Synthesis of perovskite-type (La1−xCax)FeO3 (0 ≤ x ≤ 0.2) at low temperature

Gel formation was realized by adding citric acid to a solution of La(NO₃)₃·5H₂O, Ca(NO₃)₂·4H₂O, and Fe(NO₃)₂·9H₂O. Perovskite-type (La_1−xCa_x)FeO₃ (0 ≤ x ≤ 0.2) was synthesized by firing the gel at 500 °C in air for 1 h. The crystallite size (D_1 2 1) decreased with increasing x, while the specific surface area was 6.8-9.4 m²/g and independent of x. The XPS measurement of the (La_1−xCa_x)FeO₃ surface indicated that the Ca²⁺ ion content increased with increasing x, while the Fe ion content was independent of x. Catalytic activity for CO oxidation increased with increasing x.     

Synthesis and electrical properties of ordered perovskite oxide Cd3−x−yCuxAyTeO6 (A = Li, Na; 0.00 ≤ x, y ≤ 0.15)

Polycrystalline Cd_3−x−yCu_xA_yTeO₆ (A = Li, Na) samples were prepared by solid-state reaction, and their crystal structure and electrical properties were investigated. In Cd_3−xCu_xTeO₆ and Cd_3−yA_yTeO₆ (A = Li, Na), the maxim solubility of x and y was 0.15 and 0.15 for A = Li, 0.05 for A = Na, respectively. For co-substituted samples Cd_2.9−yCu_0.1Li_yTeO₆ and Cd_2.9−yCu_0.1Na_yTeO₆, the maxim solubility of x was the same as single substitution above-mentioned. The alkali-metal substituted samples Cd_3−yA_yTeO₆ (A = Li, Na) showed a negative Seebeck coefficient, which indicates that the major conduction carriers are electron. On the other hand, the co-substituted samples Cd_2.9−yCu_0.1A_yTeO₆ (A = Li, Na) represented a positive Seebeck coefficient, and major conduction carriers were hole through substitution by copper ions.     

Synthesis, structural and magnetic properties of La1−xCdxFeO3 (0.0 ≤ x ≤ 0.3) orthoferrites

Nanocrystalline La_1−xCd_xFeO₃ (0.0 ≤ x ≤ 0.3) solid solutions have been synthesized by a single-step solution combustion method at a relatively low temperature of 400 °C. The combustion-synthesized solid solutions were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), and magnetic measurements. The crystal structure examined by XRD indicates that the samples were single-phase, and crystallize in an orthorhombic (space group, Pbnm no. 62) structure. The parent and doped compounds showed canted antiferromagnetic behavior associated with an increase in magnetic moment with Cd doping. The changes in magnetic properties of the materials are correlated to the changes in structural features resulting from the Rietveld structural refinement of the materials.     

Synthesis, structure and magnetic properties of Sr2Fe1−xGaxMoO6 (0 ≤ x ≤ 0.6) double perovskites

Polycrystalline Sr₂Fe_1−xGa_xMoO₆ (0 ≤ x ≤ 0.6) materials have been synthesized by solid state reaction method and studied by neutron powder diffraction (NPD) and magnetization measurements. Rietveld analysis of the temperature dependent NPD data shows that the compounds crystallize in the tetragonal symmetry in the space group I4/m. The anti-site (AS) defects concentration increases with Ga doping, giving rise to highly B-site disordered materials. Ga doping at the Fe-site decreases the cell volume. The evolution of bond lengths and the cation oxidation states was determined from the Rietveld refinement data. The saturation magnetization and Curie temperature decreased with the increasing Ga content in the samples. Low temperature neutron diffraction data analysis and magnetization measurements confirm the magnetic interaction as ferrimagnetic in the sample.     

Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 (0≤x≤1): synthesis, structure and dielectric properties

Oxides belonging to the families Ba₃ZnTa_2−xNb_xO₉ and Ba₃MgTa_2−xNb_xO₉ were synthesized by the solid state reaction route. Sintering temperatures of 1300°C led to oxides with disordered (cubic) perovskite structure. However, on sintering at 1425°C hexagonally ordered structures were obtained for Ba₃MgTa_2−xNb_xO₉ over the entire range (0≤x≤1) of composition, while for Ba₃ZnTa_2−xNb_xO₉ the ordered structure exists in a limited range (0≤x≤0.5). The dielectric constant is close to 30 for the Ba₃ZnTa_2−xNb_xO₉ family of oxides while the Mg analogues have lower dielectric constant of ∼18 in the range 50 Hz to 500 kHz. At microwave frequencies (5-7 GHz) dielectric constant increases with increase in niobium concentration (22-26) for Ba₃ZnTa_2−xNb_xO₉; for Ba₃MgTa_2−xNb_xO₉ it varies between 12 and 14. The “Zn” compounds have much higher quality factors and lower temperature coefficient of resonant frequency compared to the “Mg” analogues.     

Oxide-ion conductivity in CuxCe1−xO2−δ (0 ≤ x ≤ 0.10)

Up to 10 at.% of copper readily substitutes for cerium in ceria. It is found that at oxygen partial pressures between 0.21 atm and 10⁻⁵ atm, Cu_xCe_1−xO_2−δ (0 ≤ x ≤ 0.10) solid solution behave as an oxide-ion electrolyte. Interestingly, Cu_0.10Ce_0.90O_2−δ exhibits the oxide-ion conductivity of ca. 10⁻⁴ Ω⁻¹ cm⁻¹ at 600 °C at an oxygen partial pressure of 10⁻⁵ atm.     

Crystal structure and superconductivity of rubidium tungsten bronzes RbxWO3 prepared by a hybrid microwave method

The rubidium tungsten bronzes Rb_xWO₃ have been prepared from Rb₂CO₃, WO₃ and W powders using hybrid microwave method. The single hexagonal phase samples can be obtained as actual rubidium content x in the range of 0.21-0.33, and their lattice parameters a and c linearly drop and rise with the increase of rubidium content respectively. For samples with x = 0.14, 0.16, 0.18, the superconducting transition temperature T_c from resistivity measurements does not change with the rubidium content, while T_c from susceptibility measurements shows a decrease from 5.3 K for x = 0.14 to 4.8 K for x = 0.18. The charge density wave (CDW) transition appears in Rb_0.21WO₃, Rb_0.23WO₃ and Rb_0.25WO₃ at about 200-260 K. The CDW transition is most obvious in Rb_0.23WO₃ which shows the lowest degree of crystallization among the samples.     

Influence of SnO2 addition on the thermoelectric properties of Zn1 − xSnxO (0.01 ≤ x ≤ 0.05)

The grain size and the density of the Zn_1 − xSn_xO (0 ≤ x ≤ 0.05) samples decreased with increasing SnO₂ content. The addition of a small amount of SnO₂ (x ≤ 0.01) to ZnO led to an increase in both the electrical conductivity and the absolute value of the Seebeck coefficient, resulting in a significant increase in the power factor. The thermoelectric power factor was maximized to a value of 1.25 × 10⁻³ Wm⁻¹ K⁻² at 1073 K for the Zn_0.99Sn_0.01O sample.     

Crystal and magnetic structure and cation distribution of Mn2−xV1+xO4 spinels (x = 0, 1/3 and 1)

We synthesized the spinel-type compounds belonging to the Mn_2−xV_1+xO₄ series with x = 0, 1/3 and 1 as polycrystalline powders. Crystal and magnetic structures were refined using synchrotron X-ray and neutron powder diffraction. At 300 K all members crystallize in the cubic system, space group , and show a structural transition at low temperature, changing to a tetragonal symmetry (space group I4₁/amd). Cations distributions between octahedral and tetrahedral sites were refined from neutrons diffraction (ND) data and explained based on crystal field stabilization energies (CFSE) and ionic radii. The magnetic unit cell is the same as the crystallographic one, having identical symmetry relations. The magnetic structure was refined as an arrangement of collinear spins, antiferromagnetically ordered, parallel to the c-axis of the unit cell. The refined site magnetic moments are smaller than those obtained from hysteresis cycles of the M vs. H measurements, indicating that some non-collinear disordered component coexists with the ordered component along the c-axis.     

