Kinetics of smelting reduction of fluxed composite iron ore pellets

Kinetic studies on smelting reduction of unreduced fluxed composite pellets (FCP) and fluxed composite pre-reduced iron ore pellets (FCRIP) have been carried out in an induction furnace. The pellets are charged into the slag layer floating on the carbon saturated molten iron bath in a graphite crucible. The slag basicity was however varied such that it has the same value as that of the pellets charged. The temperature of the slag is varied within the range of 1623K to 1823K for the pellets of basicity 2.0. Kinetic studies show a mixed kinetic model of both diffusion and chemical reaction controlled. While the smelting of FCRIP follows the model expressed as G(or) = 1-(2/3)(α) -(1-α)^2/3, the unreduced FCP pellets initially follow the diffusion controlled model of G(α) = α² followed by a chemical reaction controlled first order model of -ln(1-α) at the latter stages of smelting reduction, where α denotes the degree of reduction. The basicity dependence on the kinetics is not very significant. Comparison of the activation energy values explains that the smelting reduction with pre-reduced pellets seems to be a rather less energy intensive process.     

板坯连铸液压振动技术的特点及其发展前景

介绍了板坯结晶器液压振动技术的发展及国内外应用情况，液压振动的结构及其特点。介绍了液压振动在高频振动时运动平稳；高频和低频振动时波形不失真；在线可随机任意设定正弦曲线和非正弦曲线波形，并可调整振幅和频率。液压振动有着机械振动所实现不了的优越性，希望液压振动技术能够在我国连铸机的振动装置上得到推广应用     

高磷铁矿石含碳球团等温还原动力学

为了研究高磷铁矿石含碳球团等温还原动力学在温度为1 173、1 273、1 323、1 373、1 423和1 473K时,采用界面化学反应模型、Jander方程、Ginstling-Broushtein方程、G Valensi-R E Carter方程等固-固/气反应机理函数对反应过程进行拟合,并采用XRD、SEM、EDX等对样品的物相组成、微观形貌和元素分布进行表征分析。研究结果表明,随着还原程度提高,反应速率由0迅速增至最大值,随后逐渐减小并趋于平缓;当温度为1 173～1 373K时,反应过程符合界面化学反应,表观活化能为70.02kJ/mol,线性相关系数为0.948 1;当温度为1 373～1 473K时,反应过程符合Jander方程,限制步骤为铁离子固相扩散,表观活化能为215.36kJ/mol,线性相关系数为0.991 2。     

漏钢预报在板坯连铸的应用

以天津钢铁有限公司炼钢厂4#板坯连铸机为应用背景,结合炼钢厂4#板坯连铸热电偶在结晶器中的实际埋设情况,对4#板坯连铸的漏钢预报系统进行了软件部分的理论分析和现场应用研究,从而实现了提高4#板坯连铸机漏钢预报系统的预报准确率和及时性的目的.     

宝钢板坯连铸漏钢预报系统（BBPS）的开发与应用

漏钢预报是连铸的一顶重要技术,文中重要介绍了宝钢开发的漏钢预报系统BBPS,该系统从1999年9月投入现场应用以来,操作性能和各项技术指标双原引进日本的漏钢预报装置有较大的提高,在提高连铸机的产能、改善铸坯质量、减少漏钢事故等方面发挥了重要作用,该技术已完全取代了原来引进日本的技术。     

连铸结晶器内粘结漏钢的形成机理及对策

连铸结晶器内钢液弯月面在连铸生产中起着至关重要的作用，本文结合钢液弯月面的行为对粘结漏钢的形成进行了详细地分析，介绍了一种新的粘结漏钢形成机理，认为钢液弯月面的破损是粘结漏钢发生的直接起因，此外，还在该机理的基础上，探讨了防止粘结漏钢的对策。     

中关铁矿制备熔剂性球团生球性能试验

 通过增加熔剂性球团矿的入炉比例,能够改善炉料结构,降低炼铁系统能耗,并且通过“源头减量”的途径可以降低炼铁过程中污染物的排放。实现高球比冶炼的核心环节是制备熔剂性球团,而熔剂性球团质量取决于生球的性能,因此,保证生球质量是探究熔剂性球团制备工艺较为重要的环节。由于中关铁矿硅含量较低、镁含量适宜,适合作为低硅熔剂性球团的原料。以中关铁矿为原料探究熔剂性球团的制备工艺,并在此基础上分析了影响熔剂性球团生球质量的因素(粒度、时间、水分、膨润土、SiO₂含量、碱度和MgO含量)。试验结果表明,生球的抗压强度、落下强度及爆裂温度受碱度、SiO₂和MgO含量变化的影响不大;生球的抗压强度、落下强度及爆裂温度主要受造球时间、水分、黏结剂用量、铁矿粉及熔剂的理化性能影响,并在造球时间维持为12 min、水分维持为8%～9%、膨润土用量为2%时,生球抗压强度、落下强度及爆裂温度较优且满足运输与入炉要求。     

VAI连铸结晶器漏钢预报系统的应用实践

介绍了鞍钢鲅鱼圈钢铁分公司连铸机结晶器漏钢预报系统的工作原理和应用实践;通过对实际应用中产生的粘结漏钢报警信息分析,找出了影响漏钢误报和漏报的原因,并提出相应的改进措施,提高了结晶器漏钢预报系统的精度,降低粘结漏钢误报率。     

酒钢板坯连铸漏钢成因分析及预防措施

对于酒钢4号、5号板坯连铸机的主要产品Q235及低合金钢的生产,近几年由于操作、设备等因素造成较高的漏钢率,给生产和设备造成极大危害.分析了漏钢的原因,在无漏钢预警系统的前提下制定了针对粘结漏钢与裂纹漏钢的预防措施,使板坯漏钢率显著下降.     

