V-doping effects on ferroelectric properties of K0.5Bi4.5Ti4O15 thin films

V-doped K_0.5Bi_4.5Ti₄O₁₅ (K_0.5Bi_{4.5 − x/3}Ti_4 − xV_xO₁₅, KBTiV-x, x = 0.00, 0.01, 0.03, and 0.05) thin films were prepared on a Pt(111)/Ti/SiO₂/Si(100) substrate by a chemical solution deposition method. The thin films were annealed by using a rapid thermal annealing process at 750 °C for 3 min in an oxygen atmosphere. Among them, KBTiV-0.03 thin film exhibited the most outstanding electrical properties. The value of remnant polarization (2P_r) was 75 μC/cm² at an applied electric field of 366 kV/cm. The leakage current density of the thin film capacitor was 5.01 × 10⁻⁸ at 100 kV/cm, which is approximately one order of magnitude lower than that of pure K_0.5Bi_4.5Ti₄O₁₅ thin film capacitor. We found that V doping is an effective method for improving the ferroelectric properties of K_0.5Bi_4.5Ti₄O₁₅ thin film.     

Enhanced ferroelectric properties of Pb(Zr0.80Ti0.20)O3/PbO thin films prepared by radio frequency magnetron sputtering

The Pb(Zr_0.80Ti_0.20)O₃ (PZT) thin films with and without a PbO buffer layer were deposited on the Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by radio frequency (rf) magnetron sputtering method. The PbO buffer layer improves the microstructure and electrical properties of the PZT thin films. High phase purity and good microstructure of the PZT thin films with a PbO buffer layer were obtained. The effect of the PbO buffer layer on the ferroelectric properties of the PZT thin films was also investigated. The PZT thin films with a PbO buffer layer possess better ferroelectric properties with higher remnant polarization (P_r = 25.6 μC/cm²), and lower coercive field (E_c = 60.5 kV/cm) than that of the films without a PbO buffer layer (P_r = 9.4 μC/cm², E_c = 101.3 kV/cm). Enhanced ferroelectric properties of the PZT thin films with a PbO buffer layer is attributed to high phase purity and good microstructure.     

Properties of La-substituted Na0.5Bi4.5Ti4O15 ferroelectric thin films

Ferroelectric Na_0.5La_0.5Bi₄Ti₄O₁₅ (NaLaBTi) thin films were prepared by a chemical solution deposition method. The NaLaBTi thin films annealed at 750 °C under oxygen atmosphere were randomly oriented polycrystalline. Electrical properties of the NaLaBTi thin films were compared to Na_0.5Bi_4.5Ti₄O₁₅ thin films and better properties were observed in the NaLaBTi thin films. Remnant polarization (2P_r) and coercive electric field (2E_c) were 43 µC/cm² and 204 kV/cm at an applied electric field of 478 kV/cm, respectively. Leakage current density was 1.95 × 10^− 6 A/cm² at 100 kV/cm. Dielectric constant and dielectric loss were 805 and 0.05 at 1 kHz, respectively. Switchable polarization was suppressed by 15% after 1.44 × 10¹⁰ switching cycles.     

Composition dependent preferential orientation, dielectric and ferroelectric properties of Pb(ZrxTi1 − x)O3 thin films derived by sol-gel process

Pb(Zr_xTi_1 − x)O₃ (x = 0.35, 0.40, 0.60, 0.65) thin films were prepared by sol-gel spin on technique. From the X-ray diffraction analysis, PZT films with Zr-rich compositions (x = 0.60 and 0.65) had (111) preferential orientation and the preferential orientation changed to (100) for Ti-rich compositions (x = 0.35 and 0.40). The dielectric measurements on the above compositions at room temperature showed that the dielectric constant values were higher in Zr-rich compositions compared to Ti-rich compositions. The ferroelectric behavior measured in terms of the remnant polarization (P_r) and coercive field (E_c) up to an applied field of 260 kV/cm depicted that the Zr-rich PZT films with (111) preferential orientation had higher P_r and lower E_c values compared to the Ti-rich PZT films with (100) preferential orientation can be understood from the domain switching mechanism.     

