Single crystal growth and structure refinements of CsMxTe2−xO6 (M = Al, Ga, Ge, In) pyrochlores

Single crystals of CsM_xTe_2−xO₆ pyrochlores with M = Al, Ga, Ge, and In have been grown from a TeO₂ flux. Structure refinements from single crystal X-ray diffraction data are reported. These results are used to discuss deviations from ideal stoichiometry that result in electronic conductivity presumably related to mixed valency of tellurium.     

Structural, magnetic and dielectric properties of Bi1−ySryFe(1−y)(1−x)Sc(1−y)xTiyO3 (x = 0-0.2, y = 0.1-0.3) ceramics

In this study, bulk ceramics with general formula Bi_1−ySr_yFe_{(1−y)(1−x)}Sc_(1−y)xTi_yO₃ (x = 0-0.2, y = 0.1-0.3 mol%) were prepared by traditional solid-state reaction method. As a comparison, bulk BiFeO₃ (BF) was also sintered by rapid sintering method. Their structural, magnetic, dielectric properties were investigated. X-ray diffraction analysis indicated that apart from a small amount of secondary phase detected in BF, all other samples crystallized in pure perovskite structure and maintained original R3c space group. The room temperature M-H curves were obtained. While BF had a coercive magnetic field (H_c) of 150 Oe, Bi_1−ySr_yFe_1−yTi_yO₃ solid solutions had a much larger value (for y = 0.1, 0.2, 0.3, H_c were 4537, 5230 and 3578 Oe, respectively). Sc³⁺ substitution decreased the H_c values of these solid solutions remarkably, and resulted in soft magnetic properties, as well as a decrease of the dielectric loss. At 1 MHz, the tan δ of Bi_0.7Sr_0.3Fe_0.7(1−x)Sc_0.7xTi_0.3O₃ with x = 0.05, 0.1, 0.15, 0.2 were 0.1545, 0.1078, 0.1046 and 0.1701, respectively.     

Synthesis, characterization, and dielectric properties of Ba(Ti1−xSnx)O3 nanopowders and ceramics

We prepared Ba(Ti_1−xSn_x)O₃ powders and ceramics by means of the sol-gel process, with dibutyltin dilaurate as the Sn precursor. The samples were characterized by means of Fourier-transform infrared spectroscopy, X-ray diffraction, transmission electron microscopy, and scanning electron microscopy, and also determined the dielectric properties of the ceramics. The powders synthesized by means of the sol-gel process had a grain size on the nanometer scale, with the grains mainly composed of a cubic BaTiO₃ phase. Sn can disperse into BaTiO₃ more uniformly in the sol-gel technique using dibutyltin dilaurate as the Sn precursor. With increasing Sn concentration, the grain size of the Ba(Ti_1-xSn_x)O₃ ceramics increased and the maximum dielectric constant (?_max) first increased and then decreased. At a Sn concentration of 5 mol%, ?_max reached its maximum value (19,235).     

Synthesis and luminescence properties of color-tunable Ba1−ySryLa4−xTbx(WO4)7 (x = 0.02-1.2, y = 0-0.4) phosphors

Ba_1−ySr_yLa_4−xTb_x(WO₄)₇ (x = 0.02-1.2, y = 0-0.4) phosphors were prepared via a solid-state reaction and their photoluminescence properties were investigated. An analysis of the decay behavior indicates that the energy migration between Tb³⁺ ions is conspicuous in the ⁵D₃ → ⁷F₄ transition due to the cross-relaxation in BaLa₄(WO₄)₇. A partial substitution of Ba²⁺ by Sr²⁺ can not only enhance the emission intensity but also increase the solid solubility of Tb³⁺ in Ba_1−ySr_yLa_4−xTb_x(WO₄)₇. The emission intensity of the ⁵D₄ → ⁷F_J (J = 4, 5, 6) transitions can be enhanced by increasing Sr²⁺ and Tb³⁺ concentrations, with the optimal conditions being x = 1.2, y = 0.4 (Ba_0.6Sr_0.4La_2.8Tb_1.2(WO₄)₇). Under near-UV excitation at 379 nm, the CIE color coordinates of Ba_1−ySr_yLa_4−xTb_x(WO₄)₇ vary from blue (0.212, 0.181) at x = 0.04, y = 0, to green (0.245, 0.607) at x = 1.2, y = 0.4.     