Electrical properties of MgAl2-2xZrxMxO4 (M = Co, Ni and x = 0.00-0.20) synthesized by coprecipitation technique using urea

This paper presents the results of a study concerning the structural and electrical properties of MgAl_2-2xZr_xM_xO₄ (x = 0.00-0.20 and M = Co²⁺ and Ni²⁺) prepared by a coprecipitation technique using urea as a precipitating agent. The X-ray diffraction data for the pure and its doped samples are consistent with the single-phase spinel and their crystallite sizes are in the range 7-20 ± 4 nm. The DC resistivity increases from 3.09 × 10⁹ Ω cm to 6.73 × 10⁹ and 8.06 × 10⁹ Ω cm whereas dielectric constant decreases from 5.80 to 5.11 and 4.95 on doping with Zr-Co and Zr-Ni, respectively. The electrical resistivity variations with increase in the dopant contents indicate two types of conduction mechanisms in operation. Several parameters such as, hopping energy (W), metal-semiconductor transition temperature (T_MS) and Debye temperature (θ_D) have also been determined. The increase in DC resistivity and decrease in dielectric constant suggest that the synthesized materials can be considered for application as an insulating and structural material in fusion reactors.     

Crystal structures and properties of BiMn1−xAlxO3 with x = 0.03 and 0.1

Crystal structures of BiMn_0.97Al_0.03O₃ (I) at 300 and 470 K and BiMn_0.9Al_0.1O₃ (II) at 90 and 300 K were studied with synchrotron X-ray powder diffraction. The strong Jahn-Teller distortion, observed at 300 K in I and associated with orbital order, disappeared at 470 K completely for one site and partially for the second site. The Mn/Al-O distances were very close to each other in I at 470 K and in II at 90 and 300 K indicating that orbital order did not appear in II even at 90 K. Magnetic properties of I and II were investigated with specific heat, high-temperature dc magnetic susceptibility, and ac magnetic susceptibility using different driving ac and applied dc magnetic fields and different ac magnetic field frequencies. The anomaly on the specific heat associated with a magnetic transition was strongly suppressed in II compared with that of I and BiMnO₃.     

Itinerant ferromagnetism to insulating spin glass in SrRu1−xCuxO3 (0 ≤ x ≤ 0.3)

The ferromagnetic metallic oxide, SrRuO₃ (T_C ∼ 165 K) undergoes structural, magnetic and metal-insulator transitions upon substitution of Cu at the Ru-site. For x = 0.2 in SrRu_1−xCu_xO₃, the structure becomes a tetragonal with the space group I4/mcm and there is a signature of both ferromagnetic (T_C = 65 K) and antiferromagnetic (T_N = 32 K) ordering due to possible magnetic phase separation. The antiferromagnetism arises due to short range ordering of Cu- and Ru-moments. Jahn-Teller distortion of (Ru,Cu)-O₆ octahedra indicates that the copper ions are in 2+ oxidation state with ⁶t2g³eg electronic configuration. For x ≥ 0.1, narrowing of Ru-4d bandwidth by the substitution of Cu ions results in semiconducting behavior. For x = 0.3, the ac and dc susceptibility measurements indicate a spin glass behavior. The origin of spin glass behavior has been attributed to competing ferromagnetic and antiferromagnetic interactions.     

