新型三元复合络合剂体系对AZ91D镁合金表面酸性化学镀Ni-P的影响

利用含新型三元复合络合剂的酸性化学镀镍液体系,在AZ91D镁合金表面通过化学镀制备Ni-P防护镀层。结果表明,镀层沉积速率随着镀液中三元复合络合剂浓度的变化而改变。利用X射线衍射（XRD）、扫描电子显微镜（SEM）和差热分析（DSC）对镀层结构、形貌以及热稳定性进行表征和分析。通过交流阻抗（EIS）和动电位扫描极化曲线对Ni-P镀层在3.5%NaCl溶液中的耐蚀性能进行评价。镀液中三元复合络合剂的浓度对Ni-P镀层的结构与形貌有显著影响。Ni-P镀层的热稳定性随着三元复合络合剂浓度的增加而降低。当镀液中三元复合络合剂浓度为0.035 mol/L时,所制备的Ni-P镀层致密、均一,在3.5%NaCl溶液中表现出良好的耐蚀性能。     

铸铁表面化学镀Ni-P合金络合剂的研究

针对化学Ni-P镀过程中镀液稳定性差、使用寿命短、沉积速率低和pH范围窄等问题,采用对比实验和正交实验方法,以镀速、孔隙率、稳定性和镀层硬度为评价指标,研究了乳酸、苹果酸、柠檬酸和丁二酸络合剂及复合络合剂对镀液和镀层性能的影响.研究得到最优的铸铁表面Ni-P镀的复合络合剂配方为:乳酸20ml/L,苹果酸9g/L,丁二酸6g/L.此复合络合剂配方配制化学镀镍液可使镀速达到14.5μm/h,孔隙率降至0.45个/cm2,稳定性提高到3500s,硬度达620HV.     

低温化学镀镍中络合剂作用研究

研究了络合剂在低温化学镀镍槽液中的作用.试验表明,络合剂的正确选择是低温镇工艺实现的关键,络合剂的稳定性不但影响槽液的稳定,而且对镀速和镀层质量都有重要影响.络合剂的稳定性与其结构及配位原子性质、位阻效应等关系密切.选用复合络合剂,有利于调整镀速与镀层质量.络合剂的缓冲作用对提高镀速有利.     

化学镀法制备SiCp-Ni复合粉体

研究了酸性化学镀在SiCp陶瓷粉末表面涂覆Ni-P合金,考察了镀液的温度、pH值及粉末粒度对镀液稳定性和镀层性能的影响.结果表明,粉体越细,稳定施镀温度越低;合理选择工艺参数可使粒径从200μm～10μm的SiCp粉末得到均匀镀层;镀层P含量随pH值升高而降低,镀层结构为非晶态.     

镀液配方及化学镀工艺对Ni-P合金镀层性能影响

通过Ni-P合金镀层硬度、耐蚀性与表面含磷量的关系,分析了镀液镍次比、pH值、络合剂、缓冲剂以及施镀温度、施镀时间、时效温度对Ni-P合金化学镀层含磷量的影响,探讨了提高镀层表面硬度、耐磨性、耐蚀性的方法.     

Q235钢表面化学镀Ni-P的研究

利用正交试验方法研究了Q235钢表面化学镀Ni-P工艺对镀层质量,组织结构和性能的影响规律.结果表明:各因素对镀速影响的显著性顺序是:施镀温度＞硼酸(络合剂)加入量＞pH值＞镍磷比[Ni2 ]/[H2PO2]＞乙酸钠(缓冲剂)加入量;Q235钢表面化学镀Ni-P的最佳工艺参数为:pH值5.4,施镀温度为80℃,镍磷比0.28(硫酸镍15 g/L,次亚磷酸纳20 g/L),硼酸5.5 g/L;所得镀层硬度为Q235钢基体硬度的3.4倍,获得了磷含量超过11%的非晶镀层.     