Effect of sintering time on crystal structure and microwave dielectric properties in aeschynite-structured (Sm1−xYx)(Ti1.5W0.5)O6 (x = 0 and 0.5) ceramics

The crystal structure and microwave dielectric properties of the (Sm_1−xY_x)(Ti_1.5W_0.5)O₆ (x = 0 and 0.5) ceramics sintered at 1375 °C for 2-50 h were investigated in this study. No secondary phase was observed in the samples sintered for various sintering times, whereas a secondary phase was formed in the (Sm_0.5Y_0.5)(Ti_1.5W_0.5)O₆ ceramic sintered at 1400 °C for 50 h. As for the microstructure analysis, the formation of the liquid phase was observed in the both of the samples sintered for 20 and 50 h. The formation of the liquid phase is related to the compositional change of Ti and W from the stoichiometric composition of the samples caused by the instability of crystal structure. The dielectric constants were increased with increased sintering time in the both of the samples, though variations in the temperature coefficient of resonant frequency of the samples were not recognized with the variation in the sintering time. Moreover, although the quality factors of the each sample increased with increasing the sintering time from 2 to 10 h, decreases in the quality factors were recognized when the sintering time was over 10 h.     

Synthesis and electrical properties of ordered perovskite oxide Cd3−x−yCuxAyTeO6 (A = Li, Na; 0.00 ≤ x, y ≤ 0.15)

Polycrystalline Cd_3−x−yCu_xA_yTeO₆ (A = Li, Na) samples were prepared by solid-state reaction, and their crystal structure and electrical properties were investigated. In Cd_3−xCu_xTeO₆ and Cd_3−yA_yTeO₆ (A = Li, Na), the maxim solubility of x and y was 0.15 and 0.15 for A = Li, 0.05 for A = Na, respectively. For co-substituted samples Cd_2.9−yCu_0.1Li_yTeO₆ and Cd_2.9−yCu_0.1Na_yTeO₆, the maxim solubility of x was the same as single substitution above-mentioned. The alkali-metal substituted samples Cd_3−yA_yTeO₆ (A = Li, Na) showed a negative Seebeck coefficient, which indicates that the major conduction carriers are electron. On the other hand, the co-substituted samples Cd_2.9−yCu_0.1A_yTeO₆ (A = Li, Na) represented a positive Seebeck coefficient, and major conduction carriers were hole through substitution by copper ions.     

Compositionally controlled rhombohedral to cubic phase transition in CsTe2−xWxO6 related to pyrochlore structure

CsTe₂O₆ adopts a rhombohedrally distorted pyrochlore related structure due to the 1:3 ordering of Te⁴⁺ and Te⁶⁺ in the octahedral sites respectively. Phases of the type CsTe_2−xW_xO₆ were found to have the cubic pyrochlore structure from x = 0.2 to 0.5. These phases all contain Te⁴⁺ and Te⁶⁺ (mixed with W⁶⁺) and are disordered in octahedral sites of the pyrochlore structure. This mixed valence situation results in strong optical absorption in the visible region of the spectrum but does not produce a measurable electrical conductivity.     

Structure analysis on the Ba3Mg(Ta1−xNbx)2O9 ceramics: Coexistence of order and disorder

The Ba₃ZnTa₂O₉ (BZT) and Ba₃MgTa₂O₉ (BMT) ceramics, a family of A₃B²⁺B⁵⁺₂O₉ complex perovskites, are extensively utilized in mobile based technologies due to their intrinsic high unloaded quality factor, high dielectric constant and a low (near-zero) resonant frequency temperature coefficient at microwave frequencies. The preparation conditions as well as size and nature of B cations have a profound effect on the final dielectric properties. In this article, we report the effect of Nb⁵⁺ at the Ta⁵⁺ site on the BMT structure prepared at four synthesis temperatures (1300, 1400, 1500 and 1600 °C). The analysis has been carried out using the Rietveld technique on the X-ray powder diffraction data. Results suggest that both the preparation temperatures and Nb⁵⁺ content have significant effect on the ordering of B cations in the Ba₃Mg(Ta_1−xNb_x)₂O₉ solid solution. A disordered (cubic) structure is preferred by the 1300 °C compounds. The weight percentage of the ordered (trigonal) phase escalates, for a given composition, with increasing calcination temperature. A fully ordered trigonal arrangement exists only for x = 0.0 and 0.2 compounds calcined at 1600 °C, and the rest are biphasic (cubic and trigonal). The increase in the cubic fraction upon Nb⁵⁺ augmentation suggests that the solid solution leans more toward the disordered structural arrangement of B²⁺ and B⁵⁺ cations.     

