蚕丝/涤纶交织物染整工艺初探

本文从蚕丝、涤纶纤维特性及其差别入手,探讨丝涤织物的染整工艺条件,并相应筛选染料和随产品要求变换染色工艺。通过对比试验,对影响蚕丝/涤纶交织物风格的各道工序进行讨论,阐明丝涤交织物染整加工的技术路线和技术关键。     

蚕丝/夜光涤纶混纺纱的纺纱工艺与性能研究

蓄能型夜光涤纶纤维是一种功能性环保新材料,其在市场上的应用越来越广.为了进一步提升夜光涤纶纤维的性能,拓宽其市场应用性,文章对夜光涤纶短纤采用蚕丝短纤与其进行混纺.通过发挥蚕丝纤维的优点,提高了夜光涤纶的余辉强度和力学性能,并改善了夜光涤纶短纤纱的外观效果.将蚕丝按不同添加比例与夜光短纤进行混纺,经过清梳联、二道并条、...     

堆置处理对蚕丝/涤纶交织物染色性能的影响

文章针对活性染料/分散染料混合染液对蚕丝/涤纶交织物轧染过程中存在的染色深度的问题,采用堆置法调节染料在两种纤维间的分配率并改善其染色性能。研究了堆置时间对分散染料在蚕丝和涤纶纤维上分配率的影响,探讨了蚕丝/涤纶交织物的染色深度和堆置时间的关系,考察了染色前后织物的耐摩擦色牢度和耐皂洗色牢度。结果表明,通过密封堆置浸轧活性染料/分散染料混合染液的蚕丝/涤纶交织物,提高了分散染料在涤纶纤维上的分配率,促进了活性染料对蚕丝的吸附和渗透,显著提升了蚕丝/涤纶交织物的染色深度。同时,染色织物具有良好的色牢度。     

导电涤纶涂层织物的制备及其性能

为制备导电涂层织物,采用研磨分散法制备导电炭黑,研究了导电炭黑的用量、导电炭黑的粒径、涂层次数、黏合剂用量、焙烘时间以及温度对导电涤纶涂层织物性能的影响。对涤纶涂层织物的表面电阻、耐水洗牢度、耐摩擦牢度、断裂强力和断裂伸长率等性能进行测试。结果表明：当涂层胶中导电炭黑含量为 15%,导电炭黑粒径为 200nm,涂覆次数为 4 次,黏合剂相对导电炭黑分散体质量分数为40%,焙烘温度为150℃,焙烘时间为 3 min时制备的导电涤纶涂层织物的表面电阻最小, 导电涤纶涂层织物的干摩擦、水洗牢度均可达到 5 级,水洗后涤纶涂层织物的表面电阻变大。     

蚕丝／氮纶包覆丝及其织物的性能研究

测试了蚕丝／氨纶包覆丝及其织物的性能，建立子预测包覆丝拉伸张力的理论模型，理论预测值和实测值有较好的一致性。研究结果表明，采用蚕丝包覆氨纶，能使蚕丝和氨纶这两种纤维在性能上互补，提高真丝织物的服用性能。     

涤纶机织物降噪音性能的研究

文章通过对不同结构的单层、双层及相同结构的不同层数的涤纶机织物的声级衰减量的测试和分析,研究了织物的厚度、组织及面密度对织物降噪音性能的影响。     

蚕丝/涤纶微纤维交织物活性/分散染料一浴法染色

选用对蚕丝沾色低和（或）碱可洗性好的分散染料及Lanasol、Levafix E-A和M型活性染料，可实现蚕丝／涤纶微纤维交织物分散／活性染料一浴二步法染色，织物的染色牢度好、强力高。     

蚕丝蛋白对涤纶织物的亲水整理研究

将碱减量预处理过的涤纶织物放入氯化亚砜密闭气体中,以DMF为催化剂,进行酰氯化反应,得到预处理涤纶织物,然后将预处理织物放入丝胶或丝素水溶液中进行接枝反应,使得丝胶或丝素被整理到涤纶织物的表面。对整理前后织物进行红外光谱、热失重、吸放湿性、断裂强力测试分析,结果表明:采用对织物进行蚕丝蛋白整理可以有效地将丝胶和丝素整理到织物的表面上,丝胶或丝素整理后织物的亲水性和吸湿性有了明显提高,断裂强力较预处理织物没有太大变化,但是热性能有所降低。     

涤纶机织拉毛产品的开发

通过比较针织拉毛产品和机织拉毛产品的工艺流程,讨论了两种织物的特点,叙述了涤纶机织拉毛产品的开发思路,提出了涤纶拉毛织物加工过程中的主要难点和解决这些难点的基本方法.     

