NiCrAlY涂层对镍基单晶高温合金氧化性能的影响

采用磁控溅射方法在镍基单晶高温合金基体上沉积NiCrAlY微晶涂层.用热重分析(TGA)、X射线衍射(XRD)、扫描电镜(SEM)等手段研究了镍基单晶高温合金及其NiCrAlY微晶涂层在900～1100℃静止空气中的氧化行为.结果表明,镍基单晶合金及其微晶涂层在900℃表现出相同的增重规律,即经初期快速增重后,两者的氧化增重都变得非常平缓;在1000℃,单晶合金的氧化膜不断剥落,使动力学曲线上下起伏,而微晶涂层经初期快速增重后,动力学曲线趋于平缓;在1100℃,单晶合金由于氧化增重远大于氧化膜剥落所造成的失重,使氧化动力学曲线在整个氧化过程中都呈迅速增长趋势,而微晶涂层的氧化动力学基本符合抛物线规律.单晶合金表面形成含Al2O3、Cr2O3、NiO、CrTaO4和Ni(Al,Cr)2O4尖晶石等的复合氧化膜.施加NiCrAlY微晶涂层后,镍基单晶合金表面形成连续、致密且结合良好的单一氧化物Al2O3,使合金的抗氧化性能明显提高.     

钼及其合金表面硅化物涂层的研究进展

钼及其合金因其具有优异的高温力学性能、高的导电导热系数和低的热膨胀系数而广泛应用于有色冶金、机械、国防和航空航天等领域。然而,由于钼及其合金高温易氧化而限制了其应用范围。MoSi_2因具有优异的高温抗氧化性能,被认为是最适合工程应用的高温涂层材料。本文介绍从MoSi_2的性能特点、制备工艺及MoSi_2涂层的研究进展三个方面综述了近年来国内外钼及其合金的硅化钼涂层防护技术,并对MoSi_2涂层的未来发展方向进行了展望。     

钼及其合金高温抗氧化涂层的制备

介绍了料浆熔烧法制备钼及其合金高温抗氧化涂层的制备工艺、涂层性能、性能检测方法以及应用和发展前景.     

Er0.5Yb1.5Si2O7 环境障涂层高温CMAS 熔盐腐蚀行为研究

硅基陶瓷材料以其优异的性能成为新一代航空发动机热端的候选材料,其在恶劣的服役环境中需要环境 障涂层 ( Environmental Barrier Coating, EBC ) 的保护。以稀土硅酸盐为面层的第三代EBC 是目前研究的热点之 一。采用大气等离子喷涂工艺制备了Er0.5Yb1.5Si2O7 环境障涂层面层样品,研究涂层在钙镁铝硅酸盐(CaO-MgOAl2O3- SiO2, CMAS) 覆盖浓度15 mg/cm2、保温温度1350 ℃、保温时间5 h 的腐蚀条件下的腐蚀行为。研究发现 Er0.5Yb1.5Si2O7 涂层与CMAS 反应后产物为磷灰石相Ca2(Er0.25Yb0.75)8(SiO4)6O2 与Er0.5Yb1.5Si2O7 相,涂层顶部残留 CMAS 熔盐,内部出现反应区和渗透区。     

M5合金的高温低周疲劳性能研究

M5合金是一种适用于高燃耗组件的新型锆合金,主要用作燃料棒包壳、端塞、导向管和定位格架材料。采用棒材试样,对M5合金在375℃温度下进行了5个应变水平的低周疲劳实验,应变比R=-1。对合金的循环响应特征进行了分析,并根据实验数据拟合出了疲劳寿命曲线和方程。用扫描电镜分析了低周疲劳样品的断口,讨论了合金的低周疲劳断裂特征。结果表明,在循环变形过程中,M5合金表现出了明显的硬化、饱和、软化阶段,其中饱和阶段所占比例较大,而硬化和软化阶段所占比例较小;其循环应变寿命特性遵循Coffin-manson关系;疲劳裂纹均起源于试样表面,且存在有多个裂纹源,断裂区布满发达的韧窝,属于明显的韧性断裂。     

铌合金抗高温氧化涂层研究现状及发展趋势

铌合金表面抗高温氧化防护涂层分为耐热合金涂层、贵金属涂层、铝化物涂层以及硅化物涂层等几类。本文综述了各类涂层材料的特点、应用、研发现状以及硅化物涂层的制备技术,对硅化物涂层研究中存在的问题及今后的发展方向进行了分析和探讨。     

