Influence of solutionising and aging temperatures on microstructure and mechanical properties of cast Al–Si–Cu alloy

Abstract

This paper presents the influence of solution and aging temperatures on the microstructure and mechanical properties of 319 secondary cast aluminium alloy. Experimental alloy was subjected to different heat treatment cycles. Heat treatments were designed with two solutionising temperatures (504 and 545°C) at two solutionising times (4 and 8 h), followed by quenching in water at 60°C and artificial aging. The artificial aging was carried out at two temperatures (200 and 154°C) for 6 h. The improvement in mechanical properties was obtained with low solution temperature (504°C) for 8 h followed by quenching in water to 60°C and aging at low temperature (154°C). The increase in the solutionising temperature from 504 to 545°C was recommendable only for short solutionising time (4 h). Increase in the aging temperature from 154 to 200°C has led to the increase in hardness with the corresponding decrease in ductility. Aging under unfavourable conditions (prolonged aging at high temperature) caused coarsening of spheroidised eutectic silicon crystals and precipitated particles resulted in deleterious effect on the tensile strength.     

Effect of Si content on microstructure and mechanical properties of Al–Si–Mg alloys

Microstructure and mechanical properties of as-cast and as-extruded Al–Si–Mg alloys with different Si content are investigated by tensile test, microstructure observation. High density of Si particles in the Al alloys can induce dynamic recrystallization during hot extrusion and it becomes more matured with an increase in the density of Si particles. The tensile strength of as-cast and as-extruded alloys can be improved with the increase of Si content and hot extrusion make the elongation of alloys increase dramatically. Considerable grain refining effect caused by recrystallization occurred during hot extrusion of S2 (equivalently commercial A356 alloy) and S3 (near eutectic alloy) alloys plays an important role in the improvement of elongation. A good combination of strength and elongation for the as-extruded S3 alloy indicates that near eutectic Al–Si alloys can be hot-extruded to produce aluminum profiles with high performance.     

Effects of Cu content on microstructure and mechanical properties of Al–14.5Si–0.5Mg alloy

This study elucidates how Cu content affects the microstructure and mechanical properties of Al–14.5Si–0.5Mg alloy, by adding 4.65 wt.% and 0.52 wt.% Cu. Different Fe-bearing phases were found in the two alloys. The acicular β-Al₅FeSi was found only in the high-Cu alloy. In the low-Cu alloy, Al₈Mg₃FeSi₆ was the Fe-bearing phase. Tensile testing indicated that the low-Cu alloy containing Al₈Mg₃FeSi₆ had higher UTS and elongation than the high-Cu alloy containing the acicular β-Al₅FeSi. It is believed that the presence of the acicular β-Al₅FeSi in the high-Cu alloy increased the number of crack initiators and brittleness of the alloy. Increasing Cu content in the Al–14.5Si–0.5Mg alloy also promoted solution hardening and precipitation hardening under as-quenched and aging conditions, respectively. The hardness of the high-Cu alloy therefore exceeded that of low-Cu alloy.     

The synergic effects of Sc and Zr on the microstructure and mechanical properties of Al–Si–Mg alloy

In order to clarify the possibility of Zr substitution for Sc on the modification of Al-Si casting alloys, the microstructural evolution and tensile properties of Al-Si-Mg based alloys with different combinations of Sc and Zr contents (Sc + Zr = 0.5 wt.%) were systematically investigated. It was found that 0.5 wt.% Sc addition could refine the microstructure significantly and modify the eutectic Si from plate-like morphology to fiber, which promotes the spheroidization of eutectic Si during heat treatment. When Zr was added to partly replace Sc, the microstructure was first further refined, but was then slightly coarsened with increasing Zr content. Moreover, high Zr content was found to decrease its modification on eutectic Si. It was observed that Zr can also concomitantly improve strength and ductility compared with the alloy modified by Sc only. The improvement of mechanical properties was attributed to microstructural refinement, particularly the modification of eutectic Si and precipitation of secondary nano-scale Al₃(Sc_1 − xZr_x) dispersoids.     