聚酯／黏胶机织物的减量处理

减量（WR）处理通常用来降低聚酯纤维的刚性、提高其弹性及柔韧性。处理黏胶需高度谨慎并采用专门技术,因为黏胶织物对强碱更为敏感。WR处理是在较高温度、强碱性条件下进行。研究发现通常对黏胶纤维有损害的WR处理适用于聚酯／黏胶（65／35）织物。结果表明：聚酯／黏胶织物的WR处理中,烧碱的使用能确保织物在色效率与更佳织物手感（即柔软性、弹性及良好光泽）方面的极大优势。WR处理后,织物表面变得更为光滑,织物起毛程度降低。此外,分散染料及活性染料染色前进行WR处理可得到更高的色效率。     

Surface roughness properties of polyester woven fabrics after abrasion

Effect of abrasion on surface roughness properties of textured polyester woven fabrics has been investigated. The effects of weft density, weft yarn filament number, fiber fineness, and weave pattern on surface roughness after abrasion were studied. Surface roughness values of control fabric (not abraded) and abraded fabrics after four different abrasion cycles were discussed according to different constructional parameters. Surface roughness values of fabrics changed according to abrasion cycles and the changes were related to yarn float lengths, yarn densities, yarn fiber fineness, and initial fabric surface roughness. A general overview of the results showed that abrasion eliminated the effect of texture especially at the fabric samples with initially high surface roughness. The surface roughness of fabrics with initially high surface roughness decreased at a greater extent than the ones with low surface roughness after abrasion. Fabrics with high surface roughness were affected more by abrasion and the effect of abrasion on rough surfaces depended on different manners regarding the compactness of woven structures.     

织物组织结构对机织物力学性能的影响

纺织品组织结构对织物的外观和应用性能具有普遍的适用性,织物的最终用途在很大程度上取决于所用的材料及其物理特性。因此,织物的结构参数直接决定了织物的性能。研究了不同组织结构对织物力学性能(包括拉伸性能、撕裂性能和耐磨性能)的影响,主要探讨了平纹、斜纹和方平组织对织物力学性能的影响。     

粘盖涤导湿机织面料的设计

导湿干爽面料是一种新型功能性面料,能使人体的汗液导出并保持皮肤的干爽。根据导湿机织面料的设计原理,对粘盖涤导湿机织面料的设计进行了探讨。     

机织物与非织造布复合材料的制备及性能

选用自制的一种特殊涤纶纤维湿法非织造布和机织物分别为单层材料,采用射流缠结方法将二者复合在一起,试制出了一种新型复合材料,对其力学性能进行了测试和分析,表明复合材料比复合前的机织骨架材料具有更好的拉伸断裂性能、抗撕裂性及耐顶破性能。     

丝/涤短纤维混纺针织纱线的开发

生丝由于细度不匀,含有丝胶,在针织生产中易出现横条疵点,可编织性差,采用丝短纤与涤纶混纺可克服这一缺点。对混纺比为丝／涤80／20的混纺针织纱的开发进行了探讨,提出了切实可行的纺纱工艺,并对纺纱过程中存在的混合难、绕罗拉等问题提出了解决措施。     

基于ABAQUS的涤/棉混纺机织物起球过程有限元仿真

为更好地了解涤/棉混纺机织物起毛起球过程,基于对织物起球过程表面毛羽测量得到的毛羽分布特征,借助PYTHON语言建立了织物及其表面毛羽的几何模型,同时利用有限元软件ABAQUS研究了涤/棉混纺机织物表面毛羽的起球过程,分析了涤纶弹性模量对涤/棉混纺机织物起球过程的起球等级、能量吸收形式的影响规律,并将有限元仿真的起球结果和实测起球结果进行对比分析。结果表明:涤纶弹性模量的增加使得涤/棉混纺机织物的起毛起球等级降低;摩擦耗散能是涤/棉混纺机织物起毛起球过程的主要能量吸收形式,织物起毛起球等级的仿真结果与实验结果的差异在7.4%以内,证明有限元仿真的可行性。     

改善彩色蚕丝织物性能的措施

彩色蚕丝织物具有良好的透气性和吸放湿性,良好的紫外线吸收能力和抗菌能力,但抗皱能力差,强力较低,伸长率较大,容易黄变。针对彩色蚕丝织物的缺点,提出了进一步改善上述性能和提高织物抗皱能力的方法和措施。