激光熔化沉积DZ408镍基高温合金的组织研究

采用激光逐层熔化沉积工艺制备了组织致密、定向性良好的DZ408镍基高温合金单道和多道扫描板状试样,对其沉积态显微组织的定向生长规律及成形机理进行了分析。结果表明,单道板试样表面光洁且形状规则,在沉积方向生成定向性良好的枝晶,而在扫描方向,枝晶受熔池形状影响,生长方向向扫描方向倾斜。多道板试样在垂直于扫描方向处,形成"Z"型组织,而在平行于扫描方向处,由于激光单道扫描结束时间长、冷却周期短,试样边界处沉积层的厚度是内侧沉积层的两倍,且熔池线向下塌陷;金属液由于重力超过表面张力而形成金属液滴,最终在多道板试样表面形成了大量金属瘤。     

Ni-Fe-Cr基高温合金表面AICrN涂层制备及高温氧化性能

采用阴极弧离子镀法在Ni-Fe-Cr基高温合金表面制备了AlCrN涂层.通过电子扫描电镜、能谱仪、X射线衍射仪和X射线光电子谱仪等分析了AlCrN涂层表面和界面的形貌、能谱、物相以及结合能谱,并进行了800和900℃高温氧化实验,研究了AlCrN涂层抗高温氧化性能及其机理.实验结果表明：AlCrN涂层主要成分为Al、Cr和N元素,添加Al元素后表现出较强的AlN择优取向;Al2p峰谱为Al—N和Al—O结合键,Cr2p峰谱为Cr—O和Cr—N结合键,N1s峰谱以Cr—N和Al—N的形态存在,另外含有少量的N—Cr—O和N—Al—O结合键;经过高温氧化后AlCrN涂层表面氧化物为Cr²O³,对高温合金基体有良好的保护作用.     

高温合金表面激光熔铸镍基合金涂层的组织与耐磨性能

研究了高温合金ＧＨ３３表面激光熔铸镍基合金涂层的组织和耐磨性能。结果表明,基材对涂层合金的稀释作用较小;涂层与基材之间形成良好的冶金接合;涂层基体组织为γ－Ｎｉ枝晶,枝晶间为γ－Ｎｉ、Ｍ２３（ＣＢ）６、Ｎｉ３Ｂ、Ｃｒ２Ｂ、ＣｒＢ、ＷＣ等;涂层耐磨性能的平均值较基材提高４倍以上。     

钽钨合金螺套高温抗氧化涂层制备研究

研究了一种能够在高温环境中与钽钨合金配套使用,具有韧性好、与基材结合力强、结构致密、性能优异的钽钨合金高温抗氧化涂层材料及其制备方法,解决了新型超音速发动机研制中钽钨合金螺套高温抗氧化防护涂层制备的难题。使钽钨合金涂层能够广泛应用在航空航天、武器装备、原子能及化工工业领域中类似弹簧螺套这种在安装或工作过程中会产生形变时涂层不会受损的高温结构部件上。     

Effect of Rare Earth on the Corrosion-Resisting Performance of Zinc-Based Alloy Coatings

The corrosion behavior of coatings of pure zinc and Zn-Al,Zn-Al-RE alloys in NaCl solu-tions was studied by salt-spray experiments,even corrosion experiments and electrochemical measurementsof bi-directional polarization curves and a.c.impedance in weak polarization region consistent regularitieswere obtained by these different methods,viz.,the corrosion resistance of Zn could be enhanced by alloying itwith Al,and particularly with Al-RE.The causes of enhancement of corrosion resistance by RE were alsodiscussed.     

Structure and Corrosion Resistance of Microarc Oxidation Coatings on AZ91D Magnesium Alloy

Magnesium alloys are widely used as shells of 3C (computer, mobile phone and consumer electronics) equipments for its impressive mechanical and physical properties, such as low density, good resistance to electromagnetic radiation, suitable for high pressure diecasting and easily recycling, etc. But poor corrosion resistance confines its extensively application. In this paper, protective coatings was successfully prepared on AZ91D magnesium alloys by micro-arc oxidation (MAO) and painting process. Microstructures and phases of MAO coatings were invesgated with scanning electron microscope (SEM) and X-Ray diffractometer. Mechanical properties of MAO coating, such as adhesive force and corrosion resistance, were also tested. Results showed that MAO coatings were a good base for painting process. MAO coatings with paint have good adhesive properties to base metal and excellent corrosion resistance. Micro-arc oxidation with painting process is a good kind of surface treatment to improve the corrosion resistance of mobile phone shell made of AZ91D magnesium alloys.     

