SURFACE OXIDATION OF THE AMORPHOUS ALLOY Ni_(68)P_(18)Cr_(14)

The surface layer of Ni_(68)P_(18)Cr_(14) amorphous alloy was studied by AES and XPS associated with ion beam sputtering. It was found that great differences existed between the surface layer and the bulk both in composition and chemical states. The dominant component elements Ni and P were of lower content in the surface laver, while Cr was enriched. Cr was drastically oxidized in the surface layer, but Ni underwent no oxidation. There was a P enriched region just helow the surface oxide layer, which was supposed to enhance the surface segregation of Cr. Ni underwent no oxidation in Ni_(68)P_(18)Cr_(14) amorphous alloy.     

HEAT CAPACITIES OF Fe_（40）Ni_（40）B_（20） GLASSY ALLOY MEASURED BY ENTHALPY METHOD

ＨＥＡＴＣＡＰＡＣＩＴＩＥＳＯＦＦｅ_（４０）Ｎｉ_（４０）Ｂ_（２０）ＧＬＡＳＳＹＡＬＬＯＹＭＥＡＳＵＲＥＤＢＹＥＮＴＨＡＬＰＹＭＥＴＨＯＤ￥ＪＩＡＮＧＱｉｎｇ;ＺＨＡＯＭｉｎｇ;ＬＩＪｉａｎｃｈｅｎ（ＪｉｌｉｎＵｎｉｖｅｒｓｉｔｙｏｆＴｅｃｈｎｏｌ?..     

深过冷合金再辉与凝固组织的研究

发现深过冷Ni_(68)B_(21)Si_(11)合金液形核过程中的多次再辉现象,揭示了二次和三次再辉的过冷条件,以及对凝固组织的影响。研究结果表明,深过冷Ni_(68)B_(21)Si_(11)合金液存在两种凝固机制:一是NilB,Nj‘si,B和Ni,B的三相共晶生长;另一个是以NilB为领先相的枝晶簇生长。当过冷度低于200K或超过310K时,合金液凝固仅伴生一次再辉,其晶体生长以第一种凝固方式进行。其他过冷范围内的合金液则发生多次再辉和枝晶簇凝固。     

预退火时间对Pd40Cu30Ni10P20玻璃转变及晶化的影响

采用示差扫描量热(DSC)分析方法,测定了大块非晶合金Pd40Cu30Ni10P20经523 K((Tg-100 K)＜7＜Tg)不同时间(0～64 h)预退火后的玻璃转变温度7g、玻璃转变峰温度TM、起始晶化温度Tx、晶化峰的峰温Tp、晶化焓以及在玻璃转变过程中的比热容增量,并根据Kissinger公式计算了晶化的表观活化能.同时,测量了不同时间预退火后样品的显微硬度.结果表明:在玻璃转变温度以下的预退火处理使Pd40Cu30Ni10P20大块非晶合金的微观原子组态发生变化,从而影响了其随后的玻璃转变行为,但对晶化的影响不大.其显微硬度随预退火时间的延长而逐步增加后趋于稳定.并利用结构弛豫理论分析了预退火对玻璃转变、晶化和显微硬度的影响.     

激光熔覆大厚度Fe57Co8Ni8Zr10Si4B13非晶表层及其微结构研究

利用激光熔覆制备出１．２ｍｍ厚的Ｆｅ５７Ｃｏ８Ｎｉ８Ｚｒ１０Ｓｉ４Ｂ１３大厚度非晶表层。用ＸＲＤ,ＥＤＳ,ＴＥＭ,ＤＳＣ及硬度仪对获得的非晶表层进行了多种分析,研究了非晶合金表层的微结构与非晶形成能力,初步探讨了大厚度非晶表层的形成机制。     