Decomposition of (Ti2xFe1−xSb1−x)O4 solid solutions below 1673 K

The pseudo-binary TiO₂-FeSbO₄ system was investigated by means of thermogravimetric analysis below 1673 K in O₂. Rutile-type solid solutions were synthesised at 1373 K in O₂ by means of a solid state reaction between the two pure end members TiO₂ (rutile) and FeSbO₄ mixed in stoichiometric amounts. Thermal stability of the (Ti_2xFe_1−xSb_1−x)O₄ solid solution increases with rutile content; equimolar (Ti_1.00Fe_0.50Sb_0.50)O₄ solid solutions decompose at about 1673 K forming a TiO₂-enriched solid solution and FeSbO₄, that subsequently decomposes into Fe₂O₃ (hematite) and a volatile Sb oxide, probably Sb₄O₆. For compositions characterised by higher Ti content the decomposition temperature is higher than 1673 K.     

Effect of substitution in the scheelite-like series, AxBa1−xBi2Mo4O16 (A = Ca, Sr, Pb)

A new series of solid solutions of the type, A_xBa_1−xBi₂Mo₄O₁₆ (A = Ca, Sr, Pb) have been isolated. The domain of the solid solutions is very narrow and is in the range (0.01 ≤ x ≤ 0.10). All the phases were synthesized by the solid-state technique. The crystal structure is similar to that of the monoclinic scheelite type BaBi₂Mo₄O₁₆. The structure consists of layers of [Bi₂O₂] units separated by (Ba/AO)₁₀ units and isolated MoO₄ tetrahedra. Their semiconductor band gaps render them as potential materials for photocatalysis.     

Eu-Mössbauer spectroscopic and X-ray diffraction study on EuyM1−yO2−x (0 ≤ y ≤ 1.0) (M = Th, U)

¹⁵¹Eu-Mössbauer spectroscopic and powder X-ray diffraction (XRD) study has been performed for the Eu_yM_1−yO_2−x (M = Th and U) systems over the entire composition range of 0 ≤ y ≤ 1.0. The XRD results of the Eu-Th system showed that a very wide defect-fluorite (DF) type phase in which oxygen vacancies (V_O) are disordered (x = y/2) is formed for 0 ≤ y < 0.5 and that two-phase regions sandwitching a narrow C-type (C) single phase around y ≈ 0.8 appear for 0.5 < y < 0.8 (DF + C) and 0.82 < y < 1.0 (C + B-type (monoclinic) Eu₂O₃). The Mössbauer results show that the isomer shifts (ISs) of Eu³⁺ in this system smoothly increase with Eu composition, y. The decrease of average coordination number (CN) of O²⁻ around Eu³⁺ with increasing y (CN = 8 − 2y) (x = y/2) results in the decrease of the average EuO bond length, which is due to the decrease of repulsion force between O²⁻ anions. This result confirms that the IS of Eu³⁺ correlates well with the average EuO bond length in oxide systems. For the Eu-U system, the lattice parameter, a₀, of the system decreases almost linearly with y, in accordance with the calculated a₀ versus y curve for the oxygen-stoichiometric (i.e. x = 0) fluorite-type dioxide (CN = 8). The ISs of Eu³⁺ in this composition range remain almost constant around 0.5 mm/s, which is comparable to those of pyrochlore oxides (Eu₂Zr₂O₇ and Eu₂Hf₂O₇ (y = 0.5)) with O²⁻-eight-fold coordinated Eu³⁺(CN = 8).     

Effect of the Mn ion on electrical and magnetic properties of orthorhombic perovskite-type Ca(Mn1−xTix)O3−δ

Orthorhombic perovskite-type Ca(Mn_1−xTi_x)O_3−δ (0 ≤ x ≤ 0.7) was synthesized at 1173 K for 12 h in a flow of oxygen from a precursor gel prepared using citric acid and ethylene glycol. The Mn³⁺ ion was generated by substituting a Ti⁴⁺ ion in CaMnO₃. The average particle size was 100-300 nm and did not depend on x. The lattice constants and the (Mn, Ti)-O distance increased linearly with increasing x. The variation in global instability index (GII) indicated that the instability of the structure increases monotonically with increasing x. Ca(Mn_1−xTi_x)O_3−δ was an n-type semiconductor that had its minimum values of electrical resistivity (ρ) and activation energy (E_a) at x = 0.1. Ca(Mn_1−xTi_x)O_3−δ (x = 0 and 0.1) exhibited a weak ferromagnetic behavior. The variation in μ_eff indicated that the spin state of the Mn³⁺ ion changes from low to high at x = 0.1, then reverts to low in the range of 0.2 ≤ x ≤ 0.7. The variations in ρ and E_a are explained by the number of electrons according to the change in the spin state of the Mn³⁺ ion.     

