涤塔夫织物拒水整理及防紫外线性能研究

为了获得具有优异拒水性能和防紫外线性能的涤塔夫织物,文中首先采用无氟拒水剂CWR-8DC对涤塔夫织物进行拒水整理,探讨拒水剂CWR-8DC质量浓度、焙烘时间、烘焙温度、洗涤次数等因素对织物拒水性能的影响。为进一步提高拒水剂CWR-8DC在涤塔夫织物上的耐洗牢度,探究了黏合剂的种类及浓度对涤塔夫织物功能整理效果的影响,并对整理后织物进行银胶涂层,测试其防紫外线性能。结果表明：拒水剂CWR-8DC质量浓度为60 g/L,黏合剂FK-C与拒水剂CWR-8DC以1∶20的体积比复配,整理后织物80℃预烘180 s,160℃焙烘90 s,经银胶涂层整理后的织物具有优异的拒水性能及防紫外线性能,其接触角可达133.1°,并且经15次洗涤后拒水等级仍能达到4级,紫外防护系数UPF值可达227.63。     

无氟拒水整理织物的静态和动态拒水性能

采用有机-无机纳米无氟防水整理剂CWR-8DY对工装纯棉、涤棉面料进行拒水整理,研究无氟拒水整理工艺对棉、涤棉织物拒水效果的影响,以及拒水面料的静态、动态防水性能;通过扫描电镜观察织物纤维微观表面形貌与宏观接触角,发现当CWR-8DY质量浓度为100 g/L时,织物接触角接近150°,接近超疏水态。     

涤/棉织物拒水拒油整理及性能

采用浸轧焙烘工艺对涤/棉织物进行拒水拒油整理。通过测试分析整理后织物的水接触角、油接触角、静水压值及拒水拒油等级,研究拒水拒油剂质量浓度、架桥剂质量浓度、焙烘温度及焙烘时间因素对织物拒水拒油性能的影响。由单因素试验,获得采用防水剂3679A对涤/棉织物进行拒水拒油整理的优化工艺如下:防水剂3679A质量浓度30 g/L,架桥剂3523质量浓度4. 5 g/L,100℃下预烘120 s,165℃下焙烘90 s。     

绿色拒水拒油餐桌布的制备

为实现餐桌布绿色拒水拒油效果,选用棉织物、棉/亚麻混纺织物和亚麻织物,采用浸轧加烘燥工艺对3种织物进行拒水拒油功能整理。通过测试及分析整理后织物的拒水拒油等级,研究环保型含氟整理剂对织物拒水拒油功能的影响,并对整理后织物接触角、透气性、悬垂性和耐水洗性能进行表征分析。棉织物与棉/麻织物在含氟整理剂648-2质量浓度为25 g/L时织物拒水拒油效果最佳;亚麻织物在含氟整理剂648-2质量浓度24 g/L时织物拒水拒油效果最佳;通过对比分析发现,亚麻织物最适合作为绿色拒水拒油餐桌布,整理剂质量浓度为24 g/L时亚麻织物的拒水等级为5级、拒油等级为8级,织物接触角为140.3°。     

涤棉混纺织物纳米无氟拒水整理

采用纳米无氟拒水剂NT-X018对涤棉混纺织物进行整理,以提高其拒水性能。探讨整理液配方、工艺过程对整理后织物拒水性能、断裂强力、透气性、耐久性及手感的影响。结果表明:整理液配方为,拒水剂NT-X018 80g/L、加强剂NT-X628 30g/L、交联剂NT-504M5g/L、催化剂NT-S228 5g/L、渗透剂OS-603 1.0g/L,浴比1∶30,pH4.0左右;采用二浸二轧,预烘条件130℃×2min,焙烘条件160℃×1min,可以达到最佳的拒水整理效果,同时,整理后织物手感基本没有影响,经多次洗涤,拒水等级仍较高,说明该拒水剂的耐久性良好。     

环保型拒水尼龙户外面料的开发

尼龙面料强力高、耐磨性好，被广泛用于箱包、帐篷等户外领域，为满足锦纶织物用于户外运动产品的特殊要求，户外面料须经过拒水整理。随着常规含氟拒水剂环保问题的日益突出，开发环保无氟拒水的尼龙户外面料迫在眉睫。对比了不同无氟拒水剂对尼龙的拒水整理效果，筛选出适合尼龙拒水整理的环保型无氟拒水剂，确定适宜的整理工艺；对拒水整理后的尼龙织物进行PU涂层，研究无氟拒水剂对织物涂层的影响；对涂层后的尼龙户外织物的耐水洗性能进行测试，结果表明：环保型拒水尼龙户外面料可以采用超支化大分子无氟拒水剂整理，当拒水剂质量浓度为60 g/L,160℃处理70 s时，尼龙织物的拒水等级可以达到90分；尼龙牛津布经超支化大分子无氟拒水剂整理对后续织物涂层无影响；经过5次水洗后布面的拒水效果仍然有80分，具有比较优异的耐水洗性。     

