Improved anticorrosion properties and electrical conductivity of 316L stainless steel as bipolar plate for proton exchange membrane fuel cell by lower temperature chromizing treatment

The lower temperature chromizing treatment is developed to modify 316L stainless steel (SS 316L) for the application of bipolar plate in proton exchange membrane fuel cell (PEMFC). The treatment is performed to produce a coating, containing mainly Cr-carbide and Cr-nitride, on the substrate to improve the anticorrosion properties and electrical conductivity between the bipolar plate and carbon paper. Shot peening is used as the pretreatment to produce an activated surface on stainless steel to reduce chromizing temperature. Anticorrosion properties and interfacial contact resistance (ICR) are investigated in this study. Results show that the chromized SS 316L exhibits better corrosion resistance and lower ICR value than those of bare SS 316L. The chromized SS 316L shows the passive current density about 3E−7 A cm⁻² that is about four orders of magnitude lower than that of bare SS 316L. ICR value of the chromized SS 316L is 13 mΩ cm² that is about one-third of bare SS 316L at 200 N cm⁻² compaction forces. Therefore, this study clearly states the performance advantages of using chromized SS 316L by lower temperature chromizing treatment as bipolar plate for PEMFC.     

An investigation into TiN-coated 316L stainless steel as a bipolar plate material for PEM fuel cells

In order to reduce the cost, weight and volume of the bipolar plates, considerable attention is being paid to developing metallic bipolar plates to replace the non-porous graphite bipolar plates that are in current use. However, metals are prone to corrosion in the proton exchange membrane (PEM) fuel cell environments, which decreases the ionic conductivity of the membrane and lowers the overall performance of the fuel cells. In this study, TiN was coated on SS316L using a physical vapor deposition (PVD) technology (plasma enhanced reactive evaporation) to increase the corrosion resistance of the base SS316L. X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical methods were used to characterize the TiN-coated SS316L. XRD showed that the TiN coating had a face-centered-cubic (fcc) structure. Potentiodynamic tests and electrochemical impedance tests showed that the corrosion resistance of SS316L was significantly increased in 0.5 M H₂SO₄ at 70 °C by coating with TiN. In order to investigate the suitability of these coated materials as cathodes and anodes in a PEMFC, potentiostatic tests were conducted under both simulated cathode and anode conditions. The simulated anode environment was −0.1 V versus SCE purged with H₂ and the simulated cathode environment was 0.6 V versus SCE purged with O₂. In the simulated anode conditions, the corrosion current of TiN-coated SS316L is −4 × 10⁻⁵ A cm⁻², which is lower than that of the uncoated SS316L (about −1 × 10⁻⁶ A cm⁻²). In the simulated cathode conditions, the corrosion current of TiN-coated SS316L is increased to 2.5 × 10⁻⁵ A cm⁻², which is higher than that of the uncoated SS316L (about 5 × 10⁻⁶ A cm⁻²). This is because pitting corrosion had taken place on the TiN-coated specimen.     

Nanocomposite-carbon coated at low-temperature: A new coating material for metallic bipolar plates of polymer electrolyte membrane fuel cells

A nanocomposite-carbon layer is coated onto the surface of 316L stainless steel (SS316) using a beam of accelerated C₆₀ ions at low temperature. The coating is composed of textured graphite nanocrystals ranging in size from 1 to 2 nm, with the graphene plane normal to the coating plane; the nanocrystals are separated by amorphous carbon. This orientation of the graphene layer provides low film resistivity in the direction of the substrate normal. Corrosion resistance tests performed in aggressive anodic and cathodic environments of a polymer electrolyte membrane fuel cell (PEMFC) show that the nanocomposite-carbon coated SS316L exhibits better anticorrosion properties than does bare SS316L. The interfacial contact resistance (ICR) of the nanocomposite-carbon coated SS316L is 12 mΩ cm², which is similar to that of graphite at a compaction force of 150 N cm⁻² and lower than a target of ∼20 mΩ cm². A low value of ICR is maintained even after corrosion tests in aggressive anodic and cathodic environments. The fabricated nanocomposite-carbon coated SS316L exhibits excellent corrosion resistance and low interfacial contact resistance under simulated PEMFC bipolar plate conditions.     