Structural and electrical properties of La2−xBaxMo2O9−x/2 (x = 0-0.18)

La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) have been prepared by solid state reaction method. The lattice parameter of La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) determined by XRD data refinement shows a linear dependence on the dopant Ba content x. For the specimen with a La/Ba molar ratio of 0.18-0.2, additional reflection of secondary phase exists in the XRD pattern, so the value of solubility limit for Ba in La₂Mo₂O₉ is defined in range of 0.18 < x < 0.2. As the replacement degree of La³⁺ by Ba²⁺ increases, the bulk conductivity of La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) decreases initially and then increases, a minimum value at La_1.9Ba_0.1Mo₂O_8.95 exists. Hebb-Wagner studies in argon atmosphere, which use an oxide-ion blocking electrode, show that La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) are predominantly oxide-ion conducting in the temperature ranging from 773 to 1173 K. The average thermal expansion coefficient of La_1.84Ba_0.16Mo₂O_8.92 determined by high-temperature XRD was deduced as great as 17.5 × 10⁻⁶ K⁻¹ between 298 and 1173 K.     

Oxygen vacancy ordering in strontium doped rare earth cobaltate perovskites Ln1−xSrxCoO3−δ (Ln = La, Pr and Nd; x > 0.60)

A family of Sr-doped perovskite compounds Ln_1−xSr_xCoO_3−δ (Ln = La³⁺, Pr³⁺ and Nd³⁺; x > 0.60), were prepared by sol-gel chemistry and reaction at 1100 °C under 1 atm of oxygen. This structural family has been shown to be present only for rare earth ions larger than Sm³⁺ and an upper limit of Sr²⁺ solubility in these phases was found to exist between x = 0.90 and 0.95. X-ray diffraction shows oxygen-deficient, simple cubic (Pm-3m) perovskite crystal structures. The combination of electron and powder neutron diffraction reveals that oxygen vacancy ordering occurs, leading to a tetragonal (P4/mmm) superstructure and a doubling of the basic perovskite unit along the crystallographic c-axis. No additional Ln³⁺/Sr²⁺ cation ordering was observed.     

Luminescence characterization of (Ca1−xSrx)(S1−ySey):Eu,M (M = Sc and Y) for high color rendering white LED

The highly efficient red phosphors (Ca_1−xSr_x)(S_1−ySe_y):Eu²⁺,M³⁺ (M = Sc and Y) were prepared, starting from CaCO₃, SrCO₃, Eu₂O₃, Sc₂O₃, Y₂O₃, S, and SeO₂ with a flux, by a conventional solid-state reaction. The optimized red phosphors converted 11.8% (Sc³⁺) and 11.7% (Y³⁺) of the absorbed blue light into luminescence. These quantum values are much higher than Q = 3.0% of CaS:Eu²⁺. For the fabrication of light-emitting diodes (LEDs), the prepared phosphors were coated with MgO from non-aqueous solution to overcome their weakness against moisture. White LEDs were fabricated by pasting the prepared red phosphors and the yellow YAG:Ce³⁺ phosphor on an InGaN blue chip (λ_ems = 446.5 nm). The incorporation of the red phosphor to the YAG:Ce³⁺ phosphor resulted in an improved color rendering index (Ra) from 70 to 80.     

6H hexagonal structure of low loss Ba3MTiWO9 (M = Mg, Zn) dielectrics

The crystal structure of Ba₃MTiWO₉ (M = Mg, Zn) oxides has been found to be 6H hexagonal, space group P6₃/mmc, parameters of unit cell: a = 5.7943(1) Å, c = 14.1642(1) Å and a = 5.7993(1) Å, c = 14.1626(1) Å for M = Mg and Zn, respectively. The tungsten and titanium atoms are randomly distributed in pairs of face-sharing octahedra separated by octahedral layers containing magnesium or zinc. It was revealed that the structures are well ordered which is believed to result in a low dielectric loss at a microwave frequency reported for these materials.     