净化对非晶形成能力和非晶热稳定性的影响SCIEI

采用玻璃熔体净化法和电磁悬浮循环过热法消除Ni_(75),B_(17)Si_R合金液内的异质核心,研究了净化对该合金液非晶形成能力和所形成的非晶合金热稳定性的影响。采用净化和忽冷相结合的工艺制备出了20×10×0.5mm的Ni_(75)B_(17)Si_8非晶试样,试样的厚度较净化前提高了4倍。     

镧对非晶态FeCr_(8.6)Ni_(12)P_(14)B_6合金耐蚀性的影响

添加微量La能显著改善FeCr_(8.6)Ni_(12)P_(14)B_6非晶态合金的耐蚀性能。在该合金中加入0.075％La后,所得非晶态合金在4N盐酸中有较好的耐蚀性能(腐蚀率小于10~(-2)毫米/年)。AES和XPS的分析结果说明,添加微量La能促进合金在HCl溶液中形成薄而致密的表面膜,这是改善其耐蚀性的主要原因。     

Al_(72)Ni_(12)Co_(16)单相准晶合金的凝固特性研究

利用普通浇注方法和SEM、XRD、DTA、TEM等分析手段,研究了Al_(72)Ni_(12)Co_(16)准晶合金的结构旋转对称特征、微观组织与凝固特性.研究结果表明,在普通铸造条件下,Al_(72)Ni_(12)Co_(16)合金为单相多孔组织.合金在凝固过程中,准晶直接从液相中析出,该合金的液相线温度与包晶反应温度相隔很近,说明该准晶为近一致熔融化合物.     

Sc对Zr基块体非晶合金晶化动力学的影响

以海绵锆为原材料,利用浇包型坩埚电弧炉倾斜铸造法制备Zr52.5Cu17.9Ni14.6Al10Ti5五元块体非晶合金楔形试样,研究活性元素Sc对合金玻璃形成能力及晶化动力学参数的影响。结果表明:Sc的加入可显著增大合金的最大非晶形成厚度,但对合金过冷液相区温度范围所表征的热稳定性影响较小。Sc虽然使合金的晶化激活能降低,但使晶化孕育期时间常数增大,晶化频率因子减小,二者的综合作用使合金晶化孕育期延长,过冷倾向增大,玻璃形成能力提高。     

机械合金化制备TiCuNiSnTa非晶粉末的研究

采用机械合金化(MA)方法,选择Ti-Cu-Ni-Sn-Ta合金体系,通过高能球磨制备钛基非晶粉末。研究球磨时间对钛基混合粉末的形貌、组织结构演化和热稳定性的影响以及合金成分对非晶形成能力的影响,并对合成的粉末进行了XRD分析。结果表明,球磨时间对非晶的形成和晶粒细化有显著影响,球磨后粉末各组元呈均匀化弥散分布;成分为Ti64Cu11.2Ni9.6Sn3.2Ta12的合金具有较宽的过冷液相区,最终获得了Ti基非晶复合材料,而成分为Ti58.8Cu1.1Ni3.2Sn5Ta31.9的合金在高能球磨过程中没有发生非晶转变。     

热处理对Co_(38)Ni_(34)Al_(28-x)Cu_x合金组织和显微硬度的影响

在Co-Ni-Al系合金的基础上用Cu部分代替Al,制备4种不同成分的合金,研究热处理对Co38Ni34Al28-xCux显微组织和显微硬度的影响。结果表明,Co38Ni34Al27.5Cu0.5合金经1350℃×2 h加热、冰水冷却至室温处理后,β基体内出现马氏体,而Co38Ni34Al27Cu1则在1350℃×2 h和1300℃×4 h处理时都出现马氏体。随铜含量的增加和铝含量的减少,合金β相晶粒变小,γ相晶粒和含量变大。Co38Ni34Al27.5Cu0.5的显微硬度随温度升高而升高,在β相晶粒内出现马氏体时,Co38Ni34Al27Cu1合金的显微硬度骤降。     

