烧结温度及Y2O3对9Cr-RAFM钢性能的影响

采用粉末冶金技术,以球磨-模压-真空烧结工艺制备2种9Cr-RAFM钢:以0.3%Y2O3(质量分数)为弥散相的ODS 9Cr铁基高温合金和不添加Y2O3的Non-ODS 9Cr铁基高温合金。研究烧结温度及Y2O3对RAFM钢的力学性能和微观组织的影响。研究结果表明:采用球磨-模压-真空烧结工艺制备的ODS合金的综合力学性能高于Non-ODS合金,并且在1 390℃烧结,保温2 h条件下制备的ODS合金具有最佳的综合力学性能(抗拉强度600 MPa,伸长率23.1%)。并对不同球磨时间的合金粉末进行XRD物相分析,用SEM及能谱分析技术研究Y2O3影响RAFM钢的微观组织成分和力学性能的机理。     

Development of a High-Strength Ultrafine-Grained Ferritic Steel Nanocomposite

This article describes the microstructural and mechanical properties of 12YWT oxide-dispersion-strengthened (ODS)-ferritic steel nanocomposite. According to the annealing results obtained from X-ray diffraction line profile analysis on mechanically alloyed powders milled for 80 hours, the hot extrusion at 1123 K (850 °C) resulted in a nearly equiaxed ultrafine structure with an ultimate tensile strength of 1470 MPa, yield strength of 1390 MPa, and total elongation of 13 pct at room temperature comparable with high-strength 14YWT ODS steel. Maximum total elongation was found at 973 K (600 °C) where fractography of the tensile specimen showed a fully ductile dimple feature compared with the splitting cracks and very fine dimpled structure observed at room temperature. The presence of very small particles on the wall of dimples at 1073 K (800 °C) with nearly chemical composition of the matrix alloy was attributed to the activation of the boundaries decohesion mechanism as a result of diffusion of solute atoms. The results of Charpy impact test also indicated significant improvement of transition temperature with respect to predecessor 12YWT because of the decreased grain size and more homogeneity of grain size distribution. Hence, this alloy represented a good compromise between the strength and Charpy impact properties.     

Fracture toughness of aisi M2 high-speed steel and corresponding matrix tool steel

The influence of microstructural variations on the fracture toughness of two tool steels with compositions 6 pct W-5 pct Mo-4 pct Cr-2 pct V-0.8 pct C (AISI M2 high-speed steel) and 2 pct W-2.75 pct Mo-4.5 pct Cr-1 pct V-0.5 pct C (VASCO-MA) was investigated. In the as-hardened condition, the M2 steel has a higher fracture toughness than the MA steel, although the latter steel is softer. In the tempered condition, MA is softer and has a higher fracture toughness than M2. When the hardening temperature is below 1095 °C (2000 °F), tempering of both steels causes embrittlement,i.e., a reduction of fracture toughness as well as hardness. The fracture toughness of both steels was enhanced by increasing the grain size. The steel samples with intercept grain size of 5 (average grain diameter of 30 microns) or coarser exhibit 2 to 3 MPa√m (2 to 3 ksi√in.) higher fracture toughness than samples with intercept grain size of 10 (average grain diameter of 15 microns) or finer. Tempering temperature has no effect on the fracture toughness of M2 and MA steels as long as the final tempered hardness of the steels is constant. Retained austenite has no influence on the fracture toughness of as-hardened MA steel, but a high content of retained austenite appears to raise the fracture toughness of as-hardened M2 steel. There is a temperature of austenitization for each tool steel at which the retained austenite content in the as-quenched samples is a maximum. The above described results were explained through changes in the microstructure and the fracture modes. CHONGMIN KIM, formerly with Climax Molybdenum Company of Michigan, Ann Arbor, MI.     

