为了获得轻质、高强和高阻尼的多孔NiTi合金,采用微波烧结协同镁造孔技术制备多孔NiTi合金.考察多孔NiTi合金的显微组织、力学性能、相变行为、超弹性和阻尼性能.结果表明:当烧结温度低于或等于900℃时,多孔NiTi合金主要由B2 NiTi相和少量B19'NiTi相组成.随着烧结温度的升高,多孔NiTi合金的孔隙率逐...     

多孔NiTi形状记忆合金的制备工艺

以NH_4HCO_3为造孔剂,利用元素粉末混合烧结法制备了多孔NiTi形状记忆合金。研究了压制压力、烧结温度和烧结时间对多孔NiTi合金孔结构的影响,并分析了其物相组成。结果表明:随压制压力的增加,平均孔径和孔隙率逐渐减小;随烧结温度提高,多孔NiTi合金的平均孔径减小、孔隙率先增加后减少,孔隙分布趋于均匀;随烧结时间延长,多孔NiTi合金的平均孔径及孔隙率先增加后减少。在造孔剂添加量50%,压制压力250 MPa,烧结温度1000℃,烧结时间6 h条件下可制备出孔结构均匀(平均孔径为314μm,孔隙率56.3%)的多孔NiTi合金,其基体相为B2(NiTi)相。     

凝胶注模制备多孔Ni-Ti合金的研究

多孔Ni-Ti合金由于其优异的形状记忆性能而广泛应用于医用植入材料领域。本文以TiH2粉及雾化Ni粉为原料,采用凝胶注模成型技术,制备出Ni-Ti凝胶生坯,通过后续真空干燥、脱脂以及烧结工艺成功制备出性能优异的医用植入多孔Ni-Ti合金。运用XRD、SEM对多孔Ni-Ti合金进行了成分及微观结构表征,分析了不同烧结温度对于多孔Ni-Ti合金孔隙率、机械性能、组织成分及微观形貌的影响。结果表明,随着烧结温度的增加,孔隙率降低,抗压强度和杨氏模量增加。对固相体积分数为45vol. %的生坯在1050 ℃条件下高真空烧结保温2h,制备出孔隙率为42.65%,抗压强度为202.65 MPa,杨氏模量为17.14 GPa,主相为NiTi相的多孔Ni-Ti合金,基本满足人体骨性能需要。     

Microstructure and Mechanical Properties of NiTi Shape Memory Alloys by In Situ Laser Directed Energy DepositionEI北大核心CSCD

以Ni粉与Ti粉为原料,采用激光定向能量沉积(LDED)技术制备NiTi形状记忆合金。利用XRD、物相拟合、SEM、EDS和DSC等测试方法,对NiTi合金的显微组织、物相含量和物相转变进行分析,随后采用压缩圆柱样品进行形状记忆效应测试,并评估其形状记忆效应。激光能量密度较低时,NiTi合金中产生大量Ni_(4)Ti_(3)相沉淀,随着激光能量密度增加,Ni_(4)Ti_(3)相消失。激光能量密度为20.0 J/mm^(2)时,NiTi合金具有2878 MPa的压缩断裂强度与34.9%的压缩失效应变,且样品在循环20 cyc后具有88.2%形状记忆恢复率。     

颗粒尺寸对微波烧结多孔NiTi合金的显微结构及力学性能的影响

以不同颗粒尺寸的Ni/Ti粉末为原料,采用微波烧结技术制备了多孔NiTi合金,并系统考察了颗粒尺寸对多孔NiTi合金的显微结构和力学性能的影响。结果表明,随着颗粒尺寸的减小,多孔NiTi合金中的Ti2Ni和Ni3Ti第二相减少而单质Ni相消失。同时,多孔NiTi合金的孔隙形貌由带尖角的不规则形状向近球形转变。此外,多孔NiTi合金的孔隙率和孔径随着颗粒尺寸的增大而增大,而洛氏硬度、抗压强度和抗弯强度均下降。因此,减小颗粒尺寸有利于获得理想的显微结构(纯净的物相和均匀的孔隙结构)和提高微波烧结多孔NiTi合金的力学性能。     