Chromium nitride/Cr coated 316L stainless steel as bipolar plate for proton exchange membrane fuel cell

Chromium nitride/Cr coating has been deposited on surface of 316L stainless steel to improve conductivity and corrosion resistance by physical vapor deposition (PVD) technology. Electrochemical behaviors of the chromium nitride/Cr coated 316L stainless steel are investigated in 0.05 M H₂SO₄ + 2 ppm F⁻ simulating proton exchange membrane fuel cell (PEMFC) environments, and interfacial contact resistance (ICR) are measured before and after potentiostatic polarization at anodic and cathodic operation potentials for PEMFC. The chromium nitride/Cr coated 316L stainless steel exhibits improved corrosion resistance and better stability of passive film either in the simulated anodic or cathodic environment. In comparison to 316L stainless steel with air-formed oxide film, the ICR between the chromium nitride/Cr coated 316L stainless steel and carbon paper is about 30 mΩ cm² that is about one-third of bare 316L stainless steel at the compaction force of 150 N cm⁻². Even stable passive films are formed in the simulated PEMFC environments after potentiostatic polarization, the ICR of the chromium nitride/Cr coated 316L stainless steel increases slightly in the range of measured compaction force. The excellent performance of the chromium nitride/Cr coated 316L stainless steel is attributed to inherent characters. The chromium nitride/Cr coated 316L stainless steel is a promising material using as bipolar plate for PEMFC.     

Anticorrosion properties of Ta-coated 316L stainless steel as bipolar plate material in proton exchange membrane fuel cells

In order to reduce the cost, volume and weight of the bipolar plates used in the proton exchange membrane fuel cells (PEMFC), more attention is being paid to metallic materials, among which 316L stainless steel (SS316L) is quite attractive. In this study, metallic Ta is deposited on SS316L using physical vapor deposition (PVD) to enhance the corrosion resistance of the bipolar plates. Simulative working environment of PEMFC is applied for testing the corrosion property of uncoated and Ta-coated SS316L. X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical methods (potentiodynamic and potentiostatic polarization) are also used for analyzing characteristics of uncoated and Ta-coated SS316L. Results show that, Ta-coated SS316L has significantly better anticorrosion property than that of uncoated SS316L, with corrosion current densities of uncoated SS316L being 44.61 μA cm⁻² versus 9.25 μA cm⁻² for Ta-coated SS316L, a decrease of about 5 times. Moreover, corrosion current densities of Ta-coated SS316L in both simulative anode (purged with H₂) and cathode (purged with air) conditions are smaller than those of uncoated SS316L.     

Electrochemical behavior of surface treated metal bipolar plates used in passive direct methanol fuel cell

Corrosion resistance performance of SS316L treated by passivation solution was investigated in a simulated environment of the passive direct methanol fuel cell (DMFC). Electrochemical impedance spectroscopic (EIS) test showed that polarization resistance of untreated and treated SS316L were 1191 Ω cm² and 9335 Ω cm², respectively. The above result agreed with the Tafel slope analysis of potentiodynamic polarization curves. Comparing the untreated and treated SS316L in the simulated environment of DMFC anode working conditions, it was observed that the corrosion current density of treated SS316L as estimated by 4000 s potentiostatic test reduced from 38.7 μA cm⁻² to 0.297 μA cm⁻², meanwhile, the current densities of untreated and treated SS316L in cathode working conditions were 3.87 μA cm⁻² and 0.223 μA cm⁻², respectively. It indicated that the treated SS316L should be suitable in both anode and cathode environment of passive DMFCs. The treated SS316L bipolar plates have been assembled in a passive single fuel cell. A peak power density of 1.18 mW cm⁻² was achieved with 1 M methanol at ambient temperature.     

Effect of manufacturing conditions on the corrosion resistance behavior of metallic bipolar plates in proton exchange membrane fuel cells

Metallic bipolar plates are one of the promising alternatives to the graphite bipolar plates in proton exchange membrane fuel cell (PEMFC) systems. In this study, stainless steel (SS304, SS316L, and SS430), nickel (Ni 270), and titanium (Grade 2 Ti) plates with an initial thickness of 51 μm were experimented as bipolar plate substrate materials in corrosion resistance tests. In addition to unformed blanks, SS316L plates were formed with stamping and hydroforming processes to obtain bipolar plates under different process conditions (stamping force, hydroforming pressure, stamping speed, hydroforming pressure rate). These bipolar plates, then, were subjected to corrosion tests, and the results were presented and discussed in detail. Potentiodynamic polarizations were performed to observe corrosion resistance of metallic bipolar plates by simulating the anodic and cathodic environments in the PEMFC. In order to determine the statistical significance of the corrosion resistance differences between different manufacturing conditions, analysis of variance (ANOVA) technique was used on the corrosion current density (I_corr, μA cm⁻²) values obtained from experiments. ANOVA for the unformed substrate materials indicated that SS430 and Ni have less corrosion resistance than the other substrate materials tested. There was a significant difference between blank (unformed) and stamped SS316L plates only in the anodic environment. Although there was no noteworthy difference between unformed and hydroformed specimens for SS316L material, neither of these materials meet the Department of Energy‘s (DOE) target corrosion rate of ≤1 μA cm⁻² by 2015 without coating. Finally, stamping parameters (i.e. speed and force levels) and hydroforming parameters (i.e. the pressure and pressure rate) significantly affected the corrosion behavior of bipolar plates.     

