_0.8Ca_0.2Fe_0.8Ni_0.2O_3−δ (LCFN) with perovskite type structure have been prepared by combustion, freeze drying, citrate-gel process and liquid mix method. The analysis of X-ray powder diffraction indicated that the samples were single phase and crystallized in an orthorhombic (space group, Pnma no. 62) structure.Transmission electron microscopy (TEM) analysis on the synthesized powder at 600 °C by liquid mix method showed clusters of 150 nm formed by nanoparticles of 20 nm. Electrochemical performance of LCFN cathodes, which are used for intermediate temperature solid oxide fuel cells, were investigated. The polarization resistance was studied using two different electrolytes: Y-doped zirconia (YSZ) and Sm-doped ceria (SDC). The dc four-probe measurement exhibits a total electrical conductivity, over 100 S cm⁻¹ at T ≥ 600 °C, pointing out that strontium can be substituted for the cheaper calcium cation without destroying the electrochemical properties. Experimental results indicate that nanoparticles have more advantages in terms of smaller particle size and better electrochemical performance.     

Low temperature synthesis of porous copper/zinc oxide

A two-step urea aqueous solution process at a low temperature (90 °C) was employed for the preparation of a copper/zinc oxide material. Well defined porous spherical particles with average sizes of around 5 μm in diameter were prepared first and then used as a support for further copper-zinc precipitation. It was found that the particle composition and shape were changed with applied stirring speed (100 rpm or 200 rpm) and that particle size is inversely proportional to the copper content in the particles. The particles preserved their size and shape after the heat treatment. Prepared Cu/ZnO samples showed catalytic activity for the reaction of steam reforming of methane. Samples were characterized by scanning field emission electron microscopy, energy dispersive X-ray analyses, X-ray powder diffraction, surface area analyses, and atomic absorption spectroscopy.     

Structural and magnetic properties of Mn nanoparticles prepared by arc-discharge

Mn nanoparticles are prepared by arc discharge technique. MnO, α-Mn, β-Mn, and γ-Mn are detected by X-ray diffraction, while the presence of Mn₃O₄ and MnO₂ is revealed by X-ray photoelectron spectroscopy. Transmission electron microscopy observations show that most of the Mn nanoparticles have irregular shapes, rough surfaces and a shell/core structure, with sizes ranging from several nanometers to 80 nm. The magnetic properties of the Mn nanoparticles are investigated between 2 and 350 K at magnetic fields up to 5 T. A magnetic transition occurring near 43 K is attributed to the formation of the ferrimagnetic Mn₃O₄. The coercivity of the Mn nanoparticles, arising mainly from Mn₃O₄, decreases linearly with increasing temperature below 40 K. Below the blocking temperature T_B ≈ 34 K, the hysteresis loops exhibit large coercivity (up to 500 kA/m), owing to finite size effects, and irreversibility in the loops is found up to 4 T, and magnetization is not saturated up to 5 T. The relationship between structure and the magnetic properties are discussed.     

Fabrication of nanocomposite particles with superparamagnetic and luminescent functionalities

A new kind of superparamagnetic luminescent nanocomposite particles has been synthesized using a modified Stöber method combined with an electrostatic assembly process. Fe₃O₄ superparamagnetic nanoparticles were coated with uniform silica shell, and then 3-aminopropyltrimethoxysilane was used to terminate the silica surface with amino groups. Finally, negatively charged CdSe quantum dots (QDs) were assembled onto the surface of the amino-terminated SiO₂/Fe₃O₄ nanoparticles through electrostatic interactions. X-ray diffraction (XRD), transmission electron microscopy (TEM), microelectrophoresis, UV-vis absorption and emission spectroscopy and magnetometry were applied to characterize the nanocomposite particles. Dense CdSe QDs were immobilized on the silica surface. The thickness of silica shell was about 35 nm and the particle size of the final products was about 100 nm. The particles exhibited favorable superparamagnetic and photoluminescent properties.     

Synthesis of size tuneable cadmium sulphide nanoparticles from a single source precursor using ammonia as the solvent

Size tuneable cadmium sulphide nanoparticles of a few nanometres in size were prepared by thermolysis of a single source precursor of cadmium xanthates with variable carbon chain length (Cd(ROCS₂)₂, where R denotes -C₂H₅, -C₄H₉, -C₈H₁₇ and -C₁₂H₂₅, respectively) in an ammonia solution. The particle size, morphology and crystallinity of these nanoparticles were characterized using X-ray powder diffractometry, transmission electron microscopy, and nitrogen adsorption/desorption techniques. The results show that hexagonal CdS nanoparticles can be produced by thermolysis of cadmium alkyl xanthate in an ammonia solution at a temperature as low as 100 °C. The size of CdS particles (between 5.60 nm and 3.71 nm) decreases with increasing length of carbon chain in the precursor, as further confirmed by UV-visible and fluorescence spectrophotometric measurements. The size tuning mechanism of CdS from cadmium alkyl xanthate is also discussed.     