颗粒尺寸对微波烧结多孔NiTi合金的显微结构及力学性能的影响（英文）

以不同颗粒尺寸的Ni/Ti粉末为原料,采用微波烧结技术制备了多孔NiTi合金,并系统考察了颗粒尺寸对多孔NiTi合金的显微结构和力学性能的影响。结果表明,随着颗粒尺寸的减小,多孔NiTi合金中的Ti_2Ni和Ni_3Ti第二相减少而单质Ni相消失。同时,多孔NiTi合金的孔隙形貌由带尖角的不规则形状向近球形转变。此外,多孔NiTi合金的孔隙率和孔径随着颗粒尺寸的增大而增大,而洛氏硬度、抗压强度和抗弯强度均下降。因此,减小颗粒尺寸有利于获得理想的显微结构(纯净的物相和均匀的孔隙结构)和提高微波烧结多孔NiTi合金的力学性能。     

孔隙对NiTi形状记忆合金中B2-R相变影响的相场模拟

建立了适用于含孔隙NiTi合金中B2-R相变的相场模型,并用该相场模型研究了多孔NiTi合金中B2-R转变的微观组织演化过程以及孔隙率和孔尺寸对R相变体生长动力学行为的影响.多孔NiTi合金中R相变体以相互协调的方式形成"带状"的三维结构和"鱼骨"状的二维组织,变体之间形成的孪晶面包括{101}B2和{001}B2 2...     

超音速火焰喷涂NiTi合金涂层的形状记忆效应

采用超音速火焰喷涂制备超致密NiTi合金涂层,通过后续热处理获得优化相变结构,并通过压痕法分析涂层的形状记忆效应。光学显微镜及扫描电镜对NiTi合金涂层微观结构表征显示,喷涂制备态涂层由内部岛状-链状界面叠片组成,涂层致密孔隙率约为0.82%。X射线衍射分析显示,NiTi涂层制备态为全奥氏体,经时效处理析出Ni₄Ti₃相。压痕法分析表明,在制备态及时效态涂层中均获得了一定的单程及双程形状记忆效应。X射线物相分析及差示扫描量热仪对比分析揭示,时效析出的第二相粒子显著增加形状记忆效应。     

医用多孔NiTi形状记忆合金的研究进展

综述多孔NiTi形状记忆舍金的制备工艺、生物力学性能及生物相容性等方面的研究进展。国内外的研究表明，多孔NiTi合金具有优良的生物相容性和高的力学性能，其独特的孔隙结构可保证组织的长入和体液的传输，使植入物与人体骨组织的结合更加牢固可靠，多孔NiTi形状记忆舍金是一种具有良好应用前号的生物医用材料。     

SPS烧结温度对NiTi/表面多孔Ti梯度合金组织和性能的影响

利用放电等离子烧结技术制备NiTi/表面多孔Ti梯度合金,研究不同烧结温度对梯度合金微观组织、表面孔隙特征、力学性能及体外生物活性的影响及机理。结果表明:随着烧结温度的升高,梯度合金组织由NiTi、α-Ti、Ni、Ti_2Ni、Ni_3Ti混合相逐渐转变为单一NiTi和α-Ti相,内外层界面形成良好冶金结合,表面孔隙率和平均孔径呈缓慢减小趋势;同时抗压强度值快速增大而弹性模量值变化不大;1000℃制备的梯度合金不仅具有良好的表面孔隙特征(孔隙率35.8%、平均孔径423μm)、较高的抗压强度(632 MPa)、较低的弹性模量(9 GPa)及优异的超弹性行为(超弹性恢复应变4%),而且体外生物活性显著提高。     

热爆反应合成多孔NiTi形状记忆合金的性能

利用热爆方法来制备了多孔NiTi形状记忆合金.研究了在不同热爆温度下制备出的样品与其机械性能之间的关系.结果表明:在1 223 K下热爆反应制备的NiTi合金,具有大的孔隙度,高开孔率和基本各向同性,同时表现出较好的超弹性.对断口分析发现,断裂为脆性断裂和韧性断裂的复合.这表明改善孔洞分布和形态,可以极大地提高多孔NiTi形状记忆合金的机械性能和超弹性.     