精纺毛织物的无氟拒水整理

针对含氟拒水剂不环保的缺点,采用无氟拒水整理剂WS CONC.赋予毛织物拒水性能。讨论了拒水整理剂WS CONC.质量浓度、催化剂BC质量浓度、焙烘温度和焙烘时间对毛织物拒水性能的影响。利用水滴接触角方法观察了毛织物的拒水性能。结果表明,在带液率为70%的情况下,较佳的整理工艺为:无氟拒水整理剂WS CONC.质量浓度60 g/L,催化剂BC质量浓度60 g/L,在170℃焙烘70 s。整理后,毛织物的初始拒水等级可达100分,5次干洗后仍可达75分,毛织物的手感不够柔软,颜色轻微泛黄,强力增加。     

基于有机氟整理剂的纯棉针织物拒水拒油整理

采用HS1800有机氟拒水拒油整理剂对纯棉针织物进行拒水拒油整理。设计正交试验探究浸渍时间、焙烘时间、焙烘温度、轧余率、整理剂质量浓度5个因素对整理效果的影响。通过单因素分析,探究拒水整理的最佳工艺,并测试其整理前后的耐水洗性能和服用性能。试验结果表明:浸渍时间对织物整理效果的影响最大,其次是整理剂质量浓度和焙烘温度,轧余率和焙烘时间对纯棉针织物的拒水效果影响较小。最佳整理工艺为:整理剂质量浓度13 g/L,浸渍时间13 min,轧余率70%,100℃条件下预烘3 min,150℃条件下焙烘1 min。拒水拒油整理后棉针织物的服用性能下降幅度不大,水接触角为142.03°,油接触角为137.48°。经35次水洗后,水接触角为132.83°,油接触角为127.94°,可满足穿着需要。     

粘棉混纺织物的拒水整理的应用研究

本文探讨了粘棉混纺织物上拒水整理的应用性能,对助剂用量,焙烘温度,焙烘时间等因素进行了分析。如果工艺条件控制适当,对粘棉织物的白度及强力影响较小,并可得到较好的拒水整理效果。     

腈氯纶/棉混纺织物的超级拒水拒油整理

采用Oleophobol有机氟拒水拒油整理剂对腈氯纶/棉混纺织物进行整理,优化后的工艺条件为:Oleophobol整理剂60 g/L,交联剂20 g/L,渗透剂JFC 1 g/L,100℃预烘3 min,150℃焙烘3 min,整理后织物获得良好的拒水拒油性能,接触角为137.4°,拒油等级可达8级,且自身的阻燃性能和强力变化较小。     

液氨处理对锦纶/棉混纺织物性能的影响

锦纶/棉混纺织物存在易折皱外观不平整的问题,制约了其在高档服装上的应用。为此,以锦纶/棉混纺织物为研究对象,在坯布预处理后染整前对其进行液氨处理,研究了液氨处理对织物拉伸强力、撕破强力、折皱回复角及表面性能的影响。通过平滑感、温暖感及柔软感3个定量指标,评价液氨处理前后锦/棉混纺织物的风格、手感变化情况。结果表明:液氨整理可以提升锦/棉织物的拉伸强力及撕破强力,处理后织物的折皱回复角从218°提升至252.3°,粗糙度波长与振幅之比从50.46降低至44.87,表明液氨处理后织物的抗皱性和平滑感均得到了明显改善;尽管液氨处理未明显改善织物的柔软感,但处理织物的热导率较未处理织物仍有一定程度降低,致使织物接触温暖感有所提升。     

Development of water-, oil-repellent and flame-retardant cotton fabrics by organic-inorganic hybrid materials

In this study, water-repellent, oil-repellent and flame-retardant cotton fabrics were developed by solgel technique. With this aim, nanosols were prepared using tetraethylorthosilicate and hexadecyltrimethoxysilane as precursors, guanidine dihydrogen phosphate as flame-retardant agent and Guard AFB as conventional water–oil-repellent agent, solvents and chelating agents. Then, to AC105, VA7110, PU1110 and FC9005 as polymeric additives, with/without FX8000 or urea and formaldehyde as cross-linking agents, were added some nanosols to improve washing fastness of the fabric samples. Cotton fabrics were treated with nanosols without polymeric additives by pad–dry–cure process, while they were coated with nanosols containing polymeric additives by knife-over-roll coating. Water–oil-repellent properties, flame-retardant properties, washing fastness, contact angle, whiteness, tear strength and add-on values of the coated fabric samples were determined. It was found that the cotton fabrics with good water–oil-repellence and flame-retardant properties with relatively durable properties could be produced using nanosols containing guanidine dihydrogen phosphate and urea, together with tetraethylorthosilicate and hexadecyltrimethoxysilane as precursors, and lower concentrations of Guard AFB as commercial water–oil-repellent agent. However, the fabric samples were still not sufficiently durable when washed. It was deduced that the durability of cotton fabric during washing is developed by means of treatment with nanosols containing polyvinyl acetate-based polymer.     