Preparation and magnetic properties of spindle porous iron nanoparticles

Spindle porous iron nanoparticles were firstly synthesized by reducing the pre-synthesized hematite (α-Fe₂O₃) spindle particles with hydrogen gas. The products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), nitrogen adsorption/desorption isotherms and vibrating sample magnetometry (VSM). A lattice shrinkage mechanism was employed to explain the formation process of the porous structure, and the adsorbed phosphate was proposed as a protective shell in the reduction process. N₂ adsorption/desorption result showed a Brunauer-Emmett-Teller (BET) surface area of 29.7 m²/g and a continuous pore size distribution from 2 nm to 100 nm. The magnetic hysteresis loop of the synthesized iron particles showed a saturation magnetization of 84.65 emu/g and a coercivity of 442.36 Oe at room temperature.     

Facile synthesis of antimony-doped tin oxide nanoparticles by a polymer-pyrolysis method

In this article, antimony-doped tin oxide (ATO) nanoparticles was synthesized by a facile polymer-pyrolysis method. The pyrolysis behaviors of the polymer precursors prepared via in situ polymerization of metal salts and acrylic acid were analyzed by simultaneous thermogravimetric and differential scanning calorimetry (TG-DSC). The structural and morphological characteristics of the products were studied by powder X-ray diffraction (XRD) and transmission electron microscope (TEM). The results reveal that the ATO nanoparticles calcined at 600 °C show good crystallinity with the cassiterite structure and cubic-spherical like morphology. The average particle size of ATO decreases from 200 to 15 nm as the Sb doping content increases from 5 mol% to 15 mol%. Electrical resistivity measurement shows that the resistivity for the 10-13 mol% Sb-doped SnO₂ nanoparticles is reduced by more than three orders compared with the pure SnO₂ nanoparticles. In addition, due to its versatility this polymer-pyrolysis method can be extended to facile synthesis of other doped n-type semiconductor, such as In, Ga, Al doped ZnO, Sn doped In₂O₃.     

Electrical, optical and vibrational characteristics of nano structured yttrium barium stannous oxide synthesized through a modified combustion method

A single step combustion process for the preparation of nanoparticles of yttrium barium stannous oxide is reported in this paper. The structure, phase purity and particulate properties of the as prepared nano YBa₂SnO_5.5 powder were examined by X-ray diffraction and transmission electron microscopy. The as prepared powder obtained itself is phase pure and possess cubic structure with lattice constant 8.240 Å. The particle size of the as prepared sample from Transmission Electron Microscopy analysis is in the range of ∼15 nm. Vibrational studies carried out on the as prepared powder also confirm the cubic structure of the as prepared sample. The thermal stability of the nano particle is analyzed by thermo gravimetric and differential thermal analysis. The material is a semiconductor with excellent luminescent properties. Chemical compatibility of the sample with YBCO is analyzed. The YBCO-YBa₂SnO_5.5 composite showed T_c(0) at 92 K.     

Hydroxy propyl cellulose capped silver nanoparticles produced by simple dialysis process

Silver (Ag) nanoparticles (∼6 nm) were synthesized using a novel dialysis process. Silver nitrate was used as a starting precursor, ethylene glycol as solvent and hydroxy propyl cellulose (HPC) introduced as a capping agent. Different batches of reaction mixtures were prepared with different concentrations of silver nitrate (AgNO₃). After the reduction and aging, these solutions were subjected to ultra-violet visible spectroscopy (UVS). Optimized solution, containing 250 mg AgNO₃ revealed strong plasmon resonance peak at ∼410 nm in the spectrum indicating good colloidal state of Ag nanoparticles in the diluted solution. The optimized solution was subjected to dialysis process to remove any unreacted solvent. UVS of the optimized solution after dialysis showed the plasmon resonance peak shifting to ∼440 nm indicating the reduction of Ag ions into zero-valent Ag. This solution was dried at 80 °C and the resultant HPC capped Ag (HPC/Ag) nanoparticles were studied using transmission electron microscopy (TEM) for their particle size and morphology. The particle size distribution (PSD) analysis of these nanoparticles showed skewed distribution plot with particle size ranging from 3 to 18 nm. The nanoparticles were characterized for phase composition using X-ray diffractrometry (XRD) and Fourier transform infrared spectroscopy (FT-IR).