R3Mn1.5CuV0.5O9 (R = Y, Ho, Er, Tm, Yb and Lu) and Lu3Mn3−3xCu2xVxO9: New noncentrosymmetric oxides related to YMnO3

We report formation of new noncentrosymmetric oxides of the formula, R₃Mn_1.5CuV_0.5O₉ for R = Y, Ho, Er, Tm, Yb and Lu, possessing the hexagonal RMnO₃ (space group P6₃cm) structure. These oxides could be regarded as the x = 0.5 members of a general series R₃Mn_3−3xCu_2xV_xO₉. Investigation of the Lu-Mn-Cu-V-O system reveals the existence of isostructural solid solution series, Lu₃Mn_3−3xCu_2xV_xO₉ for 0 < x ≤ 0.75. Magnetic and dielectric properties of the oxides are consistent with a random distribution of Mn³⁺, Cu²⁺ and V⁵⁺ atoms that preserve the noncentrosymmetric RMnO₃ structure.     

Formation, sintering, and electrical conductivity of (Nd1−xCax)CrO3 (0≤x≤0.25) using citric acid as a gelling agent

In Ca²⁺-substituted NdCrO₃, single-phase perovskite compounds (Nd_1−xCa_x)CrO₃, where x=0-0.25, have been formed by a citric acid processing. (Nd_1−xCa_x)CrO₃ powders consisting of submicrometer-size particles are sinterable; dense materials can be fabricated by sintering for 2 h at 1700°C under atmospheric pressure. The relative densities, grain sizes, and electrical conductivities increase with increased Ca²⁺ content. (Nd_0.75Ca_0.25)CrO₃ materials show an excellent electrical conductivity of 1.9×10 S m⁻¹ at 1000°C.     

Structural, electrical and optical properties of TiO2-WO3 polycrystalline ceramics

Mixed oxides from the TiO₂-WO₃ system were prepared as polycrystalline materials. Their phase composition and electrical conductivity were investigated using X-ray diffraction (XRD) and dc electrical measurements. The energy gap, evaluated on the basis of optical measurements, was presented as a function of W concentration. The influence of chemical composition on structural, semiconducting and optical properties of the TiO₂-WO₃ polycrystalline ceramics was discussed.     

Structural and electrical properties of La2−xBaxMo2O9−x/2 (x = 0-0.18)

La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) have been prepared by solid state reaction method. The lattice parameter of La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) determined by XRD data refinement shows a linear dependence on the dopant Ba content x. For the specimen with a La/Ba molar ratio of 0.18-0.2, additional reflection of secondary phase exists in the XRD pattern, so the value of solubility limit for Ba in La₂Mo₂O₉ is defined in range of 0.18 < x < 0.2. As the replacement degree of La³⁺ by Ba²⁺ increases, the bulk conductivity of La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) decreases initially and then increases, a minimum value at La_1.9Ba_0.1Mo₂O_8.95 exists. Hebb-Wagner studies in argon atmosphere, which use an oxide-ion blocking electrode, show that La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) are predominantly oxide-ion conducting in the temperature ranging from 773 to 1173 K. The average thermal expansion coefficient of La_1.84Ba_0.16Mo₂O_8.92 determined by high-temperature XRD was deduced as great as 17.5 × 10⁻⁶ K⁻¹ between 298 and 1173 K.     

Structure and magnetism in the oxygen-deficient perovskites Ce1−xSrxCoO3−δ (x ≥ 0.90)

We have examined the structure and phase behaviour of strontium-doped Ce_1−xSr_xCoO_3−δ and found that the perovskite form is stabilised over a relatively narrow solid solution range (x > 0.85). A combination of electron, powder X-ray and neutron diffraction has revealed tetragonal superstructures of the basic perovskite unit; (I4/mmm) 2a_p × 2a_p × 4a_p (x = 0.90) and (P4/mmm) a_p × a_p × 2a_p (x = 0.95). Magnetisation measurements show ferromagnetic behaviour under applied magnetic fields. Low temperature neutron diffraction of Ce_0.10Sr_0.90CoO_2.80 in zero field reveals a magnetic cell of dimension 2a_p × 2a_p × 4a_p with an ordered cobalt moment of 1.7 B.M. at 25 K.     

