Tensile fracture behaviour of microstructurally engineered Cu bearing high strength low alloy steel

Abstract

An attempt has been made to highlight the influence of precipitation and microstructural constituents on tensile fracture behaviour in Cu bearing HSLA 100 steel. Variations in the microconstituents have been incorporated in the steel by engineering the microstructures through thermal treatments consisting of solutionising, water quenching and aging at various temperatures. The microstructure in quenched condition consists of mainly lath martensite, bainite and acicular ferrite besides little amount of retained austenite, carbides and carbonitrides. Aging up to 500°C facilitated fine coherent ?-Cu precipitation that lost its coherency at >550°C. Simultaneously, recovery and recrystallisation of martensite and acicular ferrite occurred at higher temperatures. The formation of new martensite islands occurred on aging at >650°C. Carbides, carbonitrides and retained austenite remained essentially unchanged. Tensile tests were conducted at a slow strain rate to study the tensile fracture behaviour of the steel. Microstructural and fractographic evidences indicating that coherent Cu precipitate causes the brittleness in the material in initial stages of aging whereas loss of coherency of Cu precipitate in later stages results in the reappearance of ductility in the material.     

Influence of dynamic strain aging on plastic instability behaviour of near alpha titanium alloy Timetal 834

Abstract

The deformation behaviour of near alpha titanium alloy Timetal 834 was investigated by analysing Considére criterion in temperature range between 300 and 500°C at an interval of 25°C. In the dynamic strain aging (DSA) regime (400–475°C) studied in this material, Considére criterion was satisfied partially at peak DSA temperature (450°C). This was attributed to maximum DSA effect at 450°C which eventually resulted in specimen fracture at low ductility levels. Strain hardening exponent (n) values was determined using Ludwik plot, Considére criterion and obtained experimentally from uniform strain. The n values obtained from Ludwik plot and Considére criterion were greater than the uniform strain in DSA regime studied.     

Effect of additions of Ti,B and Ce on microstructural stability,creep strength and creep damage in austenitic stainless steel

Abstract

Optical and transmission electron microscopy (TEM) and X-ray diffraction (XRD) analysis of bulk extracted precipitate residues were carried out on long term (more than 80 000 h) creep tested (at 1023 K) type 304 austenitic stainless steels with different levels of Ti content to assess the microstructural stability and creep strength. B and Ce were added to the steels to suppress the creep cavitation. Finer Ti(C,N) particles with higher density and narrower size distribution were observed in steels with a higher Ti content, resulting in an increase in the creep rupture strength. However, higher Ti content increased the intergranular precipitation of the σ phase on longer creep exposure, resulting in the increase in creep cavitation and in the decrease in creep rupture strength. The study indicated an optimum level of Ti and {C + (6/7)N} content with the Ti/{C + (6/7)N} ratio close to the stoichiometric value of the Ti(C,N) precipitate particles that should also be close to their solubility limit at the solution heat treatment temperature.     

Plane strain fracture toughness of MP35N in aged and unaged conditions measured using modified CT specimens

The multiphase alloy MP35N (35% Ni, 35% Co, 10% Mo, 20% Cr) is a high strength, high toughness alloy of choice for several safety-critical applications in aerospace, oil drilling, and biomedical industries. Several previous attempts in literature to measure the plane strain fracture toughness of commercially drawn MP35N did not produce reliable values since they violated one or more of the criteria stipulated by ASTM standards for a valid measurement of K_Ic. In most cases, the requirements for plane strain and small scale yielding conditions were not met, since the commercially drawn material was available only with limited cross-sectional dimensions. In this investigation specially designed specimens (modified compact tension (CT) specimens) have been used to measure the plane strain fracture toughness of MP35N in both the unaged and the aged conditions. The K_Ic of the commercially drawn (53% reduction level) MP35N was measured to be 126 MPa√m, while that of the commercially drawn and aged MP35N was measured to be 98 MPa√m. Both these measurements satisfied all the required criteria stipulated by ASTM standards for valid measurements of K_Ic. The new procedure used in this study has been verified by the measuring of fracture toughness of Al alloy, using both the modified specimen, as designed here, and the standard one. The results for plane strain fracture toughness of MP35N alloy have been verified by the standard measurement of J_Ic values for both the aged and the unaged alloys. Finally, on a suitably normalized plot, introduced in this paper, the toughness-strength envelop for MP35 is higher than most of structural alloys, but significantly lower than that of the TRIP steels.     

