Static recrystallisation and recrystallisation during hot deformation of Al–1Mg–1Mn alloy

Abstract

Plane strain compression tests at 5 s^?1 and at temperatures of 270–480°C have been carried out on an Al–1Mg–1Mn alloy containing a bimodal distribution of intermetallic particles and after a prior heat treatment to coarsen all particles to greater than 1 μm in size. During the heat treatment, recrystallisation of the initially hot worked material only proceeded with coarsening of the fine particles. During subsequent hot deformation, thin foil electron microscopy revealed that identical subgrain structures were developed in the two materials by dynamic recovery at temperatures below 450°C. At higher temperatures, the initially recrystallised material showed localised particle stimulated dynamic recrystallisation. The subsequent static recrystallisation rate was more than 10³ times faster in the material free from small particles.

MST/751     

Effect of equivalent strain and redundant shear strain on microstructure and texture evolution during hot rolling in Mg–3Al–1Zn alloys

Equivalent strain and redundant shear strain distribution in the roll bite during normal rolling were calculated by a numerical integration method combined with the experimental method. The microstructural parameters, such as length of high-angle grain boundaries (HAGB), length of low-angle grain boundaries (LAGB) per unit area, and (0002) basal texture in surface layer and center layer were measured quantitatively by EBSD or X-ray diffraction. The effect of equivalent strain and redundant shear strain on the microstructure and (0002) basal texture evolution in AZ31 alloy during hot rolling were examined. As a result, it was found that the formation of the HAGB depends on the equivalent strain, while the formation of the LAGB is strongly affected by the redundant shear strain, which restrains the formation of the LAGB. The experimental results also suggest that the redundant shear may have little effect on improving DRX and weakening the (0002) basal texture intensity when the redundant shear strain is in small to moderate range (≤0.8).     

Effect of precipitates on subgrain growth during continuous recrystallisation in Al–4Cu

Abstract

It was found that on annealing supersaturated and cold rolled Al–4Cu at 280°C subgrains were initially formed as a result of the rearrangement of dislocations. Concurrent with the formation of subgrains having well defined boundaries, θ particles were formed, situated mostly on the subgrain boundaries, and the growth of subgrains was therefore severely hindered by the particles, leading to continuous recrystallisation for annealing times up to 10 000 min at 280°C. The pinning force due to particles located on the subgrain boundaries was much greater than that due to randomly dispersed particles. Subgrain growth was found to be arrested for particle parameters f/r of greater than 0·25 μm^?1, where f is the particle volume fraction and r is the mean particle radius.

MST/1572     

Effect of strain on cavity development during Al–Zn–Mg–Cu alloy superplastic flow

Cavitation behaviour has been investigated in an Al–Zn–Mg–Cu alloy with an average grain size of 10?µm during superplastic deformation. The superplastic tensile tests were interrupted at different true strains at 530°C and 3?×?10^?4?s^?1. The results showed that cavity nucleation occurred above a critical strain in the optimum loading condition. It was easy for cavities to form at the triple junction due to the stress concentration caused by cooperative grain boundary sliding. Since the tensile stress was higher in the middle of the sample, the cavities were arranged in a straight line parallel to the tensile axis in the centre of the sample. A more appropriate cavity growth equation considering the critical strain was proposed to describe the cavitation behaviour.     

A study of recrystallisation textures in hot band of a continuous cast Al–Mn–Mg alloy

Abstract

The hot band of a commercial continuous cast (CC) Al–Mg–Mn alloy was annealed at different temperatures ranging from room temperature to 510°C for 3 h. The evolution of microstructure and crystallographic texture was investigated during the annealing treatment. It was found that the recrystallised alloy exhibited a severely elongated grain structure and a texture that consisted of a new type of component ({113}〈110〉) and two fibre components (〈100〉//ND and 〈110〉//ND), the axes of which were along the normal direction of the rolling plane (ND) in 〈100〉 and 〈110〉 respectively. The 〈100〉//ND fibre was dominated by a ND rotated cube orientation {001}〈310〉, while the 〈110〉//ND fibre was mainly composed of Goss and P orientation ({011}〈566〉). The formation of the {113}〈110〉 texture and two fibre textures was likely to be attributed to the concurrent precipitation effect taking place upon heating in annealing treatment of the alloy.     