Enhancement on effective piezoelectric coefficient of Bi3.25Eu0.75Ti3O12 ferroelectric thin films under moderate annealing temperature

Bi_3.25Eu_0.75Ti₃O₁₂ (BET) thin films were deposited on Pt/Ti/SiO₂/Si(111) substrates by a metal-organic decomposition method. The effects of annealing temperatures 600-800 °C on microstructure, ferroelectric, dielectric and piezoelectric properties of BET thin films were studied in detail. The spontaneous polarization (87.4 × 10^− 6 C/cm² under 300 kV/cm), remnant polarization (65.7 × 10^− 6 C/cm² under 300 kV/cm), the dielectric constant (992.9 at 100 kHz) and the effective piezoelectric coefficient d₃₃ (67.3 pm/V under 260 kV/cm) of BET thin film annealed at 700 °C are better than those of the others. The mechanisms concerning the dependence of the enhancement d₃₃ are discussed according to the phenomenological equation, and the improved piezoelectric performance could make the BET thin film a promising candidate for piezoelectric thin film devices.     

Effect of Pb(Fe1/2Nb1/2)O3 modification on dielectric and piezoelectric properties of Pb(Mg1/3Nb2/3)O3-PbZr0.52Ti0.48O3 ceramics

10 mol% Pb(Fe_1/2Nb_1/2)O₃ (PFN) modified Pb(Mg_1/3Nb_2/3)O₃-PbZr_0.52Ti_0.48O₃ (PMN-PZT) relaxor ferroelectric ceramics with compositions of (0.9 − x)PMN-0.1PFN-xPZT (x = 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8 and 0.9) were prepared. X-ray diffraction investigations indicated that as-prepared ceramics were of pure perovskite phase and the sample with composition of x = 0.8 was close to morphotropic phase boundary (MPB) between rhombohedral and tetragonal phase. Dielectric properties of the as-prepared ceramics were measured, and the Curie temperature (T_c) increased sharply with increasing PZT content and could be higher than 300 °C around morphotropic phase boundary (MPB) area. At 1 kHz, the sample with composition of x = 0.1 had the largest room temperature dielectric constant ?_r = 3519 and maximum dielectric constant ?_m = 20,475 at T_m, while the sample with composition of x = 0.3 possessed the maximum dielectric relaxor factor of γ = 1.94. The largest d₃₃ = 318 pC/N could be obtained from as-prepared ceramics at x = 0.9. The maximum remnant polarization (P_r = 28.3 μC/cm²) was obtained from as-prepared ceramics at x = 0.4.     

New substitutions and novel derivatives of the Aurivillius phases, Bi5TiNbWO15 and Bi4Ti3O12

We investigated isomorphous substitution of several metal atoms in the Aurivillius structures, Bi₅TiNbWO₁₅ and Bi₄Ti₃O₁₂, in an effort to understand structure-property correlations. Our investigations have led to the synthesis of new derivatives, Bi₄LnTiMWO₁₅ (Ln = La, Pr; M = Nb, Ta), as well as Bi₄PbNb₂WO₁₅ and Bi₃LaPbNb₂WO₁₅, that largely retain the Aurivillius (n = 1) + (n = 2) intergrowth structure of the parent oxide Bi₅TiNbWO₁₅, but characteristically tend toward a centrosymmetric/tetragonal structure for the Ln-substituted derivatives. On the other hand, coupled substitution, 2Ti^IV → M^V + Fe^III in Bi₄Ti₃O₁₂, yields new Aurivillius phases, Bi₄Ti_3−2xNb_xFe_xO₁₂ (x = 0.25, 0.50) and Bi₄Ti_3−2xTa_xFe_xO₁₂ (x = 0.25) that retain the orthorhombic noncentrosymmetric structure of the parent Bi₄Ti₃O₁₂. Two new members of this family, Bi₂Sr₂Nb₂RuO₁₂ and Bi₂SrNaNb₂RuO₁₂ that are analogous to Bi₂Sr₂Nb₂TiO₁₂, possessing tetragonal (I4/mmm) Aurivillius structure have also been synthesized.     