Interrelations of cooling rate,microstructure, and mechanical properties in four HSLA steels

The present study was carried out on four steels containing 0.1 pct C-1.5 pct Mn-0.003 pct B* in common, with additions of 1 pct Cr, 0.5 pct Mo, 0.25 pct Mo + 1 pct Cr, 0.2 pct Ti + 1 pct Cr. They were designated, accordingly, as Cr, Mo, Mo-Cr, and Cr-Ti steels. All the steels exhibited a complete lath martensite microstructure with thin interlaths of retained austenite (≈0.05 pct) in the quenched condition. The normalized microstructures, granular bainite, contained massive areas of ferrite and granules of bainite laths. Both microconstituents contained a fine dispersion of cementite particles (size ≈50 Å) together with high dislocation densities. A mechanism explaining their for-mation has been given. The Cr steel, due to its low hardenability, showed in addition polygonal ferrite in the neighborhood of the so-called M-A constituent (twinned martensite and/or austenite). The annealed microstructure (using a cooling rate of 0.033 °C s^?1) of the Cr steel consisted of coarse ferrite-pearlite. Addition of 0.2 pct Ti to the Cr steel markedly refined the structure, whereas an addition of 0.25 pct Mo altered the microstructure to ferrite-lower bainite. In the 0.5 pct Mo steel, polygonal ferrite was found to be completely missing. The mechanical properties of the four steels after quenching, normalizing, and annealing were investigatedvia hardness and tensile test mea-surements. An empirical equation, relating the ultimate tensile strength to the steel composition, for steels that had granular bainite microstructures in the normalized condition, was proposed. The fracture surfaces exhibited cleavage and variable-size dimples depending on the microstructure and steel composition.     

The microstructure of chromium-tungsten steels

Chromium-tungsten steels are being developed to replace the Cr-Mo steels for fusion-reactor applications. Eight experimental steels were produced and examined by optical and electron microscopy. Chromium concentrations of 2.25, 5, 9 and 12 pct were used. Steels with these chromium compositions and with 2 pct W and 0.25 pct V were produced. To determine the effect of tungsten and vanadium, three other 2.25Cr steels were produced as follows: an alloy with 2 pct W and 0 pct V and alloys with 0 and 1 pct W and 0.25 pct V. A 9Cr steel containing 2 pct W, 0.25 pct V, and 0.07 pct Ta also was studied. For all alloys, carbon was maintained at 0.1 pct. Two pct tungsten was required in the 2.25Cr steels to produce 100 pct bainite (no polygonal ferrite). The 5Cr and 9Cr steels were 100 pct martensite, but the 12Cr steel contained about 25 pct delta-ferrite. Precipitate morphology and precipitate types varied, depending on the chromium content. For the 2.25Cr steels, M₃C and M₇C₃ were the primary precipitates; for the 9Cr and 12Cr steels, M₂₃C₆ was the primary precipitate. The 5Cr steel contained M₇C₃ and M₂₃C₆. All of the steels with vanadium also contained MC.     

Effect of Y2O3 on Spark Plasma Sintering Kinetics of Nanocrystalline 9Cr-1Mo Ferritic Oxide Dispersion-Strengthened Steels

Nanocrystalline mechanically alloyed powders of 9Cr-1Mo ferritic steels with and without yttria dispersoids were densified using spark plasma sintering (SPS) to near-theoretical density at a temperature of 1073 K (800 °C). Studies on densification behaviour revealed that steels with dispersoids densified faster when compared to Fe-9Cr-1Mo steel. The evaluation of densification mechanisms during SPS reveals that grain boundary and lattice diffusion to be predominant at relative densities ranging from >0.7 to 0.9 in both the alloys.     

15Ni?15Cr ODS钢的微观结构与力学性能

氧化物弥散强化（Oxide dispersion strengthened, ODS）钢因其良好的高温力学性能和抗辐照性能被认为是钠冷快堆包壳材料的重要候选材料. 本文通过机械合金化以及热等静压和锻造工艺制备了15Ni?15Cr ODS奥氏体钢,并且采用相同工艺制备了不加氧化物的15Ni?15Cr奥氏体钢作为参比材料. 利用透射电镜对样品的微观结构进行分析,发现15Ni?15Cr和15Ni?15Cr ODS奥氏体钢晶粒尺寸分别为0.75和0.5 μm. 15Ni?15Cr ODS奥氏体钢中分布的氧化物弥散粒子主要为δ-Y₄Zr₃O₁₂以及少量的Al₂O₃. 15Ni?15Cr ODS奥氏体钢中氧化物弥散粒子的平均粒径为12.8 nm、数密度5.5×1022 m?3、粒子间距26 nm. 相比于15Ni?15Cr奥氏体钢,15Ni?15Cr ODS奥氏体钢具有更高的强度,但是高温塑性有所降低. 15Ni?15Cr ODS奥氏体钢的室温断裂机制为韧性断裂,高温断裂机制为韧–脆混合断裂.      