Effect of nish rolling temperature on static recrystallisation in hot bands of electrical steel containing 1·3% silicon

Abstract

The effect of the finish rolling temperature (FRT) on recrystallisation behaviour in hot bands of an electrical steel containing 1·3%Si was investigated. Four sequential passes of hot rolling were carried out on the 1·3%Si electrical steel, with finish rolling temperatures ranging from 980 to 700°C, followed by isothermal annealing at 720°C. The experimental results showed that when Ar ₁ <FRT <Ar ₃, fine equiaxed subgrains formed at the boundaries between deformed and non-deformed grains in a necklacelike arrangement, and strain induced boundary migration (SIBM) was the main mechanism corresponding to the formation of recrystallisation nuclei for steels finish rolled below Ar ₁. However, the study also demonstrated that when FRT <(Ar ₁­100 K), a second nucleation mechanism, i.e. subgrain growth, became active in recrystallisation, this resulted in an increase of nucleus density. Steels in which SIBM was the dominant mechanism of recrystallisation possessed the largest grain size, and strongest textures with major component {100}〈110〉.     

Microstructural and textural evolution during large strain hot rolling (LSR) of Mg–Al (AZ31) alloy

Abstract

Grain refinement has been achieved through large strain rolling (LSR) in Mg AZ31 alloy. The evolution of microstructure and texture has been found to be dependent on the amount of reduction. After the critical amount of reduction, grain refinement proceeds through continuous dynamic recrystallisation (CDRX).     

Effect of silicon on recrystallisation of V–Ti microalloyed steel

Abstract

The dynamic recrystallisation (DRX) and static recrystallisation (SRX) behaviours of three V–Ti microalloyed steels were studied by the analysis of the true stress–strain curves and the stress relaxation curves under different deformation conditions. The results of DRX showed that deformation activation energy Q_def, peak stress and peak strain increased, as a result of the solute strengthening and dragging effect due to Si. The results of SRX showed that Si increased the SRX activation energy Q_SRX. The solute retardation parameter for static recrystallisation of Si was calculated. Based on the SRX results, to quantify the drag effect of Si and V, a new model was proposed to describe the time for 50% recrystallisation (t_0·5), which was tested and verified by previously published data on similar steels. Precipitation during recrystallisation could lead to a lower value of the Avrami exponent.     

Influence of strain and strain rate on microstructural evolution during superplasticity of Mg–Al–Zn sheet

Strain-induced abnormal grain growth was observed along the gage length during high-temperature uniaxial tensile testing of rolled Mg–Al–Zn (AZ31) sheet. Effective strain and strain rates in biaxial forming of AZ31 sheets also affected the nature of grain growth in the formed sheet. For the uniaxial testing done at 400 °C and a strain rate of 10^?1 s^?1, abnormal grain growth was prevalent in the gage sections that experienced true strain values between 0.2 and 1.0. Biaxial forming of AZ31 at 5 × 10^?2 s^?1 and 400 °C also exhibited abnormal grain growth at the cross sections which experienced a true strain of 1.7. Uniaxially tested sample at 400 °C and a strain rate of 10^?3 s^?1, however, showed no abnormal grain growth in the gage sections which experienced true local strain values ranging from 1.0 to 2.3. The normalized flow stress versus temperature and grain size compensated strain rate plot showed that the deformation kinetics of the current AZ31 alloy was similar to that reported in the literature for AZ31 alloys. Orientation image microscopy (OIM) was used to study the texture evolution, grain size, and grain boundary misorientation during uniaxial and biaxial forming. Influence of deformation parameters, namely strain rate, strain, and temperature on grain growth and refinement were discussed with the help of OIM results.     

Role of strain heterogeneity on recrystallisation of oxide dispersion strengthened Fe–Cr–Al alloys for high-temperature applications

Mechanically alloyed iron-based oxide dispersion-strengthened alloys have the potential for application in heat exchangers for biomass power plants, with operating temperature and pressure at entry of the gas turbine working fluid being around 1,100 °C and 15–30 bar, respectively. The yttria dispersion in such alloys improves the high-temperature creep and stress rupture life. The strength is further enhanced by the development of a coarse-grained microstructure during recrystallization. Factors controlling the evolution of this desirable microstructure are explored in this study, focusing specifically on PM 2000. The results can be interpreted if it is assumed that anything which makes the microstructure heterogeneous stimulates recrystallization. The combination of these results with finite element modelling is used to interpret the role of strain heterogeneity on the development of recrystallized grain structure. In this sense, larger strain gradients lead to more refined and more isotropic grain structures.     

Deformation behavior of an Al–Cu–Mg–Mn–Zr alloy during hot compression

Deformation behavior of an Al–Cu–Mg–Mn–Zr alloy during hot compression was characterized in present work by high-temperature testing and transmission electron microscope (TEM) studies. The true stress–true strain curves exhibited a peak stress at a critical stain. The peak stress decreased with increasing deformation temperature and decreasing strain rate, which can be described by Zener–Hollomon (Z) parameter in hyperbolic sine function with the deformation activation energy 277.8 kJ/mol. The processing map revealed the existence of an optimum hot-working regime between 390 and 420 °C, under strain rates ranging from 0.1 to 1 s⁻¹. The main softening mechanism of the alloy was dynamic recovery at high lnZ value; continuous dynamic recrystallization (DRX) occurred as deformed at low lnZ value. The dynamic precipitation of Al₃Zr and Al₂₀Cu₂Mn₃ dispersoids during hot deformation restrained DRX and increased the hot deformation activation energy of the alloy.     

