助剂对Cu-ZnO-Al2O3-SiO2催化剂性质和催化性能的影响

研究了助剂MgO、TiO2、ZrO2等对CO2直接加氢合成二甲醚的Cu-ZnO-Al2O3-SiO2催化剂性质和催化性能的影响,并用XRD、XPS、H2-TPD、CO2-TPD、H2-TPR等手段进行了表征.结果表明,助剂不同程度地促进了CuO和ZnO的分散;降低了Cu-ZnO-Al2O3-SiO2催化剂的TPR还原温度;加入的助剂富集于催化剂表面,除ZrO2以外的其他助剂均降低了催化剂表面Cu原子的浓度;助剂对H2、CO2吸附中心有调变作用;活性评价结果表明,CO2的转化率与表面Cu原子的浓度和催化剂吸附氢的能力有关,ZrO2是CO2加氢制二甲醚Cu-ZnO-Al2O3-SiO2催化剂的优良助剂.     

CuO-ZnO-Al_2O_3催化剂的改性及其CO_2加氢合成甲醇催化性能的研究

分别以Pd修饰的碳纳米管(Pd/CNT)、碳纳米管(CNT)、CeO2、ZrO2和Pd为促进剂对CuO-ZnO-Al2O3催化剂进行改性,在反应温度230~270℃、压力2.3~2.9 MPa、空速3 000~9 000 h-1条件下,考察各催化剂在CO2加氢合成甲醇反应中的催化活性,并利用SEM、XRD、H2-TPR、BET测试技术对催化剂进行结构表征.结果表明:促进剂对CuO-ZnO-Al2O3催化剂的改性作用依次为:Pd/CNTCNTZrO2CeO2Pd.其中,Pd/CNT作为一种高效促进剂,显著提高了催化剂的比表面积,减小了催化剂的颗粒直径,促进活性组分Cu的分散,提高催化剂的还原性能,明显改善CuO-ZnO-Al2O3催化剂的催化性能.     

Al2O3含量对Cu-ZnO-Al2O3-SiO2催化剂性能的影响

研究了Al2O3含量对Cu-ZnO-Al2O3-SiO2催化剂在CO2加氢合成二甲醚中催化性能的影响,并用XRD,H2-TPR,XPS,NH3-TPD和CO2-TPD等手段进行了表征.研究结果表明,Al2O3延缓了CuO和ZnO晶粒的长大,同时使催化剂变得难以还原.加入的Al2O3富集于催化剂表面,改变了催化剂表面Cu2+和Zn2+的摩尔分数.Al2O3还与SiO2产生无定形SiO2-Al2O3混合相,提供二甲醚合成所必需的酸碱中心.反应结果表明,Al2O3在催化剂中的质量分数低于1.4%时,对转化率的提高有促进作用;当Al2O3在催化剂中的质量分数为4.0%时,甲醇合成以及甲醇脱水的活性中心呈现出较好的"协同催化效应",目标产物二甲醚的收率最高.研究认为,Al2O3通过影响CuO与Al2O3之间的相互作用以及催化剂的表面酸性,从而使催化剂对CO2加氢合成二甲醚表现出不同的催化性能.     

纳米粉掺杂的Y2O3-ZrO2陶瓷的制备

采用纳米粉掺杂烧结制备了Y2O3-ZrO2陶瓷。测试发现，纳米粉的掺入在一定程度上可以使烧结体的密度和硬度得到提高。SEM和EDS分析表明，烧结体表面比较平滑，元素分布比较均匀，有较小的气孔存在。     

反应条件对CuO／Y2O3-ZrO2-Al2O3催化甲烷燃烧性能的影响

采用溶胶凝胶法制备CuO／Y2O3-ZrO2-Al2O3催化剂。研究了反应气甲烷与空气体积比和反应气体流速对CuO／Y2O3-ZrO2-Al2O3,催化剂性能的影响,结果显示：VCH4：VAir=1：25且气体流速为1800Loh-1时,该催化剂具有较好的催化活性和高温热稳定性。     

Structure and mechanical properties of ZrO2-mullite nano-ceramics in SiO2-Al2O3-ZrO2 system

ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray diffraction, infrared spectrum, scanning electron microscope and differential scanning calorimetric. And the mechanical properties of the nano-ceramics were studied. The results show that the bulks are still in amorphous state at 900 ℃ and the t-ZrO2 forms at about 950 ℃ with a faint spinel-like phase which changes into mullite on further heating. ZrO2 and mullite become major phases at 1 100 ℃ and an amount of m-ZrO2 occur at the same time. The sample heated at 950 ℃ for 2 h and then at 1 100 ℃ for 1 h shows very dense and homogenous microstructure with ball-like grains in size of 20-50 nm. With the increase of crystallization temperature up to 1 350 ℃, the grains grow quickly and some grow into lath-shaped grains with major diameter of 5 μm. After two-step treatment the highest micro-hardness, flexural strength and fracture toughness of the samples are 13.72 GPa, 520 MPa and 5.13 MPa·m1/2, respectively.     

Preparation of Al2O3-SiO2-TiO2-ZrO2 Composite Ceramic Membranes by Sol-Gel Method

Al2O3-SiO2- TiO2-ZrO2 supported membranes were prepared by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al2O3, TiO2 ( anatase ), Al2 SiO5 , and ZrO2 in these membranes. Changing the molar ratio of Al:Si: Ti : Zr ,the kinds and content of crystal phases of composite membranes could be different, which may lend to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investigated by XRD, SEM, AFM, EPMA. The effects of additives and heat treatments on the surface nanoscale topography and microstracture of composite ceramic membranes were also analyzed.     

