铁尾矿制备白炭黑的实验研究

以铁尾矿和NaOH为原料,利用化学沉淀法成功制备了无定型白炭黑,并研究了制备的工艺条件.用X射线衍射仪、红外光谱仪、扫描电镜、透射电镜和X射线荧光光谱仪对所制白炭黑的物相结构、粒度、形貌和成分进行分析.结果表明,白炭黑中的SiO2纯度为92.3%,化学结构为无定型的水合二氧化硅,形貌近似球状粒子,粒径在150nm以下.白炭黑的比表面积(BET)为108 m2/g,10%悬浮液中pH值为5.5～6.0,加热减量为5.42%,1000℃灼烧减量为6.16%.产品符合中国行业标准HG/T 3061-1999的要求.     

石煤尾矿制备白炭黑的研究

利用石煤尾矿制备白炭黑,考察了氢氧化钠浓度、固液比、反应温度、反应时间对二氧化硅浸出率的影响。结果表明:在氢氧化钠浓度为4 mol/L、固液比为1∶4、反应温度为100℃和反应时间为5 h条件下,二氧化硅浸出率为61.8%,白炭黑产品中二氧化硅含量超过90%,主含量达到行业标准。     

石英砂尾矿和白炭黑对环氧地坪涂料的性能影响研究

添加石英砂尾矿以及白炭黑制备环氧地坪材料,通过适当调节固化剂以及白炭黑、石英砂尾矿之间的配比,以期在一定程度上提高环氧地坪材料的硬度以及各项性能.试验结果表明:使用T-31环氧固化剂,采用涂层方法为中底涂,当水性环氧树脂含量为14 mL时,石英砂尾矿含量为1.2 g,白炭黑含量为1.6 g,环氧地坪材料的硬度可达到3H,耐洗刷次数最多可以达到7800次,耐水性提升到13 d,耐碱性提高到7 d,符合GB/T 22374-2008中优等品的要求,有效提高了环氧地坪涂料的耐磨性和附加值,有望推广应用.     

磷矿浮选尾矿煅烧铵盐法实验研究

针对瓮福磷矿浮选尾矿的资源特点,将磷尾矿作为高磷白云石矿进行处理,舍弃了传统的白云石碳化法,提出了煅烧-铵盐选择浸出工艺,不仅可以开发出具有高附加值和工业应用前景的优质氢氧化镁、氧化镁以及轻质碳酸钙,并且可获得适于湿法磷酸生产的磷精矿,较好实现资源的综合利用。研究表明:在煅烧温度为900℃时,尾矿中白云石分解,而氟磷酸钙不分解;煅烧熟料用硝酸铵浸出,CaO浸出率可达80.43%;浸出渣用硫酸铵二次浸出,MgO浸出率可达91%以上,二次浸出渣为含P2O538%以上的磷精矿;P2O5回收率达88.58%。该研究为综合利用磷矿浮选尾矿提供了基础性资料。     

高灰分浮选尾矿制砖

<正> 近几年来,随着环保意识的增强,大部分洗煤厂陆续使用了压滤机回收尾矿,但由于尾矿灰分过高,不能作燃料,销路不佳,影响了洗煤厂的正常生产。尾矿的出路问题是洗煤厂生产中急需解决的问题之一。枣庄矿务局枣庄煤矿研究了高灰分浮选尾矿烧制尾矿砖并获得成功。枣庄矿洗煤厂浮选尾矿灰分较高,一般在75％以上,不能作燃料使用。当尾矿灰分在79.88％时,低位发热量3180kJ/kg,根据烧结煤矸石砖的要求,发热量不超过     

中低品位磷矿浮选尾矿制备磷镁肥的实验研究

研究开发一种以中低品位磷矿浮选尾矿为原料,采用硫磷混酸直接分解浮选尾矿制备磷镁肥的方法。阐述了浮选尾矿的矿物特性,硫磷混酸分解浮选尾矿制备磷镁肥的基本原理、工艺条件、产品质量,论证了中低品位磷矿浮选尾矿制备磷镁肥的可行性。     

浮选磷矿尾矿再选试验探索

云南某磷矿浮选尾矿主要矿物为胶磷矿,脉石矿物为石英-硅酸盐类矿物。对该浮选尾矿进行工艺矿物学研究和再磨再选试验,结果表明,可以获得磷精矿品位26.96%,回收率65.79%,尾矿磷品位4.72%的良好指标。     

四氯化硅滴定法制备白炭黑的实验研究

以多晶硅生产过程中产生的废弃物四氯化硅为原料,在一定条件下,在保护气体(如惰性气体氮气)的保护下,将四氯化硅与等量的硅酸钠溶液同时滴定到放有氯化钠溶液的容器中,调节溶液pH至4左右,搅拌30 min后停止搅拌,转移沉淀物,漂洗至pH到7,抽滤、烘干即可得到粉状白炭黑.本文的创新点是在总结前人制备纳米白炭黑的基础上,研制出利用双水解的方法制备纳米白炭黑.     