铁矿直接还原用台车连续炉

介绍一种用于铁矿直接还原的台车连续炉，含碳球团料层铺在台车上并通过炉膛进行焙烧和还原。此炉子已经成功地用于铁精矿粉还原焙烧，所得到的海绵铁产品的金属化率大于92％，全铁约90％。和转底炉比较，台车连续炉的优点是结构简单，供热点少，台车维修方便；主要缺点是台车运转速度不能太快，焙烧时间较长。     

板坯连铸机结晶器液位波动分析及控制策略

分别从工艺与设备两个方面介绍了板坯连铸机结晶器液位波动的原因,主要分析了钢水质量、保护渣性能、铸坯鼓肚及拉矫速度变化、液位检测及控制等因素的影响,并提出控制策略。     

板坯连铸粘结型漏钢过程模拟及预报

建立了板坯连铸结晶器二维导热数学模型,计算了在正常拉坯状态下结晶器铜版的温度场及铸坯发生拉漏时结晶器温度场的变化.通过对粘结型漏钢过程的模拟和拉漏时结晶器温度场的分析,提出了对粘结型拉漏进行预报的预测参数     

略钢铸坯脱方成因分析和实践

对略钢小方坯连铸机铸坯脱方的原因进行了分析,并采取了相应的对策后,取得了较好的效果.     

Non-isothermal reduction characteristics of roasted high alumina iron ore pellets

Non-isothermal reduction of roasted Guangxi high alumina iron ore pellets with CO and H₂ was conducted with high temperature synchronisation thermal analyser (NETZSCH STA 409C/CD) to understand the reduction characteristic of the ore. Chemical analysis, X-ray diffraction examination and scanning electron microscope analysis were adopted to analyse the roasted and reduced pellets. The results show that there are three main phases of Fe₂O₃, Al₂O₃ and Al₃Fe₅O₁₂ in the roasted pellets. During reduction process, the iron bonded in hercynite and fayalite is difficult to be reduced by CO so that the final reduction degree is only 35.62% at the setting temperature of 1573?K. But with H₂ atmosphere, the reduction degree can reach 100% at about 1520?K. It suggests that the ferric ion can completely be reduced to metallic iron by H₂.     

连铸板坯角裂和边裂漏钢原因的分析

论述了板坯连铸漏钢的危害,分析了板坯角裂和边裂漏钢的原因,提出了防止措施和应注意的问题。     

白云鄂博铁球团矿异常还原膨胀的机理

通过对比白云鄂博铁矿、精矿及还原前后球团矿的显微结构,对白云鄂博球团矿异常还原膨胀的机理进行研究。研究结果表明,球团矿气孔中挥发分的爆发扩大了基体裂块间的孔隙,加快了还原气体的扩散,增加了反应面积,使还原速度加快,从而导致了球团矿恶性膨胀。白云鄂博球团矿的“挥发分膨胀理论”是一种全新的理论,对抑制白云鄂博球团矿的恶性膨胀具有重要指导意义。     

高铝铁矿焙烧球团非等温还原研究

采用CO、H_2对高铝铁矿焙烧球团在高温同步热分析仪(NETZSCH STA 409C/CD)中进行非等温还原.结果表明:焙烧球团经CO还原后,随着设定温度由1 273 K升高到1 473 K,最终还原度由32.21%仅增加到46.78%;而经H_2还原后,随着设定温度由1 273 K升高到1 573 K,最终还原度由81.93%增加到100%.在纯氢气还原条件下,高铝铁矿焙烧球团中的铁氧化物是可以被彻底还原的.     

高铝铁矿含碳球团直接还原的研究

用高铝铁矿粉配加煤粉造球,在实验室条件下,通过改变还原温度和碳氧比研究了含碳球团的还原,对还原后的球团进行化学分析以及X-射线衍射(XRD)检测。结果表明:试样在石墨坩埚中恒温还原4 h,还原完毕后立即取出通入惰性气体冷却,在还原温度为1 200℃、碳氧比为1.3时金属化率较高,达到88.45%,在此条件下,铁、铝分离效果较好。同时从工业应用角度分析了转底炉处理高铝铁矿石的可行性。     

基于模糊聚类及神经网络的连铸漏钢预报

在模糊RBF神经网络的基础上,通过融合基于贴近度的改进FCM和Conditional FCM算法,建立了改进的模糊RBF网络模型;并结合某钢厂连铸现场采集的历史数据将该模型应用于连铸漏钢预报的过程中。结果表明,改进的网络模型能更准确地辨识连铸粘结漏钢过程中典型温度模式1和模式2,对二者的预报率分别达到949%和983%,报出率均达到100%,其预报性能更佳,能更有效地预报拉漏事故。