乳酸络合剂化学镀镍锡磷合金的研究

研究了乳酸作络合剂的酸性镀液中,络合剂添加量对镀液稳定性的影响,以及硫酸镍、叫氯化锡、还原剂含量对化学镀镍-锡-磷合金镀速和镀层成分的影响。研究结果表明：在保证镀液已有与镍盐摩尔比为1：3的络合剂外,需要再加入按与锡盐摩尔比为1：7的量计算的络合剂,才能保证镀液足够的稳定性：在镀液中硫酸镍质量浓度为30g／L,四氯化锡为20g/L,次亚磷酸钠为30g/L时镀速较快;在pH值为4．8,85-90℃的操作温度下,所获镀层中锡的质量分数w(Sn)可达7．1％。     

Ni-TiO2复合电镀工艺研究

通过正交设计,研究了Ni-TiO2复合电镀工艺中镀液的pH值、搅拌速度、电流密度、微粒悬浮量、添加剂等工艺条件和参数对Ni-TiO2复合镀层的影响.在充分分析各不同镀液组成和工艺条件下,对复合镀层中微粒共析量的影响曲线和对镀层的表观形貌的观察后,得出了其最佳镀液组成和工艺参数;能量色散谱分析,制备的复合镀层中TiO2共析量为10%～24.23%(质量分数).采用SEM观察镀层的表面形貌,其外观均匀、细致.     

PP塑料化学镀铜的工艺研究

采用配方为硫酸铜3 g/L、酒石酸钾钠25 g/L、甲醛(质量分数为36%～40%)10 g/L、氢氧化钠7 g/L的镀液,通过考察施镀温度、镀液pH值、施镀时间对镀速的影响,确定了最优工艺参数,并在优化的工艺条件下制备镀层,用扫描电镜和能谱仪对镀层的形貌及成分进行了分析.结果表明:最佳工艺是镀液温度50℃,pH=12,施镀时间45～50 min;采用此优化工艺条件制备的镀层,表观光亮、均匀,与基体结合力好,成分为单一的铜.     

镀液pH值和钼酸根浓度对化学镀Ni-Mo-P沉积速度及镀层结构的影响

确定了化学镀获得不同结构Ni—Mo-P镀层的最佳工艺参数及镀液配方，探讨了络合剂、pH值、钼酸根浓度以及添加剂等参数对化学镀Ni—Mo—P合金镀层成分及结构的影响。结果表明，以柠檬酸钠作为主络合剂、醋酸钠作为辅助络合剂的络合剂体系对Ni、Mo实现共沉积有着较好的作用；Ni—Mo-P合金镀层中Mo和P含量有一定的制约关系，随着镀层中Mo含量的提高，镀层结构由非晶态向晶态转变；镀液pH值在一定范围内(pH值6．5～10)时，pH值的升高可提高沉积速度；镀液的钼酸根浓度和pH值对沉积速度的影响呈波浪形，存在一个极大值；随着沉积速度的提高，镀层的耐蚀性能也会有所改善。     

Aminoacetic acid as complexing agent in baths for electroless deposition of Ni–W–P coatings

Abstract

Ni–W–P alloy coatings were deposited from a bath containing, nickel sulphate (VI), sodium tungstate (VI), sodium hypophosphite, sodium formate, and a complexing agent. The complexing agents were formic acid, acetic acid, lactic acid, succinic acid, malic acid, malonic acid, aminoacetic acid and triethanoloamine. It is shown that Ni–W–P coatings are deposited the slowest when complexing agents with the highest stability constants are used. As the deposition rate increases, i.e. in the presence of less stable complexing compounds, the amount of tungsten in the coating decreases. When aminoacetic acid and citric acid were used, the tungsten content in the coating amounted to ～2 wt-%, depending on the complexing agent concentration and the pH of the bath.     