(Ti,Zr,Hf)-(Cu,Ni,Ag)-Al多组元合金体系的机械驱动非晶化

研究了由前过渡族金属和后过渡族金属按照等原子比替代的(Ti0.33Zr0.33Hf0.33)50(Ni0.33Cu0.33Ag0.33)40Al10多组元合金在机械研磨作用下的非晶化转变,并与由熔体急冷制备的同一成分玻璃态合金进行了对比.两种途径获得的玻璃态相似.在机械研磨的稳态产物中,仍残留有少量尺寸小于30 nm的晶体相颗粒,即非晶化转变未能完全实现.机械研磨形成的非晶相表现有明确的玻璃转变和约80 K宽的过冷液态温度区间,晶化过程分两步进行,第一步晶化转变完成后,剩余的非晶相亦具有玻璃态行为,呈现另一玻璃转变及约100 K宽的过冷液态温度区间.     

Influence of Sb addition on Martensitic and Magnetic Transformation in β+γ Two-phase Based Co-Ni-Al Shape Memory Alloy

利用OM，SEM，EDX，XRD，DSC和VSM研究了用Sb替代Al对Co41Ni32Al27合金马氏体相变和磁性的影响．结果表明Co41Ni32Al26Sb1合金仍然生成L10型马氏体，其马氏体相变温度和Curie点与淬火温度成正比关系，淬火温度每升高10K，马氏体相变温度约提高9K，而Curie点约提高7．5K．相同淬火温度下Co41Ni32Al26Sb1合金的马氏体相变温度比Co41Ni32Al27合金约高70K，而Curie点也高出15K．Co41Ni32Al26Sb1在1623K热处理时出现共晶组织，发生部分熔化现象．特别重要的是C041Ni32A12eSbl合金的马氏体相变温度范围大幅度缩小，为20-28K，只有Co41Ni32Al27合金的一半，有利于获得大磁致应变．用平均s＋d总电子浓度和平均磁价电子数分别解释了马氏体相变温度和Curie点的变化．     

Cu74Ni12—xSnxP14合金的非晶形成趋势

用X射线衍射(XRD)和差动扫描量热(DSC)法研究了Sn对液态淬火Cu_(74)Ni_(12-x)Sn_xP_(14)合金非晶形成能力的影响,并从动力学和结构化学方面进行了分析,结果表明,适量添加Sn可使合金非晶形成能力得到改善,在x=2—6at-％Sn的成分范围内得到完全非晶组织。     

BSTUDY ON Ni_(25)Ti_(50)Cu_(25) SHAPE MEMORY PARTICLE/Al MATRIX COMPOSITE

ＳＴＵＤＹＯＮＮｉ_（２５）Ｔｉ_（５０）Ｃｕ_（２５）ＳＨＡＰＥＭＥＭＯＲＹＰＡＲＴＩＣＬＥ／ＡｌＭＡＴＲＩＸＣＯＭＰＯＳＩＴＥＬ．Ｓ．Ｃｕｉ；Ｍ．Ｑｉ；Ｐ．Ｓｈｉ；Ｆ．Ｘ．ＣｈｅｎａｎｄＤ．Ｚ．Ｙａｎｇ（ＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａｌｓＥ?..     

镍基固溶体增韧Cr_(13)Ni_5Si_2合金在含Cl~-溶液中的腐蚀行为

采用极化曲线,Tafel阿和电化学限抗谱(EIS)技术,研究了镍基固溶体增韧Cr_(13)Ni_5Si_2金属硅化物合金在不同Cl~-浓度Na_2SO_4+NaCl溶液中的电化学腐蚀行为,并对其表面钝化膜进行了X射线光电子能谱(XPS)分析.结果表明:由于超高的Cr含量易于在表面形成以Cr_2O_3为主的稳定钝化膜以及组成相Cr_(13)Ni_5Si_2和Cr3Ni5Si2高的化学稳定性,合金在不同Cl~-浓度溶液中均具有良好的耐蚀性;合金的开路电位,破裂电位和腐蚀电流密度等几乎不随Cl~-浓度的增加而改变,即合金对Cl~-浓度不敏感,在中性含Cl~-介质中耐蚀性优异.     