Dependence of Zr content on electrical properties of Bi3.15Nd0.85Ti3-xZrxO12 thin films synthesized by chemical solution deposition (CSD)

The Bi_3.15Nd_0.85Ti_3-xZr_xO₁₂ (BNTZ) thin films with Zr content (x = 0, 0.05, 0. 1, 0.15, and 0.2) were prepared on Pt/Ti/SiO₂/Si (100) substrates by chemical solution deposition (CSD) technique. The crystal structures of BNTZ films were analyzed by X-ray diffraction (XRD). The effects of Zr contents on the ferroelectric, dielectric properties, and leakage current of BNTZ films were thoroughly investigated. The XRD results demonstrated that all the films possessed a single phase bismuth-layered structure and exhibited the highly preferred (117) orientation. Among these films, the film with Zr content x = 0.1 held the maximum remanent polarization (2P_r) of 50.21 μC/cm² and a low coercive field (2E_c) of 210 kV/cm.     

Effect of yttrium doping on the dielectric properties of CaCu3Ti4O12 thin film produced by chemical solution deposition

Pure and yttrium substituted CaCu₃Ti_4 − xY_xO_{12 − x / 2} (x = 0, 0.02, 0.1) thin films were prepared on boron doped silica substrate employing chemical solution deposition, spin coating and rapid thermal annealing. The phase and microstructure of the sintered films were examined using X-ray diffraction and scanning electron microscopy. Dielectric properties of the films were measured at room temperature using electrochemical impedance spectroscopy. Highly ordered polycrystalline CCTO thin film with bimodal grain size distribution was achieved at a sintering temperature of 800 °C. Yttrium doping was found to have beneficial effects on the dielectric properties of CCTO thin film. Dielectric parameters obtained for a CaCu₃Ti_4 − xY_xO_{12 − x / 2} (x = 0.02) film at 1 KHz were k ∼ 2700 and tan δ ∼ 0.07.     

Enhancement on effective piezoelectric coefficient d33 of Bi3.15Dy0.85Ti3O12 ferroelectric thin films

Effects of annealing temperature (600-800 °C) on microstructure, ferroelectric and piezoelectric properties of Bi_3.15Dy_0.85Ti₃O₁₂ (BDT) thin films prepared by metal-organic decomposition were studied. The remnant polarization 2P_r and spontaneous polarization 2P_s (16.2 µC/cm² and 23.3 µC/cm² under 690 kV/cm), effective piezoelectric coefficient d₃₃ (63 pm/V under the bipolar driving field of 310 kV/cm) of BDT thin film annealed at 700 °C are better than those of others. The higher 2P_s and relatively permittivity ε_r induced by moderate annealing temperature should be responsible for the enhancement of piezoelectric properties. The improved d₃₃ may make BDT a promising candidate for piezoelectric thin film devices.     

Nd-substituted SrBi2Ta2O9 ferroelectric thin films prepared by radio frequency magnetron sputtering

Nd-substituted SrBi₂Ta₂O₉ (SNBT) thin films are sputtered on Pt/Ta/SiO₂/Si substrates. X-ray diffraction and x-ray photoelectron spectroscopy studies indicate that Nd³⁺ is substituted into the bismuth layered perovskite structure, preferentially at the Sr²⁺ site. The annealed thin film is polycrystalline with plate/needle-like grain microstructure. Secondary ion mass spectrometry results show that elements in SNBT thin film homogeneously distribute along film depth and interfacial diffusion takes place during post annealing. The Nd substitution leads to enhanced remnant polarization (2P_r = 18 μC/cm²) and reduced coercivity (2E_c = 64 kV/cm) at 180 kV/cm measured at 25 °C. After 10¹⁰ switching cycles, around 9% remnant polarization is decreased.     

Microstructure and electrical properties of Ba0.7Sr0.3(Ti1 − xZrx)O3 thin films prepared on copper foils with sol-gel method

Ba_0.7Sr_0.3(Ti_1 − xZr_x)O₃ (x = 0, 0.1, 0.2) (BSZT) thin films have been prepared on copper foils using sol-gel method. The films were annealed in an atmosphere with low oxygen pressure so that the substrate oxidation was avoided and the formation of the perovskite phase was allowed. The X-ray diffraction results show a stable polycrystalline perovskite phase, with the diffraction peaks of the BSZT films shifting toward the smaller 2θ with increasing Zr content. Scanning electron microscopy images show that the grain size of the BSZT thin films decreases with increasing Zr content. High resolution transmission electron microscopy shows the clear lattice and domain structure in the film. The dielectric peaks of the BSZT thin films broaden with increasing Zr content. Leakage current density of Ba_0.7Sr_0.3(Ti_1 − xZr_x)O₃ (x = 0.1) thin film is the lowest over the whole applied voltage.     