Toughening mechanism of lined Al2O3-ZrO2 multiphase ceramics in SHS composite pipes

1. IntroductionEngineering ceramics is known worldwide becauseof its high operating temperature, corrosion resistanceand wear resistance. The ceramics-lined compositepipes are widely researched for their extensiveprospects in engineering application. The …     

基于Cu-Zn/Al_2O_3-ZrO_2催化剂的甲醇水蒸汽重整制氢试验

模拟内燃机尾气余热在非贵金属催化剂Cu-Zn/Al2O3-ZrO2的作用下,进行甲醇水蒸汽重整制氢试验.采用自行设计的燃料重整制氢装置,通过调整燃料重整的试验条件来提高产氢率,并得到较优的重整制氢方案.结果表明:反应温度是甲醇水蒸汽重整反应中最关键的因素,重整气中氢气的体积分数随着温度的升高而逐渐加大.空速会直接影响反应原料滞留在催化剂表面的时间,因此空速为最小值376 h-1时,重整制氢效果更好.最佳的水醇物质的量比和原料流量分别为6∶1和0.4 mL/min.在最佳的试验条件组合下,当反应温度为600℃时,重整气中氢气的体积分数可以达到56.61%.因此,基于Cu-Zn/Al2O3-ZrO2催化剂的车载甲醇水蒸汽重整制氢技术具有实际应用的可行性.     

二氧化碳加氢制甲醇反应机理研究进展

随着工业的迅速发展，化石燃料的使用给生态环境带来的负面影响越来越凸显。其中，CO2作为主要的温室气体对全球气候变化造成严重的危害。CO2选择性加氢制甲醇是解决温室效应、发展绿色能源和实现经济可持续发展的重要途径之一。Cu基催化剂以其优异的催化性能和低廉成本而被广泛应用于CO2加氢制甲醇反应研究中。Cu基催化剂化学性质和电子特性的高度可调性，往往使其反应机理具有差异性，进而展现出不同的催化性能。针对Cu基催化剂催化CO2选择性加氢制甲醇的反应机理进行综述，旨在通过对反应机理的深入认识，为高效稳定的Cu基催化剂设计提供理论指导。     

超细铜基催化剂上CO_2加氢合成甲醇催化性能研究

用溶胶-凝胶法制备得到超细Cu-ZnO/TiO2-SiO2催化剂。考察了在CO2加氢合成甲醇反应中,还原温度、反应温度、反应压力和体积空速对催化剂活性和选择性的影响。确定了该体系催化剂的适宜反应工艺条件,并对催化剂组成与催化活性的关系进行了研究。     

Preparation of Al_2O_3-SiO_2-TiO_2-ZrO_2 Composite Ceramic Membranes by Sol-Gel Method

1　Introduction Membrane techniques have had extensive applica tions in water treatment, sterilization of medicine and bev erage, recovery and purity of living things, micro elec tronics industry and gas separation[1]. In past years,many me…     

V2O5-Fe2O3催化甲醇乙醇合成异丁醛的研究

研究V2O5-Fe2O3催化剂对甲醇-乙醇一步合成异丁醛反应的催化性能.在反应温度为653 K、空速为2.72 h-1的实验条件下,乙醇的转化率和异丁醛的选择性随着V含量的增加,先增加后降低,当V2O5质量分数为80%、Fe2O3质量分数为20%时,有较好的催化效果,乙醇的转化率为84.1%,异丁醛的选择性为43.3%.当Fe与V形成Fe0.12V2O5.16结构时,对甲醇乙醇合成异丁醛反应有较好催化效果.     

在Ni /Al2O3催化剂上苯加氢反应本征动力学研究

采用ＣＤＳ８１０实验系统,在实验条件为：常压、氢苯比３、温度３６３．１５－４５３．１５Ｋ时,研究了在Ｎｉ／Ａｌ２Ｏ３催化止气相苯加氢反应的本征动力学,利用实验数据对几种可能的动力学模型进行参数估值,最后得到该反应的动力学模型为：在Ｎｉ／Ａｌ２Ｏ３催 有两类吸附中心,分别吸附氢、苯及其产物相且所有吸附达平衡;氢呈分子吸附;往苯环上加第一个氢分子为速率控制步骤。该模型方程与实验数据拟合很好,平均偏差为     

CO和CO_2同时加氢合成甲醇反应本征动力学

在 4.5 MPa、工业反应温度和一定原料气组成范围内 ,在新型 CQ2 0 1催化剂上用直流流动等温积分反应器研究了 CO和 CO2 同时加氢合成甲醇反应本征动力学。通过对动力学模型统计检验 ,模型在所研究的压力、温度和一定组分浓度范围内均是适用的。模型 ( B)较模型 ( A)合理     

改性骨架镍催化剂在3-NBSA加氢制备间氨基苯磺酸中的应用

实验研究了改性骨架镍催化剜在间硝基苯磺酸（3-NBSA）加氢还原制备间氨基苯磺酸（3-ABSA）中的应用．通过在加氢还原过程中对转化率影响备件的研究，优化加氢反应工艺条件并探讨催化剂的重复使用能力．实验结果表明，在催化剂用量为2．5％，反应温度60～80℃．反应压力2MPa的条件下，间氨基苯磺酸的收率可达99％以上．在上述反应条件下通过对催化荆使用寿命的考查表明，若每次补加0．5％-0．7％（质量分数）的催化剂，催化剂连续使用6次，产品收率依然保持在99％以上．