New cathode compositions based on La0.84Sr0.16Mn1−xMxO3, where M = Al, Ga for solid oxide fuel cell

In order to identify new cathode compositions for the high temperature solid oxide fuel cell, we have investigated the effect of the trivalent cations Al and Ga at the Mn site of the well-studied cathode composition La_0.84Sr_0.16MnO₃. All the compositions have been prepared by the low temperature citrate-nitrate auto-ignition process and sintered within the temperature range of 1150-1350 °C for 4 h. In order to understand the compatibility of the prepared samples as alternative cathode materials, we compared their electrical conductivity and thermal expansion coefficient with those of La_0.84Sr_0.16MnO₃ and yttria-stabilized zirconia. A 10 mol% Al doped La_0.84Sr_0.16MnO₃ composition exhibited a conductivity of around 122 S cm⁻¹ at 950 °C and a thermal expansion coefficient of 11.04 × 10⁻⁶ K with a minimum reactivity towards yttria-stabilized zirconia. Though the conductivity of the new composition is lower than that of La_0.84Sr_0.16MnO₃ (169 S cm⁻¹ at 950 °C), it is still high enough for use as a cathode material.     

Order-disorder phase transitions and high-temperature oxide ion conductivity of Er2+xTi2−xO7−δ (x = 0, 0.096)

The Er_2+xTi_2−xO_7−δ (x = 0.096; 35.5 mol% Er₂O₃) solid solution and the stoichiometric pyrochlore-structured compound Er₂Ti₂O₇ (x = 0; 33.3 mol% Er₂O₃) are characterized by X-ray diffraction (phase analysis and Rietveld method), thermal analysis and optical spectroscopy. Both oxides were synthesized by thermal sintering of co-precipitated powders. The synthesis study was performed in the temperature range 650-1690 °C. The amorphous phase exists below 700 °C. The crystallization of the ordered pyrochlore phase (P) in the range 800-1000 °C is accompanied by oxygen release. The ordered pyrochlore phase (P) exists in the range 1000−1200 °C. Heat-treatment at T ≥ 1600 °C leads to the formation of an oxide ion-conducting phase with a distorted pyrochlore structure (P2) and an ionic conductivity of about 10⁻³ S/cm at 740 °C. Complex impedance spectra are used to separately assess the bulk and grain-boundary conductivity of the samples. At 700 °C and oxygen pressures above 10⁻¹⁰ Pa, the Er_2+xTi_2−xO_7−δ (x = 0, 0.096) samples are purely ionic conductors.     

Synthesis and magnetic properties of layered MnPSxSe3−x (0 < x < 3) and corresponding intercalation compounds of 2,2′-bipyridine

In this work, we synthesize a series of new MnPS_xSe_3−x (0 < x < 3) compounds by high temperature solid-state reaction and also obtain the corresponding intercalation compounds (Mn_1−yPS_xSe_3−x(bipy)_4y, x = 1.2, 1.8 and 2.4) via the intercalation of 2,2′-bipyridine with MnPS_xSe_3−x. XRD results confirm that MnPS_xSe_3−x compounds show the layered structure and can be regarded as the solid solution of MnPS₃ and MnPSe₃. Magnetic measurements indicate that MnPS_xSe_3−x compounds exhibit paramagnetism with negative Weiss constant in the paramagnetic temperature region, and an antiferromagnetic phase transition occurs at the Neel temperature. It is found that the magnetic properties of MnPS_xSe_3−x slab are dramatically changed after the intercalation of 2,2′-bipyridine, which is close related to the relative ratio of S and Se atom as well as the intralayered Mn²⁺ vacancies of MnPS_xSe_3−x slab.