Ni-Zn-P三元合金化学镀镀液配方优化研究

研究了镀液配方对化学镀Ni-Zn-P三元合金施镀效果的影响,探明了镀速、镀层硬度及其腐蚀防护性,以及镀层Ni,Zn和P含量的变化规律,确定了含Zn 9.50~16.57和P 7.55~13.59 (质量分数,%) 的Ni-Zn-P镀层制备工艺。对典型试样进行了SEM和XRD分析以及耐酸、耐碱及耐盐溶液腐蚀性能测试,结果表明：镀层表面平整、均匀,结构致密,具有典型的胞状/球状及条带状微观形貌;镀层主要由非晶、微晶或其混合相组成,其中Zn和P固溶于fcc的Ni晶格中;镀层耐盐、耐碱腐蚀能力较强。     

铝合金化学镀镍工艺对镀层沉积速度的影响

针对铝合金的特点,采用一种无机酸处理工艺对铝合金进行前处理,然后直接进行化学镀镍。讨论了主盐、还原剂、络合剂、pH值等因素对化学镀镍反应沉积速度的影响,得到了较优的工艺配方。验证试验所得Ni-P合金镀层表面均匀,耐蚀性好,结合力强。     

Preparation and characterization of Cr-P coatings by electrodeposition from trivalent chromium electrolytes using malonic acid as complex

Cr-P coatings were prepared by electrodeposition from trivalent chromium plating bath using malonic acid as complex. The influences of bath composition on the trivalent chromium electrodeposition process and deposited coating properties were studied. The effects of plating parameters such as current density, bath pH and plating time on structure and morphology of deposited coatings were investigated in detail. XRD, SEM, EDAX and XPS techniques were used to characterize the Cr-P deposited coatings. Results show that the composition, microstructure and surface morphology of the Cr-P coatings depend on bath composition and plating conditions including bath pH, current density, plating time, etc. Results of EDAX and XPS indicate that the deposited coatings contain Cr(s), Cr(III), phosphorus, oxygen and carbon. The optimum bath composition was obtained using malonic acid as complex and the mechanism of Cr-P electrodeposition was analyzed. The optimum plating parameters for good-quality chromium deposited coating are pH 2-3, current density 3-12 dm², temperature 35 °C and Ti/IrO₂ as anode. These results may be of great practical and theoretical significance for further improvement of trivalent chromium plating process.     

化学镀 Ni-Mo-P 合金镀层的组织结构与防垢性能研究

目的采用材料测试方法和防垢实验,研究不同工艺条件下的化学镀Ni-Mo-P合金镀层的组织结构与防垢性能。方法在化学镀Ni-P镀层基底上,添加含有钼酸根离子杂多酸盐,在不同工艺条件下化学沉积Ni-Mo-P合金镀层,研究化学镀Ni-Mo-P合金镀层的表面形貌和组织结构,分析镀液中硼酸含量和钼酸铵含量对镀层沉积速率的影响,观测镀层在结垢实验后的表面形貌并分析结垢速率。通过SEM,XRD和EDS对化学镀Ni-Mo-P合金镀层的表面形貌和组织结构进行检测,研究在酸性镀液中硼酸含量对化学镀Ni-Mo-P工艺条件的影响。采用防垢实验测试化学镀Ni-Mo-P合金镀层的防垢性能。结果在化学镀Ni-Mo-P过程中,钼酸根离子杂多酸盐具有稳定作用。化学镀Ni-Mo-P合金镀层的化学沉积镀液的最佳工艺条件为:Ni SO4·6H_2O 16.5 g/L,Na H_2PO_2·H_2O 20 g/L,钼酸钠0.5~0.8 g/L,硼酸2 g/L,乙酸钠7.5 g/L。化学镀Ni-Mo-P合金镀层的结垢速率明显低于化学镀Ni-P镀层,具有良好的防垢能力,形成了非晶态的镀层。结论采用化学镀Ni-P镀层基底上沉积得到非晶态的Ni-Mo-P合金镀层,硼酸具有调节镀液p H值和络合作用,非晶态的Ni-Mo-P合金镀层平均结垢速率最小值为0.58μm/h,具有良好的阻垢能力。     