An investigation into the effects of a nano-thick gold interlayer on polypyrrole coatings on 316L stainless steel for the bipolar plates of PEM fuel cells

Polypyrrole is one of the most important conductive polymers because it is easily oxidized, water soluble and commercially available. Also, polypyrrole coatings have potential applications in batteries, fuel cells, electrochemical sensors, anti-corrosion coatings and drug delivery systems. In this study, a very thin gold layer was first coated on SS316L, and then a polypyrrole coating was laid on top. The nucleation and growth mechanisms of polypyrrole on the gold-coated SS316L were studied by electrochemical nucleation and growth techniques. SEM was used to characterize the polypyrrole coating morphology. Potentiodynamic tests were performed to determine the corrosion parameters of the polypyrrole coatings. Potentiostatic tests of the coated SS316L were conducted in simulated anode and cathode environments of a PEM fuel cell. The simulated anode environment was at a potential of about −0.1 V versus SCE purged with H₂ and the simulated cathode environment was at a potential of about 0.6 V versus SCE purged with O₂. After coating with Au and polypyrrole, the polarization resistance of SS316L is increased about six times, and the corrosion current density is decreased about seven times, compared to the base SS316L. Also, our calculations show that the metal ion concentration in solution for the polypyrrole/Au/SS316L had met the target of 10 ppm after 5000 h fuel cell operation.     

Surface modification and performance of inexpensive Fe-based bipolar plates for proton exchange membrane fuel cells

A reforming pack chromization with rolling pretreatment process is utilized to develop inexpensive and high-performance Fe-based metal bipolar plates (SS 420, SS 430, and SS 316 stainless steels) for PEMFC systems. Rolling process is previously performed to reduce the chromizing temperature and generate a coating possessing excellent conductivity and corrosion resistance on the steels during chromization. The power efficiencies of rolled-chromized and simple chromized bipolar plates are compared with graphite bipolar plates employed in PEMFCs. The results show that the rolled-chromized bipolar plates have a corrosion current (I_corr) of 7.87 × 10⁻⁸ A cm⁻² and an interfacial contact resistance of 9.7 mΩ cm². Moreover, the power density of the single cell assembled with rolled-chromized bipolar plates is 0.46 W cm⁻², which is very close to that of graphite (0.50 W cm⁻²), in the tested conditions of this study.     

Coated 316L stainless steel with CrxN film as bipolar plate for PEMFC prepared by pulsed bias arc ion plating

Three different kinds of Cr_xN films on 316L stainless steels were prepared by pulsed bias arc ion plating as bipolar plates for proton exchange membrane fuel cell (PEMFC). The interfacial contact resistance, corrosion resistance and surface energy of the bipolar plate samples were investigated. Among the three samples, the 316L stainless steel coated with Cr_0.49N_0.51 → Cr_0.43N_0.57 gradient film (sample 2) exhibited the best-integrated performance. The contact resistance between sample 2 and Toray carbon paper was 6.9–10.0 mΩ cm² under 0.8–1.2 MPa. The bipolar plate sample also showed improved corrosion resistance in simulated PEMFC environments. Either in the reduction environment or in the oxidation environment 25 °C and 70 °C, the corrosion current densities of sample 2 were about one to two orders of magnitude lower than those of the base metal. In addition, the open circuit corrosion potential of sample 2 was also the highest in 0.5 M H₂SO₄ + 5 ppm F⁻ solution at 25 °C. The treated bipolar plate had high surface energy; and the contact angle of sample 2 with water was about 90°, which is beneficial for water management in fuel cell.     