Reciprocating Sliding Wear Behavior of Newly Developed Bainitic Steels

The present work discusses the mechanical properties and wear behavior of newly developed bainitic rail steels with nominal composition of 0.71 pct C, 0.35 pct Si, 1.15 pct Mn, 0.59 pct Cr, 0.40 pct Cu, and 0.20 pct Ni (all in wt pct)). Isothermal transformation has been carried out at different time and temperatures for obtaining different bainitic morphologies. Linearly reciprocating sliding wear behavior of the steels has been studied and compared with that of the conventional pearlitic rail steel. Considerable improvement in mechanical properties of the bainitic steels has been noticed. The hardness of the bainitic steels increases with decrease in isothermal transformation temperature. It leads to enhancement of wear resistance of the bainitic steels compared to the conventional rail steel. Finally, it clearly draws correlation between mechanical properties, wear resistance, and microstructural variation of a series of bainitic rail steels.     

The effect of nitrogen additions upon the pitting resistance of 18 pct Cr, 18 pct Mn Stainless Steel

The effect of nitrogen additions upon the pitting resistance of 18 pct Cr, 18 pct Mn stainless steel has been investigated by potentiokinetic techniques in a 1000 ppm NaCl solution. Nitrogen additions increased the pitting resistance of the steel irrespective of structure, however, the ferritic steel was less pit resistant than the (duplex) steels containing both austenite and ferrite which, in turn, were less pit resistant than the totally austenitic steels. For steels having a duplex structure, the effect of nitrogen on the pitting resistance was observed to follow a linear function of the relative amount of austenite in these steels due to the area effects of the austenite and ferrite which are galvanically coupled in these steels. The addition of nitrogen was found to increase the amount of austenite at a rate of approximately 200 times the percent nitrogen addition from 36 pct austenite for the 0.02 pct N steel to 100 pct for the 0.40 pct nitrogen steel. The addition of nitrogen to the totally austenitic steels increased the pitting resistance at the rate of approximately 0.31 volts per pct nitrogen added, but no mechanism was found for the increased resistance. This paper is based on a presentation made at a symposium on “New Developments in Ferritic and Duplex Stainless Steels,” held at the Fall Meeting in Cleveland, Ohio, on October 19, 1972, under the sponsorship of the Corrosion Resistant Metals Committee of TMS-IMD and the Corrosion and Oxidation Activity of the ASM.     

The effect of an intercritical heat treatment on temper embrittlement of a Ni-Cr-Mo-V rotor steel

The effect of an intercritical heat treatment on tempor embrittlement has been investigated for a rotor steel containing 0.25 pct C, 3.5 pct Ni, 1.7 pct Cr, 0.5 pct Mo, 0.1 pct V, and deliberate additions of phosphorus, tin, or antimony. Both martensitic and bainitic steels were held at the intercritical temperature of 1380°F (750°C) for times up to 40 h and were then quenched or cooled to obtain martensitic or bainitic transformation. The steels were then tempered, followed by water quenching or step cooling from the tempering temperature. The residual ferrite maintained a fine plate-like shape even after 40 h at the intercritical temperature. Embrittlement induced by step cooling from the final tempering was mark edly reduced by the intercritical treatment as compared to the embrittlement observed after conventional heat treatment; for example, AFATT, the increase in the Charpy V-notch 50 pct shear fracture transition temperature caused by step cooling, was reduced by at least 80°F (45°C) as a result of the intercritical treatment of steels containing 0.02 pct P. Molybdenum effectively reduced AFATT in intercritlcally heat-treated steels as well as in conventionally treated steels. Possible mechanisms for reducing temper embrittlement with the intercritical treatment are discussed.     