Effect of microstructure on fatigue behaviour of cast Al–7Si–Mg alloy

Abstract

The fatigue behaviour of a cast Al–7Si–Mg alloy, conforming to A356, has been studied. Specimens of this material were tested in both the as cast condition and a solution treated and aged condition. It was observed that the size, number, and position of casting defects influenced the fatigue life very strongly. This marked effect nearly hides that of the heat treatment. Nevertheless, if the analysis is carried out considering only results obtained from sound specimens it is revealed that the heat treatment causes an improvement in the fatigue resistance of the alloy.     

Microstructure and mechanical properties of Al–Si cast alloy with additions of Zr–V–Ti

The microstructure and tensile properties at temperatures up to 300 °C of an experimental Al–7Si–1Cu–0.5Mg (wt.%) cast alloy with additions of Ti, V and Zr were assessed and compared with those of the commercial A380 grade. The microstructure of both alloys consisted of Al dendrites surrounded by Al–Si eutectic containing, within its structure, the ternary Al–Al₂Cu–Si phase. Whereas the Al₁₅(FeCrMn)₃Si₂ phases were present in the A380 alloy, Ti/Zr/V together with Al and Si phases, Al(ZrTiV)Si, were identified in the experimental alloy. As a result of chemistry modification the experimental alloy achieved from 20% to 40% higher strength and from 1.5 to 5 times higher ductility than the A380 reference grade. The role of chemistry in improving the alloy thermal stability is discussed.     

Development of microstructure and mechanical properties of as cast Al–Mg–Mn alloy during high temperature ECAP

Abstract

A large scale billet with diameter of 58·5 mm of an as cast Al–Mg–Mn alloy was processed by equal channel angular pressing (ECAP) at 350°C up to six passes. A significant refinement of the grains was observed after six pressings to ～2 μm. And the selected area electron diffraction (SAED) pattern showed that almost all of the grains were separated by boundaries with high angles of misorientation. A banded substructure was not observed during the hot ECAP, and a reasonably equiaxed structure was obtained just after one single pressing. Both the strength and the elongation increased abruptly in a single passage through the die, but thereafter, the increase was more gradual and exhibited a saturation effect after the fourth pressing. The good combination of strength and ductility of the Al–Mg–Mn alloy attained by the hot ECAP appeared to be attractive properties for industrial applications. Moreover, hot ECAP could possibly be used as an alternative step to hot extrusion or hot rolling in industrial processing, to break down an initial coarse as cast structure in a quite large scale billet.     

The effects of Mg amount on the microstructure and mechanical properties of Al–Si–Mg alloys

In this study, the effects of magnesium (Mg) addition to A356 aluminum alloy at different amounts on the microstructure and mechanical properties of this alloy were examined. For the experimental studies, three different alloys (0.43, 0.67 and 0.86 wt%) having various amounts of Mg were prepared through casting process in the form of plates. The plates were homogenized and cooled in the furnace. All the samples were treated with aging process (T6) and then tensile samples were prepared from the homogenized samples. The samples treated with T6 process were characterized by optical microscopy, laser confocal microscopy, Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS) and X-Ray Diffraction (XRD) examinations as well as hardness measurements and tensile tests. The phases which were formed in the microstructures for different amounts of Mg were examined. It was observed that iron-rich intermetallic compounds were also formed in addition to the phases resulting from the aging process. Fe-rich intermetallic compounds, observed from the fracture surfaces, were found to reduce the tensile strength the alloy. The results also indicate that the tensile strength and hardness of the alloy increase with increasing Mg amount.     

Effects of heat treatment on microstructure and mechanical properties of twin roll casted Al–5.5Mg–0.02Ti alloy

In the present investigation the Al–5.5Mg–0.02Ti alloy produced by twin roll casting (TRC) process (varying rolling speed, i.e., 3, 4, and 5 rpm) has been subjected to heat treatment for microstructure modification. Grain coarsening at the center of the strip has been observed during heat treatment process. Homogeneous microstructure of the alloys has been achieved by heat treatment process, and it has been found that the time to achieve homogeneous structure depends on the rolling speed. Transmission electron microscope (TEM) studies revealed that undesired Mg rich phase (Mg₅Al₈) has been successfully eliminated by heat treatment process. Fine and equi-axed grains in the alloys obtained by heat treatment process shows high strength and elongation.     