Performance of a proton exchange membrane fuel cell stack using conductive amorphous carbon-coated 304 stainless steel bipolar plates

In this study, 304 stainless steel (SS) bipolar plates are fabricated by flexible forming process and an amorphous carbon (a-C) film is coated by closed field unbalanced magnetron sputter ion plating (CFUBMSIP). The interfacial contact resistance (ICR), in-plane conductivity and surface energy of the a-C coated 304SS samples are investigated. The initial performance of the single cell with a-C coated bipolar plates is 923.9 mW cm⁻² at a cell voltage of 0.6 V, and the peak power density is 1150.6 mW cm⁻² at a current density of 2573.2 mA cm⁻². Performance comparison experiments between a-C coated and bare 304SS bipolar plates show that the single cell performance is greatly improved by the a-C coating. Lifetime test of the single cell over 200 h and contamination analysis of the tested membrane electrode assemble (MEA) indicate that the a-C coating has excellent chemical stability. A 100 W-class proton exchange membrane fuel cell (PEMFC) short stack with a-C coated bipolar plates is assembled and shows exciting initial performance. The stack also exhibits uniform voltage distribution, good short-term lifetime performance, and high volumetric power density and specific power. Therefore, a-C coated 304SS bipolar plates may be practically applied for commercialization of PEMFC technology.     

Improvement of corrosion resistance and electrical conductivity of 304 stainless steel using close field unbalanced magnetron sputtered carbon film

Carbon film has been deposited on 304 stainless steel (SS304) using close field unbalanced magnetron sputter ion plating (CFUBMSIP) to improve the corrosion resistance and electrical conductivity of SS304 acting as bipolar plates for proton exchange membrane fuel cells (PEMFCs). The corrosion resistance, interfacial contact resistance (ICR), surface morphology and contact angle with water of the bare and carbon-coated SS304 are investigated. The carbon-coated SS304 shows good corrosion resistance in the simulated cathode and anode PEMFC environment. The ICR between the carbon-coated SS304 and the carbon paper is 8.28-2.59 mΩ cm² under compaction forces between 75 and 360 N cm⁻². The contact angle of the carbon-coated SS304 with water is 88.6°, which is beneficial to water management in the fuel cell stack. These results indicate that the carbon-coated SS304 exhibits high corrosion resistance, low ICR and hydrophobicity and is a promising candidate for bipolar plates.     

Conductive amorphous carbon-coated 316L stainless steel as bipolar plates in polymer electrolyte membrane fuel cells

Amorphous carbon (a-C) film about 3 μm in thickness is coated on 316L stainless steel by close field unbalanced magnetron sputter ion plating (CFUBMSIP). The AFM and Raman results reveal that the a-C coating is dense and compact with a small size of graphitic crystallite and large number of disordered band. Interfacial contact resistance (ICR) results show that the surface conductivity of the bare SS316L is significantly increased by the a-C coating, with values of 8.3–5.2 mΩ cm² under 120–210 N/cm². The corrosion potential (E_corr) shifts from about −0.3 V vs SCE to about 0.2 V vs SCE in both the simulated anode and cathode environments. The passivation current density is reduced from 11.26 to 3.56 μA/cm² with the aid of the a-C coating in the simulated cathode environment. The a-C coated SS316L is cathodically protected in the simulated anode environment thereby exhibiting a stable and lower current density compared to the uncoated one in the simulated anode environment as demonstrated by the potentiostatic results.     

Cr–N–C multilayer film on 316L stainless steel as bipolar plates for proton exchange membrane fuel cells using closed field unbalanced magnetron sputter ion plating

To combine the advantages of chromium nitride (CrN) and amorphous carbon (a-C) film, this study proposes a novel Cr–N–C multilayer film on 316L stainless steel (SS316L) as bipolar plates for proton exchange membrane fuel cells (PEMFCs) using closed field unbalanced magnetron sputter ion plating (CFUBMSIP) method. The characterizations of Cr–N–C film are analyzed by X-ray photoelectron spectroscopy (XPS), X-ray diffractometry (XRD), and scanning electron microscopy (SEM). Scratch tests indicate that the adhesion strength between the film and SS316L substrate has been greatly improved which is beneficial to prevent the multilayer film from spalling. Interfacial contact resistance (ICR) between coated SS316L sheets and simulated gas diffusion layer (GDL) decreases to 2.64 mΩ cm² at 1.4 MPa. Potentiodynamic results reveal that the anodic corrosion potential of coated samples is more positive than the operation potential and the cathodic passivation current density is only 0.61 μA cm⁻² at 0.6 V. Potentiostatic test, contamination analysis and surface morphology results reveal that the substrate is well protected by the Cr–N–C film. This research demonstrates that the novel Cr–N–C film exhibits excellent ex-situ performance including strong adhesion strength, high corrosion resistance and low ICR.     