煤矸石酸渣制备白炭黑的实验研究

白炭黑是橡胶、塑料、涂料等化工制品的重要填料,煤矸石制取白炭黑是其高附加值利用手段之一.利用煤矸石提铝后的酸渣,制备低模数水玻璃,经新鲜酸渣提模,制取与工业水玻璃模数(n≈3.6)相近的高模数水玻璃.以二氧化碳为沉淀剂,经碳化反应制取白炭黑.采用单因素实验和正交实验相结合,确定出最佳的工艺条件:(1)煤矸石酸渣制备高模数水玻璃:提模时间1.0h、提模温度60℃及液固比为4∶1;(2)高模数水玻璃制备白炭黑:反应温度80℃、反应时间2.5h、水玻璃密度1.075 g/mL、水玻璃模数3.3、搅拌速率为350 r/min、二氧化碳浓度为20％.所制白炭黑质量好,吸油值2.2 mL/g,白度90％以上,纯度85％以上.     

钼尾矿中有用矿物回收实验研究

以辽宁某钼矿选矿厂尾矿为研究对象,在矿浆浓度25％、pH值为8.5、浮选机主轴转速为1850 r/min的条件下,以水玻璃为硅酸盐抑制剂、油酸钠为捕收剂、烷基胺为起泡剂,通过一精一扫的浮选工艺,获得精选金云母回收率约46％、品位9.6％以上,扫选金云母回收率26.46％、品位7.81％,为今后钼尾矿中金云母的浮选实践提供了理论和试验依据.     

湖北某磷矿反浮选钾长石试验研究

针对湖北某低品位难选硅钙(镁)质磷矿,主要脉石矿物为钾长石,原矿P2O5品位19.84％,SiO2品位27.78％.在磨矿细度-0.074 mm占比80.16％,预先脱除白云石及细泥的情况下,用醚胺类捕收剂T-609反浮选钾长石,可获得精矿P2O5品位33.65％,回收率达72.83％的良好指标,实现了磷灰石和钾长石的有效分离.捕收剂T-609与钾长石主要以物理吸附为主,T-609和消泡剂TOP的搭配使用,可有效改善阳离子捕收剂反浮选钾长石泡沫性能.     

金川铜镍矿浮选中矿脱镁浸渣选矿试验研究

以金川铜镍矿浮选中矿为研究对象,采用化学多元素分析、XRD衍射分析、物相分析、粒度分析等工艺矿物学检测手段,对试样性质进行了研究.经过酸浸脱镁,浸渣中镍品位为2.06％,铜品位为2.05％.为高效回收其中的铜、镍,在工艺矿物学分析基础上,采用单因素试验法,进行了选矿试验研究.结果表明,在磨矿细度为-0.037 mm占80％的情况下,采用两次粗选的试验流程处理该试样,可获得镍精矿品位3.17％,镍精矿含铜2.83％,镍、铜回收率分别为95.46％、91.78％.试验确定的工艺流程较简单,有效的回收了试样中的有价金属铜、镍,是该试样中铜、镍的理想回收工艺.     

Beneficiation of Cassiterite Fines from a Tin Tailing Slime by Froth Flotation

The beneficiation of cassiterite fines from a tailing slime in the Datun concentration plant was studied through a froth flotation process, with the chemical scheme of benzohydroxamic acid as collector, lead nitrate as activator, and pine oil as frother. It was found that tin values are mainly contained in the fine fraction of the sample and cassiterite is mostly associated with iron minerals and calcium minerals, so that the desliming treatment and the addition of dispersants and depressants can not be used as it generally results in the undesired loss of tin values. A novel flotation process with no dispersant and depressant as well as no desliming was developed. It showed that this process was effective in recovering the tin values from the tailing slime assaying 0.18% Sn, and produced a concentrate assaying 3.5% Sn with the recovery of 74.16%. It has been found that pine oil played a significant role in improving the recovery for tin values.     