Effect of solidification conditions on microstructure,mechanical and wear properties of Mg–5Al–3Ca–0.12Sr magnesium alloy

In the present study, the microstructure, mechanical and wear properties of AXJ530 alloy under different solidification condition were investigated. AXJ530 alloys were cast in a multi-step permanent mould casting (PMC) with five different cooling rates, and also in high pressure die casting (HPDC). The effect of cooling rate was determined for the room temperature mechanical properties and the dry sliding wear resistance of the AXJ530 alloys. The results showed that grain size of AXJ530 alloy was refined and thinner lamellar eutectic phase formed at higher cooling rate. It was concluded that these changes led to the observed concurrent increases in ultimate tensile strength (σ_uts), yield strength (σ_0.2) and elongation (δ) of the AXJ530 alloy. The relationship between grain size and yield strength/hardness agreed with Hall–Patch behavior. The dry sliding wear rate of the PMC specimens decreased with increasing of cooling rate, but micro-porosity/inclusion in the HPDC specimen decreased its wear resistance properties. Abrasion was determined to be the dominant wear mechanism for the AXJ530 alloys.     

Effect of cooling aging on microstructure and mechanical properties of an Al–Zn–Mg–Cu alloy

In the present work, Al–Zn–Mg–Cu alloy was aged by non-isothermal cooling aging treatment (CAT). At high initial aging temperature (IAT), the hardness was decreased with the decreased cooling rate. However, when IAT was lower than 180 °C, the hardness was increased with the decreased cooling rate. Conductivity was increased with the decreased cooling rate regardless of IAT. The tensile strength, yield strength and conductivity of Al alloy after (200–100 °C, 80 °C/h) CAT were increased 2.9%, 8.1% and 8.3% than that after T6 treatment, respectively. With an increase of IAT and decrease of cooling rate, the fine GP zone and η′ phase were transformed to be larger η′ and η precipitates. Moreover, continuous η phase at grain boundary was also grown to be individual large precipitates. Cooling aging time was decreased about 90% than that for T6 treatment, indicating cooling aging could improve the mechanical properties, corrosion resistance and production efficiency with less energy consumption.     

Effect of nickel on the microstructure and mechanical property of die-cast Al–Mg–Si–Mn alloy

The effect of nickel on the microstructure and mechanical properties of a die-cast Al–Mg–Si–Mn alloy has been investigated. The results show that the presence of Ni in the alloy promotes the formation of Ni-rich intermetallics. These occur consistently during solidification in the die-cast Al–Mg–Si–Mn alloy across different levels of Ni content. The Ni-rich intermetallics exhibit dendritic morphology during the primary solidification and lamellar morphology during the eutectic solidification stage. Ni was found to be always associated with iron forming AlFeMnSiNi intermetallics, and no Al₃Ni intermetallic was observed when Ni concentrations were up to 2.06 wt% in the alloy. Although with different morphologies, the Ni-rich intermetallics were identified as the same AlFeMnSiNi phase bearing a typical composition of Al_[100–140](Fe,Mn)_[2–7]SiNi_[4–9]. With increasing Ni content, the spacing of the α-Al–Mg₂Si eutectic phase was enlarged in the Al–Mg–Si–Mn alloy. The addition of Ni to the alloy resulted in a slight increase in the yield strength, but a significant decrease in the elongation. The ultimate tensile strength (UTS) increased slightly from 300 to 320 MPa when a small amount (e.g. 0.16 wt%) of Ni was added to the alloy, but further increase of the Ni content resulted in a decrease of the UTS.     

Effects of solution treatment on the microstructure and mechanical properties of Al–Cu–Mg–Ag alloy

The effects of solution treatment on the microstructure and mechanical properties of Al–Cu–Mg–Ag alloy were studied by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive X-ray (EDX), differential scanning calorimeter (DSC), transmission electron microscopy (TEM) and tensile test, respectively. The results show that the mechanical property increases and then decreases with increasing the solution temperature. And the residual phases are dissolved into the matrix gradually, the number fraction of the precipitation and the size of recrystallized grains increase. Compared to the solution temperature, the solution holding time has less effect on the microstructure and the mechanical properties of Al–Cu–Mg–Ag alloy. The overburnt temperature of Al–Cu–Mg–Ag alloy is 525 °C. The yield strength and the elongation get the best when the alloy is solution treated at 515 °C for 1.5 h, is 504 MPa and 12.2% respectively. The fracture mechanism of the samples is ductile fracture.     