Effect of fluoride ions on corrosion behavior of SS316L in simulated proton exchange membrane fuel cell (PEMFC) cathode environments

In order to determine the suitability of SS316L as a bipolar plate material in proton exchange membrane fuel cells (PEMFCs), its corrosion behavior is studied under different simulated PEMFC cathode corrosion conditions. Solutions of 1 × 10⁻⁵ M H₂SO₄ with a wide range of different F⁻ concentrations at 70 °C bubbled with air are used to simulate the PEMFC cathode environment. Electrochemical methods, both potentiodynamic and potentiostatic, are employed to study the corrosion behavior. Scanning electron microscopy (SEM) is used to examine the surface morphology of the specimen after it is potentiostatic polarized under simulated PEMFC cathode environments. Auger electron spectroscopy (AES) analysis is used to identify the composition and the depth profile of the passive film formed on the SS316L surface after it is polarized in simulated PEMFC cathode environments. Photo-electrochemical (PEC) method and capacitance measurements are used to characterize the semiconductor passive films. The results of both the potentiodynamic and potentiostatic analyses show that corrosion currents increase with F⁻ concentrations. SEM examination results indicate that pitting occurs under all the conditions studied and pitting is more severe with higher F⁻ concentrations. From the results of AES analysis, PEC analysis and the capacitance measurements, it is determined that the passive film formed on SS316L is a bi-layer semiconductor, similar to a p-n heterojunction consisting of an external n-type iron oxide rich semiconductor layer (electrolyte side) and an internal p-type iron-chromium oxide semiconductor layer (metal side). Further analyses of the experimental results reveal the electronic structure of the passive film and shed light on the corrosion mechanisms of SS316L in the PEMFC cathode environment.     

Corrosion characteristics and fuel cell performance of a cost-effective high Mn–Low Ni austenitic stainless steel as an alternative to SS 316L bipolar plate

In this study, newly developed high manganese (Mn) and low nickel (Ni) austenitic stainless steels were investigated as an alternative to conventionally used SS 316L for bipolar plate applications in proton exchange membrane fuel cells. Systematic studies on the corrosion behavior were carried out in simulated hydrogen and oxygen environments, for both half- and fuel-cell conditions. The Mn-based SS revealed nobler corrosion potential and comparable passive current densities to that of SS 316L. The passive current density of Mn-based SS is well within the DoE 2020 target of <1 μA cm⁻². Though MnSS1 steel has lean Ni content, the addition of Mn and N is beneficial for improving the corrosion performance, which is comparable to SS 316L. The recorded ICR values for Mn SS1 and SS 316L are 234.6 ± 20 and 155 ± 20 mΩ cm² at a compaction force of 140 N cm⁻², respectively. Both the steels do not to meet the DoE ICR target of 10 mΩ cm², which requires conductive coating or improvement in oxide conductivity. The performances of the steels (both Mn-SS and 316L SS) with varying thickness were also investigated in a single fuel cell condition with serpentine flow field design as bipolar plates with varying thickness (10, 5 and 2 mm). A maximum power density of 370 mW cm⁻² was achieved with the Mn-based metallic bipolar plates, whereas SS 316L showed 354 mW cm⁻². By changing the composition of austenitic stainless steel, that is, using Mn SS1 instead of SS 316L the overall fuel cell cost decreases by three times.     

Thin chromium nitride PVD coatings on stainless steel for conductive component as bipolar plates of PEM fuel cells: Ex-situ and in-situ performances evaluation

In this paper, two types of chromium PVD coatings (100 nm) have been elaborated on 316L stainless steel (SS) by adjusting the nitrogen flow rate. The first coating is a mixture of Cr₂N and Cr, the second one is a single phase CrN. It is shown that the performances of the material are strongly dependant of the nature of the passive film formed on the chromium nitride layers due to the galvanic coupling between the coating and the substrate. The CrN coated SS shows very good corrosion resistance in simulated PEMFC media. The surface conductivity of the SS is also greatly improved and the CrN coated SS shows an interfacial contact resistance of 10 mΩ cm² at 140 N cm⁻². Five single cells of stainless steel bipolar plates coated with the CrN film were assembled for performance test. This 5 cell stack does not show any mean voltage degradation over 200 h dynamic cycling. Moreover, the performances of the CrN coated SS bipolar plates are very close to the Au-coated SS bipolar plates.     