Enhanced ferroelectric properties of Mg doped (Ba,Sr)TiO3 thick films grown on (001) SrTiO3 substrates

Highly (001)-oriented 1 mol% Mg doped (Ba_0.67,Sr_0.33)TiO₃ (BST) films with a thickness of 1.25 μm were grown on (110) SrRuO₃/(001) SrTiO₃ substrates by pulsed laser deposition. X-ray diffraction measurements reveal that the BST thick films have very high crystalline quality, and have a distorted lattice with a large tetragonality a/c = 1.012. The BST thick films have a remanent polarization (P_r) value as large as 10.1 μC/cm² and a coercive electric field (E_c) value of 65.0 kV/cm. The films possess dielectric constant and loss values of ε_r = 385.36 and tgδ = 0.038 at 1 kHz and room temperature. The leakage currents of the films are on the order of 10^− 5 A/cm² at ± 150 kV/cm. The mechanism for enhancing electric properties of the Mg doped BST films was also discussed.     

Ferroelectric and dielectric properties of Bi4-xNdxTi3O12 thin films prepared by sol–gel method

Bi_4-xNd_xTi₃O₁₂ (BNT-x, x = 0, 0.25, 0.50, 0.75 and 1.0) thin films were prepared on Pt/Ti/SiO₂/Si substrates by a sol–gel method. The microstructure, ferroelectric and dielectric properties of BNT-x thin films were investigated. The single-phase BNT-x thin films were obtained. With increasing Nd content, the preferred orientation changed from random to (117) and surface morphologies changed from the mixture of rod- and plate-like grains to rod-like grains. The Nd substitution improved the ferroelectric and dielectric properties of BTO films. BNT-x films showed better electrical properties at x = 0.50—1.0. BNT-0.75 film exhibited the best electrical properties with remanent polarization (2P _r) of 26.6 μC/cm², dielectric constant (ε _r) of 366 (at 1 MHz), dielectric loss (tanδ) of 0.034 (at 1 MHz), leakage current density (J) of ±3.0 × 10⁻⁶ A/cm² (at ± 5 V) and fatigue-free characteristics.     

Structural and optical properties of Er-doped Y2Ti2O7 thin films by sol-gel method

Er³⁺-doped Y₂Ti₂O₇ and Er₂Ti₂O₇ thin films were fabricated by sol-gel spin-coating method. A well-defined pyrochlore phase Er_xY_2-xTi₂O₇ was observed while the annealing temperature exceeded 800 °C. The average transmittance of the Er_xY_2-xTi₂O₇ thin films annealed at 400 to 900 °C reduces from ∼ 87 to ∼ 77%. The refractive indices and optical band gaps of Er_xY_2-xTi₂O₇ (x = 0-2) annealed at 800 °C/1 h vary from 2.20 to 2.09 and 4.11 to 4.07 eV, respectively. The ∼ 1.53 μm photoluminescence spectrum of Er³⁺ (5 mol%)-doped Y₂Ti₂O₇ thin films annealed at 700 °C/1 h exhibits the maximum intensity and full-width at half maximum (∼ 60 nm).     

Effects of annealing process and Mn substitution on structure and ferroelectric properties of BiFeO3 films

The BiFe_1 − xMn_xO₃ (BFMO) (x = 0.03, 0.05 and 0.07) thin films were deposited on indium tin oxide/glass substrates using a metal organic decomposition method. X-ray diffraction analysis reveals that the structure of BiFeO₃ films is distorted somewhat by Mn substitution. The leakage measurements indicate that Mn doping content is a dominant factor affecting the leakage current of BFMO films. Due to the poor crystallinity, a small remanent polarization (P_r) is observed in the BFMO_x = 0.05 thin film annealed using the conventional method. The P_r values for the sequential-layer annealed BFMO films are found to be related to the intensity of (012) peak and the content of defect complexes between the oxygen vacancies and acceptors.     