The 885° f (475° c) embrittlement of ferritic stainless steels

The 885odgF (475°C) embrittlement of seven heats of chromium steels was investigated: four vacuum-melted heats with C + N < 0.008 pct and 14 pct Cr, 14 pet Cr-2 pet Mo, 18 pct Cr, or 18 pet Cr-2 pet Mo, and three air-melted heats with C + N > 0.09 pet and 18 pet Cr, 18 pct Cr-2 pet Mo, or 18 pet Cr-2 pet Mo-0.5 pct Ti. The steels were heated at 600° (316°), 700° (371°), 800° (427°), 900° (482°), and 1000°F (538°C) for various times up to 4800 h and the influence of this aging was investigated by hardness measurements, impact tests, and electron metallography. It was demonstrated that the embrittlement due to 885°F (475°C) exposure was caused by precipitation of a chromium-rich α^’ phase on dislocations. The nucleation rate of α^’ was calculated with the aid of Becker’s theory and the results were used to extrapolate experimental data obtained in this study. After an exposure of about 1000 h at 1000°F (538°C), a decrease in room temperature toughness was observed for all steels investigated. The decrease in toughness was not caused by immobilization of dislocations by α^’, but by precipitation of carbonitrides.     

Continuously Cooled Ultrafine Bainitic Steel with Excellent Strength–Elongation Combination

Serious efforts have been made to simultaneously improve the strength and ductility of steels for different applications. However, steel with the ultimate tensile strength (UTS) above 1200 MPa with minimum elongation of 20 pct is still difficult to produce. In the current work, an effort has been made to design such a steel that could be directly produced in any hot strip mill, after accelerated cooling on the runout table followed by coiling. Basically this steel consisted of C, Mn, Si, and Cr and the intended final microstructure at room temperature was about 80 pct carbide-free bainite and 20 pct retained austenite. The steel was exposed to a thermal treatment which is generally experienced by a hot strip coil. This newly developed steel possesses an UTS of minimum ~1370 MPa with minimum ~21 pct elongation. The combination of such encouraging mechanical properties can be primarily attributed to the formation of ultrafine bainite plates (~100 to 130 nm) and a high density of dislocations arising out of the bainitic transformation. The presence of sufficient quantity of retained austenite (minimum 21 pct) in the final microstructure could be the reason for the attainment of outstanding ductility values at such a high strength level.     

Reversible temper embrittlement of rotor steels

The susceptibility to temper embrittlement of eight different rotor steels has been studied in terms of the effects of composition, of cooling rate from tempering temperature, of isothermal aging, of steel-making practice and of strength level and tempering temperature. The Ni Cr Mo V steels tested showed increasing susceptibility to temper embrittlement with increasing nickel content. The normally marked susceptibility of a high phosphorus 3 pct Cr Mo steel was eliminated by the removal of manganese. Embrittlement in a 3 pct Ni Cr Mo V steel was caused by the equilibrium segregation of solute atoms to the prior austenite grain boundaries. Two Cr Mo V steels tested were not susceptible to temper embrittlement. Electroslag remelting and refining had very little effect on the susceptibility of the steels tested. Strength level and tempering temperature had no effect on the degree of embrittlement of the 3 pct Ni Cr Mo V disc steel. The possibilities of remedial action include an adjustment of the post tempering cooling rate, to optimize the conflicting interests of minimum temper embrittlement and adequate stress relief, and the production of very low manganese rotor steels.     