金属间化合物（Fe60Ni40）3（V98Ti2）的蠕变断裂

对有序金属间化合物(Fe_(60)Ni_(40))_3(V_(98)Ti_2)的蠕变断裂行为进行了初步研究。用透射电镜观察了稳态蠕变过程中位错亚结构的变化,发现存在大量的堆垛层错和成对位错以及较高密度的位错网络。对断口及近断口剖面的扫描电镜观察指出,晶界上空洞所形成的沿晶断裂是(Fe_(60)Ni_(40))_3(V_(98)Ti_2)蠕变断裂的主要机制。     

A Comparative Study on the Corrosion Performance of Ni_(47)Ti_(49)Co_4 and Ni_(51)Ti_(49) Shape Memory Alloys in Simulated Saliva Solution for Dental Applications

In this study, the corrosion behavior of Ni_(47)Ti_(49)Co_4 shape memory alloy(SMA) was investigated in simulated saliva solution with the binary alloy Ni_(51)Ti_(49) as a reference. The surface morphology and the chemical composition of the oxide films were characterized by scanning electron microscopy and X-ray photoelectron spectroscopy before and after immersion in the test solutions, respectively. The results showed that the ternary alloy was less affected by the test solution,owning to the formation of passive layer composed mainly of the oxides of titanium and cobalt in several oxidation states.Cyclic voltammetry, electrochemical impedance spectroscopy and potentiodynamic polarization measurements affirmed that the passive oxide film significantly improved the corrosion resistance of Ni_(47)Ti_(49)Co_4 SMAs as demonstrated by the smaller corrosion current density, larger resistance and smaller capacitance. Consequently, alloying with cobalt, which has paramount importance in enhancing the passive layer, expands the use of Ni_(47)Ti_(49)Co_4 SMAs in dental work as new nitinol alloys with high corrosion resistances.     

Al_(82)Ni_(10)Y_8合金雾化粉末的超高压固结成形及晶化过程

用紧耦合气雾化方法制备了Al_(82)Ni_(10)Y_8合金粉末.利用X射线衍射仪(XRD)、扫描电镜(SEM)、透射电镜(TEM)和差示扫描量热(DSC)方法分析了粉末特征.结果表明,粒径＜26 μm的粉末具有非晶和纳米晶结构.在450 ℃对粒径＜26 μm的合金粉末进行了超高压固结,随后在600 ℃对固结块体合金进行了1 h的热处理.利用电子探针分析了热处理后Al_(82)Ni_(10)Y_8合金的晶化过程,根据雾化粉末的XRD分析结果,表明其晶化过程为:非晶→α-Al+非晶→α-Al+非晶+Al_(19)Ni_5Y_3→α-Al+Al_3(Ni,Y)+ Al_(23)Ni_6Y_4 + Al_(19)Ni_5Y_3.     

Mg_(80)Cu_(15)Y_5合金的非晶形成能力及晶化行为

采用单辊快速凝同法制备出厚约40μm的Mg_(80)Cu_(15)Y_5非品合金薄带,利用XRD、DSC、TEM和HRTEM研究了非品合金的非品形成能力和晶化行为,分析了品化对合金组织结构与性能的影响.结果表明:Mg_(80)Cu_(15)Y_5合金的过冷液态温度区间△T_x和约化玻璃转变温度T_(rg)分别为55K和0.58,表明其具有较强的非晶形成能力;该合金在退火温度高于473 K后发牛明显晶化,从非品基体中析出 Mg_2Cu、Cu_2Y和Mg晶体相;随着退火温度的升高,合金的硬度呈现出先升高后降低的变化趋势,这与纳米品体相颗粒的弥散析出、重溶及粗化有关.