LOW DENSITY AND HIGH STRENGTH NiTi MEMORY ALLOYS WITH CONTROLLABLE PORE CHARATERISTICS AND THEIR SUPERELASTICITY

采用球形尿素颗粒预造孔工艺结合梯级粉末烧结方法制备出孔形规则、孔径大的轻质高 强多孔NiTi形状记忆合金. 通过控制造孔剂(尿素)的含量可有效调节多孔合金的孔隙特征, 获得孔径均匀、孔形圆整和孔隙率可控的样品, 其中孔径为296-732 um, 孔隙率为31%-61.6%; 尿素形状和尺寸对多孔合金的孔隙特征有决定性影响, 具 有几何形态遗传性; 尿素对多孔NiTi合金的组成相影响很小, 相变仍具有马氏体相变特征; 合金具有优良的力学性能和稳定的线性超弹性.     

纳米SiC颗粒增强NiTi形状记忆复合材料制备及其力学性能和阻尼行为

采用粉末冶金梯级烧结法成功制备出轻质、高强且具有一定孔隙率的纳米SiC颗粒增强NiTi合金基形状记忆复合材料(SiC/NiTi).研究发现,所制备的SiC/NiTi复合材料具有稳定的线性超弹性;SiC颗粒的引入使SiC/NiTi复合材料具有较高的压缩强度和等效压缩强度,且强度随SiC含量的增加而提高.研究还表明,SiC...     

Porous NiTi fabricated by self-propagating high-temperature synthesis of elemental powders

Porous NiTi shape memory alloy has been an active area of research for medical application due to their similar microstructure to human bone. In this study, porous product was obtained by self-propagating high-temperature synthesis (SHS) of compacts prepared from elemental nickel and titanium powders and the effects of the green porosity and preheating temperature were examined. The porosity in the synthesised products was in the range of 45–59 vol.%, with the green porosity being the primary source of final porosity. NiTi was present as the dominant phase in the porous product with other secondary intermetallic compounds and element powders. The effect of green porosity and preheating temperature was found to have an effect on the pore morphology and microstructure.     

Pore formation mechanism and characterization of porous NiTi shape memory alloys synthesized by capsule-free hot isostatic pressing

Porous NiTi alloys with different porosities were fabricated by capsule-free hot isostatic pressing (CF-HIP) with ammonium acid carbonate (NH₄HCO₃) as a space-holder. The microstructure and porosity of porous NiTi produced with different NH₄HCO₃ contents and sintering temperatures were determined. Two different creep expansion models are used to explain the pore expansion mechanism during the sintering process, which involves slow and continuous reduction of the argon pressure at high temperatures. When the NH₄HCO₃ content is 30 wt.% and the sintering temperature is 1050 °C, an ideal porous NiTi alloy with 48 vol.% porosity and circular pores (50–800 μm) is obtained. Compression tests indicate that the porous NiTi alloys with 21–48% porosity possess not only lower Young’s moduli of 6–11 GPa (close to that of human bones) but also higher compression strength and excellent superelasticity. Cell cultures reveal that the porous NiTi prepared here has no apparent cytotoxicity. The porous materials are thus promising biomaterials in hard tissue replacements.     

Properties of Al/TiNi composite using porous TiNi fabricated by a self-propagating high temperature synthesis method

In the present study, equi-atomic porous TiNi shape-memory alloys have been successfully prepared by self-propagating high-temperature synthesis (SHS) using elemental titanium and nickel powders. The porous TiNi alloys thus obtained have an open porous structure with about 64 vol.% porosity, and the pore size is about 1.8 mm. The effect of preheating temperature on the microstructure has been investigated. It was found that the pore size increased with increasing preheating temperature. Moreover, the preheating temperature was shown to have a significant effect on the microstructure of the SHS-synthesized porous TiNi shape memory alloys. Aluminum was infiltrated into porous TiNi shape-memory alloys and the damping property of Al/TiNi was measured by a vibration analyzer (FFT analyzer). The specific damping capacity of Al/TiNi composites is 70% that of a pure TiNi ingot.     

SHS法制备高孔隙度TiNi合金