Effect of rolling strain on microstructure and tensile properties of dual-phase Mg–8Li–3Al–2Zn–0.5Y alloy

This study was conducted to discuss the effect of rolling strain on microstructure and tensile properties of dual-phase Mg–8Li–3Al–2Zn–0.5Y (wt%) alloy, which was prepared by casting, and then homogenized and rolled at 200?°C. The rolling process was conducted with 10% reduction per pass and five different accumulated strains, varying from 10% to 70%. The results indicate that the as-cast and as-rolled Mg–8Li–3Al–2Zn–0.5Y alloys are composed of α-Mg, β-Li, AlLi and Al₂Y phases. After rolling process, anisotropic microstructure was observed. α-Mg phase got elongated in both rolling direction and transverse direction with the addition of rolling strain. Consequently, the strength of the alloy in both directions was notably improved whereas the elongation declined, mainly caused by strain hardening and dispersion strengthening. The tensile properties of the as-rolled alloys in the RD, no matter the YS, UTS or the elongation, are higher than those of the TD due to their larger deformation strain and significant anisotropy in the hcp α-Mg phase. In addition, the fracture and strengthening mechanism of the tested alloys were also investigated systematically.     

Influence of cold rolling on the precipitation in an Al–Mn–Zr alloy

The aim of the experiments was to study the influence of the rolling reduction (39, 87, and 96%) on the size and distribution of secondary particles and recrystallization behaviour of Al–Mn sheets with Zr addition prepared by twin-roll casting (TRC) in the industrial conditions. Samples, cold rolled on a laboratory mill, were subjected to a two-step precipitation annealing. Their microstructure (grain structure, substructure, particle analysis) as well as mechanical and physical properties (microhardness, electrical conductivity, resisitivity) were then characterized. The material cold worked with 39% reduction shows a moderate decrease of microhardness due to recovery, while sheets cold worked with 87 and 96% reduction soften more due to recrystallization. Regardless of the cold rolling reduction, the highest density of precipitates of α-Al(Mn,Fe)Si phase form during heating to 450 °C in the temperature range from 350 °C to 450 °C. Quantitative particle analysis of the sheets after the whole annealing cycle indicate that the alloy deformed 96% shows the highest density of particles in the size range from 50 to 140 nm. In addition, many spherical particles up to 15 nm were observed by transmission electron microscopy, some of them were identified by electron diffraction as Al₃Zr phase with L1₂ crystal structure.     

Flow stress and recrystallisation during hot deformation of Cu–9%Sn alloys

Abstract

Compression tests were carried out on two compositions of Cu–Sn bronze: Cu–9·2Sn and Cu–9·1Sn–0·26Zn (wt-%). The experiments were performed at temperatures from ambient up to 750°C and at nominal (initial) strain rates in the range 10^-3 to 10^-1 s^-1. The measured data were converted into true stress–true strain curves; these displayed yield drops as well as single peaks (or maxima) at higher temperatures and lower strain rates. The mean rate sensitivity applicable to the curves was 0·25. Optical metallography indicated that dynamic recrystallisation of the ‘grain refinement’ type was taking place at the higher temperatures and proceeded by necklace formation. Electron backscattered diffraction measurements were also carried out; these revealed that twinning plays an important role in these materials. The present results show that the progress of recrystallisation is considerably slower than in OFHC copper and that the recrystallised grain size is appreciably finer. These observations, taken together, all indicate that the high temperature flow behaviour of the tin bronzes is controlled by solute drag and is not of the conventional ‘pure metal’ type.     

Changes of flow stress and microstructure during hot deformation of Al–1Mg–1Mn

Abstract

Plane strain compression tests have been carried out at strain rates between 0·5 and 10 s^?1 and temperatures in the range 275–510°C, both under nominally isothermal conditions and with temperature decreasing. Also, temperature or strain rate have been changed in the interval between two deformations. In all cases, the stress–strain curves obeyed a mechanical equation of state, described by constitutive relationships in terms of strain and instantaneous value of Zener–Hollomon parameter Z. When the value of Z varies slowly during deformation, flow stress is uniquely related to subgrain size and to dislocation density within subgrains, but these relationships break down in transition structures developed after a change of Z between two deformations. The existence of an equation of state for mechanical behaviour, but not for microstructure, is considered to result from important contributions of both dislocation velocity and density to hot strength.