Effects of La substitution for Nd in (Nd2−xLax)BaZnO5 solid solutions on microwave dielectric properties and crystal structure

The synthesis and microwave dielectric characterization of (Nd_2−xLa_x)BaZnO₅ solid solutions were studied. The samples obtained were single phase over the whole composition range and the lattice parameters of solid solutions were linearly increased with increasing the composition. Moreover, the expansion of the volume in the RO₈ (R=Nd and La) and BaO₁₀ polyhedra and ZnO₄ tetrahedron were recognized when Nd ions were substituted by La. These variations in the lattice parameters and volumes of the polyhedra are basically attributed to the differences in ionic radii between Nd³⁺ and La³⁺ ions. From the evaluation of microwave dielectric properties, it was shown that the appropriate τ_f values ranging from 4.6 to −5.0 ppm/°C are obtained by La substitution for Nd ion, and the highest Q · f value was 17,832 GHz at x=2.     

Effect of B-site doping on Sm0.5Sr0.5MxCo1−xO3−δ properties for IT-SOFC cathode material (M = Fe, Mn)

The crystal structure, thermal expansion rate, electrical conductivity and electrochemical performance of Sm_0.5Sr_0.5M_xCo_1−xO_3−δ (M = Fe, Mn) have been investigated. Two crystal structures have been observed in the specimens of Sm_0.5Sr_0.5Fe_xCo_1−xO_3−δ (SSFC) at room temperature, the perovskite structure of SSFC has an orthorhombic symmetry for 0 ≤ x ≤ 0.4 and a cubic symmetry for 0.5 ≤ x ≤ 0.9. The specimens of Sm_0.5Sr_0.5Mn_xCo_1−xO_3−δ (SSMC) crystallize in an orthorhombic structure. The adjustment of thermal expansion rate to electrolyte, which is one of the main problems of SSC, can be achieved to lower TEC values with more Fe and Mn substitution. Especially, Sm_0.5Sr_0.5Mn_0.8Co_0.2O_3−δ exhibits good thermal compatibility with La_0.8Sr_0.2Ga_0.8Mg_0.2O₃. High electrical conductivities are obtained for all the specimens and they demonstrate above 100 S/cm at 800 °C in SSFC system. The polarization resistance increases with increasing Mn content, Nevertheless, the polarization resistance of SSFC increases with increasing Fe content, but when the amount of Fe reaches to 0.4, the maximum is obtained while the resistance will decrease when the amount of Fe reaches above 0.4. Sm_0.5Sr_0.5Fe_0.8Co_0.2O_3−δ electrode exhibits high catalytic activity for oxygen reduction operating at temperature from 700 to 800 °C.     

X-ray Rietveld analysis and Fourier transform infrared spectra of the solid solutions [Eu2−xMx][Sn2−xMx]O7−3x/2 (M = Mg or Zn)

Two series of mixed oxides with formula [Eu_2−xM_x][Sn_2−xM_x]O_7−3x/2 (M = Mg or Zn) have been synthesized. The study by X-ray diffraction and Fourier transform infrared spectroscopy shows that the solids obtained are new non-stoichiometric solid solutions with the pyrochlore type structure. For both series a decrease of the cell parameter is observed when the degree of substitution, x, increases. The structural refinements (X-ray studies) were achieved in the space group Fd-3m, no. 227 (origin at center -3m) by using the Fullprof software. The Rietveld refinements show that the divalent cations M²⁺ (Mg²⁺, Zn²⁺) substitute isomorphically for Eu³⁺ and Sn⁴⁺ ions producing vacancies in the anionic sublattice.     

Crystal structures and properties of BiMn1−xAlxO3 with x = 0.03 and 0.1

Crystal structures of BiMn_0.97Al_0.03O₃ (I) at 300 and 470 K and BiMn_0.9Al_0.1O₃ (II) at 90 and 300 K were studied with synchrotron X-ray powder diffraction. The strong Jahn-Teller distortion, observed at 300 K in I and associated with orbital order, disappeared at 470 K completely for one site and partially for the second site. The Mn/Al-O distances were very close to each other in I at 470 K and in II at 90 and 300 K indicating that orbital order did not appear in II even at 90 K. Magnetic properties of I and II were investigated with specific heat, high-temperature dc magnetic susceptibility, and ac magnetic susceptibility using different driving ac and applied dc magnetic fields and different ac magnetic field frequencies. The anomaly on the specific heat associated with a magnetic transition was strongly suppressed in II compared with that of I and BiMnO₃.