Enrichment of Silica Sand Ore by Cyclojet Flotation Cell

Cyclojet flotation is an alternative technique of jet flotation. It essentially has a mechanism for bubble formation with pulp jet spouting from the apex of hydrocyclone. The size of the bubbles formed with pulp jet in the cyclojet cell is very small, and the quantity of bubbles produced also limits its potential to produce high bubble-particle collision. This is particularly efficient in beneficiation of fine-grained ores. In this study, the performance of the cyclojet flotation cell was tested for removing iron-oxides from silica sand ore. Whether it can be used as an alternative to conventional mechanical cells was studied. The findings obtained from the cyclojet cell were compared with findings obtained from the conventional cell. It was seen that the cyclojet cell produced slightly better results than the conventional cell. Under the best conditions, while the cyclojet cell reduced the iron-oxide content in silica sand from 0.41% to 0.08%, the conventional cell reduced it to 0.10%. While iron removal efficiency was 80.49% for the cyclojet flotation, it was calculated as 75.61% for the conventional cell. These findings showed that cyclojet flotation can be used as an alternative method to conventional flotation for the removal of iron oxides from silica sand.     

浮选尾煤粗粒回收系统改造

吕家坨矿洗煤厂增加浮选粗粒回收系统后,年收益为2160万元,同时也净化了洗煤用水,改善了浮选效果,并简要介绍了粗粒回收系统的配置,开停车操作程序及应注意事项。     

铁矿石尾矿粉催化还原NO的实验研究

以马鞍山钢铁集团南山矿铁矿石尾矿为主要原料制备无载体催化剂,对其进行了XRF, BET和XRD表征,并于电加热石英玻璃管固定床中实验研究了催化剂对NH3还原NO的催化活性. 结果表明,用铁尾矿所制催化剂在反应温度500?600℃下具有良好的催化活性,600℃时催化还原率达97.5%,且粒径越小催化还原率越高;氧含量对催化还原率有较大影响,350℃时增加氧含量可提高催化还原率,500℃时增加氧含量会降低催化还原率;氧化铁作为主要活性组分,在催化剂中含量越高催化还原率越高,但氧化铁高温时易烧结,会降低催化还原率.     

某白钨多金属矿浮选尾矿中萤石提取技术研究

为了缓解萤石资源严峻形势,提高低品位难选萤石矿以及共（伴）生型萤石矿的综合利用水平,结合矿石性质分析基础上,进行了系列条件试验研究、部分流程开路试验研究以及全流程闭路试验研究,研究结果表明：在一次粗选二次扫选,粗精矿再磨后进行五次精选,中矿顺序返回的原则流程条件下,以油酸为捕收剂、水玻璃和腐植酸钠为组合抑制剂、碳酸钠为pH调整剂,可实现该白钨多金属矿尾矿中萤石二次资源的有效回收利用;当捕收剂油酸用量450 g／t,组合抑制剂2．8 kg／t,碳酸钠1 kg／t时,在给矿CaF2品位16．41％的条件下,获得了CaF2品位为87．92％、CaF2回收率为53．53％的萤石精矿。     

菱镁矿尾矿与硼泥合成橄榄石研究

本实验以菱镁矿尾矿、硼泥和硅石为主要原料,通过固相反应烧结制备镁橄榄石,研究随着硼泥和添加剂铁红(Fe2O3)引入量的不同对合成镁橄榄石材料相组成、结构及烧结性能的影响.利用XRD和SEM对烧后试样的矿物相组成和显微结构进行表征.结果表明:硼泥可以促进烧后镁橄榄石材料中晶粒异常长大,随着烧后镁橄榄石材料结构中液相的增多,系统中出现了顽火辉石相,烧后镁橄榄石材料体积密度逐渐增大,硼泥对镁橄榄石有促烧结作用.添加剂铁红与氧化镁形成镁铁固溶体,促进镁橄榄石材料结构致密,系统中引入3.51％铁红,烧后镁橄榄石材料体积密度提高24％.     

利用贵州锑矿资源大力开发锑系列化工产品

对贵州锑矿资源的开发利用状况进行了研究，指出大力发展锑系列化工产品的方向，并提出几点建议。