MST/1066     

Influence of titanium and nitrogen on hot ductility of C–Mn–Nb–Al steels

Abstract

The influence of small additions of titanium on the hot ductility of C–Mn–Nb–Al steels has been examined. Titanium and nitrogen levels varied in the ranges 0·014–0·045 and 0·004–0·011 wt-%, respectively, so that a wide range of Ti/N ratios could be studied. The tensile specimens were cast and cooled at average cooling rates of 25, 100, and 200 K min^-1 to test temperatures in the range 1100–800°C and strained to failure at a strain rate of 2 × 10^-3 s^-1. It was found that ductility in the titanium containing niobium steels improved with a decrease in the cooling rate, an increase in the size of the titanium containing precipitates, and a decrease in the volume fraction of precipitates. Coarser particles could be obtained by increasing the Ti/N ratio above the stoichiometric ratio for TiN and by testing at higher temperatures. However, ductility was generally poor for these titanium containing steels and it was equally poor when niobium was either present or absent. For steels with ～0·005 wt-%N ductility was very poor at the stoichiometric Ti/N ratio of 3·4 : 1. Ductility was better at the higher Ti/N ratios but only two of the titanium containing niobium steels gave better ductility than the titanium free niobium containing steels and then only at temperatures below about 950–900°C. One of these steels had the lowest titanium addition (0·014 wt-%), thus limiting the volume fraction of fine Ti containing particles and the other had the highest Ti/N ratio of 8 : 1. However, even for these two steels ductility was worse than for the titanium free steels in the higher temperature range. The commercial implications of these results are discussed.     

Effect of pretreatment and texture on recovery and recrystallisation in Al–4·5Mg–0·7Mn alloy

Abstract

The development of recovery and recrystallisation in cold rolled Al–4·5Mg–0·7 Mn (designated AA 5083) was analysed metallographically, by measuring hardness and electrical conductivity, and by means of texture analysis. The precipitation state and the initial texture were varied using appropriate pretreatments before cold rolling in order to study the influence of these parameters on kinetics and texture evolution during deformation, recovery, and recrystallisation. Finally, the results obtained were compared with those obtained for conventionally produced material.

MST/1960     

Effect of hot rolling on the enhancement of mechanical properties of low density Cu–Cr–Nb sintered alloy

Studies have been carried out on the effect of hot rolling on the enhancement of mechanical properties of sintered low density Cu–8 at.% Cr–4 at.% Nb alloy made from gas-atomised powders by vacuum hot pressing using varying pressure and temperature. The pressure is varied from 10 to 30 MPa whereas, 800, 900 and 1000 °C are three hot-pressed temperatures. Though hot rolling of porous low density hot-pressed samples results in near theoretical density, the hot-pressed sintered material with higher initial porosity shows lower strength and ductility after rolling. Hot-pressed compacts below certain density could not be rolled and the sample has cracked during rolling. The higher density material could be easily rolled and significant improvement in mechanical properties has been noticed. This has been attributed to the conversion of porosities into microscopic cracks which could not be healed due to the presence of Cr₂Nb precipitates. Finally, structure property correlation has been established.     

Effect of grain size on strain rate sensitivity of cryomilled Al–Mg alloy

Al–Mg alloy powder was cryomilled to achieve a nanocrystalline (NC) structure having an average grain size of 50 nm with high thermal stability, and then consolidated by quasi-isostatic forging. The consolidation resulted in a bulk material with ultrafine grains of about 250 nm, and the material exhibited enhanced strength compared to conventionally processed Al–Mg alloy. The hardness of as-cryomilled powder, the forged ultrafine-grained (UFG) material, and the conventional coarse-grained (CG) alloy were measured by nanoindentation using various loading rates, and the results were compared with strain rate sensitivity (SRS) from uniaxial compression tests. Negative SRS was observed in the cryomilled NC powder and the forged UFG material, while the conventional alloy was relatively insensitive to strain rate. The dependence on loading rate was stronger in the NC powders than in the UFG material.     

Effect of rolling conditions on the structure and shape memory properties of Fe–Mn–Si alloys

Lattice defects play an important role in controlling the γ → ε martensitic transformation in shape memory ferrous alloys. This work focuses on the relation between various rolling and annealing processes, the microstructure resulting from the processes, and strain recovery of two Fe–Mn–Si alloys with different stacking fault energies (SFEs). Rolling experiments, conducted over a temperature range from 20 °C to 1000 °C, produce quite different microstructures, which vary from a high dislocation density to a structure containing only few isolated dislocations. In addition, annealing temperature has a very important influence not only on the dislocation arrays but also on the stacking faults remaining in the austenite, whose density depends on the SFE value for the alloy. Within the framework of the processing parameters selected for this work, i.e. roll speed, rolling reductions, processing temperatures and schedules, rolling at intermediate temperatures and annealing at a temperature of 650 °C seem to be the most appropriate methods to obtain a microstructure favorable for a nearly full degree of shape recovery.