An investigation into nickel implanted 316L stainless steel as a bipolar plate for PEM fuel cell

A nickel-rich layer about 100 μm in thickness with improved conductivity was formed on the surface of austenitic stainless steel 316L (SS316L) by ion implantation. The effect of ion implantation on the corrosion behavior of SS316L was investigated in 0.5 M H₂SO₄ with 2 ppm HF solution at 80 °C by potentiodynamic test. In order to investigate the chemical stability of the ion implanted SS316L, the potentiostatic test was conducted in an accelerated cathode environment and the solutions after the potentiostatic test were analyzed by inductively coupled plasma atomic emission spectrometer (ICP-AES). The results of potentiodynamic test show that the corrosion potential of SS316L is shifted toward the positive direction from −0.3 V versus SCE to −0.05 V versus SCE in anode environment and the passivation current density at 0.6 V is reduced from 11.26 to 7.00 μA cm⁻² in the cathode environment with an ion implantation dose of 3 × 10¹⁷ ions cm⁻². The potentiostatic test results indicate that the nickel implanted SS316L has higher chemical stability in the accelerated cathode environment than the bare SS316L, due to the increased amount of metallic Ni in the passive layer. The ICP results are in agreement with the electrochemical test results that the bare SS316L has the highest dissolution rate in both cathode and anode environments and the Ni implantation markedly reduces the dissolution rate. A significant improvement of interfacial contact resistance (ICR) is achieved for the SS316L implanted with nickel as compared to the bare SS316L, which is attributed to the reduction in passive layer thickness caused by the nickel implantation. The ICR values for implanted specimens increase with increasing dose.     

Corrosion properties and contact resistance of TiN, TiAlN and CrN coatings in simulated proton exchange membrane fuel cell environments

In this study, the contact resistance (CR) and electrochemical properties of TiN, CrN and TiAlN electron beam physical vapor deposition (EBPVD) coatings and their stainless steel 316L (SS316L) substrate were investigated in a simulated proton exchange membrane (PEM) fuel cell environment. The potentiodynamic polarization corrosion tests were conducted at 70 °C in 1 M H₂SO₄ purged with either O₂ or H₂, and the potentiostatic corrosion tests were performed under both simulated cathodic (+0.6 V vs. Ag/AgCl reference electrode purged with O₂) and anodic conditions (−0.1 V vs. Ag/AgCl reference electrode purged with H₂) for a long period (4 h). SEM was used to observe the surface morphologies of the samples after corrosion testing. All the TiN-, TiAlN- and CrN-coated SS316L showed a lower CR than the uncoated SS316L. While the corrosion performance of the coatings was dependent on the cathodic and anodic conditions, the CrN coating exhibited a higher (in the anodic environment) or similar (in the cathodic environment) corrosion resistance to the uncoated SS316L. Thus, the CrN-coated SS316L could potentially be used as a bipolar plate material in the PEM fuel cell environment. Although the EBPVD process greatly reduced number of pinholes in the coatings compared to other plasma enhanced reactive evaporations, future research efforts should be directed to eliminate the pinholes in the coatings for long-term durability in fuel cell applications.     

Chromium-containing carbon film on stainless steel as bipolar plates for proton exchange membrane fuel cells

A series of chromium-containing carbon films are deposited on 316L stainless steel (SS316L) as bipolar plates for proton exchange membrane fuel cells (PEMFCs) by pulsed bias arc ion plating (PBAIP). The film characterizations are evaluated by X-ray photoelectron spectroscopy (XPS) and X-ray diffractometry (XRD). Interfacial contact resistance (ICR) between the coated SS316L samples and carbon paper is measured. Potentiodynamic and potentiostatic tests in the simulated corrosive circumstance of PEMFC are conducted to evaluate the corrosion resistance of the coated SS316L samples. The results indicate the films are primarily composed of pure carbon atoms with amorphous structure, including sp³ and sp² carbon atoms. The contents of sp³ and sp² carbon atom are remarkably influenced by the doping chromium. ICR and corrosion resistance of the coated SS316L sample are greatly improved owing to the surface film. The lowest ICR between the coated SS316L sample and carbon paper is only 2.8 mΩ cm² at the compaction force of 120 N cm⁻². The ICR has a close relationship with the contents of sp³ and sp² carbon atom, and the lowest ICR is obtained for the Cr_0.23C_0.77 film with the lowest sp³ carbon atom content and highest sp² carbon atom content. The SS316L sample with Cr_0.23C_0.77 film also exhibits the best corrosion resistance. Finally, the variations of ICR and surface morphology of the coated sample before and after corrosion testing are discussed.