Ca对AZ40 M、ZK61 M镁合金铸态组织和力学性能的影响

选择Ca为AZ40M、ZK61M的合金化元素,采用光学显微镜、X射线衍射仪、扫描电镜能谱等手段,开发性试验不同量Ca对镁合金AZ40M、ZK61M铸态组织和铸态力学性能的影响,通过合理控制合金化元素Ca的加入量,使AZ40M、ZK61 M镁合金的抗拉强度、屈服强度和延伸率均获得最佳值;并测试了拉伸性能随Ca含量不同的变化规律,获得镁合金AZ40M和ZK61M铸锭内部组织均匀化。     

稀土和铬对铁基自熔合金涂层耐蚀性的影响

本研究着眼于考察稀土和合金成分对铁基自熔合金涂层的耐蚀性的影响,对不同成分的合金涂层进行了三酸一盐的浸蚀试验。结果表明在硫酸和硝酸溶液中,稀土的添加对合金涂层的耐蚀性有利,但在盐酸和氯化钠溶液中,稀土的添加对合金涂层耐蚀性无益。铬含量高的铁基自熔合金涂层在硝酸溶液中有优良的耐蚀性,但在硫酸和盐酸中的耐蚀性不如铬含量低的铁基自熔合金涂层。文中分析了不同合金在试验中的不同表现的原因,进而为铁基自熔合金的进一步工业应用提供有用的信息。     

Preparation and Corrosion Resistance of Rare Earth Conversion Coatings on AZ91 Magnesium Alloy

Magnesiumalloysarewidelyusedinweaponin dustry,spacenavigationandhavegoodpotentialof applicationanddevelopmentindailycommunication facilitiesduetotheirpropertiesoflightweightandhighstrength[1].Appliedasstructuralmaterials,mag nesiumalloysmayeasilycrackduet…     

冷热循环对Ni─Ti形状记忆合金马氏体相变及形状记忆效应的影响

通过电阻及回复特性的测定,研究了在冷热循环条件下ＮｉＴｉ形状记忆合金记忆效应的稳定性问题。实验结果表明：对不同的ＮｉＴｉ合金固溶处理后,冷热循环对其形状记忆效应均产生影响。但时该合金在再结晶温度下时效处理或退火,冷热循环对其相变温度几乎均不产生影响。同时对产生以上规律的内在机制进行了初步探讨。     

万宁地区铝及铝合金不同距海点的大气腐蚀研究

研究了铝及铝合金在万宁近海大气不同距海点暴露 0 .5a ,1a ,2a的腐蚀行为 ,观察了锈层的形貌、相组成及锈层中合金元素的分布。试验结果表明距离海岸线越近 ,失重率越大 ,腐蚀速度越快 ,说明Clˉ对铝及铝合金有很强的腐蚀作用 ,能加速铝合金的腐蚀。同时在万宁海洋大气环境下 ,纯铝在暴露初期更易腐蚀 ,其腐蚀率是锻铝的 2倍 ,此后随着暴露时间的延长而减缓。     

Mg、Si对Al—Mg2Si3铸造铝合金力学性能和耐蚀性能的影响

研究了合金元素Ｍg、Ｓi对Al-Mg2Si3铸造铝合金性能的影响．在Ｍg含量一定时,随Ｓi含量的增高,合金的抗拉强度逐渐增高;当SI＞3．０％时,其变化趋势减弱,且耐蚀性变差。当Si含量一定时,随Ｍｇ含量的增高,合金强度、塑性均下降,耐蚀性无明显变化。通过恒应变速率拉伸试验（ＣＥＲＴ）试验和徽观组织结构分析,指出了晶界Mg偏析加速应力腐蚀．     

镍钴离子浓度比对化学镀Co-Ni-P合金组织结构和性能的影响

化学镀ＣｏＮｉＰ合金层镀态下为非晶态结构，以层片状沉积，表面有胞状结构。［Ｎｉ２＋］／［Ｃｏ２＋］的比值越大，胞块越大，晶化倾向越大，镀层显微硬度越高，矫顽力越小，矩形比越大。其易磁化方向与膜面垂直。随加热温度升高，化学镀ＣｏＮｉＰ合金发生了晶化转变，析出了第二相，显微硬度在４００℃／１ｈ热处理后达到最高值。     

双级时效对含钪Al-Cu-Li-Zr合金力学性能与抗腐蚀性的影响

采用室温力学性能测试、透射电镜分析和腐蚀实验等方法,研究了双级时效对含钪Al-Cu-Li-Zr合金的力学性能与抗腐蚀性的影响.结果表明,经双级时效处理的合金可获得较佳的强塑性组合,与T8峰时效态合金相比,双级时效态合金可在不降低强度的情况下提高延伸率;T1相是合金的主要沉淀强化相,合金经双级时效处理后,晶内析出的T1相细小弥散且分布均匀,从而改善合金的抗腐蚀性.