Mixed mode fracture analysis of CCBD specimens based on the extended maximum tangential strain criterion

The maximum tangential strain (MTSN) criterion has been modified to include the effects of T‐stress and stress intensity factors in conditions of both plane stress and plane strain. Further, both the T‐stress and Poisson's ratio affecting the crack propagation are also discussed according to the extended MTSN (EMTSN) criterion, which is a modified MTSN criterion. Finally, the generalized maximum tangential stress (GMTS) criterion and the EMTSN criterion are used to predict the test results obtained with central cracked Brazilian disc (CCBD) specimens. The results indicate that the T‐stress and Poisson's ratio have a remarkable influence on the mixed mode fracture resistance based on the EMTSN criterion. Theoretical values of both the EMTSN and the GMTS criteria are in very good agreement with the test results. Moreover, the EMTSN criterion provides a better prediction for pure mode II.     

基于TiC_(0.5)N_(0.5)/Si_3N_4复相陶瓷基体的PVD及CVD涂层刀具性能

首先,以15vol%或25vol%的TiC0.5N0.5粉体为导电第二相,利用热压烧结法制备了TiC0.5N0.5/Si3N4复相陶瓷;然后,分别通过物理气相沉积(PVD)和化学气相沉积(CVD)技术在TiC0.5N0.5/Si3N4陶瓷刀具表面沉积了CrAlN和TiN/Al2O3/TiN涂层;最后,通过对TiC0.5N0.5/Si3N4刀具进行连续切削灰铸铁实验,研究了TiC0.5N0.5含量和涂层类型对刀具磨损特征的影响,并探讨了刀具的磨损机制。结果表明:TiC0.5N0.5含量的增加有利于提高TiC0.5N0.5/Si3N4复相陶瓷刀具基体的硬度和电导率,但对耐磨性和切削寿命的影响较小;采用PVD技术沉积CrAlN涂层时,随着TiC0.5N0.5含量的增加,涂层的厚度、结合强度和硬度都得到提高,涂层刀具的磨损性能显著提高,切削寿命也明显延长;而采用CVD技术沉积TiN/Al2O3/TiN涂层时,TiC0.5N0.5含量的变化对涂层的厚度、结合强度和硬度基本没有影响,TiN/Al2O3/TiN涂层刀具整体切削性能变化不大。CrAlN涂层和TiN/Al2O3/TiN涂层都可明显改善TiC0.5N0.5/Si3N4复相陶瓷刀具的耐磨性和切削寿命;相对于TiN/Al2O3/TiN涂层,CrAlN涂层具有更高的涂层硬度和粘着强度,但TiN/Al2O3/TiN涂层具有较大的涂层厚度,TiN/Al2O3/TiN涂层刀具表现出更加优异的耐磨性和切削寿命。TiC0.5N0.5/Si3N4复相陶瓷刀具的磨损机制以机械摩擦导致的磨粒磨损为主,伴随有少量的粘结磨损。     

ZrO2增韧Al2O3颗粒增强Fe45复合材料拉伸断裂的有限元-离散元耦合方法仿真ZrO2增韧Al2O3颗粒增强Fe45复合材料拉伸断裂的有限元-离散元耦合方法仿真

采用有限元-离散元耦合方法（FEM-DEM方法）,进行了氧化锆增韧氧化铝颗粒增强Fe45复合材料（ZrO₂-Al₂O₃/Fe45）轴对称代表体元模型的拉伸断裂仿真分析。分析了FEM-DEM模型对单元尺寸的敏感性,结果表明采用,二阶实体单元加双零厚度内聚力单元的FEM-DEM模型降低了计算结果对单元尺寸的敏感性。ZrO₂-Al₂O₃/Fe45复合材料拉伸断裂的模拟结果表明,颗粒形状对裂纹的扩展会产生较大影响,复合材料的开裂首先在垂直于拉力方向的界面处发生,界面裂纹扩展至基体应力集中处之后基体发生开裂,裂纹由开裂的界面和基体裂纹共同组成。