多胺型固色剂FT-2的应用

用自制的多胺型固色剂FT-2对直接染料和活性染料染色后的纯棉织物进行固色处理,并对固色处理中的各项工艺条件进行探讨和优化.实验结果表明,该固色剂对直接染料染色纯棉织物的最佳固色工艺为:直接染料染色后棉织物→两浸两轧(固色剂80g/L,pH为9,轧余率80％)→预烘(70℃,3min)→焙烘(130℃,3min);对活性...     

聚酯/聚酰胺及其棉混纺织物的染色性能

通过测试聚酯/聚酰胺织物（以下简称改性聚酯）的沸水收缩率,改性聚酯/棉(65/35)混纺织物的最佳前处理条件,改性聚酯织物常压染色和改性聚酯/棉织物分散/活性染料一浴一步法染色的K/S、色牢度,对新型改性聚酯及其棉混纺织物的染色性能进行了研究。实验结果表明：染前热定型后,改性聚酯及其棉混纺织物的经向、纬向收缩率都低于5%;改性聚酯/棉织物的前处理优化工艺条件为：双氧水4g/L、精炼剂3g/L 、NaOH4g/L;改性聚酯织物可以常压染色;改性聚酯/棉分散/活性染料一浴一步碱性染色匀染性良好,染色样品的熨烫、日晒、干摩擦牢度都达到4级及以上。     

芳纶/阻燃粘胶/阻燃锦纶混纺织物制备及其性能

为获得长效阻燃、高强、耐磨且服用性能好的织物,将芳纶1414、阻燃粘胶与阻燃锦纶3种本质阻燃纤维混纺织造,探讨了混纺比、纱线捻度、织物组织结构和黏合剂种类对纱线及其织物力学性能、阻燃性能和色牢度的影响。结果表明：芳纶1414/阻燃粘胶/阻燃锦纶(30/45/25)混纺纱线同时具备优异的力学性能和阻燃性能,阻燃锦纶的加入使三元混纺纱线断裂强度相比芳纶/阻燃粘胶二元混纺纱线提升56%,耐磨次数提升58%,其纱线的力学性能随着捻度增加先增强后降低,峰值捻度为680捻/m;织物采用斜纹组织结构时,其阻燃性能和力学性能优于平纹和缎纹组织;采用非离子型丙烯酸酯共聚物G-BD作为印花浆料黏合剂,可使得到的高强耐磨阻燃织物水洗20次后变色牢度级数仍保持在2级以上。     

含氟硅油拒水整理剂在棉织物上应用性能研究

自制了单组分和双组分氟硅拒水整理剂并应用于棉织物整理.对比研究了该2种氟硅整理剂的整理功效,其中双组分氟硅整理剂整理效果更好.研究了双组分氟硅油焙烘温度、焙烘时间及整理剂用量对拒水整理功效的影响,并测试了拒水整理后棉织物的物理机械性能.确定了双组分氟硅油最佳整理工艺为:二浸二轧(轧余率75%左右),100℃预烘120 s,170℃焙烘120 s.由此得到的拒水整理织物综合性能优良.     

篷盖布的阻燃-拒水拒油同浴整理工艺

对纯棉篷盖布进行涂料染色、拒水拒油整理、阻燃整理等同浴复合整理加工,筛选了阻燃剂和拒水拒油整理剂,探讨了拒水拒油整理剂用量、阻燃剂用量、黏合剂用量、焙烘温度等对复合整理效果的影响。优化的复合整理工艺为:阻燃剂CFR 350 g/L,催化剂C52 40 g/L,尿素20 g/L,防水剂TG-435 60 g/L,增效剂BN-69 10 g/L,涂料50 g/L,黏合剂811-1 60 g/L,160℃焙烘2 m in。经复合多功能整理后,纯棉篷盖布的耐湿摩擦色牢度达到4级,阻燃可达B1级,拒水拒油达到4级以上。     

印整结合的天然纤维织物转移印花

针对分散染料转移印花对纤维的局限性，采用苯乙烯接技聚合的预处理方法，将预处理剂和分散染料同浆印制转移印花纸，达到既印花又整理的目的，实现天然纤维织物的转移印花。文章以涤棉混纺、丝涤交织和真丝织物为例，对印整结合转移印花后织物的物理性能和染色牢度进行比较。     

自着色水性聚氨酯制备及其在棉织物涂层中的应用

为解决低分子染料的耐热迁移性差和涂层色浆配制时外添加涂料、染料等着色剂的烦琐性,将1-氨基-4-羟基-2(6-羟基己氧基)蒽醌通过共价键引入水性聚氨酯骨架中合成端羟基自着色水性聚氨酯。借助红外光谱仪、紫外-可见光谱仪和热重分析仪研究了自着色水性聚氨酯的化学结构和热稳定性。考察了蒽醌发色体质量分数、固化剂质量分数和焙烘条件对涂层棉织物K/S值、色牢度和手感的影响。结果表明:随着自着色水性聚氨酯制备过程中蒽醌发色体质量分数增加,涂层棉织物K/S值增大;当固化剂质量分数为20%,于150 ℃焙烘5 min,涂层棉织物K/S值为5.20,干、湿摩擦色牢度为4~5级,褪色牢度为3~4级,沾色牢度为4~5级,手感为3级。