冲击载荷下低屈服比高强钢板的拉伸性能

通过室温下的仪器化冲击试验和静态拉伸试验,研究一种低屈服比高强度钢板在冲击载荷下的力学性能和断裂机理.结果表明:试验钢的组织由细小岛状马氏体与针状铁素体为主构成,马氏体体积分数为27.6%.与静态拉伸性能相比,在名义应变速率为100 s-1的冲击载荷作用下,试验用钢屈服强度提高31.6%,延伸率不降低.在静态和动态载荷下,该钢均以显微空洞长大聚集的方式发生韧性断裂,但显微空洞的形核和长大方式不同.在静态载荷下,显微空洞形核于颈缩区的铁素体晶粒内部或铁素体-马氏体两相界面处,空洞主要通过两相界面的脱开而形成长大;在动态载荷下,显微空洞主要形核于颈缩区的两相界面处,空洞主要通过马氏体粒子的开裂而形成长大.     

Mechanical properties of new stainless steels based on the system Fe‐30Mn‐5A1‐XCr‐0.5C

New stainless steels based on the system Fe‐30Mn‐5AI‐XCr‐0.5C (Cr mass contents of ≤ 9 %) were developed and evaluated as a replacement of conventional AISI 304 steel. The alloys were produced by induction melting and thermomechanically processed to obtain a fine equiaxed microstructure. A typical thermomechanical processing for AISI 300 austenitic stainless steels was used and included forging at 1200°C, rolling at 850 °C and final recrystallization at 1050 °C. A final fully austenitic microstructure with grains of about 150 μm in size was obtained in all the steels. Tensile tests at temperatures ranging from ‐196 to 400 °C showed similar results for the various alloys tested. In accordance with the values for the elongation to fracture, this temperature range was subdivided into three regions. In the temperature range of ‐196 °C to room temperature, elongation to fracture increases with decreasing temperature. At temperatures ranging from 100 to 300 °C, elongation to fracture increases with testing temperature and serrations on the stress‐strain curve were observed. Finally, higher testing temperatures were accompanied by a decrease in ductility. Examination of the microstructures after deformation led to the conclusion that mechanical twinning was the dominant mechanism of deformation at the tested temperatures.     

Microstructures and mechanical properties of melt-quenched ferritic stainless steels

Using the twin-roller type melt-quenching technique, the effects of rapid solidification on the microstructures and mechanical properties of ferrite have been examined in 17 pct Cr and 17 pct Cr-M steels where M = Ti, Nb, Si, or Al. The melt-quenched 17 pct Cr steels have the columnar and equiaxed grains which become finer with decreasing of specimen thickness. But the yield strength of these steels, which is about 0.48 GPa, remains almost unchanged with grain size refinement, contrary to predictions based on Hall-Petch’s relationship. The columnar structure of the melt-quenched 17 pct Cr-M steels is very fine on alloying with Ti and Si, while it is slightly coarse on alloying with Nb and Al. The hardness, yield strength, and fracture strength of these 17 pct Cr-M steels increase with increased amount of alloying element, these maximum values being about 460 DPN, 1.0 GPa, and 1.35 GPa, respectively, for 17 pct Cr- 6 pct Si steel, in the ductile compositional range. These are suitable values for a fine-gauge material having high hardness and strength as well as good ductility.     

Fabrication of ultrahigh nitrogen austenitic steels by nitrogen gas absorption into solid solution

For the purpose of fabricating ultrahigh nitrogen austenitic steels (>1 mass pct N), the phenomenon of nitrogen absorption into solid solution was thermodynamically analyzed and applied to Fe-Cr-Mn system ternary alloy. During the annealing of the steel in a nitrogen gas atmosphere of 0.1 MPa at 1473 K (nitrogen absorption treatment), the nitrogen content of the steel was increased with the absorption of nitrogen gas from the material surface and then saturated when the system reached a state of equilibrium. Effect of the steel composition on an equilibrium nitrogen content was formulated taking account of interactions among Cr, Mn, and N atoms, and the condition for fabrication of ultrahigh nitrogen austenitic steels was clarified. The nitrogen addition to ultrahigh content markedly increased proof stress and tensile stress of the austenitic steels without losing moderate ductility. For example, Fe-24Cr-10Mn-1.43N (mass pct) alloy has 830 MPa in 0.2 pct proof stress, 2.2 GPa in true tensile stress, and 75 pct in total elongation. As a result of tensile tests for various nitrogen-bearing austenitic steels, it was found that the proof stress is increased in proportion to (atomic fraction of nitrogen)^2/3.     