环保型 AZ91D 镁合金直接化学镀镍工艺研究

目的开发一种无铬、低氟、稳定的镁合金直接化学镀镍工艺。方法通过SEM,EDX及浸泡实验、动电位极化曲线、划格试验等方法 ,以稳定系数和镀速等参数为对象,对比新工艺和传统工艺对镀层或镀液性能的影响。结果在以硫酸镍为主盐的基础液中,添加质量浓度为0.5 mg/L的硫脲,镀液的稳定性可得到明显的提高。在使用硝酸+磷酸酸洗后的镁合金试样表面,获得了良好的腐蚀形貌结构,这种结构有利于增强镀层与基底间的机械咬合作用。新工艺获得的镀层属高P镀层(P的质量分数约为11%),在Na Cl溶液中的自腐蚀电位由-1.5 V正移至-0.5 V,腐蚀电流密度降低了约3个数量级。结论以硫酸镍主盐镀液获得的镀层耐蚀性优于碱式碳酸镍主盐镀液获得的镀层,镀液的最佳p H=5,化学镀镍温度为82℃。     

pH值对中温化学镀镍-磷的影响

化学镀镍-磷技术作为表面强化的一种途径,已经得到越来越广泛的应用和不断的发展.为了研究pH值对镀层性能的影响,采用中温化学镀镍工艺,以醋酸钠为缓冲剂,以乳酸为络合剂,在酸性体系中化学沉积镍-磷合金.研究了溶液的pH值对化学镀镍-磷合金的沉积速度、镀层性能的影响.结果表明:pH值对镀速的影响较大,随着pH值的升高,镀速逐渐增加,镀层磷含量逐渐降低;在一定范围内硬度和腐蚀速度随pH值的升高而增加,在pH值为5.1时,镀层的综合性能达到最好.     

Ni-TiO2基纳米复合电刷镀层微观结构及腐蚀电化学行为

研究了用电刷镀在Q235钢上制备出Ni-TiO2纳米复合镀层复合镀液中,纳米颗粒的加入量及不同的表面活性剂对镀层性能的影响。采用SEM对复合镀层的表面形貌进行分析,用极化曲线研究了纳米复合镀层在NaCl溶液中的腐蚀电化学行为,结果表明:与纯Ni镀层相比,Ni-TiO2纳米复合镀层晶粒更加细小,空隙率更低,阳离子表面活性剂分散镀液所得镀层效果最为显著;复合镀液中纳米TiO2质量浓度为10g/L时,复合镀层的耐腐蚀性能最优;纳米颗粒含量相等的情况下,阳离子表面活性剂分散镀液所得镀层具有最好的耐腐蚀性能。     

Influence of process parameters for coating of nickel–phosphorous on carbon fibers

The nickel–phosphorous (Ni–P) coating on carbon fiber was studied, using sodium hypophosphite as a reducing agent in alkaline medium. The effects of process parameters such as time, stabilizer concentrations, pH of the plating bath and plating bath's temperature on the electroless Ni–P coating efficiency were investigated. Structural study using X-ray diffraction (XRD) indicates that nickel deposition rate increases with increasing coating time and temperature. The nickel (Ni) recovery efficiency decreases with an increase of stabilizer concentration. From scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX), it has been confirmed that the coating thickness and nickel content increase with an increase of coating time and temperature. The bath temperature of 25 °C, pH of 9, and stabilizer concentration of 25 g/L is good to get a good and uniform coating of Ni on carbon fiber. Thermal stability was studied by thermogravimetric analysis (TGA) and differential thermal analysis (DTA). From TGA study it is evident that the nickel coating increases thermal stability of the nickel-coated carbon fiber. I–V (current vs voltage) measurement shows Ni-coated fiber is more conducting in nature.     

化学镀Ni-Co-P工艺与性能研究

采用复合络合剂-柠檬酸钠和乳酸,通过正交试验优化了化学镀Ni-Co-P工艺,并对镀层的形貌、成分、组织结构及性能进行了检测和分析.结果表明,优化后的化学镀Ni-Co-P镀液稳定性好,镀速高;所得镀层为纳米晶结构,晶粒尺寸在40～60 nm,具有Ni(Co)(111)取向,整个热处理过程中晶粒没有明显长大,在428℃左右镀层发生重结晶,析出Ni3P相:镀层硬度HV10为8867 MPa,在400℃处理后HV10可提高至9892 MPa;镀层矫顽力Hc为556.27×79.6 A/m,饱和磁化强度Ms为48.73(A·m2)/kg,整个热处理过程中,镀层磁性参数变化不大.镀层具有良好的热稳定性.