Evaluating the microstructure and mechanical properties of friction stir processed Al–Si alloy

In this study, mechanical behaviour and microstructural evolution in friction stir processing (FSP) of casting hypereutectic A390 aluminium alloy have been investigated. The mechanical behaviour of FSP samples was investigated by measuring the strain rate sensitivity using shear punch testing. The room-temperature shear punch tests were conducted at shear strain rates in the range of 10^?4–10^?1?s^?1. The results indicate that the strain rate sensitivity index increases from about 0.015 to 0.120 for as-cast A390 after third FSP pass and then experiences a further growth in FSP passes. The increase in the grain size and CuAl₂ intermetallic particle size result in a reduction in strain sensitivity index as well as shear strength after third FSP pass.     

Effect of minor cerium additions on microstructure and mechanical properties of cast Al – Cu – Mg – Ag alloy

Abstract

A series of cast Al – Cu – Mg – Ag based alloys with minor cerium additions have been investigated using optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy and transmission electron microscopy. It was found that increasing the cerium content from 0 to 0.45 wt-% increased the tensile strength at the test temperatures of 25°C and 300°C. The high strength of the casting alloys with cerium is attributed to the refined grains and the high density of fine ω precipitates. However, the addition of 0.2 wt-%Ce to the alloy with 0.25 wt-%Ti induced a detrimental effect on the mechanical properties. The cause of this was found to be the formation of the intermetallic compound Al_x Ti₆ Ce₃ Cu.     

Microstructure and mechanical properties of Al–Si–Mg–Cu–Ti alloy with trace amounts of scandium

The effect of Sc on the microstructure and mechanical properties of Al–Si–Mg–Cu–Ti alloy was investigated. Results obtained in this research indicate that, with increasing Sc content, the microstructure of the investigated alloys exhibits finer equiaxed dendrites with rounded edges and the morphology of the eutectic Si shows a complete transition from a coarse needle-like structure to a fine fibrous structure upon modification of eutectic Si. Subsequent T6 heat treatment had further induced the precipitation of nano-scaled secondary Al₃(Sc, Ti) phase, as well as spheroidisation of eutectic Si. Combined with T6 heat treatment, the ultimate tensile strength, yield strength, percentage elongation and hardness were achieved in 0.20?wt-% Sc-modified alloy.     

Effect of modification treatment on the microstructure and mechanical properties of Al–0.35%Mg–7.0%Si cast alloy

The effects of barium modifier content on the mechanical properties, microstructures, and wear resistance of Al–Mg–Si alloys at room temperature have been analyzed. The modification caused the disappearance of primary silicon with the formation of solid solution dendrites and fine fiber or rod-like eutectic silicon instead of plate-like structures. This resulted in a highly branched filamentary form with a better distribution of Si particles. The Ba modifier with 1.0 wt.% exhibited the best results for the mechanical properties of alloy. The Al–Mg–Si alloy with modification had good remelting property. The effect of modification was still obvious after being remelted for four times. The scanning electron microscope fractographs of tensile samples at different magnifications revealed that the alloys failed in a mixed-mode fracture comprising of intergranular fracture, quasi-cleavage plane, and transgranular shear.     

Effect of processing variables on structure and tensile properties of investment cast Al–Si–Mg casting alloy

Abstract

A research programme was conducted to study the effects of grain refinement, eutectic silicon modification, filtering, pouring and shell preheat temperatures, and heat treatment on the structure and tensile properties of an investment cast Al–Si–Mg alloy, LM25 (BS 1490 : 1988). The principal findings of the research were that: an increase in shell preheat temperature adversely affects the structure and, hence, the tensile properties; grain refinement was enhanced as the titanium content was increased to about 0·28% but the tensile properties were not affected; a modified eutectic silicon structure was achieved with strontium additions in the range 0·01–0·02%, with the optimum addition, based on tensile properties, being 0·01%; and, as would be expected, heat treatment improved the tensile properties. On the basis of the interrelationships between process variables, structural changes, and tensile properties observed, an optimum processing route was identified. The optimum tensile properties were obtained in fully heat treated specimens that had been both grain refined and modified and produced in moulds poured at ambient temperature.