Role of Tungsten in the Tempered Martensite Embrittlement of a Modified 9 Pct Cr Steel

The effect of tempering on the mechanical properties and fracture behavior of two 3 pct Co-modified 9 pct Cr steels with 2 and 3 wt pct W was examined. Both steels were ductile in tension tests and tough under impact tests in high-temperature tempered conditions. At T ≤ 923 K (650 °C), the addition of 1 wt pct W led to low toughness and pronounced embrittlement. The 9Cr2W steel was tough after low-temperature tempering up to 723 K (450 °C). At 798 K (525 °C), the decomposition of retained austenite induced the formation of discontinuous and continuous films of M₂₃C₆ carbides along boundaries in the 9Cr2W and the 9Cr3W steels, respectively, which led to tempered martensite embrittlement (TME). In the 9Cr2W steel, the discontinuous boundary films played a role of crack initiation sites, and the absorption energy was 24 J cm^?2. In the 9Cr3W steel, continuous films provided a fracture path along the boundaries of prior austenite grains (PAG) and interlath boundaries in addition that caused the drop of impact energy to 6 J cm^?2. Tempering at 1023 K (750 °C) completely eliminated TME by spheroidization and the growth of M₂₃C₆ carbides, and both steels exhibited high values of adsorbed energy of ≥230 J cm^?2. The addition of 1 wt pct W extended the temperature domain of TME up to 923 K (650 °C) through the formation of W segregations at boundaries that hindered the spheroidization of M₂₃C₆ carbides.     

The relation of microstructure and fracture properties of electron beam melted,modified SAE 4620 steels

A method is described for the transmission and scanning electron microscope study of the relationship between the microstructure and the fracture properties of two quenched and tempered, electron beam melted, modified SAE 4620 steels consisting of tempered low carbon martensite. Among all the microstructure constituents considered, the constituentR (randomly oriented, “tempered low carbon martensite, TLCM”) achieved the highest probability for dimple fracture. The thick TLCM laths (designated as the microstructure constituent II) exhibited higher probability of dimple plus quasi-dimple mode of fracture than the thin laths (I). It is concluded that the steel EB1035 derived the high toughness from a) the high concentration of the “high toughness” microstructure constituentsR and II, b) “non-embrittled” prior austenite grain boundaries with 50 pct probability for smooth plus quasi-smooth mode and 50 pct dimple plus quasi-dimple mode of intergranular fracture. In contrast, besides having low content ofR and II, the steel EB1014 displayed “completely embrittled” prior austenite grain boundaries with 100 pct probability for smooth plus quasi-smooth intergranular fracture. The conclusions derived from the microconstituentsR, II and I seemed to reflect the “embrittling” effect of decreased spacings between the pseudo twin related laths and between the lath boundary cementite films, and the “toughening” effect of the randomly oriented laths. Auger spectra obtained from the fracture surface before and after sputtering is analyzed to determine the presence of grain boundary sulfur segregation.     

Hydrogen assisted ductile fracture of spheroidized carbon steels

The effects of hydrogen on ductile fracture were studied in two spheroidized plain carbon steels, containing 0.16 and 0.79 pct C. A combination of fractography and quantitative metallography on sectioned, deformed specimens permitted separation of the effects of hydrogen on the initiation, growth, and link-up of voids. In both steels, hydrogen was found to have no significant effect on either the initiation of voids at carbides, or early growth of voids, prior to link-up. In the higher carbon steel the fracture surface dimple size increased after hydrogen exposure with no other evident change in the fracture surface appearance; it is therefore inferred that hydrogen primarily assists void growth during link-up in this steel. In the lower carbon steel the fracture appearance changed and a decrease in void size due to hydrogen was found fractographically; thus, both initiation and growth of voids are apparently enhanced during the link-up phase of fracture in this steel. It is hypothesized that these effects may be due largely to a void pressure mechanism if hydrogen is transported by mobile dislocations. Formaly Graduate Student, Department of Metallurgy and Materials Science, Carnegie-Mellon University