Sputter-epitaxy and electric properties of multiferroic Bim + 1Fem-3Ti3O3m + 3 thin films

Growth conditions suitable for sputter-epitaxy of Bi_m + 1Fe_m-3Ti₃O_3m + 3 (BFTO) thin films with layered structure have been investigated. The amount of oxygen during deposition was found to be specifically essential for obtaining a good-quality thin film of BFTO with a large m. The (001) epitaxial thin films of BFTO with m of nearly 10 which is expected to retain magnetic order up to room temperature have been successfully grown on (001) SrTiO₃ substrates under the determined optimum condition. The film exhibited leakage current as low as order of 10⁻²-10⁻¹ A/m² limited by Schottky emission at the interfaces between the electrodes and the film. In addition, the film showed a ferroelectric polarization curve with Pr = 6 μC/cm² for applied field of 35 MV/m at room temperature though the curve was unsaturated. These indicate that the BFTO (m = 10) thin films are promising as multiferroics at room temperature.     

Electrical properties of Pb0.97La0.02(Zr0.95Ti0.05)O3 antiferroelectric thin films on TiO2 buffer layer

Pb_0.97La_0.02(Zr_0.95Ti_0.05)O₃ antiferroelectric thin films with thickness of 500 nm were successfully deposited on TiO₂ buffered Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) and Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates via sol-gel process. Microstructure of Pb_0.97La_0.02(Zr_0.95Ti_0.05)O₃ thin films was studied by X-ray diffraction analyses. The antiferroelectric nature of the Pb_0.97La_0.02(Zr_0.95Ti_0.05)O₃ thin films was confirmed by the double hysteresis behaviors of polarization and double buffer fly response of dielectric constant versus applied voltage at room temperature. The capacitance-voltage behaviors of the Pb_0.97La_0.02(Zr_0.95Ti_0.05)O₃ films with and without TiO₂ buffer layer were studied, as a function of temperature. The temperature dependence of dielectric constant displayed a similar behavior and the Curie temperature (T_c) was 193 °C for films on both substrates. The current caused by the polarization and depolarization of polar in the Pb_0.97La_0.02(Zr_0.95Ti_0.05)O₃ films was detected by current density-electric field measurement.     

Effects of Mn doping on structural and dielectric properties of sol-gel-derived (Ba0.835Ca0.165)(Zr0.09Ti0.91)O3 thin films

We reported the effects of Mn doping on the structure and dielectric properties of (Ba_0.835Ca_0.165)(Zr_0.09Ti_0.91)O₃ (BCZT) thin films prepared by sol-gel method. The (Ba_0.835Ca_0.165)Mn_x(Zr_0.09Ti_0.91)_1 − xO₃ (x = 0, 0.002, 0.005, and 0.01) thin films exhibited a pure pseudo-cubic perovskite structure with random orientation. Scanning electron microscopy and atomic force microscopy observation showed that increasing Mn-doping amount caused a decrease in particle size and a cluster of the particles, while the film surface remained smooth and crack-free. Compared with the undoped film, Mn doped BCZT thin films exhibited smaller dielectric constant and lower dielectric loss. The figure of merit reached the maximum value of 16.7 with a tunability of 53.6% for the film with 0.5 mol % Mn doping, when a bias electric field of 400 kV/cm was applied at 100 kHz. The results indicated that the Mn doped BCZT thin films are suitable for tunable microwave device applications.     

Microstructure and thermoelectric properties of Sn-doped Bi2Te2.7Se0.3 thin films deposited by flash evaporation method

(Bi_1 − xSn_x)₂Te_2.7Se_0.3 thermoelectric thin films with thickness of 800 nm have been deposited on glass substrates by flash evaporation method at 473 K. The structures, morphology of the thin films were analyzed by X-ray diffraction and field emission scanning electron microscopy respectively. Effects of Sn-doping concentration on thermoelectric properties of the annealed thin films were investigated by room-temperature measurement of Seebeck coefficient and electrical resistivity. The thermoelectric power factor was enhanced to 12.8 μW/cmK² (x = 0.003). From x = 0.004 to 0.01 Sn doping concentration, the Seebeck coefficients are positive and show p-type conduction. The Seebeck coefficient and electrical resistivity gradually decrease with increasing Sn doping concentration.